CN109624467A - A kind of ground glue combined producing tech - Google Patents
A kind of ground glue combined producing tech Download PDFInfo
- Publication number
- CN109624467A CN109624467A CN201910034476.XA CN201910034476A CN109624467A CN 109624467 A CN109624467 A CN 109624467A CN 201910034476 A CN201910034476 A CN 201910034476A CN 109624467 A CN109624467 A CN 109624467A
- Authority
- CN
- China
- Prior art keywords
- layer
- pvc
- glue
- enhancement layer
- scraped
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of ground glue combined producing tech, including stock, surface layer, enhancement layer, foaming layer process, finally by compound by surface layer, enhancement layer, foaming layer hot paste or pressing are pasted, with obtaining finished product glue, the present invention is with PVC powder, color masterbatch powder is base-material, production obtains surface layer respectively, enhancement layer, foaming layer, the different demands of each layer are cooperated to add other preparations, surface layer, enhancement layer, synthetically glue is finally pasted in foaming layer, production difficulty can be reduced by individually producing each layer, improve industrialization degree, molding ground glue is with elasticity is good, wearability is good, the advantages that stability is high, process flow is simple, each layer of production can be independent, convenient for enterprise implement, with biggish industrial application value.
Description
Technical field
The invention belongs to ground glue technical fields, specifically, being related to a kind of ground glue combined producing tech.
Background technique
Ground glue can absorb impact and alleviate knee fatigue, provide comfortable feel, can compared with solid wooden floor board and consolidated floor
To reduce the effect of body burden nearly 40%, it is comfortably incomparable that its impact foot can be buffered, while stability will not deform well, energy
It is enough to remain stationary for a long time, there is good sound-proofing, heat conductivity, hard wear resistant, superiority be significantly larger than solid wooden floor board,
Consolidated floor, press compoiste wood floor, rubber floor covering and cork flooring, be widely used in hospital, school, office building, laboratory,
The demand of business place and household, the following glue over the ground is more and more, and in view of this present invention is specifically proposed.
Summary of the invention
The technical problem to be solved in the present invention is that overcoming the deficiencies of the prior art and provide a kind of ground glue laminating production work
Skill, in order to solve the above technical problems, the present invention is using the basic conception of technical solution:
A kind of ground glue combined producing tech, includes the following steps,
Step 1, it stocks up: being mixed in proportion with PVC powder, color masterbatch powder, hardening agent with water, be uniformly mixing to obtain starchiness
PVC solution；It is mixed in proportion with PVC powder, color masterbatch powder, foaming agent with water, is uniformly mixing to obtain starchy PVC foam
Mixed solution；It is mixed in proportion with PVC powder, foaming agent with water, is uniformly mixing to obtain starchiness frothing solution；
Step 2, surface layer: PVC solution is uniformly sprayed in release paper, after scraper plate painting is scraped, is dried into heated oven
8-10 seconds, obtain surface layer；
Step 3, enhancement layer: PVC solution is uniformly sprayed in release paper, after scraper plate painting is scraped, is dried into heated oven
8-10 seconds dry, strengthened layer；
Step 4, foaming layer: PVC foam mixed solution is uniformly sprayed in release paper, after scraper plate painting is scraped, into adding
Oven heat is dried 8-10 seconds, then frothing solution is uniformly sprayed above, obtains first product after scraper plate painting is scraped, first product is by back
Plate sizing axis extrudes backboard shape, enters heated oven within operation 2-3 seconds and dries 8-10 seconds, after cutting machine cutting shaping size,
Obtain foaming layer；
Step 5, compound: surface layer, enhancement layer, foaming layer being sequentially stacked, pasted through hot paste or pressing, with obtaining finished product
Glue.
Further, the step 2 are as follows: uniformly spray PVC solution in release paper, after scraper plate painting is scraped, into adding
Oven heat is dried 8-10 seconds, is kept being embossed under certain high temperature by clean steel roller bearing, after being cooled to room temperature, is cut and be formed through cutting machine
After size, surface layer is obtained.
Further, it is additionally provided with step 21 between step 2 and step 3: PVC powder, hardening agent are mixed in proportion with water,
It is stirred into starchiness, is uniformly sprayed onto release paper, after scraper plate painting is scraped, dries 8-10 seconds, obtains into heated oven
Sparkling and crystal-clear wearing layer；Corresponding, step 5 is to be sequentially stacked sparkling and crystal-clear wearing layer, surface layer, enhancement layer, foaming layer, through hot paste or pressing
It pastes, with obtaining finished product glue.
Further, the step 3, which is divided, is:
Step 31, PVC solution is uniformly sprayed in release paper, after scraper plate painting is scraped, dries 8-10 into heated oven
Second, obtain the first enhancement layer；
Step 32, layer of glass fiber fabric is added on the basis of first layer enhancement layer, is pressed together on first layer by roller bearing and reinforces
On layer；
Step 33, PVC solution is uniformly sprayed on glass-fiber-fabric, after scraper plate painting is scraped, dries 8-10 into heated oven
Second, form the second enhancement layer；
Step 34, a strata ester grid cloth is added on the basis of second layer enhancement layer, is pressed together on the second layer by roller bearing
On enhancement layer；
Step 35, PVC solution is uniformly sprayed on polyester grid cloth, after scraper plate painting is scraped, is dried into heated oven
8-10 seconds, third enhancement layer is formed, after being cooled to room temperature, arrives finished product enhancement layer after cutting machine cuts shaping size.
Further, the step 5 are as follows: be sequentially stacked surface layer, enhancement layer, foaming layer, at a certain temperature by pressing
Device is pasted together, with obtaining finished product glue.
Further, the step 5 are as follows: be sequentially stacked surface layer, enhancement layer, foaming layer, the face being bonded two-by-two uniformly applies
Environment-friendlyglue glue is covered, is pasted by pressing, product must be changed into glue.
Further, the mode of the sprinkling are as follows: sent slurries to elevating hopper with feeding pump, slurries are uniformly sprayed in feeding funnel
It spills；The scraper plate applies the mode scraped are as follows: is uniformly applied and is scraped with the thick scraper plate of control.
Further, the step 34, polyester grid cloth can be substituted with glass-fiber-fabric in 35.
Further, the weight ratio of the PVC powder, color masterbatch powder, hardening agent and water is 100:5:10:150, PVC powder
The weight ratio at end, color masterbatch powder, foaming agent and water is 100:5:10:120, and the weight ratio of PVC powder, foaming agent and water is 100:
10:120.
Further, the surface layer, enhancement layer, foaming layer thickness set according to demand.
After adopting the above technical scheme, the present invention has the advantages that compared with prior art.
The present invention is using PVC powder, color masterbatch powder as base-material, and production obtains surface layer, enhancement layer, foaming layer respectively, and cooperation is each
The different demands of layer add other preparations, and synthetically glue is finally pasted in surface layer, enhancement layer, foaming layer, and individually producing each layer can drop
Low production difficulty improves industrialization degree, and molding ground glue has many advantages, such as that elasticity is good, wearability is good, stability is high, technique stream
Journey is simple, and each layer of production can be independent, is convenient for enterprise implement, has biggish industrial application value.
Specific embodiment
In order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below to the technical side in embodiment
Case is clearly and completely described, and the following examples are used to illustrate the present invention, but are not intended to limit the scope of the present invention..If not
It refers in particular to, all parts, percentage are unit of weight.
Embodiment 1
A kind of ground glue combined producing tech, includes the following steps,
Step 1, it stocks up: being mixed in proportion with PVC powder, color masterbatch powder, hardening agent with water, be uniformly mixing to obtain starchiness
PVC solution；It is mixed in proportion with PVC powder, color masterbatch powder, foaming agent with water, is uniformly mixing to obtain starchy PVC foam
Mixed solution；It is mixed in proportion with PVC powder, foaming agent with water, is uniformly mixing to obtain starchiness frothing solution.Wherein, PVC powder
The weight ratio at end, color masterbatch powder, hardening agent and water be 100:5:10:150, PVC powder, color masterbatch powder, foaming agent and water weight
For amount than being 100:5:10:120, the weight ratio of PVC powder, foaming agent and water is 100:10:120, according to how much proportions of dosage,
Water consumption can slightly increase and decrease according to slurry.
Step 2, surface layer: PVC solution is uniformly sprayed in release paper, after scraper plate painting is scraped, is dried into heated oven
It 8-10 seconds, keeps being embossed under certain high temperature by clean steel roller bearing, after being cooled to room temperature, after cutting machine cuts shaping size, obtain
To surface layer.PVC solution is by the way that, into elevating hopper, the transmission for being uniformly spread to release paper (release paper of smooth surface) fills on 1 feeding pump
It sets, then scraped by controlling thick scraper plate painting, it is about 8-10 seconds that release paper transporting apparatus operation 2-3 seconds, which enter heated oven runing time,
What is this time processed is the surface layer of ground glue, and surface layer is by keeping the clean steel roller bearing under certain high-temperature condition by being printed on different decorative patterns
After (pressure roller for also having pure smooth surface) is cooled to normal temperature, by two sides width cutting machine sizing width, it is long to again pass by finished product
Degree cutting machine is cut into fixed length, and what is produced is the surface layer in this combination process.
Step 21: PVC powder, hardening agent being mixed in proportion with water, are stirred into starchiness, is uniformly sprayed to release
On paper, after scraper plate painting is scraped, is dried 8-10 seconds into heated oven, obtain sparkling and crystal-clear wearing layer.PVC powder+water+hardening agent is abundant
It is mixed into paste-like, by the way that the transmission device of release paper (release paper of smooth surface) is uniformly spread on 1 feeding pump into elevating hopper,
Scrape release paper transporting apparatus and run that enter within 2-3 second heated oven runing time be about 8-10 seconds by controlling thick scraper plate painting again, formation
Sparkling and crystal-clear wearing layer.
Step 3, enhancement layer: PVC solution is uniformly sprayed in release paper, after scraper plate painting is scraped, is dried into heated oven
8-10 seconds dry, strengthened layer.Specifically it is divided into,
Step 31, PVC solution is uniformly sprayed in release paper, after scraper plate painting is scraped, dries 8-10 into heated oven
Second, obtain the first enhancement layer.PVC solution passes through in the release paper for being uniformly sprinkling upon smooth surface to hopper on 1 feeding pump, by controlling
It is about 8-10 seconds that thick scraper plate painting, which is directly entered heated oven runing time after scraping, forms first layer enhancement layer.
Step 32, layer of glass fiber fabric is added on the basis of first layer enhancement layer, is pressed together on first layer by roller bearing and reinforces
On layer.Addition is equal to fiberglass layer (the base area glue different demands increase and decrease glass of grown place glue width on the basis of the first enhancement layer
Nanogram weight (g/ ㎡)).
Step 33, PVC solution is uniformly sprayed on glass-fiber-fabric, after scraper plate painting is scraped, dries 8-10 into heated oven
Second, form the second enhancement layer.PVC solution on 2 feeding pumps to hopper by being uniformly sprinkling upon on glass-fiber-fabric, by controlling thick scraper plate
Painting is directly entered heated oven runing time after scraping be about 8-10 seconds, forms the second enhancement layer.
Step 34, a strata ester grid cloth is added on the basis of second layer enhancement layer, is pressed together on the second layer by roller bearing
On enhancement layer.Second layer enhancement layer adds polyester grid cloth (the specification 4mm*4mm/3mm*3mm for being equal to grown place glue width
It is with good grounds need plus the grid cloth (g/ ㎡) of different size), (glass-fiber-fabric simultaneously sometimes is pressed on second layer enhancement layer by roller bearing
With polyester grid cloth, product demand is mainly seen).
Step 35, PVC solution is uniformly sprayed on polyester grid cloth, after scraper plate painting is scraped, is dried into heated oven
8-10 seconds, third enhancement layer is formed, after being cooled to room temperature, arrives finished product enhancement layer after cutting machine cuts shaping size.
PVC solution is applied by 3 feeding pumps to be uniformly sprinkling upon on the enhancement layer that secondary painting is scraped three times to hopper on feeding pump, thick by control
It is about that carry out within 8-10 seconds is to apply that scrape is that enhancement layer (pays attention to this step for four times that heated oven runing time is directly entered after scraper plate
Solution quantitative foaming agent can also be added as needed) be cooled to normal temperature after, be formed by two sides width cutting machine wide
Degree again passes by finished product length cutting machine and is cut into fixed length, and what is produced is the enhancement layer of this combination process.
Step 4, foaming layer: PVC foam mixed solution is uniformly sprayed in release paper, after scraper plate painting is scraped, into adding
Oven heat is dried 8-10 seconds, then frothing solution is uniformly sprayed above, obtains first product after scraper plate painting is scraped, first product is by back
Plate sizing axis extrudes backboard shape, enters heated oven within operation 2-3 seconds and dries 8-10 seconds, after cutting machine cutting shaping size,
Obtain foaming layer.PVC foam mixed solution passes through in the release paper for being uniformly sprinkling upon on 1 feeding pump to hopper and applying and scraping smooth surface,
It is about 8-10 seconds being directly entered heated oven runing time after controlling thick scraper plate, what this time painting of progress was scraped is foaming layer；
Frothing solution applies by 2 feeding pumps and scrapes four foaming layers that painting is scraped, and is the first product of foaming layer by above-mentioned process, warp
It crosses backboard sizing axis and extrudes backboard shape (to guarantee that backboard is smooth, uniformly discharging frothing inhibitor before backboard sizing axis) operation 2-
It is about 8-10 seconds, after being cooled to normal temperature that 3 seconds, which enter heated oven runing time, is formed by two sides width cutting machine wide
Degree, again passes by finished product length cutting machine and is cut into fixed length, what is produced is the foaming layer of this combination process.
Step 5, compound: sparkling and crystal-clear wearing layer, surface layer, enhancement layer, foaming layer are sequentially stacked, pasted through hot paste or pressing,
With obtaining finished product glue.There are two types of the modes that each layer is combined with each other, and one is hot pastes: by the surface layer of above step, enhancement layer, hair
After cover of the alveolar layer Jing Guo certain temperature is uniformly pasted together, formed we need the combination process of hot paste sum at
Product ground glue；Another kind is cold patch: it is viscous by pressing that the surface layer of above step, enhancement layer, foaming layer are uniformly coated with Environment-friendlyglue glue
After sticking together, our with needing the finished product of the combination process of cold fitting glue are formed.No matter which kind of mode, obtained finished product
Glue can satisfy performance requirement.Need exist for illustrating, surface layer, enhancement layer, foaming layer thickness set according to demand, generally
The integral thickness of glue have 1.6mm, 2.0mm, 2.2mm, 3.0mm, 3.5mm, 4.0mm, 4.5mm, 5.0mm, 6.0mm, 7.0mm,
8.0mm, 10.0mm, the different requirements of base area glue, thickness requirements, selective decision surface layer, enhancement layer, foaming layer
Thickness.
The present invention is using PVC powder, color masterbatch powder as base-material, and production obtains surface layer, enhancement layer, foaming layer respectively, and cooperation is each
The different demands of layer add other preparations, and synthetically glue is finally pasted in surface layer, enhancement layer, foaming layer, and individually producing each layer can drop
Low production difficulty improves industrialization degree, and molding ground glue has many advantages, such as that elasticity is good, wearability is good, stability is high, technique stream
Journey is simple, and each layer of production can be independent, is convenient for enterprise implement, has biggish industrial application value.
The above is only presently preferred embodiments of the present invention, is not intended to limit the present invention in any form, though
So the present invention has been disclosed as a preferred embodiment, and however, it is not intended to limit the invention, any technology people for being familiar with this patent
Member without departing from the scope of the present invention, when the technology contents using above-mentioned prompt make it is a little change or be modified to
The equivalent embodiment of equivalent variations, but anything that does not depart from the technical scheme of the invention content, it is right according to the technical essence of the invention
Any simple modification, equivalent change and modification made by above embodiments, in the range of still falling within the present invention program.
Claims (10)
1. a kind of ground glue combined producing tech, which is characterized in that include the following steps,
Step 1, it stocks up: mixing, be uniformly mixing to obtain starchy in proportion with PVC powder, color masterbatch powder, hardening agent with water
PVC solution；It is mixed in proportion with PVC powder, color masterbatch powder, foaming agent with water, it is mixed to be uniformly mixing to obtain starchy PVC foam
Close solution；It is mixed in proportion with PVC powder, foaming agent with water, is uniformly mixing to obtain starchiness frothing solution；
Step 2, surface layer: PVC solution is uniformly sprayed in release paper, after scraper plate painting is scraped, dries 8-10 into heated oven
Second, obtain surface layer；
Step 3, enhancement layer: PVC solution is uniformly sprayed in release paper, after scraper plate painting is scraped, dries 8- into heated oven
10 seconds, strengthened layer；
Step 4, foaming layer: PVC foam mixed solution is uniformly sprayed in release paper, after scraper plate painting is scraped, is dried into heating
Case is dried 8-10 seconds, then frothing solution is uniformly sprayed above, obtains first product after scraper plate painting is scraped, first product is fixed by backboard
Profile shaft extrudes backboard shape, enters heated oven within operation 2-3 seconds and dries 8-10 seconds, after cutting machine cuts shaping size, obtains
Foaming layer；
Step 5, compound: surface layer, enhancement layer, foaming layer being sequentially stacked, pasted through hot paste or pressing, with obtaining finished product glue.
2. glue combined producing tech in a kind of ground according to claim 1, which is characterized in that the step 2 are as follows: PVC is molten
Liquid uniformly sprays in release paper, after scraper plate painting is scraped, dries 8-10 seconds into heated oven, keeps under certain high temperature by pure
The embossing of steel roller bearing after being cooled to room temperature, after cutting machine cuts shaping size, obtains surface layer.
3. glue combined producing tech in a kind of ground according to claim 1, which is characterized in that also set between step 2 and step 3
There is step 21: PVC powder, hardening agent being mixed in proportion with water, are stirred into starchiness, uniformly sprays onto release paper,
After scraper plate painting is scraped, is dried 8-10 seconds into heated oven, obtain sparkling and crystal-clear wearing layer；Corresponding, step 5 is will be sparkling and crystal-clear wear-resisting
Layer, surface layer, enhancement layer, foaming layer are sequentially stacked, and are pasted through hot paste or pressing, with obtaining finished product glue.
4. glue combined producing tech in a kind of ground according to claim 1, which is characterized in that the step 3, which is divided, is:
Step 31, PVC solution is uniformly sprayed in release paper, after scraper plate painting is scraped, dries 8-10 seconds, obtain into heated oven
To the first enhancement layer；
Step 32, layer of glass fiber fabric is added on the basis of first layer enhancement layer, is pressed together on first layer enhancement layer by roller bearing；
Step 33, PVC solution is uniformly sprayed on glass-fiber-fabric, after scraper plate painting is scraped, is dried 8-10 seconds into heated oven, shape
At the second enhancement layer；
Step 34, a strata ester grid cloth is added on the basis of second layer enhancement layer, is pressed together on the second layer by roller bearing and is reinforced
On layer；
Step 35, PVC solution is uniformly sprayed on polyester grid cloth, after scraper plate painting is scraped, dries 8-10 into heated oven
Second, third enhancement layer is formed, after being cooled to room temperature, arrives finished product enhancement layer after cutting machine cuts shaping size.
5. glue combined producing tech in a kind of ground according to claim 1, which is characterized in that the step 5 are as follows: by surface layer,
Enhancement layer, foaming layer are sequentially stacked, and are pasted together at a certain temperature by cover, with obtaining finished product glue.
6. glue combined producing tech in a kind of ground according to claim 1, which is characterized in that the step 5 are as follows: by surface layer,
Enhancement layer, foaming layer are sequentially stacked, and the face being bonded two-by-two uniformly coats Environment-friendlyglue glue, are pasted by pressing, with must changing into product glue.
7. -4 any a kind of ground glue combined producing tech according to claim 1, which is characterized in that the mode of the sprinkling
Are as follows: slurries are sent to elevating hopper with feeding pump, slurries are uniformly sprayed in feeding funnel；The scraper plate applies the mode scraped are as follows: thick with control
Scraper plate is uniformly applied and is scraped.
8. glue combined producing tech in a kind of ground according to claim 4, which is characterized in that the step 34, polyester in 35
Grid cloth can be substituted with glass-fiber-fabric.
9. glue combined producing tech in a kind of ground according to claim 1, which is characterized in that the PVC powder, color masterbatch powder
End, hardening agent and water weight ratio be 100:5:10:150, PVC powder, color masterbatch powder, foaming agent and water weight ratio be 100:
5:10:120, the weight ratio of PVC powder, foaming agent and water are 100:10:120.
10. glue combined producing tech in a kind of ground according to claim 1, which is characterized in that the surface layer, enhancement layer, hair
The thickness of alveolar layer is set according to demand.