CN109665765A - 透水混凝土 - Google Patents
透水混凝土 Download PDFInfo
- Publication number
- CN109665765A CN109665765A CN201811205596.3A CN201811205596A CN109665765A CN 109665765 A CN109665765 A CN 109665765A CN 201811205596 A CN201811205596 A CN 201811205596A CN 109665765 A CN109665765 A CN 109665765A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- pervious concrete
- cement
- binder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种透水混凝土，包括：水泥，中砂，骨料，增强纤维，粘结剂，外加剂和水；所述各组份质量配比如下：水泥200‑300份；中砂100‑200份；骨料50‑150份；增强纤维10‑20份，粘结剂5‑10份，外加剂3‑8份，水100‑200份；所述外加剂包括减水剂和稳定剂；所述粘结剂为苯乙烯‑丁二烯类共聚物，所述稳定剂采用海藻酸钠。本发明能够兼顾透水性，强度，抗震性和抗压性，作为河道或水库的生态堤坝建材。
Description
技术领域
本发明属于建筑材料技术领域，具体来说涉及一种透水混凝土。
背景技术
混凝土通常是指用水泥作胶凝材料，以砂、石作集料；与水按一定比例配合，经搅拌而得的水泥混凝土，被广泛应用于土木工程。随着城市绿色环保理念的推进，城市建设规划中首次提出了将绿色植被种植到河道或水库的堤坝上的生态堤坝理念。但是传统的混凝土不具备透水性能，无法通过微量持续的渗析河水或水库水浇灌种植在生态堤坝上的绿色植被，因此无法用来作为生态河提的建筑材料。不符合当今倡导的绿色城市化理念。随着技术的进步目前市场上已经开始出现具备透水性能的透水混凝土。但是现有技术中的透水性混凝土主要应用于城市透水道路的铺设，其强度和抗压能力尚不足以满足作为制作堤坝材料的要求。因此，如何开发出一种新型的透水混凝土，能够在保证孔隙率和渗水性的基础上具备较佳的强度和抗压性能，可以作为河道和水库的生态堤坝的建材，是本领域技术人员需要研究的方向。
发明内容
本发明提供了一种透水混凝土，能够兼顾透水性，强度，抗震性和抗压性，作为河道或水库的生态堤坝建材。
其采用的技术方案如下：
一种透水混凝土，包括：水泥，中砂，骨料，增强纤维，粘结剂，外加剂和水；所述各组份质量配比如下：水泥200-300份；中砂100-200份；骨料50-150份；增强纤维10-20份，粘结剂5-10份，外加剂3-8份，水100-200份；所述外加剂包括减水剂和稳定剂；所述粘结剂为苯乙烯-丁二烯类共聚物，所述稳定剂采用海藻酸钠。
采用这种技术方案：通过在配方中添加增强纤维提高透水混凝土的整体抗震性能，而在配方中添加海藻酸钠作为稳定剂乃是因为海藻酸钠是一种具有羟基的粘性高分子化合物。其能够对苯乙烯-丁二烯类共聚物起到良好的协助作用，大幅提高混凝土内部的作用力和承压性能。
更优选的是，上述透水混凝土中：所述减水剂由磺酸钠、氢氧化钾、硝酸钙、高锰酸钾、膨润土和硅粉构成；且各组份质量配比如下：磺酸钠8～13份、氢氧化钾15～50份、硝酸钙3～7份、高锰酸钾1～3份、膨润土40～50份、硅粉1～3份。
进一步优选的是，上述透水混凝土中：所述骨料的粒径为3-12mm。
更进一步优选的是，上述透水混凝土中：所述中砂的细度模数大于2.5。
再进一步优选的是，上述透水混凝土中：所述水泥采用P.042.5等级的火山灰质硅酸盐水泥。
再进一步优选的是，上述透水混凝土中：水灰比为0.44。
与现有技术相比，本发明提供的透水混凝土，不但具备优秀的透水性能，且具备良好的强度，抗震性和抗压性，能够作为河道和水库的生态堤坝的建材。
具体实施方式
为了更清楚地说明本发明的技术方案，下面将对本发明作进一步描述。
实施例1：
一种透水混凝土，包括：水泥，中砂，骨料，增强纤维，粘结剂，外加剂和水；所述各组份质量配比如下：水泥150份；中砂150份；骨料100份；增强纤维15份；粘结剂10份，外加剂5份，水150份；所述外加剂包括减水剂和稳定剂；所述粘结剂为苯乙烯-丁二烯类共聚物，所述骨料的粒径为3-12mm。中砂的细度模数控制在2.6-2.7之间。水泥采用P.042.5 等级的火山灰质硅酸盐水泥。水灰比为0.44。所述稳定剂采用海藻酸钠。所述减水剂采用聚羟酸减水剂。
实施例2：
一种透水混凝土，包括：水泥，中砂，骨料，增强纤维，粘结剂，外加剂和水；所述各组份质量配比如下：水泥150份；中砂150份；骨料100份；增强纤维15份；粘结剂10份，外加剂5份，水150份；所述外加剂包括减水剂和稳定剂；所述粘结剂为苯乙烯-丁二烯类共聚物，所述骨料的粒径为3-12mm。中砂的细度模数控制在2.6-2.7之间。水泥采用P.042.5 等级的火山灰质硅酸盐水泥。水灰比为0.44。所述稳定剂采用海藻酸钠。所述减水剂由磺酸钠、氢氧化钾、硝酸钙、高锰酸钾、膨润土和硅粉构成；且各组份质量配比如下：磺酸钠 11份、氢氧化钾30份、硝酸钙5份、高锰酸钾2份、膨润土45份、硅粉2份。
实施例3：
一种透水混凝土，包括：水泥，中砂，骨料，增强纤维，粘结剂，外加剂和水；所述各组份质量配比如下：水泥200份；中砂100份；骨料50份；增强纤维10份；粘结剂5份，外加剂3份，水100份；所述外加剂包括减水剂和稳定剂；所述粘结剂为苯乙烯-丁二烯类共聚物，所述骨料的粒径为3-12mm。中砂的细度模数控制在2.6-2.7之间。水泥采用P.042.5等级的火山灰质硅酸盐水泥。水灰比为0.44。所述稳定剂采用海藻酸钠。所述减水剂由磺酸钠、氢氧化钾、硝酸钙、高锰酸钾、膨润土和硅粉构成；且各组份质量配比如下：磺酸钠8份、氢氧化钾15份、硝酸钙3份、高锰酸钾1份、膨润土40份、硅粉1份。
实施例4：
一种透水混凝土，包括：水泥，中砂，骨料，增强纤维，粘结剂，外加剂和水；所述各组份质量配比如下：水泥300份；中砂200份；骨料150份；增强纤维20份；粘结剂10份，外加剂8份，水200份；所述外加剂包括减水剂和稳定剂；所述粘结剂为苯乙烯-丁二烯类共聚物，所述骨料的粒径为3-12mm。中砂的细度模数控制在2.6-2.7之间。水泥采用P.042.5 等级的火山灰质硅酸盐水泥。水灰比为0.44。所述稳定剂采用海藻酸钠。所述减水剂由磺酸钠、氢氧化钾、硝酸钙、高锰酸钾、膨润土和硅粉构成；且各组份质量配比如下：磺酸钠 13份、氢氧化钾50份、硝酸钙7份、高锰酸钾3份、膨润土50份、硅粉3份。
对比例：采用现有市场上的用于铺设路面的普通透水混凝土。
各项实施例与对比例的实验检测结果如下：
| 透水系数/cm/s | 孔隙率％ | 抗压强度/MPA | 抗折强度/MPA | |
| 对比例1 | 0.180 | 15.8％ | 15.5 | 32.3 |
| 实施例1 | 0.176 | 15.2％ | 18.6 | 35.6 |
| 实施例2 | 0.175 | 15.5％ | 20.5 | 41.3 |
| 实施例3 | 0.182 | 14.9％ | 19.7 | 40.8 |
| 实施例4 | 0.177 | 16.2％ | 23.3 | 39.8 |
由上述表格可见：本发明各实施例提供的透水混凝土在保障了渗水率的基础上，相比现有技术中的透水混凝土具有更佳的强度和抗震、抗压性能。
以上所述，仅为本发明的具体实施例，但本发明的保护范围并不局限于此，任何熟悉本领域技术的技术人员在本发明公开的技术范围内，可轻易想到的变化或替换，都应涵盖在本发明的保护范围之内。本发明的保护范围以权利要求书的保护范围为准。
Claims (6)
1.一种透水混凝土，其特征在于包括：水泥，中砂，骨料，增强纤维，粘结剂，外加剂和水；所述各组份质量配比如下：水泥200-300份；中砂100-200份；骨料50-150份；增强纤维10-20份，粘结剂5-10份，外加剂3-8份，水100-200份；所述外加剂包括减水剂和稳定剂；所述粘结剂为苯乙烯-丁二烯类共聚物，所述稳定剂采用海藻酸钠。
2.如权利要求1所述透水混凝土，其特征在于：所述减水剂由磺酸钠、氢氧化钾、硝酸钙、高锰酸钾、膨润土和硅粉构成；且各组份质量配比如下：磺酸钠8～13份、氢氧化钾15～50份、硝酸钙3～7份、高锰酸钾1～3份、膨润土40～50份、硅粉1～3份。
3.如权利要求2所述透水混凝土，其特征在于：所述骨料的粒径为3-12mm。
4.如权利要求3所述透水混凝土：所述中砂的细度模数大于2.5。
5.如权利要求4所述透水混凝土，其特征在于：所述水泥采用P.042.5等级的火山灰质硅酸盐水泥。
6.如权利要求5所述透水混凝土，其特征在于：水灰比为0.44。