CN109576870A - A kind of production method of mould proof cloth - Google Patents
A kind of production method of mould proof cloth Download PDFInfo
- Publication number
- CN109576870A CN109576870A CN201910076171.5A CN201910076171A CN109576870A CN 109576870 A CN109576870 A CN 109576870A CN 201910076171 A CN201910076171 A CN 201910076171A CN 109576870 A CN109576870 A CN 109576870A
- Authority
- CN
- China
- Prior art keywords
- yarn
- fabric
- mould proof
- cloth
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of production methods of mould proof cloth, comprising the following steps: A, prepares material: preparing the material for mould proof cloth yarn of weaving, and divides according to allocation ratio;B, thread material is handled: the material for being used to spin is pre-processed;C, it spins: the yarn handled well being subjected to comb yarn, the material combed is spinned;D, it dyes: the yarn weaved is dyed, and the yarn after dyeing is subjected to thermophilic digestion;E, fabric is weaved: the yarn spun first being carried out warping, the good yarn of warping is carried out cloth weaving;F, fabric is handled: yarn extra on the fabric weaved is removed;G, it cleans: being cleaned after web surface is handled, and the cloth of cleaning is subjected to drying and processing, this fabric antibiotic property of the invention is strong, by still keeping good anti-microbial property after repeatedly washing, the mould proof anti-mite finishing agent ABM used in formula, so that the fabric, has good acid-fast alkali-proof, resistance to mould.
Description
Technical field
The present invention relates to the manufacture technology field of mould proof cloth, specially a kind of production method of mould proof cloth.
Background technique
Clothes are made with fabric, and fabric is exactly the material for making clothes.As one of clothes three elements, fabric
The style and characteristic of clothes can be not only annotated, but also directly controls the expression effect of the color of clothes, moulding.Presentation is come from
The noble quality of body is perfect, soft.
China is the big country of 1,300,000,000 populations, is the maximum Clothing Consuming state in the whole world and producing country.Chinese in recent years
Rag trade has biggish development, and the development of rag trade has pushed the development of China's national economy, textile garment in 2005 significantly
The gross output value account for about 1/10th of the national gross output value, and continuous 5 years foreign exchange earning favorable balances first, clothes industry are always
Chinese exports, which are earned foreign exchange, has made huge contribution.China has become the maximum garment production processing base in the whole world, full generation simultaneously
Every three clothes in boundary, wherein one from domestic product.
Fabric is the important raw material for manufacturing ready-made clothes, and existing fabric variety is numerous, but with people's living standard
Raising, it is desirable to provide be able to satisfy different crowd needs new varieties.Requirement of the people to clothes not only to clothes fashion, do
The requirement of work is more the requirement to clothes quality, this requires to get caught up in the development of clothing form on garment material,
The feature of the fabrics such as functional, comfortable, environmental protection, health becomes the topic that people increasingly pay close attention to.
But many things will appear mildew, not only food will appear mildew, and clothing in certain circumstances equally can be mould
Become, fabric is also in this way, mould is a part of fungi, its main feature is that mycelium is more developed, without biggish fructification.With other
Fungi is the same, also there is cell wall, and parasitic or saprophytic mode is survived.Mould some makes food be changed into noxious material, some possibility
Toxin, i.e. mycotoxin are generated in food.Since finding aflatoxin, the pollution of mould and mycotoxin to food
Increasingly draw attention.It is very harmful caused by human health, it is mainly shown as that slow poisoning, carcinogenic, teratogenesis, mutagenesis are made
With.
Mould is the general designation to form the fungi of branch mycelia.It is not taxonomic noun, Eumycota is belonged in classification
Each subphylum.The basic unit for constituting mould body is known as mycelia, is in elongated tubular, 2~10 microns of width, can constantly grow from front end
And branch.Without every or have every tool 1 is to multiple nucleus.Cell wall is divided into three layers: the unbodied beta glucan of outer layer (87nm);In
Layer is glycoprotein, protein net central filler glucan (49nm);Internal layer is chitin microfibre, is mingled with amorphous protein
(20nm).When growing on solid matrix, part mycelia gos deep into matrix absorption nutriment, referred to as matrix mycelia or vegetative hyphae;To
The title aerial hyphae stretched in the air can further develop for vegetative hyphae, generation spore.A large amount of mycelia are woven into villiform, wadding
Shape is netted etc., referred to as mycelium.Mycelium normal white, brown, grey, or (bacterium colony is that white is hairy in chromatic colour
Be Mucor, green for mould, yellow is aspergillus flavus), some, which can produce pigment, makes coloration of substrates.Mould breeding is rapid,
The a large amount of Biodeteriorations of food, apparatus are often resulted in, but many beneficial types have been widely used, is sharp earliest in human practice activity
With the quasi-microorganism with understanding.
Therefore, many fabrics for specific use can all carry out mould proof processing at present, or be spun using mould proof material
It is made into fabric.
Summary of the invention
The purpose of the present invention is to provide a kind of environmental protection, the production method of comfortable mould proof cloth, to solve above-mentioned background
The problem of being proposed in technology.
To achieve the above object, the invention provides the following technical scheme: a kind of production method of mould proof cloth, including it is following
Step: a kind of production method of mould proof cloth, the following steps are included:
A, prepare material: preparing the material for mould proof cloth yarn of weaving, and divide according to allocation ratio;
B, thread material is handled: the material for being used to spin is pre-processed;
C, it spins: the yarn handled well being subjected to comb yarn, the material combed is spinned;
D, it dyes: the yarn weaved is dyed, and the yarn after dyeing is subjected to thermophilic digestion;
E, fabric is weaved: the yarn spun first being carried out warping, the good yarn of warping is carried out cloth weaving;
F, fabric is handled: yarn extra on the fabric weaved is removed;
G, it cleans: being cleaned after web surface is handled, and the cloth of cleaning is subjected to drying and processing.
Preferably, the material according to step A for mould proof cloth yarn of weaving includes 30-60 parts of bamboo charcoal fiber, ox
20-30 parts of milk proem fiber, 10-15 parts of ramee, 15-35 parts of tencel fiber, 15-35 parts of Wormwood fiber, antibacterial finishing agent
10-12, mould proof anti-mite finishing agent ABM3-12 parts.
Preferably, described ready material is put into clear water according to step B is cleaned, and is put into after cleaning
30min-60min is impregnated in 15% sodium hydroxide solvent, pulls drying after immersion out.
Preferably, the material consolidation of the spinning that will have been pre-processed according to step C is neat, by bamboo charcoal fiber, milk
Azelon, ramee, tencel fiber, Wormwood fiber carry out twisted filament using twisting frame according to: the ratio of 2:1:1:3:5.
Preferably, the yarn that will have been twisted according to step D, which is put into 50 DEG C -60 DEG C of color pond, impregnates 6h-7h, fishing
Quickly removed water after yarn using dryer out, until yarn is dry, placed into after drying containing antibacterial finishing agent with it is mould proof
Drying is taken out after impregnating 5-6h in the solution of anti-mite finishing agent ABM3.
Preferably, described to be weaved according to step E using shark number high-speed air-jet looms are flown, the weaving of cloth is completed,
The horizontal ratio through with perpendicular warp of textile fabric is 6:4.
Preferably, described that two surfaces of fabric and the both sides of the edge of fabric are carried out using defeathering unit according to step F
The both sides of the edge of fabric are carried out flanging by defeathering.
Preferably, described fabric is put into clear water first according to step G impregnates 2h-3h, then using pure water into
It goes and rinses, pure water rinses 2-3 times, and the fabric after taking out cleaning is simultaneously put into revolving speed getting rid of in machine for 1800-2000rad/min
Water removal, is finally putting into baking oven and dries.
Compared with prior art, the beneficial effects of the present invention are:
(1) material used in the cloth will not damage human body, while having mould proof for the natural material of environmental protection
The advantages of insect prevention, and comfort is good;
(2) this fabric antibiotic property of the invention is strong, by still keeping good anti-microbial property after repeatedly washing, matches
The mould proof anti-mite finishing agent ABM used in side has good acid-fast alkali-proof, resistance to mould, resistance to damages by worms, anti-so that the fabric
Popularizing for mould fabric has extensive market prospects.
Specific embodiment
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment
Only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this field
Art personnel every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
The invention provides the following technical scheme: a kind of production method of mould proof cloth, the following steps are included:
A, prepare material: preparing the material for mould proof cloth yarn of weaving, and divide according to allocation ratio;
B, thread material is handled: the material for being used to spin is pre-processed;
C, it spins: the yarn handled well being subjected to comb yarn, the material combed is spinned;
D, it dyes: the yarn weaved is dyed, and the yarn after dyeing is subjected to thermophilic digestion;
E, fabric is weaved: the yarn spun first being carried out warping, the good yarn of warping is carried out cloth weaving;
F, fabric is handled: yarn extra on the fabric weaved is removed;
G, it cleans: being cleaned after web surface is handled, and the cloth of cleaning is subjected to drying and processing.
Material for mould proof cloth yarn of weaving includes 30-60 parts of bamboo charcoal fiber, and 20-30 parts of milk protein fiber, ramie
10-15 parts of flaxen fiber, 15-35 parts of tencel fiber, 15-35 parts of Wormwood fiber, antibacterial finishing agent 10-12, mould proof anti-mite finishing agent
ABM3-12 parts, ready material is put into clear water and is cleaned, is put into after cleaning in 15% sodium hydroxide solvent
30min-60min is impregnated, pulls drying after immersion out, the material consolidation of the spinning pre-processed is neat, by bamboo charcoal fiber, ox
Milk proem fiber, ramee, tencel fiber, Wormwood fiber carry out twisted filament using twisting frame according to: the ratio of 2:1:1:3:5.
The yarn twisted is put into 50 DEG C -60 DEG C of color pond and impregnates 6h-7h, pull out after yarn using dryer into
Row quickly water removal places into the solution containing antibacterial finishing agent Yu mould proof anti-mite finishing agent ABM3 after dry until yarn is dry
Drying is taken out after middle immersion 5-6h, is weaved using winged shark number high-speed air-jet looms, completes the weaving of cloth, textile fabric
It is horizontal through and perpendicular warp ratio be 6:4.
Embodiment 1, the material for mould proof cloth yarn of weaving include 30 parts of bamboo charcoal fiber, and 20 parts of milk protein fiber,
10 parts of ramee, 15 parts of tencel fiber, 15 parts of Wormwood fiber, antibacterial finishing agent 10 mould proof anti-mite finishing agent ABM3 parts, will be quasi-
The material got ready, which is put into clear water, to be cleaned, and is put into 15% sodium hydroxide solvent after cleaning and is impregnated 30min-
60min pulls drying out after immersion, the material consolidation of the spinning pre-processed is neat, and by bamboo charcoal fiber, milk protein is fine
Dimension, ramee, tencel fiber, Wormwood fiber carry out twisted filament using twisting frame according to: the ratio of 2:1:1:3:5.
The yarn twisted is put into 50 DEG C -60 DEG C of color pond and impregnates 6h-7h, pull out after yarn using dryer into
Row quickly water removal places into the solution containing antibacterial finishing agent Yu mould proof anti-mite finishing agent ABM3 after dry until yarn is dry
Drying is taken out after middle immersion 5-6h, is weaved using winged shark number high-speed air-jet looms, completes the weaving of cloth, textile fabric
It is horizontal through and perpendicular warp ratio be 6:4.
Embodiment 2, the material for mould proof cloth yarn of weaving include 35 parts of bamboo charcoal fiber, and 25 parts of milk protein fiber,
It 12 parts of ramee, 20 parts of tencel fiber, 20 parts of Wormwood fiber, 10 parts of antibacterial finishing agent, mould proof anti-mite finishing agent ABM5 parts, will
Ready material, which is put into clear water, to be cleaned, and is put into 15% sodium hydroxide solvent after cleaning and is impregnated 30min-
60min pulls drying out after immersion, the material consolidation of the spinning pre-processed is neat, and by bamboo charcoal fiber, milk protein is fine
Dimension, ramee, tencel fiber, Wormwood fiber carry out twisted filament using twisting frame according to: the ratio of 2:1:1:3:5.
The yarn twisted is put into 50 DEG C -60 DEG C of color pond and impregnates 6h-7h, pull out after yarn using dryer into
Row quickly water removal places into the solution containing antibacterial finishing agent Yu mould proof anti-mite finishing agent ABM3 after dry until yarn is dry
Drying is taken out after middle immersion 5-6h, is weaved using winged shark number high-speed air-jet looms, completes the weaving of cloth, textile fabric
It is horizontal through and perpendicular warp ratio be 6:4.
Embodiment 3, the material for mould proof cloth yarn of weaving include 45 parts of bamboo charcoal fiber, and 27 parts of milk protein fiber,
13 parts of ramee, 25 parts of tencel fiber, 25 parts of Wormwood fiber, antibacterial finishing agent 12 mould proof anti-mite finishing agent ABM8 parts, will be quasi-
The material got ready, which is put into clear water, to be cleaned, and is put into 15% sodium hydroxide solvent after cleaning and is impregnated 30min-
60min pulls drying out after immersion, the material consolidation of the spinning pre-processed is neat, and by bamboo charcoal fiber, milk protein is fine
Dimension, ramee, tencel fiber, Wormwood fiber carry out twisted filament using twisting frame according to: the ratio of 2:1:1:3:5.
The yarn twisted is put into 50 DEG C -60 DEG C of color pond and impregnates 6h-7h, pull out after yarn using dryer into
Row quickly water removal places into the solution containing antibacterial finishing agent Yu mould proof anti-mite finishing agent ABM3 after dry until yarn is dry
Drying is taken out after middle immersion 5-6h, is weaved using winged shark number high-speed air-jet looms, completes the weaving of cloth, textile fabric
It is horizontal through and perpendicular warp ratio be 6:4.
Embodiment 4, the material for mould proof cloth yarn of weaving include 50 parts of bamboo charcoal fiber, and 29 parts of milk protein fiber,
14 parts of ramee, 30 parts of tencel fiber, 30 parts of Wormwood fiber, antibacterial finishing agent 12 mould proof anti-mite finishing agent ABM10 parts, will
Ready material, which is put into clear water, to be cleaned, and is put into 15% sodium hydroxide solvent after cleaning and is impregnated 30min-
60min pulls drying out after immersion, the material consolidation of the spinning pre-processed is neat, and by bamboo charcoal fiber, milk protein is fine
Dimension, ramee, tencel fiber, Wormwood fiber carry out twisted filament using twisting frame according to: the ratio of 2:1:1:3:5.
The yarn twisted is put into 50 DEG C -60 DEG C of color pond and impregnates 6h-7h, pull out after yarn using dryer into
Row quickly water removal places into the solution containing antibacterial finishing agent Yu mould proof anti-mite finishing agent ABM3 after dry until yarn is dry
Drying is taken out after middle immersion 5-6h, is weaved using winged shark number high-speed air-jet looms, completes the weaving of cloth, textile fabric
It is horizontal through and perpendicular warp ratio be 6:4.
Embodiment 5, the material for mould proof cloth yarn of weaving include 55 parts of bamboo charcoal fiber, and 30 parts of milk protein fiber,
15 parts of ramee, 32 parts of tencel fiber, 32 parts of Wormwood fiber, antibacterial finishing agent 12 mould proof anti-mite finishing agent ABM12 parts, will
Ready material, which is put into clear water, to be cleaned, and is put into 20% sodium hydroxide solvent after cleaning and is impregnated 30min-
60min pulls drying out after immersion, the material consolidation of the spinning pre-processed is neat, and by bamboo charcoal fiber, milk protein is fine
Dimension, ramee, tencel fiber, Wormwood fiber carry out twisted filament using twisting frame according to: the ratio of 2:1:1:3:5.
The yarn twisted is put into 50 DEG C -60 DEG C of color pond and impregnates 6h-7h, pull out after yarn using dryer into
Row quickly water removal places into the solution containing antibacterial finishing agent Yu mould proof anti-mite finishing agent ABM3 after dry until yarn is dry
Drying is taken out after middle immersion 5-6h, is weaved using winged shark number high-speed air-jet looms, completes the weaving of cloth, textile fabric
It is horizontal through and perpendicular warp ratio be 6:4.
Embodiment 6, the material for mould proof cloth yarn of weaving include 60 parts of bamboo charcoal fiber, and 30 parts of milk protein fiber,
15 parts of ramee, 35 parts of tencel fiber, 35 parts of Wormwood fiber, antibacterial finishing agent 12 mould proof anti-mite finishing agent ABM12 parts, will
Ready material, which is put into clear water, to be cleaned, and is put into 20% sodium hydroxide solvent after cleaning and is impregnated 30min-
60min pulls drying out after immersion, the material consolidation of the spinning pre-processed is neat, and by bamboo charcoal fiber, milk protein is fine
Dimension, ramee, tencel fiber, Wormwood fiber carry out twisted filament using twisting frame according to: the ratio of 2:1:1:3:5.
The yarn twisted is put into 50 DEG C -60 DEG C of color pond and impregnates 6h-7h, pull out after yarn using dryer into
Row quickly water removal places into the solution containing antibacterial finishing agent Yu mould proof anti-mite finishing agent ABM3 after dry until yarn is dry
Drying is taken out after middle immersion 5-6h, is weaved using winged shark number high-speed air-jet looms, completes the weaving of cloth, textile fabric
It is horizontal through and perpendicular warp ratio be 6:4.
Defeathering is carried out to two surfaces of fabric and the both sides of the edge of fabric using defeathering unit, by the both sides of the edge of fabric
Flanging is carried out, so that the surface of cloth is become smooth clean, cloth will be made to be not easy to reel off raw silk from cocoons after the flanging of cloth two sides, cloth is by surface
After processing, fabric is put into clear water impregnates 2h-3h first, be then rinsed using pure water, pure water rinses 2-3
It is secondary, the slurry on cloth is removed, while fabric being made to become soft clean, it also can be clear by the pigment of some dyeing on cloth
It removes, taking out the fabric after cleaning and being put into revolving speed is that getting rid of in machine for 1800-2000rad/min removes water, and accelerates to remove on fabric
Moisture content, be finally putting into 70-80 DEG C of baking oven accelerate drying design on fabric surface moisture content, be finally completed the manufacture craft of fabric.
The material used in the cloth will not damage human body for the natural material of environmental protection, while have mould proof anti-
The advantages of worm, and comfort is good, and this fabric antibiotic property of the invention is strong, good by still keeping after repeatedly washing
Anti-microbial property, the mould proof anti-mite finishing agent ABM used in formula so that the fabric, have good acid-fast alkali-proof, resistance to mould,
It is resistance to damage by worms, have extensive market prospects in popularizing for Mould-proof shell fabric.
In conclusion of the invention
The beneficial effects of the present invention are:
(1) material used in the cloth will not damage human body, while having mould proof for the natural material of environmental protection
The advantages of insect prevention, and comfort is good;
(2) this fabric antibiotic property of the invention is strong, by still keeping good anti-microbial property after repeatedly washing, matches
The mould proof anti-mite finishing agent ABM used in side has good acid-fast alkali-proof, resistance to mould, resistance to damages by worms, anti-so that the fabric
Popularizing for mould fabric has extensive market prospects.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (8)
1. a kind of production method of mould proof cloth, it is characterised in that: the following steps are included:
A, prepare material: preparing the material for mould proof cloth yarn of weaving, and divide according to allocation ratio;
B, thread material is handled: the material for being used to spin is pre-processed;
C, it spins: the yarn handled well being subjected to comb yarn, the material combed is spinned;
D, it dyes: the yarn weaved is dyed, and the yarn after dyeing is subjected to thermophilic digestion;
E, fabric is weaved: the yarn spun first being carried out warping, the good yarn of warping is carried out cloth weaving;
F, fabric is handled: yarn extra on the fabric weaved is removed;
G, it cleans: being cleaned after web surface is handled, and the cloth of cleaning is subjected to drying and processing.
2. a kind of production method of mould proof cloth according to claim 1, it is characterised in that: it is described to be used for according to step A
The material of mould proof cloth yarn of weaving includes 30-60 parts of bamboo charcoal fiber, and 20-30 parts of milk protein fiber, ramee 10-15
Part, 15-35 parts of tencel fiber, 15-35 parts of Wormwood fiber, antibacterial finishing agent 10-12, mould proof anti-mite finishing agent ABM3-12 parts.
3. a kind of production method of mould proof cloth according to claim 1, it is characterised in that: it is described will be quasi- according to step B
The material got ready, which is put into clear water, to be cleaned, and is put into 15% sodium hydroxide solvent after cleaning and is impregnated 30min-
60min pulls drying out after immersion.
4. a kind of production method of mould proof cloth according to claim 1, it is characterised in that: it is described will be pre- according to step C
The material consolidation for the spinning first handled well is neat, by bamboo charcoal fiber, milk protein fiber, ramee, tencel fiber, wormwood fibre
Dimension carries out twisted filament using twisting frame according to: the ratio of 2:1:1:3:5.
5. a kind of production method of mould proof cloth according to claim 1, it is characterised in that: it is described to be twisted according to step D
Good yarn, which is put into 50 DEG C -60 DEG C of color pond, impregnates 6h-7h, is quickly removed water after pulling yarn out using dryer,
Until yarn is dry, placed into after dry in the solution containing antibacterial finishing agent and mould proof anti-mite finishing agent ABM3 after impregnating 5-6h
Take out drying.
6. a kind of production method of mould proof cloth according to claim 1, it is characterised in that: it is described to be used according to step E
Fly shark number high-speed air-jet looms to be weaved, completes the weaving of cloth, the horizontal ratio through with perpendicular warp of textile fabric is 6:4.
7. a kind of production method of mould proof cloth according to claim 1, it is characterised in that: it is described to be used according to step F
Defeathering unit carries out defeathering to two surfaces of fabric and the both sides of the edge of fabric, and the both sides of the edge of fabric are carried out flanging.
8. a kind of production method of mould proof cloth according to claim 1, it is characterised in that: it is described according to step G first
Fabric is put into clear water and impregnates 2h-3h, is then rinsed using pure water, pure water rinses 2-3 times, after taking out cleaning
Fabric and be put into revolving speed be getting rid of in machine for 1800-2000rad/min remove water, be finally putting into baking oven and dry.