CN109666386A - 一种醇酸树脂复合外墙涂料 - Google Patents
一种醇酸树脂复合外墙涂料 Download PDFInfo
- Publication number
- CN109666386A CN109666386A CN201710955317.4A CN201710955317A CN109666386A CN 109666386 A CN109666386 A CN 109666386A CN 201710955317 A CN201710955317 A CN 201710955317A CN 109666386 A CN109666386 A CN 109666386A
- Authority
- CN
- China
- Prior art keywords
- parts
- alkyd resin
- exterior wall
- resin composite
- wall coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于建筑材料领域,提出一种醇酸树脂复合外墙涂料,原料按重量份包括:醇酸树脂40‑50份,丙酮5‑10份,40%浓度硫酸铜溶液10‑15份,酚醛树脂5‑10份,邻苯二甲酸二(2‑乙基己)酯3‑5份,双氧水3‑5份;干燥时间快,有利于提高外墙涂料的施工效率;耐水耐污性能力强,自洁能力优异;韧性好,耐高低温性能佳,长期使用无起泡、脱落现象,可大规模推广应用。
Description
技术领域
本发明属于建筑材料领域,具体涉及一种醇酸树脂复合外墙涂料。
背景技术
外墙涂料作为建筑外围护结构表皮,要求有耐水、保色、耐污染、 耐老化以及良好的附着力,同时还应具有抗冻融性好、成膜温度低的特点。中国涂料产业在下游产业的推动下日益壮大,而作为其中一个分支的建筑涂料,也得到了长足的发展。随着人性化理念的普及,及新型和谐社会的构成,设计一种干燥时间短及耐水性优异的外墙涂料是非常必要的。
发明内容
本发明的目的在于提高外墙涂料的施工效率及耐水耐污性,提出一种醇酸树脂复合外墙涂料。
技术方案
为实现上述发明目的,本发明提供了以下技术方案:
一种醇酸树脂复合外墙涂料,原料按重量份包括:醇酸树脂40-50份,丙酮5-10份,40%浓度硫酸铜溶液10-15份,酚醛树脂5-10份,邻苯二甲酸二(2-乙基己)酯3-5份,双氧水3-5份。
本发明的有益作用在于:
1.干燥时间快,有利于提高外墙涂料的施工效率。
2.耐水耐污性能力强,自洁能力优异。
3.韧性好,耐高低温性能佳,长期使用无起泡、脱落现象,可大规模推广应用。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白易懂,下面结合具体实施例对本发明进一步详细说明,但本发明的内容完全不局限于此。
实施例1
一种醇酸树脂复合外墙涂料,原料按重量份包括:醇酸树脂40Kg,丙酮5Kg,40%浓度硫酸铜溶液11Kg,酚醛树脂5Kg,邻苯二甲酸二(2-乙基己)酯3Kg,双氧水3Kg。
实施例2
一种醇酸树脂复合外墙涂料,原料按重量份包括:醇酸树脂44Kg,丙酮7Kg,40%浓度硫酸铜溶液13Kg,酚醛树脂7Kg,邻苯二甲酸二(2-乙基己)酯3Kg,双氧水4Kg。
实施例3
一种醇酸树脂复合外墙涂料,原料按重量份包括:醇酸树脂49Kg,丙酮9Kg,40%浓度硫酸铜溶液14Kg,酚醛树脂9Kg,邻苯二甲酸二(2-乙基己)酯5Kg,双氧水5Kg。
以上所述,仅为本发明较佳的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本技术领域的技术人员在本发明揭露的技术范围内,根据本发明的技术方案及其发明构思加以等同替换或改变,都应涵盖在本发明的保护范围之内。
Claims (1)
1.一种醇酸树脂复合外墙涂料,其特征在于,原料按重量份包括:醇酸树脂40-50份,丙酮5-10份,40%浓度硫酸铜溶液10-15份,酚醛树脂5-10份,邻苯二甲酸二(2-乙基己)酯3-5份,双氧水3-5份。