CN109593490A - A kind of glue and its adhesion technique flutterred for bonding multi layer colour solid latex powder - Google Patents
A kind of glue and its adhesion technique flutterred for bonding multi layer colour solid latex powder Download PDFInfo
- Publication number
- CN109593490A CN109593490A CN201811373521.6A CN201811373521A CN109593490A CN 109593490 A CN109593490 A CN 109593490A CN 201811373521 A CN201811373521 A CN 201811373521A CN 109593490 A CN109593490 A CN 109593490A
- Authority
- CN
- China
- Prior art keywords
- glue
- parts
- natural rubber
- nitrile rubber
- powder puff
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The glue and adhesion technique that the invention discloses a kind of to flutter for bonding multi layer colour solid latex powder, the glue include the ingredient of following parts by weight: 1~3 part of toluene, 15~40 parts of nitrile rubber, 15~40 parts of natural rubber, 400~600 parts of water.The present invention is by can be deployed into the glue that can be used for pasting, the product of different colours is pasted and is can be processed afterwards using raw material adjustment proportion together.Latex powder puff is mainly with nitrile rubber, butadiene-styrene rubber, natural rubber forms a kind of machinable product blank material after high temperature vulcanized reaction, and raw material of the invention is from the raw material nitrile rubber of the processing of latex powder puff, natural rubber, the raw material processed by the allotment of glue from powder puff, so characteristic and service performance and the performance of powder puff are the same, the product processed is bonded in glue layer junction, it is squeezed by external force indeformable, it is not hardened, it is non-yellowing, not delamination, the practicability that powder puff itself has is not changed, the class ornamental value and collection of product are increased simultaneously.
Description
Technical field
The present invention relates to cosmetic applicators processing technique fields, more particularly to one kind is for bonding multi layer colour solid latex powder
Glue flutterred and preparation method thereof.
Background technique
Latex powder puff is mainly with nitrile rubber (NBR), butadiene-styrene rubber (SBR), natural rubber (NR) by high temperature vulcanized
A kind of machinable product blank material is formed after reaction.Traditional powder puff processing can only generally be foamed using the product of solid color
And process, multilayered color-forming product can not be bonded together processing.And manufacturing procedure is loaded down with trivial details, fabrication cycle is long.The reason is that every time
Needed after bonding by the static precompressed of pressing plate two more than hour, and place drying chamber dry four more than hour just can be carried out it is next
Process processing, and bond after latex powder puff it is soaked after be easy to tear it is rotten.
Summary of the invention
The present invention is to solve existing technological deficiency, provides a kind of glue flutterred for bonding multi layer colour solid latex powder
Water and its adhesion technique.Glue of the invention realizes the application processing of multi layer colour powder puff, changes traditional solid color powder puff
Processing method, increase powder puff processing number of ways and meet different consumer demands, improve powder puff appreciative value and can
Collection.
Its specific technical solution is as follows: the glue flutterred for bonding multi layer colour solid latex powder, the glue packet
Include the ingredient of following parts by weight: 1~3 part of toluene, 15~40 parts of nitrile rubber, 15~40 parts of natural rubber, 400~600 parts of water.
The present invention is by that can be deployed into the glue that can be used for pasting, by the production of different colours using raw material adjustment proportion
Product are pasted to be can be processed afterwards together.Latex powder puff is mainly with nitrile rubber (NBR), butadiene-styrene rubber (SBR), natural rubber (NR)
Form a kind of machinable product blank material after high temperature vulcanized reaction, and raw material of the invention from latex powder puff plus
Raw material nitrile rubber, the natural rubber of work, because of the raw material that the allotment of glue is processed from powder puff, so characteristic and service performance
Performance with powder puff be it is the same, bond the product that processes in glue layer junction, squeezed by external force indeformable, constant
Firmly, non-yellowing, not delamination does not change the practicability that powder puff itself has, while increasing the class ornamental value and collection of product.
Preferably, the glue includes the ingredient of following parts by weight: 2 parts of toluene, 32 parts of nitrile rubber, natural rubber 30
Part, 500 parts of water.
Preferably, the glue includes the ingredient of following parts by weight: 1.8 parts of toluene, 22 parts of nitrile rubber, natural rubber
20 parts, 500 parts of water.
Preferably, the mass ratio of nitrile rubber and natural rubber is (20~26): (22~16).In nitrile rubber and naturally
Total rubber content be 42 parts in the case where, the different mass ratio of the two can have an impact the performance of glue, when nitrile rubber with
The mass ratio of natural rubber is (20~26): when (22~16), tool is in invagination situation, dropping situations, delamination, deformation feelings
Condition, the situation that is hardened, jaundice situation have good evaluation result, it is highly preferred that working as the mass ratio of nitrile rubber and natural rubber
For (21~24): when (21~18), evaluation effect is more excellent, when the mass ratio of nitrile rubber and natural rubber is 22:20, reaches
To optimal effect.
Preferably, the preparation method of the glue is to mix toluene, nitrile rubber, natural rubber and water according to the weight ratio
It closes uniform.
The present invention also provides a kind of technique for carrying out bonding multiple color face powder puff with the glue, the technique is by powder puff
Raw material is put into square box and foams to obtain different colours powder puff sheet material, then sheet material is carried out prebake, with the glue after drying
The bonding place for being coated in each sheet material is bonded, then is taken by sheet material 40~60 minutes after the fixed fitting of pressure frame, then by sheet material
Dried again out, after drying with clamping plate mould press from both sides 30~50 minutes, then lift down carry out drying can edging.
Preferably, the temperature of the prebake and drying is 65~75 DEG C.
Beneficial effects of the present invention: the glue main component used is raw material nitrile rubber, natural rubber, with product spy
Property is consistent；The product that processes is bonded in glue layer junction, by external force squeeze it is indeformable, be not hardened, it is non-yellowing, do not take off
Layer；The present invention provides powder puff processing novel approach, realize the novel powder puff that different colours are integrated in one, and it is practical to collect traditional powder puff
Property and novel powder puff appreciative value are.
Detailed description of the invention
Fig. 1 is the sheet material of the powder puff bonded using glue of the present invention；
Fig. 2 is the powder puff perspective view after being bonded using glue of the present invention；
Fig. 3 is the powder puff perspective view after being bonded using glue of the present invention.
Specific embodiment
The present invention is further described in detail with reference to the accompanying drawing, these attached drawings are simplified schematic diagram, only
The basic structure that the invention is illustrated in a schematic way, the direction of this specific implementation is using the direction Fig. 1 as standard.
Embodiment 1
As of the invention for bonding a kind of embodiment for the glue that multi layer colour solid latex powder is flutterred, the glue
Ingredient including following parts by weight: 2 parts of toluene, 32 parts of nitrile rubber, 30 parts of natural rubber, 500 parts of water.
The preparation method of glue of the invention is to carry out toluene, nitrile rubber, natural rubber, water that system is mixed evenly
?.
The glue of the present embodiment is applied to the bonding of multiple color face powder puff, adhesion technique is the following steps are included: by powder puff original
Material is put into square box and foams to obtain different colours powder puff sheet material, then by sheet material in 65~75 DEG C of progress prebakes, such as Fig. 1 institute
Show, bonded after drying with the bonding place 1 that glue of the invention is coated in each sheet material, is divided into 3 one layer and 4 one layer of progress
Fitting, then by sheet material 40~50 minutes after the fixed fitting of pressure frame, then sheet material is taken out and is dried at 65~75 DEG C, it dries
Afterwards with clamping plate mould press from both sides 30~50 minutes, then lift down carry out drying can edging.Powder puff such as Fig. 2 institute of the present embodiment production
Show, is flutterred for seven toners.
Embodiment 2
As of the invention for bonding a kind of embodiment for the glue that multi layer colour solid latex powder is flutterred, the glue
Ingredient including following parts by weight: 1.8 parts of toluene, 22 parts of nitrile rubber, 20 parts of natural rubber, 500 parts of water.
The glue preparation method of the present embodiment is same as Example 1.
The glue of the present embodiment is applied to the bonding of multiple color face powder puff, adhesion technique is the following steps are included: by powder puff original
Material is put into square box and foams to obtain two kinds of color powder puff sheet materials, then sheet material is dried at 65~75 DEG C, with this after drying
The glue of invention is coated to be bonded in the bonding place of each sheet material, then by sheet material 50 minutes after the fixed fitting of pressure frame, then
Sheet material is taken out and is dried at 65~75 DEG C, is pressed from both sides 25 minutes after drying with clamping plate mould, then is lifted down and dry and can grind
Side.
Embodiment 3
As of the invention for bonding a kind of embodiment for the glue that multi layer colour solid latex powder is flutterred, the glue
Ingredient including following parts by weight: 1 part of toluene, 15 parts of nitrile rubber, 15 parts of natural rubber, 400 parts of water.
The glue preparation method and adhesion technique of the present embodiment are same as Example 1.
Embodiment 4
As of the invention for bonding a kind of embodiment for the glue that multi layer colour solid latex powder is flutterred, the glue
Ingredient including following parts by weight: 3 parts of toluene, 40 parts of nitrile rubber, 40 parts of natural rubber, 600 parts of water.
The glue preparation method and adhesion technique of the present embodiment are same as Example 1.
Comparative example 1
The adhesion technique difference from Example 1 of this comparative example is that glue used is commercial product.
Embodiment 5
Volunteer 80 are chosen, the multiple color face powder puff after being bonded with the glue of embodiment 1 to 4 and comparative example 1, which is used, appoints
Meaning, which is held, to be squeezed color and connects level, using blank scoring mechanism, respectively from the invagination situation of glue layer junction, fall off feelings
Condition, delamination, turn to be yellow, be hardened and by powder puff it is soaked after whether be easy to tear it is rotten score, each full marks is 10 points, invagination
With squeeze after powder puff rebound do not invaginated completely for 10 points, not falling off completely is 10 points, completely it is not stratified be 10 points and difficulty tear it is rotten
It is 10 points, appraisal result is as shown in table 1:
Table 1
| Invagination situation | Dropping situations | Delamination | Jaundice | It is hardened | Tear rotten situation | |
| Embodiment 1 | 10 | 9.9 | 10 | 10 | 9.9 | 9.9 |
| Embodiment 2 | 10 | 10 | 10 | 10 | 10 | 10 |
| Embodiment 3 | 9.8 | 9.6 | 9.5 | 9.4 | 9.6 | 9.8 |
| Embodiment 4 | 9.8 | 9.6 | 9.7 | 9.5 | 9.7 | 9.7 |
| Comparative example 1 | 7.5 | 7.6 | 7.5 | 7.1 | 7.0 | 7.3 |
As seen from Table 1, the powder puff of bonding different color is carried out using glue of the invention, powder puff is held with any
It squeezes color to connect level, has and do not invaginate, do not fall off, is not stratified, is indeformable, not being hardened, is non-yellowing, so that product has pole
High ornamental value and usability, and the evaluation of its various aspects is much higher than comparative example 1.
Embodiment 6
The present embodiment, which has investigated nitrile rubber and the weight ratio of natural rubber, influences the performance of glue of the invention, this reality
Apply a difference from Example 2 to be only that, the difference of the weight ratio of the nitrile rubber and natural rubber, other with reality
It is identical to apply example 2, wherein the parts by weight content of nitrile rubber and natural rubber is as shown in table 2；
Table 2
The glue that the preparation of experimental group 1~9 is respectively adopted is evaluated, and evaluation method is as described in Example 5, and evaluation result is such as
Shown in table 3:
Table 3
As can be seen from Table 3, in the case where nitrile rubber and natural rubber total content are 42 parts, the different mass ratio of the two
The performance of glue can be had an impact, when the mass ratio of nitrile rubber and natural rubber is (20~26): when (22~16), tool
There is good evaluation result in invagination situation, dropping situations, delamination, deformation, the situation that is hardened, jaundice situation, more
Preferably, when the mass ratio of nitrile rubber and natural rubber is (21~24): when (21~18), evaluation effect is more excellent, works as fourth
When the mass ratio of nitrile rubber and natural rubber is 22:20, reach optimal effect.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Within mind and principle, any modification, equivalent substitution, improvement and etc. done be should be included within the scope of the present invention.
Claims (9)
1. for bonding the glue that multi layer colour solid latex powder is flutterred, which is characterized in that the glue includes following parts by weight
Ingredient: 1~3 part of toluene, 15~40 parts of nitrile rubber, 15~40 parts of natural rubber, 400~600 parts of water.
2. glue according to claim 1, which is characterized in that the glue includes the ingredient of following parts by weight: toluene 2
Part, 32 parts of nitrile rubber, 30 parts of natural rubber, 500 parts of water.
3. glue according to claim 1, which is characterized in that the glue includes the ingredient of following parts by weight: toluene
1.8 parts, 22 parts of nitrile rubber, 20 parts of natural rubber, 500 parts of water.
4. glue according to claim 1, which is characterized in that the mass ratio of nitrile rubber and natural rubber be (20~
26): (22~16).
5. glue according to claim 1, which is characterized in that the mass ratio of the nitrile rubber and natural rubber is (21
~24): (21~18).
6. glue according to claim 1, which is characterized in that the mass ratio of the nitrile rubber and natural rubber is 22:
20。
7. glue according to claim 1, which is characterized in that the preparation method of the glue be by toluene, nitrile rubber,
Natural rubber and water are uniformly mixed according to the weight ratio.
8. a kind of technique for carrying out bonding multiple color face powder puff with the described in any item glue of claim 1 to 7, which is characterized in that institute
Stating technique is powder puff raw material to be put into square box to foam to obtain different colours powder puff sheet material, then sheet material is carried out prebake, is dried
It is bonded after dry with the bonding place that the glue is coated in each sheet material, then pressure frame is fixed into 40~60 points of sheet material after fitting
Clock, then sheet material taking-up is dried again, it is pressed from both sides 30~50 minutes after drying with clamping plate mould, then lift down and dry and can grind
Side.
9. technique according to claim 8, which is characterized in that the temperature of the prebake and drying is 65~75 DEG C.