CN109576846A - Wood pulp Modal fibre and combed long staple cotton blended fine count spinning technique - Google Patents
Wood pulp Modal fibre and combed long staple cotton blended fine count spinning technique Download PDFInfo
- Publication number
- CN109576846A CN109576846A CN201710907459.3A CN201710907459A CN109576846A CN 109576846 A CN109576846 A CN 109576846A CN 201710907459 A CN201710907459 A CN 201710907459A CN 109576846 A CN109576846 A CN 109576846A
- Authority
- CN
- China
- Prior art keywords
- cotton
- modal fibre
- fibre
- fiber
- modal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of environmental protection wood pulp Modal fibre and combed long staple cotton blended fine count, it is 50% that wherein Modal fibre, which accounts for the weight percent of mixed yarn, and combed long staple cotton accounts for the weight percent 50% of mixed yarn；Its processing step are as follows: the pretreatment of wood pulp Modal fibre, opening and cleaning step, carding step, combing process, mixing in doubling step, Roving Frames, spinning process, winding procedure are carried out in proportion blended, spin out 14.5 Tekes high grade cotton yarns, reach two kinds of fibre property complementations, improve the comprehensive performance of Modal fibre, it realizes environmental protection, energy-saving and emission-reduction, promotes product competitiveness.
Description
Technical field
The present invention relates to cotton spinning spinninging technical field, specifically a kind of wood pulp Modal fibre and combed long staple cotton are mixed
High-count yarn spun weaving process.
Background technique
Modal fibre is the environmentally friendly wood pulp cellulose of 21 century most potential quality, which is Austrian Lenzin company research and development
A kind of high-modulus viscose rayon, beech of the raw material from Europe, is made by special spinning technique, entire production process
In there is no any pollution, and being capable of natural degradation.It dry by force close to terylene, it is wet to be better than common viscose fiber by force, it combines
The excellent texture of natural fiber and the practicability of synthetic fibers, manufactured fabric have " softness of cotton, the gloss of silk, fiber crops simultaneously
It is smooth ", hygroscopicity, dyeability, flexibility etc. are superior to pure cotton fabric, after washing several times after still with pleasant soft touching
Sense, pendency sense and fabulous endurable performance, it is considered to be.But modal fiber fabric is easily fluffed in the process of wearing
Ball, influences the appearance style of fabric, and production cost is also relatively expensive.Company in process of production, has accepted one external
The Large Order Number of company, to overcome, the easy pilling of current Modal fibre, the pure wide property of spinning modal fiber fabric be poor, pure spinning price
The deficiencies of expensive, company develops a kind of environmentally friendly wood pulp cellulose and combed cotton blended high grade cotton yarn, by combed long staple cotton and Modal
Fiber blend can be enhanced two kinds of interfibrous frictions, reduce the unusual fluctuation of Modal fibre, enhance the wide performance of its product,
Modal fibre and combed cotton blended yarn can be used for producing high-grade underwear, sportswear, easy dress, swimsuit, shirt etc., realize green
Colour circle is protected, and reduces overall cost, meets the demand of different clients.
Summary of the invention
To overcome the easy pilling of current Modal fibre, the pure wide property of spinning modal fiber fabric are poor, pure spinning is expensive etc.
Deficiency will not generation it is an object of that present invention to provide a kind of environmentally friendly wood pulp cellulose and combed long staple cotton blended fine count production technology
Your fiber and smart combed long staple cotton two kinds of fibers of fiber proportionally carry out blended, reach two kinds of fibre property complementations, raising is not
The comprehensive performance of Dai Er fiber realizes environmental protection, energy-saving and emission-reduction, promotes product competitiveness.
To achieve the above object, the technical scheme is that a kind of environmental protection wood pulp Modal fibre and combed long staple cotton
Blended fine count, it is 50% that wherein Modal fibre, which accounts for the weight percent of mixed yarn, and combed long staple cotton fiber accounts for the weight of mixed yarn
Measure percentage 50%.A kind of environmental protection wood pulp Modal fibre and combed long staple cotton fiber blending high count yarn weaving process, technique step
It is rapid as follows:
1, environmentally friendly wood pulp Modal fibre pretreatment
The regain of Modal fibre (Modal) in normal conditions is larger, and moisture adsorption and releasing speed is especially fast, in spinning process
Between Modal fibre, fiber and parts friction can generate a large amount of electrostatic, cause to wind roller and rubber roller, influence production efficiency and
Product quality.Therefore, it needs to pre-process Modal fibre before production and processing.According to the regain of Modal fibre
And the size of oil content humidifies 5 kilograms of clear water, the not generation that will be humidified according to hundred kilograms of Modal fibres to it before feeding intake
You put the health of cotton storehouse by fiber.It is required that: Modal fibre is banked up regular in cotton storehouse；Cotton storehouse is closed；Conditioned time: 8 hours, to protect
It demonstrate,proves fiber and is in moisture releasing state in later each process production process.
2, opening and cleaning step
Modal fibre and long-staple cotton fiber are integrally spent, almost without short flannel impurity, scutching cotton process using " tip-tap, more pines,
The technological principle of light quantitative, slow train speed ".
Opening and cleaning step uses domestic opening picking equipment, Modal fibre scutching cotton process main technologic parameters: grabs cotton hired roughneck
Speed 850r/min, running efficiency 90%, carding beating speed 400r/min, coiled comprehensive Beater Speed 700r/min are respectively fallen miscellaneous
Dirt stick gauge is transferred to minimum, cotton rolling quantity 400g/m, cotton roll length 32m, cotton roll elongation 1.3%.
Long-staple cotton fiber scutching cotton process main technologic parameters: cotton Beater Speed 900r/min, running efficiency 92%, cotton carding are grabbed
Beater Speed 500r/min, coiled comprehensive Beater Speed 900r/min, cotton rolling quantity 410g/m, cotton roll length 32m, cotton roll elongation
Rate 1.3%.
3, carding step
The process uses domestic FA201 type carding machine, and carding step has to keep machine performance good, and keeps the clear of cotton net
Clear degree, phenomena such as without edge damage, broken hole.
When processing two kinds of fibers of Modal fibre and combed long staple cotton fiber using " low velocity, in it is quantitative, sufficiently turn
The technological principle of shifting, few noil, small tension receiving coil " selects AC2030 type Bearded-needle knitted cloth, cotton carding eedle cloth fills less, fiber load is light,
Fibre migration rate is high, fibre damage is few, reduces fibre hook and cotton knot quantity.
4, combing process
The process uses Shanxi foundation for a great undertaking SXF1272 type combing machine.Combing process in advance and using 5 and closes, plays details to resultant yarn
The effect of reduction.
5, mixing in doubling step
According to the specific feature of product and Modal fibre, in order to improve mixed effect, key is Modal fibre drafting work
The design of skill parameter mixes in Modal fibre mixing in doubling step using " one pre- three is mixed " and uses three.Simultaneously 5, head, amalgamation mixes
Two and mixed three each 8.
6, Roving Frames
The process is weaved A186F fly frame using longitude and latitude, and Roving Frames are using " big gauge, light quantitative, pressurization, small tension receiving coil, again again
The technological principle of pressurization ", so that thick Yarn Evenness is uniform.Since Modal fibre crimp percent is low, coherent is poor, is also easy to produce accident
Drawing-off causes rove evenness fault, thus roving twist factor need to the appropriate grasp bigger than normal in the case where guaranteeing spun yarn not harmful drafting.
Relative humidity is 65%.Main technologic parameters: roller gauge 14mm × 36mm × 38mm, nip gauge 5.5mm, spindle revolving speed
800r/min, regular roving feeding 6.4g/10m, design twist factor 99,5.5 times of total draft multiple, 1.24 times of first break draft multiple.
7, spinning process
The process combines bamboo pulp because of the yarn category knitting yarn of exploitation using Ma Zuoli (East Platform) DTM129 type spinning frame
Fiber, china-hemp fibers feature, using the technological principle of " big gauge is again pressurizeed, small nip gauge, small back area draft ", back zone is led
Stretch multiple grasp less than normal in the case where guaranteeing not harmful drafting, and twist factor grasp bigger than normal.The relative humidity control in workshop exists
65%。
8, winding procedure
The process uses Germany's Schlafhorst AC338 type automatic winder, due to bamboo pulp fiber, china-hemp fibers, polyester fiber
Between cohesive force it is poor, but fiber crops, bamboo, the wettability power of terylene are stronger, so select the technological principle of small tension receiving coil, low velocity,
The air pressure of automatic joint, air splicer wants sufficient, and workshop relative humidity is controlled 65%.Winder main technologic parameters: winder speed
Degree is 750m/min, cotton knot 6.0.
The beneficial effects of the present invention are: being 50% by the weight percent that Modal fibre accounts for mixed yarn, combed long staple cotton accounts for
The weight percent 50% of mixed yarn；It carries out in proportion blended, spins out 14.5 Tekes high grade cotton yarns, reach two kinds of fibre properties
Complementation improves the comprehensive performance of Modal fibre, realizes environmental protection, energy-saving and emission-reduction, promotes product competitiveness.
Specific embodiment
Below with reference to embodiment, specific embodiments of the present invention will be described in further detail:
A kind of environmental protection wood pulp Modal fibre and combed long staple cotton fiber blending high count yarn, wherein Modal fibre accounts for mixed yarn
Weight percent is 50%, and combed long staple cotton fiber accounts for the weight percent 50% of mixed yarn；
Modal fibre selects the Modal wood pulp cellulose of Austrian Lenzin company research and development, and Modal fibre belongs to a new generation again
Raw cellulose fibre, main comprise material is cellulose；Selected Modal fibre raw material main feature and content are as follows
Table 1:
| Project | Modal fibre |
| Line density (dtex) | 1.6 |
| Density (g/cm3) | 1.5 |
| Dry strength (cN/dtex) | 3.6 |
| Dry elongation at break (%) | 14 |
| Wet strength (cN/dtex) | 2.0 |
| Wet fracture productivity (%) | 15 |
| 5% elongation wet modulus (cN/dtex) | 109 |
| Water suction volume expansion rate (%) | 71 |
| Official regain (%) | 12.6 |
Combed long staple cotton fiber: combed long staple cotton fabric hand is soft, and soft glossy, gas permeability is strong, there is good wearability.
Company selects 1 grade of raw cotton, combed long staple cotton fiber when producing environmentally friendly wood pulp cellulose and combed long staple cotton fiber blending high count yarn
Containing miscellaneous few, line density 1.67 divides Tekes, average length 35mm.The main performance index of combed long staple cotton fiber is shown in Table 2:
| Project | Long-staple cotton fiber |
| Principal length (mm) | 35 |
| Mic value | 4.0 |
| Quality length (mm) | 39.45 |
| Short fiber content (%) | 9.64 |
| Maturity | 1.67 |
| Monofilament strength (cN) | 4.11 |
| Fibre fineness (dtex) | 1.84 |
| Regain (%) | 9.37 |
| Percentage of impurity (%) | 2.14 |
Processing step is as follows:
1, environmentally friendly wood pulp Modal fibre pretreatment
The regain of Modal fibre (Modal) in normal conditions is larger, and moisture adsorption and releasing speed is especially fast, in spinning process
Between Modal fibre, fiber and parts friction can generate a large amount of electrostatic, cause to wind roller and rubber roller, influence production efficiency and
Product quality.Therefore, it needs to pre-process Modal fibre before production and processing.According to the regain of Modal fibre
And the size of oil content humidifies 5 kilograms of clear water, the not generation that will be humidified according to hundred kilograms of Modal fibres to it before feeding intake
You put the health of cotton storehouse by fiber.It is required that: Modal fibre is banked up regular in cotton storehouse；Cotton storehouse is closed；Conditioned time: 8 hours, to protect
It demonstrate,proves fiber and is in moisture releasing state in later each process production process.
2, opening and cleaning step
Modal fibre and long-staple cotton fiber are integrally spent, almost without short flannel impurity, scutching cotton process using " tip-tap, more pines,
The technological principle of light quantitative, slow train speed ".
Opening and cleaning step uses domestic opening picking equipment, Modal fibre scutching cotton process main technologic parameters: grabs cotton hired roughneck
Speed 850r/min, running efficiency 90%, carding beating speed 400r/min, coiled comprehensive Beater Speed 700r/min are respectively fallen miscellaneous
Dirt stick gauge is transferred to minimum, cotton rolling quantity 400g/m, cotton roll length 32m, cotton roll elongation 1.3%.
Long-staple cotton fiber scutching cotton process main technologic parameters: cotton Beater Speed 900r/min, running efficiency 92%, cotton carding are grabbed
Beater Speed 500r/min, coiled comprehensive Beater Speed 900r/min, cotton rolling quantity 410g/m, cotton roll length 32m, cotton roll elongation
Rate 1.3%.
3, carding step
The process uses domestic FA201 type carding machine, and carding step has to keep machine performance good, and keeps the clear of cotton net
Clear degree, phenomena such as without edge damage, broken hole.
When processing two kinds of fibers of Modal fibre and long-staple cotton using " low velocity, in it is quantitative, sufficiently transfer, few noil,
The technological principle of small tension receiving coil " selects AC2030 type Bearded-needle knitted cloth, and cotton carding eedle cloth fills less, fiber load is light, fibre migration rate
Height, fibre damage are few, reduce fibre hook and cotton knot quantity.Carding step main technologic parameters are shown in Table 3:
| Project | Long-staple cotton fiber | Modal fibre |
| Cylinder speed/rmin-1 | 350 | 280 |
| Licker-in speed/rmin-1 | 860 | 600 |
| Cover plate speed/mmmin-1 | 210 | 150 |
| Tension draft | 1.131 | 1.083 |
| Pierce rod and cylinder gauge/mm | 0.11 | 0.49 |
| Cylinder and doffer's gauge/mm | 0.11 | 0.16 |
| Cylinder and Flat Gauge/mm | 0.15,0.13,0.13,0.13,0.13 | 0.20,0.20,0.20,0.20,0.23 |
| Upper cover plate gauge/mm suitable for reading | 0.51 | Not noil |
| Cotton strip quantity/5m | 19.6 | 16.8 |
| Carded sliver short fiber content/% | 11 | 2.3 |
| Irregularity/% | 3.6 | 3.0 |
| Cylinder and licker-in speed ratio | 2.0 | 2.34 |
4, combing process
The process uses Shanxi foundation for a great undertaking SXF1272 type combing machine.Combing process is pre- and uses 5 and closes, and plays details to resultant yarn
The effect of reduction.The technique of yarn is according to 4 parameter configuration of table:
| Project | Technological parameter |
| Unevenness CV/% | 4 |
| Yarn short fiber content/% | 7.4 |
| Fibers parallel degree of stretching/% | 28 |
| Hooked fibre percentage composition/% | 4.8 |
| Quantitative/g(5m)-1 | 17.9 |
| Revolving speed lead/time min-1 | 220 |
| Detaching distance/mm | 11.11 |
| Roller gauge/mm | 4 |
| Uster sliver/% | 3.3 |
| Noodles cotton knot/grain g-1 | 17 |
5, mixing in doubling step
According to the specific feature of product and Modal fibre, in order to improve mixed effect, key is Modal fibre drafting work
The design of skill parameter mixes in Modal fibre mixing in doubling step using " one pre- three is mixed " and uses three.Simultaneously 5, head, amalgamation mixes
Two and mixed three each 8.Modal fibre drafting main technologic parameters are shown in Table 5:
| Project | Modal fibre is in advance simultaneously | Amalgamation | Mixed two | Mixed three |
| Total draft/times | 5.023 | 8.3 | 8.4 | 8.5 |
| First break draft multiple/times | 1.71 | 1.61 | 1.41 | 1.21 |
| It holds away from/mm | 10×12×20 | 11×7×19 | 11×7×19 | 11×7×19 |
| Dry Weight per Unit/g(5m)-1 | 16.3 | 18 | 17 | 16 |
| Number of doubling/root | 5 | 8 | 8 | 8 |
| Weight unevenness/% | 2.0 | 1.6 | 1.2 | 0.8 |
| CV/% | 4.24 | 3.87 | 3.60 | 3.0 |
| Front roller sliver exporting speed/mmin-1 | 200 | 300 | 300 | 300 |
6, Roving Frames
The process is weaved A186F fly frame using longitude and latitude, and Roving Frames are using " big gauge, light quantitative, pressurization, small tension receiving coil, again again
The technological principle of pressurization ", so that thick Yarn Evenness is uniform.Since Modal fibre crimp percent is low, coherent is poor, is also easy to produce accident
Drawing-off causes rove evenness fault, thus roving twist factor need to the appropriate grasp bigger than normal in the case where guaranteeing spun yarn not harmful drafting.
Relative humidity is 65%.Main technologic parameters: roller gauge 14mm × 36mm × 38mm, nip gauge 5.5mm, spindle revolving speed
800r/min, regular roving feeding 6.4g/10m, design twist factor 99,5.5 times of total draft multiple, 1.24 times of first break draft multiple.
7, spinning process
The process combines bamboo pulp because of the yarn category knitting yarn of exploitation using Ma Zuoli (East Platform) DTM129 type spinning frame
Fiber, china-hemp fibers feature, using the technological principle of " big gauge is again pressurizeed, small nip gauge, small back area draft ", back zone is led
Stretch multiple grasp less than normal in the case where guaranteeing not harmful drafting, and twist factor grasp bigger than normal.The relative humidity control in workshop exists
65%。
Main technologic parameters: spun yarn Dry Weight per Unit 18.6g/100m, nip gauge 2.2mm, roller gauge 18mm × 30mm are twisted
75.3 twirls/10cm is spent, rings is serial using PG, and 26.5 times of total draft multiple, 1.25 times of back area draft.Resultant yarn main performance is shown in Table
4:
| Dry Weight per Unit (g/ 100m) | Spun yarn weight irregularity cv/% | It is strong singly to kill fracture Power/cN | Single thread force irregularity CV/% | Item is dry CV/% | Slubbing/(a/ Km) | Details/(a/ Km) | Cotton knot/(a/ Km) | 3mm or more filoplume/ (root/10m) |
| 1.8533 | 1.7 | 536 | 1.4 | 12.1 | 14 | 26 | 32 | 34.3 |
8, winding procedure
The process uses Germany's Schlafhorst AC338 type automatic winder, due to bamboo pulp fiber, china-hemp fibers, polyester fiber
Between cohesive force it is poor, but fiber crops, bamboo, the wettability power of terylene are stronger, so select the technological principle of small tension receiving coil, low velocity,
The air pressure of automatic joint, air splicer wants sufficient, and workshop relative humidity is controlled 65%.Winder main technologic parameters: winder speed
Degree is 750m/min, cotton knot 6.0.
Environmentally friendly wood pulp Modal fibre and combed long staple cotton blended fine count weaving process, weave Modal fibre account for it is mixed
The weight percent of spinning is 50%, and combed long staple cotton fiber accounts for 14.5 Tekes high branch of the weight percent 50% of mixed yarn
Yarn.
Claims (1)
1. a kind of environmental protection wood pulp Modal fibre and combed long staple cotton blended fine count spinning technique, wherein Modal fibre accounts for mixed
The weight percent of spinning is 50%, and combed long staple cotton fiber accounts for the weight percent 50% of mixed yarn, it is characterized in that: its technique walks
It is rapid as follows:
(1), wood pulp Modal fibre pretreatment process
It needs to pre-process Modal fibre before production and processing, according to the regain and oil content of Modal fibre
Size 5 kilograms of clear water are humidified according to every hundred kilograms of Modal fibres to it before feeding intake, the Modal fibre humidified is put
Into the health of cotton storehouse；It is required that: Modal fibre is banked up regular in cotton storehouse；Cotton storehouse is closed；Conditioned time: 8 hours, to guarantee that fiber exists
Moisture releasing state is in later each process production process；
(2), opening and cleaning step
Modal fibre and long-staple cotton fiber are integrally spent, almost without short flannel impurity, scutching cotton process using " tip-tap, more pines,
The technological principle of light quantitative, slow train speed "；
Opening and cleaning step uses domestic opening picking equipment, Modal fibre scutching cotton process main technologic parameters: grabs cotton Beater Speed
850r/min, running efficiency 90%, carding beating speed 400r/min, coiled comprehensive Beater Speed 700r/min respectively fall miscellaneous dirt stick
Gauge is transferred to minimum, cotton rolling quantity 400g/m, cotton roll length 32m, cotton roll elongation 1.3%；
Long-staple cotton fiber scutching cotton process main technologic parameters: cotton Beater Speed 900r/min, running efficiency 92%, carding beating are grabbed
Speed 500r/min, coiled comprehensive Beater Speed 900r/min, cotton rolling quantity 410g/m, cotton roll length 32m, cotton roll elongation
1.3%；
(3), carding step
The process uses domestic FA201 type carding machine, and carding step has to keep machine performance good, and keeps the clear of cotton net
Clear degree, phenomena such as without edge damage, broken hole；
When processing two kinds of fibers of Modal fibre and long-staple cotton using " low velocity, in quantitative, sufficiently transfer, few noil, Xiao Zhang
The technological principle of power " selects AC2030 type Bearded-needle knitted cloth, cotton carding eedle cloth fills less, fiber load is light, fibre migration rate is high,
Fibre damage is few, reduces fibre hook and cotton knot quantity；
(4), combing process
The process uses Shanxi foundation for a great undertaking SXF1272 type combing machine;Combing process in advance and using 5 and closes, plays details to resultant yarn
The effect of reduction；
(5), mixing in doubling step
According to the specific feature of product and Modal fibre, in order to improve mixed effect, key is Modal fibre drafting work
The design of skill parameter mixes in Modal fibre mixing in doubling step using " one pre- three is mixed " and uses three；Simultaneously 5, head, amalgamation mixes
Two and mixed three each 8；
(6), Roving Frames
The process is weaved A186F fly frame using longitude and latitude, and Roving Frames are using " big gauge, light quantitative, pressurization, small tension receiving coil, again again
The technological principle of pressurization ", so that thick Yarn Evenness is uniform；Since Modal fibre crimp percent is low, coherent is poor, is also easy to produce accident
Drawing-off causes rove evenness fault, thus roving twist factor need to the appropriate grasp bigger than normal in the case where guaranteeing spun yarn not harmful drafting；
Relative humidity is 65%；Main technologic parameters: roller gauge 14mm × 36mm × 38mm, nip gauge 5.5mm, spindle revolving speed
800r/min, regular roving feeding 6.4g/10m, design twist factor 99,5.5 times of total draft multiple, 1.24 times of first break draft multiple；
(7), spinning process
The process combines bamboo pulp because of the yarn category knitting yarn of exploitation using Ma Zuoli (East Platform) DTM129 type spinning frame
Fiber, china-hemp fibers feature, using the technological principle of " big gauge is again pressurizeed, small nip gauge, small back area draft ", back zone is led
Multiple grasp less than normal in the case where guaranteeing not harmful drafting is stretched, and twist factor grasp bigger than normal, the relative humidity control in workshop exist
65%；
(8), winding procedure
The process uses Germany's Schlafhorst AC338 type automatic winder, due to bamboo pulp fiber, china-hemp fibers, polyester fiber
Between cohesive force it is poor, but fiber crops, bamboo, the wettability power of terylene are stronger, so select the technological principle of small tension receiving coil, low velocity,
The air pressure of automatic joint, air splicer wants sufficient, and workshop relative humidity is controlled 65%；Winder main technologic parameters: winder speed
Degree is 750m/min, cotton knot 6.0.