CN109674574A - A kind of hot compress sticking dressing and preparation method thereof - Google Patents
A kind of hot compress sticking dressing and preparation method thereof Download PDFInfo
- Publication number
- CN109674574A CN109674574A CN201910038616.0A CN201910038616A CN109674574A CN 109674574 A CN109674574 A CN 109674574A CN 201910038616 A CN201910038616 A CN 201910038616A CN 109674574 A CN109674574 A CN 109674574A
- Authority
- CN
- China
- Prior art keywords
- parts
- dressing
- sodium chloride
- hot compress
- chloride solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of hot compress sticking dressing and preparation method thereof, which includes that following parts by weight raw material are prepared: 2-4 parts of vermiculite, 2-3 parts of active carbon, 1-2 parts of sodium chloride, 45-48 parts of iron powder, 22-28 parts of water；The dressing adjusts raw material composition and ratio by specific aim, makes dressing electrothermal calefactive rate faster, and fever time is longer, the effect of hot compress is more preferable；Meanwhile the method also by sodium chloride solution being added several times in mixture keeps dressing fever time longer to inhibit oxidation reaction speed in dressing, fomentation effect is more preferable, and will not generate high temperature and cause to scald, and use is safer.
Description
Technical field
The present invention relates to health care product fields, and in particular to a kind of hot compress sticking dressing and preparation method thereof.
Background technique
Hot compress is a kind of common method of health-care hospital, and internal disease, internal injury have good medical health effect.Existing skill
Articles in art for hot compress mainly have hot water hot compress bag, electric heating deposited bag, variable phase hot compress bag and hot compress paste etc. several.Wherein hot water
Hot compress bag, soaking time is short, needs to be replaced frequently hot water, and user's trip is not convenient enough；Electric heating deposited bag can only have electricity
It is used under occasion, is not easy to trip and carries hot compress；Although variable phase hot compress bag carrying is more convenient, soaking time also compares
Long, but after its cooling, the umklapp transformation of certain time is needed heat, when trip, does not often have the condition that phase transformation is heated, Chang Wu
Method carries out hot compress use；Hot compress paste provides heat source using dressing, and light, soaking time is long, is a kind of convenient for carrying hot compress
Most widely used hot compress articles.Electrothermal calefactive rate, fever time and the maximum temperature of dressing are by oxidation reaction speed therein
With time effects, and the speed of oxidation reaction is determined by reactant concentration, and the reaction time is determined by reaction-ure mixture, because
This, reactant concentration and reaction-ure mixture during adjustment dressing fever, just can control the fever time of dressing, electrothermal calefactive rate and
Maximum temperature.But dressing used in existing hot compress paste, it is unreasonable due to its raw material and proportion, lead to dressing fever speed
Degree is slow, fever time is short, maximum temperature is high, has seriously affected the fomentation effect of hot compress paste.
Summary of the invention
It is an object of the invention to overcome the shortcomings of that dressing electrothermal calefactive rate is slow in existing hot compress paste, fever time is short, provide
A kind of hot compress sticking dressing and preparation method thereof；The dressing adjusts raw material composition and ratio by specific aim, makes dressing fever speed
It spends faster, and fever time is longer, the effect of hot compress is more preferable, is imitated using the hot compress paste of the dressing with better health care
Fruit.
In order to achieve the above-mentioned object of the invention, the present invention provides a kind of hot compress sticking dressings, including following parts by weight raw material
It is prepared: 2-4 parts of vermiculite, 2-3 parts of active carbon, 1-2 parts of sodium chloride, 45-48 parts of iron powder, 22-28 parts of water.
Wherein, it is preferred that the hot compress sticking dressing is prepared including following parts by weight raw material: 3 parts of vermiculite,
2.25 parts of active carbon, 1 part of sodium chloride, 46.875 parts of iron powder, 25 parts of water.
Wherein, it is preferred that the partial size of the vermiculite is 0.1-1.0mm；Preferred vermiculite partial size has preferably water suction, protects
Wet, heat insulation function keeps the heating continuing time of dressing longer.
Wherein, it is preferred that the partial size of the active carbon is 0.5-2.0mm；Preferred activated carbon particle size, which has, preferably to be inhaled
Water, moisture-keeping functions keep the heating continuing time of dressing longer.
Wherein, it is preferred that the partial size of the iron powder is 0.5-1.0mm；Preferred iron powder partial size has oxidation speed faster
Degree, makes the electrothermal calefactive rate of dressing faster.
In order to achieve the above-mentioned object of the invention, further, the present invention provides a kind of preparation method of hot compress sticking dressing, packets
Include following steps:
(1) it is uniformly mixed vermiculite, active carbon and iron powder to obtain mixture according to the ratio；Sodium chloride is dissolved with water, is obtained
Sodium chloride solution；
(2) it by 2-5 addition mixture of sodium chloride solution average mark, requires to be stirred after sodium chloride solution is added every time
Mixing obtains hot compress sticking dressing after the completion of mixing.
Sodium chloride solution point is added in mixture several times for a kind of preparation method of above-mentioned hot compress sticking dressing, this method, and
It is absorbed by active carbon and vermiculite, so that during dressing fever intermittent the chlorination absorbed can be discharged in active carbon and vermiculite
Sodium solution is suppressed oxidation reaction speed in dressing, keeps dressing fever time longer, and fomentation effect is more preferable, and will not produce
Raw high temperature causes to scald, and use is safer.
Wherein, it is preferred that in step (2), sodium chloride solution is equally divided into 3 addition mixtures.
Wherein, it is preferred that the speed stirred in step (2) is 100-300r/min, time 2-5mn；It is deposited by preferred
More evenly, active carbon and vermiculite are more preferable to the assimilation effect of sodium chloride solution, and the heating property of dressing is more preferable for material mixing.
Compared with prior art, beneficial effects of the present invention:
1, dressing of the present invention adjusts raw material composition and ratio by specific aim, makes dressing electrothermal calefactive rate faster, and fever time
Longer, the effect of hot compress is more preferable.
2, the dressing that preparation method of the present invention is prepared can be such that oxidation reaction speed is controlled, and make dressing fever time
Longer, fomentation effect is more preferable, and will not generate high temperature and cause to scald, and use is safer.
3, preparation method of the present invention is simple, reliable, is suitble to the large-scale production of dressing.
Specific embodiment
Below with reference to test example and specific embodiment, the present invention is described in further detail.But this should not be understood
It is all that this is belonged to based on the technology that the content of present invention is realized for the scope of the above subject matter of the present invention is limited to the following embodiments
The range of invention.
Embodiment 1
(1) it is uniformly mixed 3 parts of vermiculite, 2.25 parts of active carbon and 46.875 parts of iron powder to obtain mixture；By 1 part
Sodium chloride dissolved with 25 parts of water, obtain sodium chloride solution；
(2) sodium chloride solution is averagely added three times in mixture, is added after sodium chloride solution all in the speed of 200r/min every time
Mixing 3min is stirred under degree, sodium chloride solution obtains hot compress sticking dressing after the completion of mixing with mixture.
Embodiment 2
(1) it is uniformly mixed 2 parts of vermiculite, 3 parts of active carbon and 45 parts of iron powder to obtain mixture；By 2 parts of chlorination
Sodium is dissolved with 28 parts of water, obtains sodium chloride solution；
(2) it by 2 addition mixtures of sodium chloride solution average mark, is added after sodium chloride solution all 100r/min's every time
Mixing 5min is stirred under speed, sodium chloride solution obtains hot compress sticking dressing after the completion of mixing with mixture.
Embodiment 3
(1) it is uniformly mixed 4 parts of vermiculite, 2 parts of active carbon and 48 parts of iron powder to obtain mixture；By 1 part of chlorination
Sodium is dissolved with 22 parts of water, obtains sodium chloride solution；
(2) it by 5 addition mixtures of sodium chloride solution average mark, is added after sodium chloride solution all 300r/min's every time
Mixing 2min is stirred under speed, sodium chloride solution obtains hot compress sticking dressing after the completion of mixing with mixture.
Comparative example 1
(1) it is uniformly mixed 3 parts of vermiculite, 4 parts of active carbon and 46.875 parts of iron powder to obtain mixture；By 1 part
Sodium chloride is dissolved with 25 parts of water, obtains sodium chloride solution；
(2) sodium chloride solution is averagely added three times in mixture, is added after sodium chloride solution all in the speed of 200r/min every time
Mixing 3min is stirred under degree, sodium chloride solution obtains hot compress sticking dressing after the completion of mixing with mixture.
Comparative example 2
(1) it is uniformly mixed 3 parts of vermiculite, 1 part of active carbon and 46.875 parts of iron powder to obtain mixture；By 1 part
Sodium chloride is dissolved with 25 parts of water, obtains sodium chloride solution；
(2) sodium chloride solution is averagely added three times in mixture, is added after sodium chloride solution all in the speed of 200r/min every time
Mixing 3min is stirred under degree, sodium chloride solution obtains hot compress sticking dressing after the completion of mixing with mixture.
Comparative example 3
(1) it is uniformly mixed 3 parts of vermiculite, 2.25 parts of active carbon and 46.875 parts of iron powder to obtain mixture；By 1 part
Sodium chloride dissolved with 25 parts of water, obtain sodium chloride solution；
(2) sodium chloride solution is added at one time in mixture, is carried out under the speed of 200r/min after sodium chloride solution is added
It is stirred 3min, sodium chloride solution obtains hot compress sticking dressing after the completion of mixing with mixture.
Comparative example 4
(1) it is uniformly mixed 3 parts of vermiculite, 2.25 parts of active carbon and 46.875 parts of iron powder to obtain mixture；By 1 part
Sodium chloride dissolved with 25 parts of water, obtain sodium chloride solution；
(2) it by 6 addition mixtures of sodium chloride solution average mark, is added after sodium chloride solution all in the speed of 200r/min every time
Mixing 3min is stirred under degree, sodium chloride solution obtains hot compress sticking dressing after the completion of mixing with mixture.
Comparative example 5
Existing hot compress sticking dressing: mixed by following composition: iron powder 55%, vermiculite 10%, active carbon 5%, natural mineral salt 4%,
Drinking water 20%.
Identical hot compress paste is made in above-described embodiment 1-3 and comparative example the 1-5 dressing being prepared, in identical experiment item
Performance detection is carried out under part (temperature is 25 DEG C) (when hot compress paste temperature is greater than 35 DEG C, to be denoted as and start to generate heat；When temperature is lower than 35
DEG C, being denoted as fever terminates；When temperature is more than 47 DEG C, human body will generate cusalgia sense), record experimental result is as follows:
| Serial number | Start fever time (s) | Heating continuing time (h) | It generates heat maximum temperature (DEG C) |
| Embodiment 1 | 187 | 14.5 | 43.6 |
| Embodiment 2 | 196 | 14.3 | 44.2 |
| Embodiment 3 | 203 | 14.2 | 43.4 |
| Comparative example 1 | 286 | 16.4 | 39.8 |
| Comparative example 2 | 153 | 11.7 | 51.3 |
| Comparative example 3 | 178 | 12.5 | 48.1 |
| Comparative example 4 | 237 | 15.8 | 38.9 |
| Comparative example 5 | 216 | 10.8 | 53.7 |
According to above-mentioned experimental result: dressing of the present invention is fast with electrothermal calefactive rate in embodiment 1-3, and fever time is long, fever
The advantages of moderate temperature, can significantly improve the effect of hot compress；In the raw material ratio of comparative example 1, the dosage of active carbon is more than this
The regulation of invention, causes oxidation reaction to slow, although extending heating continuing time, starts fever time and significantly prolongs
Long, fever maximum temperature is significantly low, and the effect of hot compress is deteriorated；In the raw material ratio of comparative example 2, the dosage of active carbon is less than this
The regulation of invention causes oxidation reaction speed to be accelerated, and shortens although starting fever time, and heating continuing time significantly shortens,
Fever maximum temperature significantly improves, and may cause burning for human skin；In the preparation method of comparative example 3, sodium chloride solution one
Secondary property is added, and causes the speed of oxidation reaction during generating heat in dressing that cannot inhibit, to cause heating continuing time aobvious
It writes and shortens, fever maximum temperature significantly improves；In the preparation method of comparative example 4, the number that sodium chloride solution is added is more than this hair
Bright regulation causes to inhibit excessively the oxidation reaction speed during generating heat in dressing, although extending heating continuing time,
But start fever time significantly to extend, fever maximum temperature is significantly low, and the effect of hot compress is deteriorated；Embodiment 4 is existing dressing,
Its heating effect is significantly worse than the dressing in 1-3 of the embodiment of the present invention, i.e., dressing of the present invention, heating property is significantly better than existing
Casting product.
Claims (8)
1. a kind of hot compress sticking dressing, which is characterized in that be prepared including following parts by weight raw material: 2-4 parts of vermiculite, 2-3
Active carbon, 1-2 parts of the sodium chloride, 45-48 parts of iron powder, 22-28 parts of water of part.
2. dressing according to claim 1, which is characterized in that be prepared including following parts by weight raw material: 3 parts of leech
Stone, 2.25 parts of active carbon, 1 part of sodium chloride, 46.875 parts of iron powder, 25 parts of water.
3. dressing according to claim 1, which is characterized in that the partial size of the vermiculite is 0.1-1.0mm.
4. dressing according to claim 1, which is characterized in that the partial size of the active carbon is 0.5-2.0mm.
5. dressing according to claim 1, which is characterized in that the partial size of the iron powder is 0.5-1.0mm.
6. a kind of preparation method of hot compress sticking dressing, which comprises the following steps:
(1) it is uniformly mixed vermiculite, active carbon and iron powder to obtain mixture according to the ratio；Sodium chloride is dissolved with water, is obtained
Sodium chloride solution；
(2) it by 2-5 addition mixture of sodium chloride solution average mark, requires to be stirred after sodium chloride solution is added every time
Mixing obtains hot compress sticking dressing after the completion of mixing.
7. preparation method according to claim 6, which is characterized in that sodium chloride solution is equally divided into 3 addition mixtures
In.
8. preparation method according to claim 6, which is characterized in that the speed stirred in step (2) is 100-300r/
Min, time 2-5min.