CN104529291A - 一种砌筑砂浆及其制备方法 - Google Patents

一种砌筑砂浆及其制备方法 Download PDF

Info

Publication number
CN104529291A
CN104529291A CN201410793346.1A CN201410793346A CN104529291A CN 104529291 A CN104529291 A CN 104529291A CN 201410793346 A CN201410793346 A CN 201410793346A CN 104529291 A CN104529291 A CN 104529291A
Authority
CN
China
Prior art keywords
parts
mixing
mortar
water
minute
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410793346.1A
Other languages
English (en)
Inventor
魏超产
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410793346.1A priority Critical patent/CN104529291A/zh
Publication of CN104529291A publication Critical patent/CN104529291A/zh
Pending legal-status Critical Current

Abstract

一种砌筑砂浆,由下列重量份的原料制成：氯化钾2-3、硫酸铝钾2-4、三异丙醇胺2-3、炉渣80-90、炭化稻壳10-15、甘蔗渣15-20、活性炭10-15、四氯化钛2-3、单硬脂酸甘油酯1-2、柠檬酸钙2-3、水适量、助剂20-25、水泥150-170、砂220-240、漂珠10-15；本发明砂浆易和性好，硬化后具有良好的物理力学性能和耐水性,以及较高的韧性，适用于多种场合的砌筑；通过使用本发明助剂，提高了砂浆的抗压、抗折强度，改善了和易性、抗流挂性、触变性和防沉降性。

Description

一种砌筑砂浆及其制备方法
技术领域
本发明属于建筑材料领域，特别涉及一种砌筑砂浆及其制备方法。
背景技术
砂浆为建筑用普通材料，属于建筑施工中的必备材料。根据性能划分，砂浆分为很多种，有结合砂浆、嵌缝砂浆、保温砂浆等；按用途分为砌筑砂浆、抹面砂浆（包括装饰砂浆、防水砂浆）、粘结砂浆等。
目前砂浆的性能品质不一，影响着使用。具体来讲影响砂浆性能的因素包括新拌砂浆的和易性、流动性、保水性，还有就是硬化砂浆的强度。需要研究新的砂浆，使其具有优异的施工性和加工性、抗流挂性、触变性、防沉降性、贮存稳定性、改善泵送性和剪切稀化性，还需要寻找新的材料，以提高其使用性能和强度，以及降低综合成本。
发明内容
本发明的目的在于提供一种砌筑砂浆及其制备方法，该砂浆易和性好，硬化后具有良好的物理力学性能和耐水性,以及较高的韧性。
本发明的技术方案如下：
一种砌筑砂浆,其特征在于由下列重量份的原料制成：氯化钾2-3、硫酸铝钾2-4、三异丙醇胺2-3、炉渣80-90、炭化稻壳10-15、甘蔗渣15-20、活性炭10-15、四氯化钛2-3、单硬脂酸甘油酯1-2、柠檬酸钙2-3、水适量、助剂20-25、水泥150-170、砂220-240、漂珠10-15；
所述助剂由下列重量份的原料制成：木炭粉末1-2、虫胶树脂1-2、羧甲基纤维素2-3、乙醇3-5、不锈钢纤维6-7、双季戊四醇六丙烯酸酯4-5、E-12环氧树脂2-3、环氧丙烯酸酯3-4、硼酸锌1-1.4、膨润土3-4、10-15%氢氧化钠5-7、三聚磷酸钠1-1.5、硫酸钙晶须3-4、烟片胶1-2、196不饱和聚酯树脂3-4、亚硫酸钙2-3、异佛尔酮0.4-0.5、油酸钠0.2-0.3、过硫酸铵0.1-0.2、过硫酸钾0.1-0.2、水17-20；制备方法为：将膨润土放入煅烧炉中，在670-700℃下煅烧3-4小时，取出，放入10-15%氢氧化钠溶液中研磨至20-40μm浆料，调浆料PH值为中性，喷雾干燥得粉末；将水、油酸钠混合，加入羧甲基纤维素、乙醇、双季戊四醇六丙烯酸酯、E-12环氧树脂、环氧丙烯酸酯、196不饱和聚酯树，搅拌均匀，加热至70-80℃，加入过硫酸钾搅拌反应20-30分钟，再加入所述粉末以及其他剩余成分，加热至80-90℃，搅拌反应30-40分钟，即得。
所述的砌筑砂浆的制备方法，其特征在于包括以下步骤：
（1）将炉渣、三异丙醇胺混合，粉碎成140-180目颗粒；
（2）将氯化钾、硫酸铝钾、四氯化钛、单硬脂酸甘油酯、柠檬酸钙、水混合，搅拌均匀得到浆料；
（3）将助剂、、炭化稻壳、甘蔗渣、活性炭混合，分散研磨20-30分钟，得到混合物料；
（4）将其他剩余成分与第（1）步、第（2）步、第（3）步得到的物料混合均匀，搅拌反应10-15分钟，即得。
本发明的有益效果
本发明砂浆易和性好，硬化后具有良好的物理力学性能和耐水性,以及较高的韧性，适用于多种场合的砌筑；通过使用本发明助剂，提高了砂浆的抗压、抗折强度，改善了和易性、抗流挂性、触变性和防沉降性。
具体实施方式
一种砌筑砂浆,由下列重量份(公斤)的原料制成：氯化钾2.5、硫酸铝钾3、三异丙醇胺2.5、炉渣85、炭化稻壳13、甘蔗渣17、活性炭13、四氯化钛2.5、单硬脂酸甘油酯1.5、柠檬酸钙2.5、水适量、助剂23、水泥160、砂230、漂珠13；
所述助剂由下列重量份（公斤）的原料制成：木炭粉末1.5、虫胶树脂1.5、羧甲基纤维素2.5、乙醇4、不锈钢纤维6.5、双季戊四醇六丙烯酸酯4.5、E-12环氧树脂2.5、环氧丙烯酸酯3.5、硼酸锌1.2、膨润土3.5、15%氢氧化钠6、三聚磷酸钠1.3、硫酸钙晶须3.5、烟片胶1.5、196不饱和聚酯树脂3.5、亚硫酸钙2.5、异佛尔酮0.5、油酸钠0.3、过硫酸铵0.1、过硫酸钾0.2、水19；制备方法为：将膨润土放入煅烧炉中，在690℃下煅烧3.5小时，取出，放入15%氢氧化钠溶液中研磨至30μm浆料，调浆料PH值为中性，喷雾干燥得粉末；将水、油酸钠混合，加入羧甲基纤维素、乙醇、双季戊四醇六丙烯酸酯、E-12环氧树脂、环氧丙烯酸酯、196不饱和聚酯树，搅拌均匀，加热至75℃，加入过硫酸钾搅拌反应25分钟，再加入所述粉末以及其他剩余成分，加热至85℃，搅拌反应35分钟，即得。
所述的砌筑砂浆的制备方法，包括以下步骤：
（1）将炉渣、三异丙醇胺混合，粉碎成170目颗粒；
（2）将氯化钾、硫酸铝钾、四氯化钛、单硬脂酸甘油酯、柠檬酸钙、水混合，搅拌均匀得到浆料；
（3）将助剂、、炭化稻壳、甘蔗渣、活性炭混合，分散研磨25分钟，得到混合物料；
（4）将其他剩余成分与第（1）步、第（2）步、第（3）步得到的物料混合均匀，搅拌反应14分钟，即得。
实验数据：
该实施例的砂浆28d的抗压强度为47MPa，抗折强度 15MPa，吸水率1.9%。

Claims (2)

1.一种砌筑砂浆,其特征在于由下列重量份的原料制成：氯化钾2-3、硫酸铝钾2-4、三异丙醇胺2-3、炉渣80-90、炭化稻壳10-15、甘蔗渣15-20、活性炭10-15、四氯化钛2-3、单硬脂酸甘油酯1-2、柠檬酸钙2-3、水适量、助剂20-25、水泥150-170、砂220-240、漂珠10-15；
所述助剂由下列重量份的原料制成：木炭粉末1-2、虫胶树脂1-2、羧甲基纤维素2-3、乙醇3-5、不锈钢纤维6-7、双季戊四醇六丙烯酸酯4-5、E-12环氧树脂2-3、环氧丙烯酸酯3-4、硼酸锌1-1.4、膨润土3-4、10-15%氢氧化钠5-7、三聚磷酸钠1-1.5、硫酸钙晶须3-4、烟片胶1-2、196不饱和聚酯树脂3-4、亚硫酸钙2-3、异佛尔酮0.4-0.5、油酸钠0.2-0.3、过硫酸铵0.1-0.2、过硫酸钾0.1-0.2、水17-20；制备方法为：将膨润土放入煅烧炉中，在670-700℃下煅烧3-4小时，取出，放入10-15%氢氧化钠溶液中研磨至20-40μm浆料，调浆料PH值为中性，喷雾干燥得粉末；将水、油酸钠混合，加入羧甲基纤维素、乙醇、双季戊四醇六丙烯酸酯、E-12环氧树脂、环氧丙烯酸酯、196不饱和聚酯树，搅拌均匀，加热至70-80℃，加入过硫酸钾搅拌反应20-30分钟，再加入所述粉末以及其他剩余成分，加热至80-90℃，搅拌反应30-40分钟，即得。
2.根据权利要求1所述的砌筑砂浆的制备方法，其特征在于包括以下步骤：
（1）将炉渣、三异丙醇胺混合，粉碎成140-180目颗粒；
（2）将氯化钾、硫酸铝钾、四氯化钛、单硬脂酸甘油酯、柠檬酸钙、水混合，搅拌均匀得到浆料；
（3）将助剂、、炭化稻壳、甘蔗渣、活性炭混合，分散研磨20-30分钟，得到混合物料；
（4）将其他剩余成分与第（1）步、第（2）步、第（3）步得到的物料混合均匀，搅拌反应10-15分钟，即得。
CN201410793346.1A 2014-12-20 2014-12-20 一种砌筑砂浆及其制备方法 Pending CN104529291A (zh)