CN109624583A - A kind of resin mosaic technology for wrapping up clay sculpture - Google Patents
A kind of resin mosaic technology for wrapping up clay sculpture Download PDFInfo
- Publication number
- CN109624583A CN109624583A CN201811526555.4A CN201811526555A CN109624583A CN 109624583 A CN109624583 A CN 109624583A CN 201811526555 A CN201811526555 A CN 201811526555A CN 109624583 A CN109624583 A CN 109624583A
- Authority
- CN
- China
- Prior art keywords
- resin
- clay sculpture
- parts
- sculpture
- clay
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of resin mosaic technology for wrapping up clay sculpture includes the following steps: production clay sculpture, and with 60-75 parts of diatomite, 10-15 parts of polyvinyl alcohol, 20-40 parts of mineral wax, 10-15 parts of dehydrated alcohol, 3-6 parts of croci mixings, sculpture shapes, after natural air drying surface moisture;Resin is smeared on clay sculpture surface, then solidifies, slots on mosaic;It will be in embedded groove after clay sculpture resin package molding.The resin mosaic technology of package clay sculpture of the present invention, clay sculpture can be wrapped in transparent resin and be embedded on wooden comb, form a kind of new wooden comb product pattern, realize richer color and modeling transformation combination.
Description
Technical field
The invention belongs to Material Fields, are related to a kind of material processing forming technique, and in particular to a kind of tree for wrapping up clay sculpture
Rouge mosaic technology.
Background technique
Comb is the tool for combing hair, and comb divides utility comb, technique comb, Tourist's comb, high-grade essence in kind
The series of products such as product comb, health-care comb, current high-end comb mainly use the materials such as wooden, cutin, can with resin and resin-bonded
To reduce the materials of timber and keratin materials, while the aesthetics and feel of comb are promoted, while retaining the function of wooden comb, horn combs
Effect, provides a kind of specific embodiment of the comb using timber and resin combination formation as shown in Figure 1, and main part 1 is wood
Material, inlay part 2 are resin.
Summary of the invention
To develop a kind of more beautiful wooden comb new product, the invention discloses a kind of resin bed setters for wrapping up clay sculpture
Skill.
The resin mosaic technology of package clay sculpture of the present invention, includes the following steps:
Make clay sculpture, with 60-75 parts of diatomite, 10-15 parts of polyvinyl alcohol, 20-40 parts of mineral wax, 10-15 parts of dehydrated alcohol, oxygen
Change iron powder 3-6 parts of mixing, sculpture shapes, after natural air drying surface moisture;Resin is smeared on clay sculpture surface, is then solidified,
It slots on mosaic;It will be in embedded groove after clay sculpture resin package molding.
Preferably, the mineral wax is polyester wax.
Preferably, after resin is smeared on clay sculpture surface, before solidification, if it find that clay sculpture surface has bubble to overflow or find
Hole: clay sculpture, which is immersed in resin, and vacuumizes negative pressure maintains 30-60 minutes, then restores normal pressure 30-60 minutes.
The resin mosaic technology of package clay sculpture of the present invention, clay sculpture can be wrapped in transparent resin and be embedded in
On wooden comb, a kind of new wooden comb product pattern is formed, realizes richer color and modeling transformation combination.
Detailed description of the invention
Fig. 1 provides a kind of specific embodiment of the comb of the present invention formed using timber and resin combination
1- main part, 2- inlay part.
Specific embodiment
Specific embodiments of the present invention will be described in further detail below.
A kind of resin mosaic technology for wrapping up clay sculpture of the present invention, includes the following steps:
Make clay sculpture, with 60-75 parts of diatomite, 10-15 parts of polyvinyl alcohol, 20-40 parts of mineral wax, 10-15 parts of dehydrated alcohol, oxygen
Change iron powder 3-6 parts of mixing, sculpture shapes, after natural air drying surface moisture;Resin is smeared on clay sculpture surface, is then solidified,
It slots on mosaic;It will be in embedded groove after clay sculpture resin package molding.
After resin is smeared on clay sculpture surface, before solidification, if it find that clay sculpture surface has bubble to overflow or finds hole:
Clay sculpture is immersed in resin and vacuumizes negative pressure and is maintained 30-60 minutes, is then restored normal pressure 30-60 minutes.
Mineral wax preferably uses polyester wax, and polyester wax is mostly that raw material reaction is made with silica resin (Silicone), with
The associativity of diatomite and resin is good, and crystalline solid is fine, can effectively fill the gap between diatomite, reduces the sky in clay
Gas, and aquo-compound can be formed in conjunction with water, to solidify the excessive moisture in diatomite.
Ethyl alcohol has double action of sterilizing and absorb water, and can persistently inhibit microorganism therein after hardening;Using oxidation
Iron can reinforce the hardness after diatomite solidifies, and statue is squeezed after avoiding resin package from shrinking, it is caused to deform polyvinyl alcohol tool
There is linking agent effect, by diatomite and mineral wax, the components such as iron oxide link together, and can have one with subsequent resin
Fixed compatibility, enables resin effectively to wrap up sculpture.
The resin mosaic technology of package clay sculpture of the present invention, clay sculpture can be wrapped in transparent resin and be embedded in
On wooden comb, a kind of new wooden comb product pattern is formed, realizes richer color and modeling transformation combination.
The present invention can be by punching on comb or slotting, and the inlay part that resin is made into is stuck in wooden comb main part
On.
Specific embodiment 1
In the recessing of wooden comb back, it can be carved and be slotted with sloyd knife, one layer of epoxy resin be sprayed after fluting on groove face to protect
Section is protected, avoids seeping water;
Take 30 grams of diatomite, 6 grams of polyvinyl alcohol, 12 grams of paraffin, 6 grams of dehydrated alcohol, 2 grams of croci;Diatomite and oxidation
Iron crosses 80 meshes, and iron oxide can be the native iron oxygen powder containing ferrous oxide and ferroso-ferric oxide.
By diatomite, paraffin, polyvinyl alcohol, ethyl alcohol and croci be mixed into pureed, sculpture at needs shape
Shape, such as spherical, star, simple toy, flower, Leaves'Shape etc..About 10-30 minutes air-dried table is stood after sculpture forming
Face moisture, puts it into the slot held successfully on wooden comb.
Wooden comb is entirely placed on electric heating stove plate, electric heating stove plate surface temperature is on 80 degrees centigrades, stone or metal plate for standing a stove on as a precaution against fire
Generally in 70 degrees centigrades, the antipyretic wherein moisture that is conducive to further evaporates, epoxy resin is sprayed into first side space temperature
Behind clay sculpture surface about 10-30 seconds, before the epoxy resin cure on surface, then spray epoxy is to filling up groove and shape;Such as
The whole spraying rapidly of fruit, epoxy resin and clay sculpture are there are the larger temperature difference, and coefficient of thermal expansion and contraction is inconsistent, in subsequent cooling procedure
In, epoxy resin layer is easy to fall off or is cracked with clay sculpture surface contact surface.
Specific embodiment 2
In the recessing of wooden comb back, it can be carved and be slotted with sloyd knife, one layer of epoxy resin be sprayed after fluting on groove face to protect
Section is protected, avoids seeping water;
Take 30 grams of diatomite, 6 grams of polyvinyl alcohol, 15 grams of polyester wax, 6 grams of dehydrated alcohol, 1.5 grams of croci;Diatomite and
Iron oxide crosses 80 meshes, and iron oxide can be the native iron oxygen powder containing ferrous oxide and ferroso-ferric oxide.
By diatomite, paraffin, polyvinyl alcohol, ethyl alcohol and croci be mixed into pureed, sculpture at needs shape
Shape, such as spherical, star, simple toy, flower, Leaves'Shape etc..About 10-30 minutes air-dried table is stood after sculpture forming
Face moisture,
After resin is smeared on clay sculpture surface, before solidification, if it find that clay sculpture surface has bubble to overflow or finds hole: by mud
Modeling is immersed in resin and vacuumizes negative pressure and maintains 45 minutes, then restores normal pressure 45 minutes, resin extruded hole can be made empty
Gas simultaneously fills clay sculpture hole.
Wooden comb is entirely placed on electric heating stove plate, electric heating stove plate surface temperature is on 80 degrees centigrades, stone or metal plate for standing a stove on as a precaution against fire
Generally in 70 degrees centigrades, heating is conducive to wherein moisture and further evaporates side space temperature, and epoxy resin is sprayed into first
Behind clay sculpture surface about 10-30 seconds, before the epoxy resin cure on surface, before the epoxy resin cure on surface, then epoxy is sprayed
Resin is to filling up groove and shape.
Previously described is each preferred embodiment of the invention, if the preferred embodiment in each preferred embodiment
It is not obvious contradictory or premised on a certain preferred embodiment, each preferred embodiment can any stack combinations
Use, the design parameter in the embodiment and embodiment only for the purpose of clearly stating the inventor's invention verification process, and
It is non-to limit scope of patent protection of the invention, scope of patent protection of the invention is still subject to the claims, all
It is that similarly should be included within the scope of the present invention with the variation of equivalent structure made by description of the invention.
Claims (3)
1. a kind of resin mosaic technology for wrapping up clay sculpture, characterized by the following steps:
Make clay sculpture, with 60-75 parts of diatomite, 10-15 parts of polyvinyl alcohol, 20-40 parts of mineral wax, 10-15 parts of dehydrated alcohol, oxygen
Change iron powder 3-6 parts of mixing, sculpture shapes, after natural air drying surface moisture;Resin is smeared on clay sculpture surface, is then solidified,
It slots on mosaic;It will be in embedded groove after clay sculpture resin package molding.
2. the resin mosaic technology of package clay sculpture as described in claim 1, which is characterized in that the mineral wax is polyester wax.
3. the resin mosaic technology of package clay sculpture as described in claim 1, which is characterized in that smear resin on clay sculpture surface
Afterwards, before solidification, if it find that clay sculpture surface has bubble to overflow or finds hole: clay sculpture to be immersed in resin and vacuumize
Negative pressure maintains 30-60 minutes, then restores normal pressure 30-60 minutes.