CN109651903A - A kind of polytetrafluoroethylmodified modified chemical-resistant reagent special anticorrosive coating - Google Patents
A kind of polytetrafluoroethylmodified modified chemical-resistant reagent special anticorrosive coating Download PDFInfo
- Publication number
- CN109651903A CN109651903A CN201811596516.1A CN201811596516A CN109651903A CN 109651903 A CN109651903 A CN 109651903A CN 201811596516 A CN201811596516 A CN 201811596516A CN 109651903 A CN109651903 A CN 109651903A
- Authority
- CN
- China
- Prior art keywords
- anticorrosive coating
- reagent special
- modified chemical
- resistant reagent
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention discloses a kind of polytetrafluoroethylmodified modified chemical-resistant reagent special anticorrosive coating, belongs to special coating technical field.The coating belongs to bicomponent system, including the component based on mass percentage: fluorocarbon resin 40-60, dispersing agent 0-1, defoaming agent 0-1, substrate wetting agents 0-0.5, levelling agent 0-0.5, auxiliary rheological agents 0-1, hydrophobic auxiliary agent 0-0.2, polytetrafluorethylepowder powder 5-15, titanium dioxide 3-10, barium sulfate 2-5, mica powder 5-15, carbon black 0-5, ceramic composition 10-30, plasticizer 0.5-2, the mixed solvent of suitable drier and surplus, curing agent are aliphatic polymeric isocyanate.Wherein mixed solvent is dimethylbenzene: butyl acetate: glycol methyl ether acetate=5: 3: 2, the coating can be using construction technologies such as spraying, brushing, roller coating, compact in paint film, plentiful, glossiness is high, chemical resistance is good, can using with desulfurizing tower, chimney and desulfurating dust-removing equipment, antiseptic property is excellent.
Description
Technical field
The invention belongs to special coating technical fields, and in particular to a kind of polytetrafluoroethylmodified modified chemical-resistant reagent special type is anti-
The preparation method of rotten coating.
Technical background
The development of chemical industry has become an important indicator for influencing national economy, especially with electric power, petroleum, chemical industry
Etc. industries, each enterprise be owned by a considerable amount of chemical reagent, especially acid, the storage tank of alkali equal solvent, storage tank and transport set
Standby, enterprise requires to put into a large amount of human and material resources, financial resources every year as equipment progress care and maintenance.
Special anticorrosive coating due to it is at low cost, easy for construction, have good decorative effect, by more and more
The favor of enterprise, a large amount of chemically-resistant solvent sapecial coating in the market, mainly using epoxy resin or modified epoxy as at
Film object, the infiltration that can withstand most of chemical solvents cause to corrode to equipment, and have good adhesive force and application property
Can, have become the first choice of most of chemically-resistant coatings volatile organic compounds, but due to epoxy resin or modified epoxy weatherability compared with
Difference generally cannot function as outdoor equipment finishing coat, and service life is shorter in oxidisability chemical solvent, so, exploitation is new
The special anticorrosive coating of type can just better meet the demand in market.
Polytetrafluoroethylene (PTFE) (PTFE) is high-molecular compound made of tetrafluoroethene is aggregated, has the title of King, has
The characteristics such as excellent chemical stability, corrosion resistance, high lubrication and non-stickiness.
The invention patent is drawn on fluororesin main chain in the method for tetrafluoroethylene monomer and functional form monomer copolymerization
The monomer for entering part functional group reduces the crystalline modified polytetrafluoroethylresin resin of original fluororesin as main film forming matter
Matter adds the bi-component air-curing coatings of the compositions such as wear-resistant acid and alkali-resistance filler, polytetrafluoroethylene powder (PTFE), nanoparticle.
Due to addition PTFE powder, more F-C keys are introduced, since F-C key is a kind of chemical bond of high energy, it is excellent to assign coating
The excellent performances such as different guarantor light colour retention, weatherability, heat-resisting, corrosion-resistant, chemicals-resistant, stain resistant.The addition of nanoparticle,
It reduces corrosive media diffusion rate in the coating and reduces the rate of corrosion process, coating impedance is larger in addition, resists
Cathodic disbonding ability is strong, thus plays to corrosion and effectively prevent.
Summary of the invention
For most of chemically-resistant solvent sapecial coatings currently on the market there are the drawbacks of, this patent discloses one kind poly- four
The preparation method of fluoride modified chemical-resistant reagent special anticorrosive coating.With tetrafluoroethylene monomer and functional form monomer copolymerization
Method introducing portion functional group on fluororesin main chain monomer, reduce the crystalline modified polytetrafluoroethyl-ne of original fluororesin
Olefine resin adds the compositions such as wear-resistant acid and alkali-resistance filler, polytetrafluoroethylene powder (PTFE), nanoparticle as main film forming substance
Bi-component air-curing coatings.Since PTFE powder is added, more F-C keys are introduced, since F-C key is a kind of chemistry of high energy
Therefore key assigns the excellent guarantor's light colour retention of coating, weatherability, heat-resisting, corrosion-resistant, chemicals-resistant, stain resistant, resistance to oxidation etc.
Excellent performance.
1 a kind of polytetrafluoroethylmodified modified chemical-resistant reagent special anticorrosive coating, which is characterized in that based on mass percentage
Component: fluorocarbon resin 40-60, dispersing agent 0-1, defoaming agent 0-1, substrate wetting agents 0-0.5, levelling agent 0-0.5, auxiliary rheological agents
0-1, hydrophobic auxiliary agent 0-0.2, polytetrafluorethylepowder powder 5-15, titanium dioxide 3-10, barium sulfate 2-5, mica powder 5-15, carbon black 0-5,
Ceramic composition 10-30, plasticizer 0.5-2, the mixed solvent of suitable drier and surplus, curing agent are aliphatic poly isocyanide
Acid esters.
2 a kind of polytetrafluoroethylmodified modified chemical-resistant reagent special anticorrosive coating, fluorocarbon resin are according to claim 1
With the monomer of tetrafluoroethylene monomer and method introducing portion functional group on fluororesin main chain of functional form monomer copolymerization, drop
The crystalline modified polytetrafluoroethylresin resin of low original fluororesin.
A kind of 3 polytetrafluoroethylmodified modified chemical-resistant reagent special anticorrosive coatings according to claim 1, ceramic composition
For silicon carbide, zirconium oxide, huge sum of money stone, glass-cermic powder mixture, mixed proportion be silicon carbide: zirconium oxide: huge sum of money stone: glass-cermic powder
=5: 1: 3: 8.
A kind of 4 polytetrafluoroethylmodified modified chemical-resistant reagent special anticorrosive coatings according to claim 1, drier used
For organic tin drier, more preferably dibutyl tin dilaurate.
A kind of 5 polytetrafluoroethylmodified modified chemical-resistant reagent special anticorrosive coatings according to claim 1, it is used hydrophobic to help
Agent is tego6010 or one of SMF-1720 or SMF-1728 or a variety of mixing, preferably SMF-1728.
A kind of 6 polytetrafluoroethylmodified modified chemical-resistant reagent special anticorrosive coatings according to claim 1, curing agent is section
Think wound N3390.
A kind of 7 polytetrafluoroethylmodified modified chemical-resistant reagent special anticorrosive coatings according to claim 1, plasticizer are neighbour
Dibatyl phithalate: acetate=1: 2.
8 a kind of polytetrafluoroethylmodified modified chemical-resistant reagent special anticorrosive coatings according to claim 1, wherein mixing molten
Agent is dimethylbenzene: butyl acetate: glycol methyl ether acetate: isophorone=5: 3: 2: 2
Raw material sources and model
Specific implementation method
A kind of polytetrafluoroethylmodified modified chemical-resistant reagent special anticorrosive coating that this patent provides, each component and each group
Point content matched by reasonably optimizing, the synthesis such as acidproof, alkaline-resisting, antioxidant with higher, coating are fine and close, permeability resistance is strong
Performance.It can be widely used in most of chemical solvent anti-corrosion.
Specific embodiments of the present invention will be described in further detail below.The following examples are intended to illustrate the invention,
But it is not intended to limit the scope of the invention.
A kind of polytetrafluoroethylmodified modified chemical-resistant reagent special anticorrosive coating, the coating the preparation method comprises the following steps:
A kind of 1 preparation of polytetrafluoroethylmodified modified chemical-resistant reagent special anticorrosive coating component A
(1) four fluorine-type fluorocarbon resins are added in a mixing bowl;
(2) part mixed solvent is added in a mixing bowl, and is stirred evenly with 100-150rpm mixing speed, formed equal
Even mixture;
(3) dispersing agent, substrate wetting agents, defoaming agent are added to the mixed of (2) step formation under 50-100rpm mixing speed
It closes in object, and 200-350rpm mixing speed stirs evenly, and forms uniform mixture;
(4) pigments and fillers such as polytetrafluoroethylene powder, titanium dioxide, mica powder, ceramic composition are added to the mixed of (3) step formation
It closes in object, and 1000rpm mixing speed stirs evenly, and forms uniform mixture;
(5) slurry obtained by step (4) is ground by grinder, is ground 2 hours, so that coating average grain diameter D50
≤10um。
(6) plasticizer, levelling agent, hydrophobic auxiliary agent are added in the ground slurry of step (5) and is stirred with 100-150rpm
Speed is mixed to stir evenly.
(7) remaining mixed solvent is added, addition auxiliary rheological agents adjust viscosity, and stir 30min with 150rpm mixing speed
To substantially uniformity, that is, form desulphurization plant anti-corrosion bottom-coating component A.
Specific embodiment
A kind of 2 preparations of polytetrafluoroethylmodified modified chemical-resistant reagent special anticorrosive coating B component
(1) curing agent N3390 is added in a mixing bowl;
(2) mixed solvent is added in a mixing bowl, and is stirred evenly with 100-150rpm mixing speed, formed uniform
Mixture;
(3) deicer is added in the case where stirring at low speed in the mixture of (2) step formation, and with 100rpm mixing speed
30min is stirred, uniform mixture is formed, as required curing agent.
Ingredient | Real column one | Real column two | Real column three | Real column four |
Curing agent | 80.5 | 85.5 | 90 | 95 |
Solvent | 19.4 | 14.4 | 9.85 | 4.85 |
Deicer | 0.1 | 0.1 | 0.15 | 0.15 |
A/B | 13/1 | 14/1 | 13/1 | 12/1 |
Claims (8)
1. a kind of polytetrafluoroethylmodified modified chemical-resistant reagent special anticorrosive coating, which is characterized in that based on mass percentage
Component: fluorocarbon resin 40-60, dispersing agent 0-1, defoaming agent 0-1, substrate wetting agents 0-0.5, levelling agent 0-0.5, auxiliary rheological agents 0-
1, hydrophobic auxiliary agent 0-0.2, polytetrafluorethylepowder powder 5-15, titanium dioxide 3-10, barium sulfate 2-5, mica powder 5-15, carbon black 0-5, pottery
Ceramic composite 10-30, plasticizer 0.5-2, the mixed solvent of suitable drier and surplus, curing agent are aliphatic poly isocyanic acid
Ester.
2. a kind of polytetrafluoroethylmodified modified chemical-resistant reagent special anticorrosive coating according to claim 1, fluorocarbon resin be with
The monomer of method introducing portion functional group on fluororesin main chain of tetrafluoroethylene monomer and functional form monomer copolymerization reduces
The crystalline modified polytetrafluoroethylresin resin of original fluororesin.
3. a kind of polytetrafluoroethylmodified modified chemical-resistant reagent special anticorrosive coating, ceramic composition are according to claim 1
Silicon carbide, zirconium oxide, huge sum of money stone, glass-cermic powder mixture, mixed proportion be silicon carbide: zirconium oxide: huge sum of money stone: glass-cermic powder=
5∶1∶3∶8。
4. a kind of polytetrafluoroethylmodified modified chemical-resistant reagent special anticorrosive coating, drier used are according to claim 1
Organic tin drier, more preferably dibutyl tin dilaurate.
5. a kind of polytetrafluoroethylmodified modified chemical-resistant reagent special anticorrosive coating according to claim 1, hydrophobic auxiliary agent used
For tego6010 or one of SMF-1720 or SMF-1728 or a variety of mixing, preferably SMF-1728.
6. a kind of polytetrafluoroethylmodified modified chemical-resistant reagent special anticorrosive coating according to claim 1, curing agent is Cohan
Create N3390.
7. a kind of polytetrafluoroethylmodified modified chemical-resistant reagent special anticorrosive coating according to claim 1, plasticizer is adjacent benzene
Dibutyl carboxylic acid: acetate=1: 2.
8. a kind of polytetrafluoroethylmodified modified chemical-resistant reagent special anticorrosive coating according to claim 1, wherein mixed solvent
For dimethylbenzene: butyl acetate: glycol methyl ether acetate: isophorone=5: 3: 2: 2.