CN109610071A - A kind of production technology of terylene imitated cotton yarn conducting fabric - Google Patents
A kind of production technology of terylene imitated cotton yarn conducting fabric Download PDFInfo
- Publication number
- CN109610071A CN109610071A CN201811449780.2A CN201811449780A CN109610071A CN 109610071 A CN109610071 A CN 109610071A CN 201811449780 A CN201811449780 A CN 201811449780A CN 109610071 A CN109610071 A CN 109610071A
- Authority
- CN
- China
- Prior art keywords
- cotton yarn
- machine
- production technology
- yarn
- conducting fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production technologies of terylene imitated cotton yarn conducting fabric, 100D/72F special yarn is used to pass through as first, 75D conductive yam is second warp, first is arranged through second through 1:1, the warped length of warping machine is set as 5600m, warping radical is set as 10098, warped length carries out beaming after reaching, denting selects No. 17 reeds, every reed 3 penetrates, reed width is 198cm, 28 shuttles of weft density on machine/cm is set, Cropping Length is set as 200 meters/, 180D special type is used to imitate cotton yarn as weft yarn, Quan Jiawei sprays latitude, card is 2/2 twill-weave, speed is controlled in 650r/min, use storage latitude roller rotation type weft accumulator.The product dyeing effect of the production technology preparation of the terylene imitated cotton yarn conducting fabric is good, and anti-static effect is good, is made comfortable and easy to wear after ready-made clothes.
Description
Technical field:
The present invention relates to field of textiles, are especially a kind of production technology of terylene imitated cotton yarn conducting fabric.
Background technique:
Imitative cotton product orientation is the good characteristic for having cotton Yu polyester (PET) fiber concurrently, reaches imitative cotton like cotton, imitative cotton and wins cotton
Effect.Conductive yam by a certain proportion of stainless steel fibre or other conductive fibers with general fibre is blended is made, conductive yam energy
Make to accumulate in the electrostatic on human body to disappear quickly, is mostly used for anti-static clothing.It is made although having imitate cotton yarn on the market
Conducting fabric, but this kind of shell-fabric dyeing and finishing effect is poor, and color is securely bad, and for conductive effect, reduces and take comfort level.
Summary of the invention:
The technical problem to be solved by the invention is to provide a kind of lifes of the good terylene imitated cotton yarn conducting fabric of dyeing effect
Production. art, the product of production technology preparation are made comfortable and easy to wear after ready-made clothes, and anti-static effect is good.
The technical solution of the invention is as follows, provides a kind of production technology of terylene imitated cotton yarn conducting fabric, uses 100D/
72F special yarn is passed through as first, and 75D conductive yam is second warp, and first is arranged through second through 1:1, and the warped length of warping machine is set as
5600m, warping radical are set as 10098, and warped length carries out beaming after reaching, denting selects No. 17 reeds, and every reed 3 penetrates,
Reed width is 198cm, and 28 shuttles of weft density on machine/cm is arranged, and Cropping Length is set as 200 meters/, use 180D special type imitate cotton yarn as
Weft yarn, full first latitude spray latitude, and card is 2/2 twill-weave, and speed control stores up latitude in 650r/min, using storage latitude roller rotation type
Device;Fabric examines through original cloth after finishing the weaving, uncoiling, and connector, white embryo clot cold dome makes cloth cover obtain uniform shrinkage, then carry out
Pre-treatment, when pre-treatment, are directly entered preshrinking machine, and 180 DEG C of preshrinking machine set temperature, the cloth cover that preshrinking machine is handled well enters predetermined
Type machine, pre-setting temperature setting are 200 DEG C, and speed 30m/min, through then being dyed to overfeeding 10%, technique is set as
Acid dyes 4%, high-efficiency polyester disperse dyes 2g/L, pH adjusting agent AB-45 1g/L, Ao and dispersing agent 1g/L, bath raio 1:7, dye
The color time is 95 DEG C of * 60min, and temperature rate is 0.5 DEG C/min.
Preferably, further including arranging sizing again, setting temperature is 160-170 DEG C, time 30-60s, and clear water is added
Softening agent 10g/L, nonionic antistatic 10g/L, super hair softening agent 10g/L, speed 60m/min, overfeeding 4-5%, process use
One immersing and rolling, pick-up rate 5%.
Further, fixation treatment, process conditions are also carried out when dyeing are as follows: acidic color fixing agent 1.5g/L, glacial acetic acid 1g/L,
Bath raio 1:7, color fixing temperature time are 80 DEG C of * 40min.Dyeing completes cloth and enters automatic dehydrator, and dewatering time is about
15min。
After the above technical solution is adopted compared with prior art, the invention has the following advantages that the product is primarily adapted for use in
Work clothes, ready-made clothes moisture absorbing and sweat releasing is personal, comfortable and easy to wear, very real in the workplace that electrostatic can impact working environment
With the electrostatic of generation can be discharged by the conductive fiber in conductive yam rapidly, play the role of to safety work highly important.Together
When, for this product since dyeing effect is good, color is securely high, can also be applied to autumn and winter clothes, thermal property is good, and the autumn and winter
It is electrostatic multiple season, a large amount of electrostatic will not be generated using the clothes of this fabric.
Specific embodiment:
With regard to specific embodiment, the invention will be further described below:
A kind of production technology of terylene imitated cotton yarn conducting fabric, it is raw using the 4th textile machine Manufacturing Co., Ltd of Jiangyin
The SHGA215C sectional warper of production uses 100D/72F special yarn to pass through as first, and 75D conductive yam is second warp, and first is through second through 1:1
Arrangement, the warped length of warping machine are set as 5600m, and warping radical is set as 10098, and warped length is fallen after reaching
Axis, denting select No. 17 reeds, and every reed 3 penetrates, reed width 198cm, and 28 shuttles of weft density on machine/cm is arranged, and Cropping Length is set as 200
Rice/, use 180D special type to imitate cotton yarn as weft yarn, full first latitude sprays latitude, and card is 2/2 twill-weave, and speed is controlled in 650r/
Min uses storage latitude roller rotation type weft accumulator.
Dyeing and finishing technology are as follows: fabric is examined through original cloth, and inspection content includes physical index and cloth cover flaw, through uncoiling, connector,
White embryo clot cold dome, makes cloth cover obtain uniform shrinkage, for next procedure further bounce back increase elasticity carry out adequate preparation.Due to
For the product of our company's production without starching, pretreatment stage does not need open-width desizing, is prepared to enter into preshrinking machine, preshrinking machine setting
180 DEG C of temperature, the cloth cover that preshrinking machine is handled well enters pre-setting machine, and pre-setting temperature setting is 200 DEG C, speed 30m/min,
Through to overfeeding 10%, since spandex covered yarn linear elasticity is excellent, machine back panel wide direction relaxation shrinkage is up to 40%-50% under embryo cloth,
It needs by preshrunk pre-setting, so that the regulation breadth of fabric and relaxation shrinkage reach balance.Technique is set as De Sida import acid
Property dyestuff (O.W.F) 4%, high-efficiency polyester disperse dyes 2g/L, PH regulator AB-45 1g/L, Ao and dispersing agent TF-510C
1g/L, bath raio 1:7, dyeing time are 95 DEG C of * 60min, and temperature rate is 0.5 DEG C/min.
To make cloth cover have higher color fastness, imitative cotton conducting fabric color fastness can reach 4 grades, fixation work can be added
Skill, process conditions are as follows: acidic color fixing agent 1.5g/L, ice vinegar 1g/L, bath raio 1:7, the color fixing temperature time is 80 DEG C of * 40min.Dyeing
It completes cloth and enters ZSH-2000 type automatic dehydrator, dewatering time is about 15min.
To make cloth cover have more good feel, style, breadth, the cloth for being dehydrated completion can arrange sizing again.One
As setting setting temperature be 160-170 DEG C, time 30-60s, be added clear water softening agent TF-406B10g/L, nonionic resists quiet
Electric TF-480A 10g/L, super hair softening agent 10g/L, speed 60m/min, overfeeding 4-5%, process use an immersing and rolling, pick-up rate
It is 5%.
The product is primarily adapted for use in work clothes, and ready-made clothes moisture absorbing and sweat releasing is personal, comfortable and easy to wear, can make to working environment in electrostatic
Very practical at the workplace of influence, the electrostatic of generation can be discharged by the conductive fiber in conductive yam rapidly, to safety work
Play the role of highly important.Meanwhile this product due to dyeing effect it is good, color fastness is high, can also be applied to autumn and winter
Clothes, thermal property is good, and the autumn and winter are electrostatic multiple seasons, will not generate a large amount of electrostatic using the clothes of this fabric.
Claims (3)
1. a kind of production technology of terylene imitated cotton yarn conducting fabric, it is characterised in that: use 100D/72F special yarn to pass through as first,
75D conductive yam is second warp, and first is arranged through second through 1:1, and the warped length of warping machine is set as 5600m, and warping radical is set as
10098, warped length carries out beaming after reaching, and denting selects No. 17 reeds, and every reed 3 penetrates, reed width 198cm, machine in setting
28 shuttles of filling density/cm, Cropping Length are set as 200 meters/, use 180D special type to imitate cotton yarn as weft yarn, full first latitude sprays latitude, card
For 2/2 twill-weave, speed control uses storage latitude roller rotation type weft accumulator in 650r/min;Fabric is after finishing the weaving through original
Cloth examines, uncoiling, and connector, white embryo clot cold dome makes cloth cover obtain uniform shrinkage, then carry out pre-treatment, when pre-treatment directly into
Enter preshrinking machine, 180 DEG C of preshrinking machine set temperature, the cloth cover that preshrinking machine is handled well enters pre-setting machine, and pre-setting temperature setting is
200 DEG C, speed 30m/min, through then being dyed to overfeeding 10%, technique is set as acid dyes 4%, high-efficiency polyester
Disperse dyes 2g/L, pH adjusting agent AB-45 1g/L, Ao and dispersing agent 1g/L, bath raio 1:7, dyeing time are 95 DEG C of * 60min,
Temperature rate is 0.5 DEG C/min.
2. the production technology of terylene imitated cotton yarn conducting fabric according to claim 1, it is characterised in that: further include whole again
Reason sizing, setting temperature are 160-170 DEG C, time 30-60s, and clear water softening agent 10g/L, the antistatic 10g/ of nonionic is added
L, super hair softening agent 10g/L, speed 60m/min, overfeeding 4-5%, process use an immersing and rolling, pick-up rate 5%.
3. the production technology of terylene imitated cotton yarn conducting fabric according to claim 1, it is characterised in that: also carried out when dyeing
Fixation treatment, process conditions are as follows: acidic color fixing agent 1.5g/L, glacial acetic acid 1g/L, bath raio 1:7, color fixing temperature time are 80 DEG C of *
40min.Dyeing completes cloth and enters automatic dehydrator, and dewatering time is about 15min.