CN109647060A - A kind of high-efficient energy-saving environment friendly health formula idle call filtering material - Google Patents
A kind of high-efficient energy-saving environment friendly health formula idle call filtering material Download PDFInfo
- Publication number
- CN109647060A CN109647060A CN201811477369.6A CN201811477369A CN109647060A CN 109647060 A CN109647060 A CN 109647060A CN 201811477369 A CN201811477369 A CN 201811477369A CN 109647060 A CN109647060 A CN 109647060A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment friendly
- efficient energy
- saving environment
- idle call
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high-efficient energy-saving environment friendly health formula idle call filtering material, the high-efficient energy-saving environment friendly health formula idle call filtering material is made of raw material from the following weight: 40-60 parts of polyester fiber non-woven fabric, 10-30 parts of ceramic fibre, 10-20 parts of active carbon.The present invention passes through polyester fiber non-woven fabric, it may filter that the macromolecular in air, the mixing of ceramic fibre, active carbon, glass fibre and sub- glass fibre further can cross air filtering, simultaneously, barium titanate electret can enhance filter effect using electrostatic effect, the addition of silver nitrate solution and nano-titanium dioxide, the effect of sterilization can be enhanced, extract solution from aloe can absorb the formaldehyde in air, it is more environmentally-friendly, it can be seen that, this material not only has the function of filtering, pernicious gas in air can also be absorbed, the feature of environmental protection is more preferable.
Description
Technical field
The present invention relates to filtering material technical field more particularly to a kind of high-efficient energy-saving environment friendly health formula idle call filter materials
Material.
Background technique
The principle of filtering is very simple, dust is exactly trapped from Dual-Phrase Distribution of Gas olid using filtering material, and enable gas
The equipment of purification.It is indoor feeding after the low air cleaning processing of dustiness, to guarantee that the technique in clean room requires and one
As air purity in air-conditioned room;Filtering material effect at present on air-conditioning is relatively simple, can only play the role of filtering,
It cannot play the role of purifying air pernicious gas.
Summary of the invention
The purpose of the present invention is to solve disadvantages existing in the prior art, and a kind of high-efficiency energy-saving ring health care proposed
Health formula idle call filtering material.
To achieve the goals above, present invention employs following technical solutions:
A kind of high-efficient energy-saving environment friendly health formula idle call filtering material, the high-efficient energy-saving environment friendly health formula idle call filtering
Material is made of raw material from the following weight: 40-60 parts of polyester fiber non-woven fabric, 10-30 parts of ceramic fibre, active carbon 10-20
Part, 10-20 parts of glass fibre, sub- 8-16 parts of glass fibre, 10-20 parts of extract solution from aloe, 8-16 parts of negative-ion fiber, nanometer two
10-20 parts of titanium oxide, 6-12 parts of silver nitrate solution, 6-10 parts of barium titanate, 15-25 parts of glue, 10-20 parts of emulsifier.
Preferably, the high-efficient energy-saving environment friendly health formula idle call filtering material is made of raw material from the following weight: poly-
45-55 parts of ester fiber non-woven fabrics, 15-25 parts of ceramic fibre, 12-18 parts of active carbon, 12-18 parts of glass fibre, sub- glass fibre
10-14 parts, 12-18 parts of extract solution from aloe, 10-14 parts of negative-ion fiber, 12-18 parts of nano-titanium dioxide, silver nitrate solution 8-
10 parts, 6-10 parts of barium titanate, 15-25 parts of glue, 12-18 parts of emulsifier.
Preferably, the high-efficient energy-saving environment friendly health formula idle call filtering material is made of raw material from the following weight: poly-
50 parts of ester fiber non-woven fabrics, 30 parts of ceramic fibre, 15 parts of active carbon, glass fibre 15, sub- 12 parts of glass fibre, extract solution from aloe
15 parts, 12 parts of negative-ion fiber, 15 parts of nano-titanium dioxide, 9 parts of silver nitrate solution, 8 parts of barium titanate, 20 parts of glue, emulsifier
15 parts.
Preferably, the glue is one of sesbania gum, guar gum, agar-agar, flax gum and fenugreek gum.
Preferably, the partial size of the nano-titanium dioxide is 30-60nm.
A kind of preparation method of high-efficient energy-saving environment friendly health formula idle call filtering material, comprising the following steps:
S1, active carbon crushed into powder is spare, partial size 0.075-0.095mm;
S2, by the active carbon powder and ceramic fibre, glass fibre, sub- glass fibre, extract solution from aloe, anion in S1
Fiber, nano-titanium dioxide, silver nitrate solution, barium titanate, glue and emulsifier are stirred and are mixed into thick, formed mixed
Close object;
S3, the punching on polyester fiber non-woven fabric, aperture 4-8mm, are then folded over, in putting down between layers for folding
The mixture in S2 is spread, and uniformly applies pressure, pressure 2-4MPa;
S4, natural drying, can be prepared by.
Preferably, the speed of agitator is 600-800r/min, time 10-20min.
Compared with prior art, the beneficial effects of the present invention are: the present invention may filter that air by polyester fiber non-woven fabric
In macromolecular, the mixing of ceramic fibre, active carbon, glass fibre and sub- glass fibre further can cross air filtering, meanwhile, titanium
Sour barium electret can enhance filter effect using electrostatic effect, and the addition of silver nitrate solution and nano-titanium dioxide can increase
The effect of strong sterilization, extract solution from aloe can absorb the formaldehyde in air, more environmentally-friendly, it can be seen that, this material not only had
The function of filter, moreover it is possible to absorb pernicious gas in air, the feature of environmental protection is more preferable.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.
Embodiment 1
A kind of high-efficient energy-saving environment friendly health formula idle call filtering material, high-efficient energy-saving environment friendly health formula idle call filtering material
It is made of raw material from the following weight: 40 parts of polyester fiber non-woven fabric, 10 parts of ceramic fibre, 10 parts of active carbon, glass fibre 10
Part, sub- 8 parts of glass fibre, 10 parts of extract solution from aloe, 8 parts of negative-ion fiber, 10 parts of nano-titanium dioxide, 6 parts of silver nitrate solution,
6 parts of barium titanate, 15 parts of glue, 10 parts of emulsifier.
Glue is one of sesbania gum, guar gum, agar-agar, flax gum and fenugreek gum.
The partial size of nano-titanium dioxide is 30nm.
A kind of preparation method of high-efficient energy-saving environment friendly health formula idle call filtering material, comprising the following steps:
S1, active carbon crushed into powder is spare, partial size 0.075mm;
S2, by the active carbon powder and ceramic fibre, glass fibre, sub- glass fibre, extract solution from aloe, anion in S1
Fiber, nano-titanium dioxide, silver nitrate solution, barium titanate, glue and emulsifier are stirred and are mixed into thick, formed mixed
Close object;
S3, the punching on polyester fiber non-woven fabric, aperture 4mm, are then folded over, in the tiling between layers of folding
Mixture in S2, and uniformly apply pressure, pressure 2MPa;
S4, natural drying, can be prepared by.
Speed of agitator is 600r/min, time 10min.
Embodiment 2
A kind of high-efficient energy-saving environment friendly health formula idle call filtering material, high-efficient energy-saving environment friendly health formula idle call filtering material
It is made of raw material from the following weight: 50 parts of polyester fiber non-woven fabric, 20 parts of ceramic fibre, 15 parts of active carbon, glass fibre 15
Part, sub- 12 parts of glass fibre, 15 parts of extract solution from aloe, 12 parts of negative-ion fiber, 15 parts of nano-titanium dioxide, silver nitrate solution 9
Part, 8 parts of barium titanate, 20 parts of glue, 15 parts of emulsifier.
Glue is one of sesbania gum, guar gum, agar-agar, flax gum and fenugreek gum.
The partial size of nano-titanium dioxide is 45nm.
A kind of preparation method of high-efficient energy-saving environment friendly health formula idle call filtering material, comprising the following steps:
S1, active carbon crushed into powder is spare, partial size 0.085mm;
S2, by the active carbon powder and ceramic fibre, glass fibre, sub- glass fibre, extract solution from aloe, anion in S1
Fiber, nano-titanium dioxide, silver nitrate solution, barium titanate, glue and emulsifier are stirred and are mixed into thick, formed mixed
Close object;
S3, the punching on polyester fiber non-woven fabric, aperture 6mm, are then folded over, in the tiling between layers of folding
Mixture in S2, and uniformly apply pressure, pressure 3MPa;
S4, natural drying, can be prepared by.
Speed of agitator is 700r/min, time 15min.
Embodiment 3
A kind of high-efficient energy-saving environment friendly health formula idle call filtering material, high-efficient energy-saving environment friendly health formula idle call filtering material
It is made of raw material from the following weight: 60 parts of polyester fiber non-woven fabric, 30 parts of ceramic fibre, 20 parts of active carbon, glass fibre 20
Part, sub- 16 parts of glass fibre, 20 parts of extract solution from aloe, 16 parts of negative-ion fiber, 20 parts of nano-titanium dioxide, silver nitrate solution 12
Part, 10 parts of barium titanate, 25 parts of glue, 20 parts of emulsifier.
Glue is one of sesbania gum, guar gum, agar-agar, flax gum and fenugreek gum.
The partial size of nano-titanium dioxide is 60nm.
A kind of preparation method of high-efficient energy-saving environment friendly health formula idle call filtering material, comprising the following steps:
S1, active carbon crushed into powder is spare, partial size 0.095mm;
S2, by the active carbon powder and ceramic fibre, glass fibre, sub- glass fibre, extract solution from aloe, anion in S1
Fiber, nano-titanium dioxide, silver nitrate solution, barium titanate, glue and emulsifier are stirred and are mixed into thick, formed mixed
Close object;
S3, the punching on polyester fiber non-woven fabric, aperture 8mm, are then folded over, in the tiling between layers of folding
Mixture in S2, and uniformly apply pressure, pressure 4MPa;
S4, natural drying, can be prepared by.
Speed of agitator is 800r/min, time 20min.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (7)
1. a kind of high-efficient energy-saving environment friendly health formula idle call filtering material, which is characterized in that the high-efficient energy-saving environment friendly health formula
Idle call filtering material is made of raw material from the following weight: 40-60 parts of polyester fiber non-woven fabric, is lived at 10-30 parts of ceramic fibre
Property 10-20 parts of charcoal, 10-20 parts of glass fibre, sub- 8-16 parts of glass fibre, 10-20 parts of extract solution from aloe, negative-ion fiber 8-16
Part, 10-20 parts of nano-titanium dioxide, 6-12 parts of silver nitrate solution, 6-10 parts of barium titanate, 15-25 parts of glue, emulsifier 10-20
Part.
2. a kind of high-efficient energy-saving environment friendly health formula idle call filtering material according to claim 1, which is characterized in that described
High-efficient energy-saving environment friendly health formula idle call filtering material is made of raw material from the following weight: 45-55 parts of polyester fiber non-woven fabric,
15-25 parts of ceramic fibre, 12-18 parts of active carbon, 12-18 parts of glass fibre, sub- 10-14 parts of glass fibre, extract solution from aloe 12-
18 parts, 10-14 parts of negative-ion fiber, 12-18 parts of nano-titanium dioxide, 8-10 parts of silver nitrate solution, 6-10 parts of barium titanate, glue
15-25 parts, 12-18 parts of emulsifier.
3. a kind of high-efficient energy-saving environment friendly health formula idle call filtering material according to claim 1 or 2, which is characterized in that
The high-efficient energy-saving environment friendly health formula idle call filtering material is made of raw material from the following weight: polyester fiber non-woven fabric 50
Part, 30 parts of ceramic fibre, 15 parts of active carbon, glass fibre 15, sub- 12 parts of glass fibre, 15 parts of extract solution from aloe, anion are fine
Tie up 12 parts, 15 parts of nano-titanium dioxide, 9 parts of silver nitrate solution, 8 parts of barium titanate, 20 parts of glue, 15 parts of emulsifier.
4. a kind of high-efficient energy-saving environment friendly health formula idle call filtering material according to claim 1, which is characterized in that described
Glue is one of sesbania gum, guar gum, agar-agar, flax gum and fenugreek gum.
5. a kind of high-efficient energy-saving environment friendly health formula idle call filtering material according to claim 1, which is characterized in that described
The partial size of nano-titanium dioxide is 30-60nm.
6. a kind of preparation method of high-efficient energy-saving environment friendly health formula idle call filtering material a method as claimed in any one of claims 1 to 5,
Characterized by comprising the following steps:
S1, active carbon crushed into powder is spare, partial size 0.075-0.095mm;
S2, by S1 active carbon powder and ceramic fibre, glass fibre, sub- glass fibre, extract solution from aloe, anion it is fine
Dimension, nano-titanium dioxide, silver nitrate solution, barium titanate, glue and emulsifier are stirred and are mixed into thick, formation mixing
Object;
S3, the punching on polyester fiber non-woven fabric, aperture 4-8mm, are then folded over, in the tiling S2 between layers of folding
In mixture, and uniformly apply pressure, pressure 2-4MPa;
S4, natural drying, can be prepared by.
7. a kind of high-efficient energy-saving environment friendly health formula idle call filtering material according to claim 6, which is characterized in that described
Speed of agitator is 600-800r/min, time 10-20min.