CN109627972A - A kind of nanoporous aerogel thermal insulation paint - Google Patents
A kind of nanoporous aerogel thermal insulation paint Download PDFInfo
- Publication number
- CN109627972A CN109627972A CN201811596518.0A CN201811596518A CN109627972A CN 109627972 A CN109627972 A CN 109627972A CN 201811596518 A CN201811596518 A CN 201811596518A CN 109627972 A CN109627972 A CN 109627972A
- Authority
- CN
- China
- Prior art keywords
- agent
- thermal insulation
- mixing speed
- added
- insulation paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention discloses a kind of nanoporous aerogel thermal insulation paint, belongs to special coating technical field.The aerogel heat-insulating thermal insulation coatings include the component based on mass percentage: water 5-15, auxiliary agent 1-6, pigments and fillers 20-55, binder 10-30, coupling agent 1-3, fire retardant 5-15, infrared light screening agent 5-20.Wherein pigments and fillers include functional low heat conductivity filler: nanometer titanium dioxide silica aerogel;Constitution filler: talcum powder, precipitated calcium carbonate, wollastonite;Functional anti-corrosion paint trbasic zinc phosphate;Binder includes water-soluble organic silicon resin, water soluble acrylic acid high temperature resistant lotion, water soluble acrylic acid elastic emulsion.Coating heat transfer coefficient of the invention is low, and heat insulation is excellent;With good anti-corrosion effect, the use of anti-corrosion primer can be reduced;And have the effect of self-cleaning hydrophobic.
Description
Technical field
The invention belongs to special coating technical fields, and in particular to a kind of nanoporous aerogel thermal insulation paint preparation side
Method.
Technical background
The utilization efficiency that unnecessary heat transfer results in energy under various environment reduces, and increases the additional energy and disappears
Consumption.In building field, traditional external wall insulation is mostly based on styrofoam, although having lower thermal coefficient, heat-proof quality
It is excellent, but levels of audit quality is uneven in the market, and needs special mounting process, since insulation board is by adhesive in wall
Body is adhered to one, and as time increases, Organic adhesive aging causes falling for external wall insulation large area, exist compared with
Big security risk.
In industrial circle, high-temperature service, especially jet chimney, dyeing apparatus etc., due to it is most of do not do it is special
Isothermal holding, surface temperature are mostly higher than 150 DEG C, not only cause the huge waste of the energy, but also workers with long time near work,
Especially during the broiling summer, worker's dress is thiner, it is easy to worker be caused to scald.
Nanometer titanium dioxide silica aerogel is a kind of novel light nanoporous material, has low-density, high porosity, low
The features such as refractive index and low-thermal conductivity.The unique nanoporous network structure of aerosil makes it have excellent guarantor
Warm heat-proof quality, aerosil are a kind of new materials with nano-porous structure, be it is most light in the world at present, every
The best solid insulating material of hot property.With three-dimensional net structure, with up to 90% or more porosity, nanometer titanium dioxide
The thermal conductivity of silica aerogel consists of three parts: gas thermal conductivity, solid-state thermal conductivity, radiant heat conductanc.Air molecule is averaged
Free layer is in 70mn or so, and the pore size of nanometer titanium dioxide silica aerogel is 20-50nm, is much smaller than this critical dimension,
Material internal eliminates the need for convection current, and gas thermal conductivity is just very low;And lower density limits office of the heat in sparse skeleton again
It propagates in portion.
Summary of the invention
For either building field or industrial circle currently on the market, some problems existing for Conventional insulation,
This patent discloses a kind of aerogel heat-insulating thermal insulation coatings and preparation method thereof, select inside current inorganic porous solids material most
Light nanometer titanium dioxide silica aerogel as functional heat-barrier material, using the special three-dimensional net structure of nano silica and
The form of construction work of spraying or blade coating can be used so that coating has the thermal coefficient of polar region in lower pore size, has preferable
Adiabatic heat insulating effect.
Coating prepared by the invention patent, thermal coefficient is extremely low, generally only needs 1-5mm that is, conventional vacuum rock wool
The heat insulation effect of 10-50cm, in building field, especially in summer sweltering heat, winter sombre south can be applied to interior wall or outer
Wall has the effect of heat insulation decoration integrated;In industrial circle, especially jet chimney or dyeing apparatus, due to by character and sky
Between limit, do not use traditional thicker thermal insulation material generally, and be chronically in the environment of high temperature and humidity, corrosion of metal is phase
When serious, the coating of invention, high-efficiency rust-preventive pigment is added, there is good anti-corrosion effect, and surface hydrophobicity, Yi Qing
It is clean.
A kind of 1 nanoporous aerogel thermal insulation paint, which is characterized in that the component based on mass percentage: water 5-15,
Auxiliary agent 1-6, pigments and fillers 20-55, binder 10-30, coupling agent 1-3, fire retardant 5-15, infrared light screening agent 5-20.
2 a kind of nanoporous aerogel thermal insulation paint, coupling agent include KH-550 and KH-570 according to claim 1
One or both of.
A kind of 3 nanoporous aerogel thermal insulation paints according to claim 1, infrared light screening agent are titanium dioxide, six titaniums
One of sour potassium whisker, carbon black or a variety of mixing.
A kind of 4 nanoporous aerogel thermal insulation paints according to claim 1, the auxiliary agent include dispersing agent 0.5-2,
Wetting agent 0-1, defoaming agent 0-1, thickener 0-1, coalescing agent 1-5, fungicide 0-1, antifreezing agent 1-5, hydrophobic auxiliary agent 0-1.
A kind of 5 nanoporous aerogel thermal insulation paints according to claim 4, preferred dispersing agent be KYK-190,
Defoaming agent is Tego901W, wetting agent BYK-349, thickener Tego3030, hydrophobic auxiliary agent are SM-1728, coalescing agent
For propylene glycol monomethyl ether, the mixture of dipropylene glycol methyl ether, and mixed proportion is propylene glycol monomethyl ether: dipropylene glycol methyl ether=3: 5.It kills
The mixture that microbial inoculum is E25, antifreezing agent is ethylene glycol and glycerine, and mixed proportion is ethylene glycol: glycerine=2: 1.
A kind of 6 nanoporous aerogel thermal insulation paints according to claim 1, nanometer titanium dioxide silica aerogel is because first matching
Be made 30% paste it is stand-by, preparation method are as follows:
(1) part water is added in a mixing bowl:
(2) dispersing agent 0.5-2, wetting agent 0-1, defoaming agent 0-1, thickener 0-1 are added in a mixing bowl, and with 50-
100rpm mixing speed stirs evenly, and forms uniform mixture;
(3) it is slowly added to coupling agent and is stirred evenly with 100-150rpm mixing speed, form uniform mixture;As
Modified binder.
(4) nanometer titanium dioxide silica aerogel is added to the mixture of (3) step formation under 150-200rpm mixing speed
In the middle, and 150-200rpm mixing speed stirs evenly, and forms uniform mixture;
A kind of 7 nanoporous aerogel thermal insulation paints according to claim 1 prepare 15% infrared light screening agent, can root
According to color needed for coating, black or white infrared light screening agent slurries, preparation method are prepared are as follows:
(1) part water is added in a mixing bowl;
(2) dispersing agent 0.5-2, wetting agent 0-1, defoaming agent 0-1, thickener 0-1 are added in a mixing bowl, and with 50-
100rpm mixing speed stirs evenly, and forms uniform mixture;
(3) it is slowly added to coupling agent and is stirred evenly with 100-150rpm mixing speed, form uniform mixture;As
Modified binder.
(4) nanometer crystal whisker of hexa potassium titanate, titanium dioxide or carbon black are added to (3) step shape under 300-500rpm mixing speed
At mixture in, and 1000rpm mixing speed stirs evenly, and forms uniform mixture;
Raw material sources and model
Specific implementation method
The content of the nanoporous aerogel thermal insulation paint coating that this patent provides, each component and each component passes through conjunction
Manage Optimized Matching, comprehensive performance with higher when making nanoporous aerogel thermal insulation paint as thermal insulating warm-keeping layer.
Specific embodiments of the present invention will be described in further detail below.The following examples are intended to illustrate the invention,
But it is not intended to limit the scope of the invention.
The nanoporous aerogel thermal insulation paint, the coating the preparation method comprises the following steps:
(1) it adds water in a mixing bowl;
(2) infrared light screening agent is added in a mixing bowl, and is stirred evenly with 50-100rpm mixing speed, formed uniform
Mixture;
(3) antifreezing agent, hydrophobic auxiliary agent and dispersing agent are slowly added to and is stirred evenly with 100-150rpm mixing speed, is formed
Uniform mixture;As modified binder.
(4) anti-corrosion paint and constitution filler, fire retardant are added to the formation of (3) step under 300-500rpm mixing speed
In mixture, and 1000rpm mixing speed stirs evenly, and forms uniform mixture;
(5) slurry obtained by step (4) is ground by grinder, is ground 2 hours, so that coating average grain diameter D50
≤20um。
(6) nanometer titanium dioxide silica aerogel slurries are added in the ground slurry of step (5), and are stirred with 200-300rpm
It mixes speed and stirs 30min to substantially uniformity;
(7) fungicide, coalescing agent is added in step (6) and 10min is stirred to complete with 200-300rpm mixing speed
Uniformly, it is eventually adding thickener adjustment viscosity.
Specific implementation column
Claims (7)
1. a kind of nanoporous aerogel thermal insulation paint, which is characterized in that the component based on mass percentage: water 5-15, helping
Agent 1-6, pigments and fillers 20-55, binder 10-30, coupling agent 1-3, fire retardant 5-15, infrared light screening agent 5-20.
2. a kind of nanoporous aerogel thermal insulation paint, coupling agent include in KH-550 and KH-570 according to claim 1
One or two.
3. a kind of nanoporous aerogel thermal insulation paint according to claim 1, infrared light screening agent is titanium dioxide, potassium hexatitanate
One of whisker, carbon black or a variety of mixing.
4. a kind of nanoporous aerogel thermal insulation paint according to claim 1, the auxiliary agent includes dispersing agent 0.5-2, profit
Humectant 0-1, defoaming agent 0-1, thickener 0-1, coalescing agent 1-5, fungicide 0-1, antifreezing agent 1-5, hydrophobic auxiliary agent 0-1.
5. a kind of nanoporous aerogel thermal insulation paint according to claim 4, preferred dispersing agent is KYK-190, disappears
Infusion is Tego901W, wetting agent BYK-349, thickener Tego3030, hydrophobic auxiliary agent are SM-1728, coalescing agent is
The mixture of propylene glycol monomethyl ether, dipropylene glycol methyl ether, and mixed proportion is propylene glycol monomethyl ether: dipropylene glycol methyl ether=3: 5.Sterilization
The mixture that agent is E25, antifreezing agent is ethylene glycol and glycerine, and mixed proportion is ethylene glycol: glycerine=2: 1.
6. a kind of nanoporous aerogel thermal insulation paint according to claim 1, nanometer titanium dioxide silica aerogel is because first preparing
Stand-by, the preparation method at 30% paste are as follows:
(1) part water is added in a mixing bowl;
(2) dispersing agent 0.5-2, wetting agent 0-1, defoaming agent 0-1, thickener 0-1 are added in a mixing bowl, and with 50-
100rpm mixing speed stirs evenly, and forms uniform mixture;
(3) it is slowly added to coupling agent and is stirred evenly with 100-150rpm mixing speed, form uniform mixture;It is as modified
Binder.
(4) nanometer titanium dioxide silica aerogel is added under 150-200rpm mixing speed in the mixture of (3) step formation,
And 150-200rpm mixing speed stirs evenly, and forms uniform mixture.
It, can be according to painting 7. a kind of nanoporous aerogel thermal insulation paint according to claim 1 prepares 15% infrared light screening agent
Color needed for expecting prepares black or white infrared light screening agent slurries, preparation method are as follows:
(1) part water is added in a mixing bowl;
(2) dispersing agent 0.5-2, wetting agent 0-1, defoaming agent 0-1, thickener 0-1 are added in a mixing bowl, and with 50-
100rpm mixing speed stirs evenly, and forms uniform mixture;
(3) it is slowly added to coupling agent and is stirred evenly with 100-150rpm mixing speed, form uniform mixture;It is as modified
Binder.
(4) nanometer crystal whisker of hexa potassium titanate, titanium dioxide or carbon black are added to the formation of (3) step under 300-500rpm mixing speed
In mixture, and 1000rpm mixing speed stirs evenly, and forms uniform mixture.