CN109576819A - A kind of multi-functional moxa fiber and preparation method thereof for low frequency electromagnetic physiotherapy cushion - Google Patents
A kind of multi-functional moxa fiber and preparation method thereof for low frequency electromagnetic physiotherapy cushion Download PDFInfo
- Publication number
- CN109576819A CN109576819A CN201811428297.6A CN201811428297A CN109576819A CN 109576819 A CN109576819 A CN 109576819A CN 201811428297 A CN201811428297 A CN 201811428297A CN 109576819 A CN109576819 A CN 109576819A
- Authority
- CN
- China
- Prior art keywords
- parts
- low frequency
- frequency electromagnetic
- fiber
- physiotherapy cushion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention belongs to fiber arts, and in particular to a kind of multi-functional moxa fiber and preparation method thereof for low frequency electromagnetic physiotherapy cushion.Provided by the present invention for the multi-functional moxa fiber of low frequency electromagnetic physiotherapy cushion, including following components and its parts by weight: 9-12 parts of moxa, 2-4 parts of sodium alginate, 2-4 parts of carboxymethyl chitosan, 0.5-1 parts of composite mineral matter, 0.2-0.4 parts and deionized water 500-600 parts of glycerol.It is vdiverse in function provided by the present invention for the multi-functional moxa fiber of low frequency electromagnetic physiotherapy cushion, there is significant anti-mold effect, anti-microbial property is good, has good water absorbing properties.
Description
Technical field
The invention belongs to fiber arts, and in particular to a kind of multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion and its
Preparation method.
Background technique
Low frequency electromagnetic physiotherapy cushion is mainly made of physical therapy pad body, electromagnetic pole and input signal cable, due to being provided with
There are the metal parts such as electromagnetic pole, input signal cable, therefore it cannot be cleaned and be destroyed to prevent metal parts, but manages
Pad is treated typically directly to be covered on skin and uses, if do not cleaned after being used for a long time, have sweat that a large amount of human bodies generate,
Sebum and various secretion are attached on physiotherapy cushion, and under hot humid conditions, these substances become the breeding ground for breeding germ, are led
Cause the generation of skin disease and animal infectious diease.However, current low frequency electromagnetic physiotherapy cushion generallys use cotton fiber or other changes
It is fine blended as bedding core, the effect of bumper and absorbing shock is functioned only as, the sanitary clean of low frequency electromagnetic physiotherapy cushion is unfavorable for.With strong
The development of Kang Guannian, higher requirements are also raised to the hygienic function for low frequency electromagnetic physiotherapy cushion bedding core by people.
Chinese patent application CN106245192A discloses a kind of anti-bacterial fibre fabric, comprising: bamboo fibre, milk fibre,
Flax fiber, silver fiber, polyester fiber, bamboo charcoal fiber, chitin fiber, nano-silver ionic fiber, ethoxyquinoline, poly- six Asia
Methyl biguanide hydrochloride, acetate fiber, the anti-bacterial fibre fabric is calculated by mass percentage, including following parts by weight:
2-4 parts of bamboo fibre, 1-5 parts of milk fibre, 3-6 parts of flax fiber, 1-5 parts of silver fiber, 4-9 parts of polyester fiber, bamboo charcoal fiber 1-6
Part, 1-7 parts of chitin fiber, 2-4 parts of nano-silver ionic fiber, 5-6 parts of ethoxyquinoline, hexamethylene 3-
4 parts, 4-7 parts of acetate fiber.
Chinese patent application CN104404649A discloses a kind of anti-bacterial fibre, is prepared from the following raw materials in parts by weight:
6-10 parts of methylcellulose, 3-8 parts of talcum powder, 4-9 parts of toluene di-isocyanate(TDI), 3-5 parts of epoxidized soybean oil, sodium pyrophosphate 4-7
Part, 1-5 parts of diglycol, 6-9 parts of dihydrogen phosphoric acid tridecane base ester, 4-7 parts of potassium chloride, 6-8 parts of polyacrylonitrile fibre, sword
5-9 parts of bast yarn and thread, 4-8 parts of TENCEL YARNS, 3-6 parts of polypropylene, 11-19 parts of silver oxide powder, 8-11 parts of penta sodium pentachlorophenate.
As the improvement of people's living standards, people are to environment and health problem growing interest, to comfort and wholesomeness
The requirement of energy aspect is also higher and higher.Currently, existing for low frequency electromagnetic physiotherapy cushion bedding core there are functions more single, water absorbing capacity
Power is poor, and anti-microbial property is bad, the defect of fungicidal properties difference.
Summary of the invention
In view of the deficiencies of the prior art, the purpose of the present invention is to provide a kind of for the multi-functional of low frequency electromagnetic physiotherapy cushion
Moxa fiber and preparation method thereof.It is vdiverse in function provided by the present invention for the multi-functional moxa fiber of low frequency electromagnetic physiotherapy cushion,
With significant anti-mold effect, anti-microbial property is good, has good water absorbing properties.
The technical scheme is that
A kind of multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion, including following components and its parts by weight: moxa
9-12 parts, 2-4 parts of sodium alginate, 2-4 parts of carboxymethyl chitosan, 0.5-1 parts of composite mineral matter, 0.2-0.4 parts of glycerol and go from
Sub- water 500-600 parts.
Further, the multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion, including following components and its again
Measure number: 10 parts of moxa, 3 parts of sodium alginate, 2.5 parts of carboxymethyl chitosan, 0.6 part of composite mineral matter, 0.3 part of glycerol and go from
550 parts of sub- water.
Further, the composite mineral matter by weight percentage, is grouped as by following group: attapulgite 30-40%,
Chlorite 25-35%, sepiolite 8-14% and hydroxyapatite 11-37%.
Further, the composite mineral matter by weight percentage, is grouped as by following group: attapulgite 35%,
Chlorite 30%, sepiolite 12% and hydroxyapatite 23%.
Further, the composite mineral matter the preparation method comprises the following steps: by attapulgite, chlorite, sepiolite and hydroxyl phosphorus
Lime stone mixing, be put into nanoscale grinder and grind, be ground to gained fine powder partial size be 5-10 μm to get.
Further, the partial size that gained fine powder is ground in the preparation method of the composite mineral matter is 8 μm.
In addition, the present invention also provides the preparation sides of the multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion
Method, comprising the following steps:
Moxa is put into nanoscale grinder and grinds by S1, and the partial size for being ground to gained fine powder is 10-20 μm, must end
Suede powder;
S2 mixes sodium alginate and carboxymethyl chitosan, and deionized water is added, and stirring is filtered to being completely dissolved, removed
Insoluble matter obtains filtrate, and above-mentioned filtrate is stood 10-14h, obtains mixed liquor;
Moxa powder obtained by composite mineral matter and step S1 is added in mixed liquor obtained by step S2 by S3, stirring, stirring speed
Degree is 3000-4000r/min, mixing time 15-25min, and glycerol is added, and continues to stir 2-5min, deaeration obtains spinning original
Liquid;
Spinning solution obtained by step S3 is squeezed out spinneret orifice and enters coagulating bath by S4, solution coagulation forming, into one in air bath
Step stretch, draw ratio be 4-6 to get.
Further, it is 15 μm that the step S1, which is ground to the partial size of gained fine powder,.
Further, above-mentioned filtrate is stood 13h by the step S2.
Further, the step S3 mixing speed is 3600r/min, mixing time 23min, and glycerol is added, and is continued
Stir 3min.
Further, the step S4 draw ratio is 5.
Water retention measurement test discovery through the multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion, it is prepared by the present invention
Water retention >=23% of multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion, hence it is evident that be higher than comparative example 1 and be prepared by comparative example 2
The multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion water retention, this explanation, it is prepared by the present invention be used for low frequency electromagnetic
The multi-functional moxa fiber water retention with higher of physiotherapy cushion has good moisture absorption.Illustrate simultaneously, the present invention is by recessed
Convex stick soil, chlorite, sepiolite and hydroxyapatite press the composite mineral matter of constant weight percentage composition, mutually cooperate with, and rise
Enhance the effect of wettability power.
Fungicidal properties testing experiment discovery through the multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion, present invention preparation
The multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion mould proof rate >=99.19%, and continuous and effective.This explanation, this hair
The bright multi-functional moxa fiber obtained for low frequency electromagnetic physiotherapy cushion has significant anti-mold effect.Illustrate simultaneously, the present invention
The composite mineral matter being made of attapulgite, chlorite, sepiolite and hydroxyapatite by constant weight percentage, with the present invention
In other raw materials such as moxa, sodium alginate and carboxymethyl chitosan ingredient between have collaboration anti-mold effect.
Bacteriostatic test discovery through the multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion, it is prepared by the present invention for low
The multi-functional moxa fiber of frequency electromagnetic physiotherapy pad is to staphylococcus aureus, Escherichia coli, Candida albicans, pseudomonas aeruginosa
There are significant fungistatic effect, bacteriostasis rate >=99.05% with bacillus subtilis.This explanation, the present invention is by attapulgite, green mud
Stone, sepiolite and hydroxyapatite press the composite mineral matter of constant weight percentage composition, such as with other raw materials in the present invention
It is mutually cooperateed between the ingredients such as moxa, sodium alginate and carboxymethyl chitosan, plays a part of to enhance bacteriostasis.
Provided by the present invention for low frequency electromagnetic physiotherapy cushion multi-functional moxa fiber by moxa, sodium alginate, carboxymethyl
The raw materials such as chitosan and composite mineral matter are prepared, and each raw material is mutually coordinated, have significant anti-mold effect, anti-microbial property
It is good, there are good water absorbing properties, good permeability, resilience are good, and pulling force is very big, permanency shape, durable, not aging,
It is harmless, easily biological-degradable.
Compared with prior art, have provided by the present invention for the multi-functional moxa fiber of low frequency electromagnetic physiotherapy cushion following
Advantage:
(1) provided by the present invention for the multi-functional moxa fibre antibacterial excellent performance of low frequency electromagnetic physiotherapy cushion, to golden yellow
Staphylococcus, Escherichia coli, Candida albicans, pseudomonas aeruginosa, bacillus subtilis have significant fungistatic effect.
(2) provided by the present invention for the multi-functional moxa fiber water retention with higher of low frequency electromagnetic physiotherapy cushion, this
Illustrate it with good water absorbing properties.
(3) there is significant anti-mold effect provided by the present invention for the multi-functional moxa fiber of low frequency electromagnetic physiotherapy cushion.
Specific embodiment
The following describes the present invention further through the description of specific embodiments, but it is to limit of the invention that this, which is not,
System, those skilled in the art's basic thought according to the present invention can make various modifications or improvements, but without departing from this
The basic thought of invention, is all within the scope of the present invention.
Moxa of the present invention is purchased from Pingyi Feng Tai medicinal material Import and Export Co., Ltd., article No. AXAR0081;Attapulgite is commercially available
From hundred Feng Kuangchanpinjiagongchang of Lingshou County, brand hundred is rich;Chlorite is purchased from Haicheng City decorated archway Zhenghai Rock Powder factory, top grade product;
Hydroxyapatite is purchased from Shenzhen city stone Jin Gu Science and Technology Ltd., model 1306-06-5.
Embodiment 1, a kind of multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion
The multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion includes following components and its parts by weight: moxa 9
Part, 2 parts of sodium alginate, 2 parts of carboxymethyl chitosan, 0.5 part of composite mineral matter, 0.2 part and 500 parts of deionized water of glycerol;It is described
Composite mineral matter by weight percentage, is grouped as by following group: attapulgite 30%, chlorite 25%, sepiolite 8% and hydroxyl
Base apatite 37%.
The composite mineral matter the preparation method comprises the following steps: by attapulgite, chlorite, sepiolite and hydroxyapatite mix,
Be put into nanoscale grinder and grind, be ground to gained fine powder partial size be 5 μm to get.
The preparation method of the multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion, comprising the following steps:
Moxa is put into nanoscale grinder and grinds by S1, and the partial size for being ground to gained fine powder is 10 μm, obtains moxa
Powder;
S2 mixes sodium alginate and carboxymethyl chitosan, and deionized water is added, and stirring is filtered to being completely dissolved, removed
Insoluble matter obtains filtrate, and above-mentioned filtrate is stood 10h, obtains mixed liquor;
Moxa powder obtained by composite mineral matter and step S1 is added in mixed liquor obtained by step S2 by S3, stirring, stirring speed
Degree is 3000r/min, mixing time 15min, and glycerol is added, and continues to stir 2min, deaeration obtains spinning solution;
Spinning solution obtained by step S3 is squeezed out spinneret orifice and enters coagulating bath by S4, solution coagulation forming, into one in air bath
Step stretch, draw ratio be 4 to get.
Embodiment 2, a kind of multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion
The multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion includes following components and its parts by weight: moxa 12
Part, 4 parts of sodium alginate, 4 parts of carboxymethyl chitosan, 1 part of composite mineral matter, 0.4 part and 600 parts of deionized water of glycerol;It is described multiple
It closes minerals by weight percentage, is grouped as by following group: attapulgite 40%, chlorite 35%, sepiolite 14% and hydroxyl
Base apatite 11%.
The composite mineral matter the preparation method comprises the following steps: by attapulgite, chlorite, sepiolite and hydroxyapatite mix,
Be put into nanoscale grinder and grind, be ground to gained fine powder partial size be 10 μm to get.
The preparation method of the multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion, comprising the following steps:
Moxa is put into nanoscale grinder and grinds by S1, and the partial size for being ground to gained fine powder is 20 μm, obtains moxa
Powder;
S2 mixes sodium alginate and carboxymethyl chitosan, and deionized water is added, and stirring is filtered to being completely dissolved, removed
Insoluble matter obtains filtrate, and above-mentioned filtrate is stood 14h, obtains mixed liquor;
Moxa powder obtained by composite mineral matter and step S1 is added in mixed liquor obtained by step S2 by S3, stirring, stirring speed
Degree is 4000r/min, mixing time 25min, and glycerol is added, and continues to stir 5min, deaeration obtains spinning solution;
Spinning solution obtained by step S3 is squeezed out spinneret orifice and enters coagulating bath by S4, solution coagulation forming, into one in air bath
Step stretch, draw ratio be 6 to get.
Embodiment 3, a kind of multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion
The multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion includes following components and its parts by weight: moxa 10
Part, 3 parts of sodium alginate, 2.5 parts of carboxymethyl chitosan, 0.6 part of composite mineral matter, 0.3 part and 550 parts of deionized water of glycerol;Institute
It states composite mineral matter by weight percentage, is grouped as by following group: attapulgite 35%, chlorite 30%, sepiolite 12%
With hydroxyapatite 23%.
The composite mineral matter the preparation method comprises the following steps: by attapulgite, chlorite, sepiolite and hydroxyapatite mix,
Be put into nanoscale grinder and grind, be ground to gained fine powder partial size be 8 μm to get.
The preparation method of the multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion, comprising the following steps:
Moxa is put into nanoscale grinder and grinds by S1, and the partial size for being ground to gained fine powder is 15 μm, obtains moxa
Powder;
S2 mixes sodium alginate and carboxymethyl chitosan, and deionized water is added, and stirring is filtered to being completely dissolved, removed
Insoluble matter obtains filtrate, and above-mentioned filtrate is stood 13h, obtains mixed liquor;
Moxa powder obtained by composite mineral matter and step S1 is added in mixed liquor obtained by step S2 by S3, stirring, stirring speed
Degree is 3600r/min, mixing time 23min, and glycerol is added, and continues to stir 3min, deaeration obtains spinning solution;
Spinning solution obtained by step S3 is squeezed out spinneret orifice and enters coagulating bath by S4, solution coagulation forming, into one in air bath
Step stretch, draw ratio be 5 to get.
Comparative example 1, a kind of multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion
The multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion includes following components and its parts by weight: moxa 10
Part, 3 parts of sodium alginate, 2.5 parts of carboxymethyl chitosan, 0.6 part of composite mineral matter, 0.3 part and 550 parts of deionized water of glycerol;Institute
It states composite mineral matter by weight percentage, is grouped as by following group: attapulgite 38%, chlorite 34% and hydroxyapatite
28%.
The preparation method of composite mineral matter and the multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion and 3 class of embodiment
Seemingly.
Difference with embodiment 3 is, does not add sepiolite, increases attapulgite, chlorite and hydroxyapatite
Weight percent.
Comparative example 2, a kind of multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion
The multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion includes following components and its parts by weight: moxa 10
Part, 3 parts of sodium alginate, 2.5 parts of carboxymethyl chitosan, 0.6 part of composite mineral matter, 0.3 part and 550 parts of deionized water of glycerol;Institute
It states composite mineral matter by weight percentage, is grouped as by following group: attapulgite 35%, chlorite 30%, 12% He of zeolite
Hydroxyapatite 23%.
The preparation method of composite mineral matter and the multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion and 3 class of embodiment
Seemingly.
Difference with embodiment 3 is, sepiolite is replaced with zeolite.
Test example one, for low frequency electromagnetic physiotherapy cushion multi-functional moxa fiber water retention measure test
1, test material: prepared by embodiment 1, embodiment 2, embodiment 3, comparative example 1 and comparative example 2 is used for low frequency electromagnetic
The multi-functional moxa fiber of physiotherapy cushion.
2, test method:
Water retention is an index for measuring water absorption of fabrics ability height.Test material is put into deionized water when test
In, 4h is impregnated, with the speed centrifugal dehydration 10min of 3000r/min, weighing is denoted as W1, then vacuum oven is placed in 105 DEG C of perseverances
Temperature is dry to constant weight, then claims to obtain dry fiber weight W0, water retention=(W1-W0)/W0× 100%.
3, test result:
Test result is as shown in table 1.
Table 1: the water retention measurement result of the multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion
Project | Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative example 1 | Comparative example 2 |
Water retention | 24% | 23% | 26% | 10% | 12% |
As can be seen from Table 1, what prepared by embodiment 1, embodiment 2, embodiment 3, comparative example 1 and comparative example 2 is used for low frequency
The water retention of the multi-functional moxa fiber of electromagnetic physiotherapy pad is respectively 24%, 23%, 26%, 10% and 12%, embodiment 1-3 system
The water retention of the standby multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion is apparently higher than prepared by comparative example 1 and comparative example 2
The water retention of multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion, this explanation are prepared by the present invention to manage for low frequency electromagnetic
Treat the multi-functional moxa fiber water retention with higher of pad.
Test example two, for low frequency electromagnetic physiotherapy cushion multi-functional moxa fiber bacteriostatic test
1, test material: prepared by embodiment 1, embodiment 2, embodiment 3, comparative example 1 and comparative example 2 is used for low frequency electromagnetic
The multi-functional moxa fiber of physiotherapy cushion.
2, subjects: staphylococcus aureus, Escherichia coli, Candida albicans, pseudomonas aeruginosa, bacillus subtilis
Bacterium.
3, test method:
The single colonies typical of separation is taken to be inoculated into ordinary nutrient agar medium slant, for 24 hours in 37 DEG C of cultures.It will be fresh
Slant culture is washed down with phosphate buffer (PBS), and dilution is configured to bacteria suspension.
It weighs 0.75g test material respectively to be added in the sterilizing conical flask of 250mL, every bottle of addition 70mLPBS and 5mL
Bacteria suspension, as sample sets.In addition, prepare battery of tests material concentration it is identical but it is not bacteria-containing as a control group.Triangle is burnt
Bottle, which is fixed in oscillator, to be vibrated, and is put into 37 DEG C of constant incubators, and test material and bacterium solution is made to come into full contact with 1h.Then,
Bacterium solution is diluted to required multiple with PBS buffer solution, is inoculated with plate with agar tilt-pour process, and put it into 37 DEG C of constant temperature incubations
It is cultivated for 24 hours in case.Viable bacteria number on agar plate is counted, test 3 times is repeated.Bacteriostasis rate R=(control group average colony
Number-sample sets average colony number)/control group average colony number.
4, test result:
Test result is as shown in table 2.
Table 2: the bacteriostatic test result of the multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion
As can be seen from Table 2, embodiment 1, embodiment 2 and the embodiment 3 more function obtained for being used for low frequency electromagnetic physiotherapy cushion
Energy moxa fiber has staphylococcus aureus, Escherichia coli, Candida albicans, pseudomonas aeruginosa and bacillus subtilis
There is significant inhibitory effect, fungistatic effect is substantially better than comparative example 1 and comparative example 2 is obtained for the more of low frequency electromagnetic physiotherapy cushion
Function moxa fiber.
Test example three, for low frequency electromagnetic physiotherapy cushion multi-functional moxa fiber fungicidal properties testing experiment
1, test material: prepared by embodiment 1, embodiment 2, embodiment 3, comparative example 1 and comparative example 2 is used for low frequency electromagnetic
The multi-functional moxa fiber of physiotherapy cushion.
2, subjects: black-koji mould
3, test method:
By test material be put into equipped with 1mL dilution aspergillus niger bacterium solution shaking flask in, 30 DEG C at a temperature of, with 170r/min
Speed oscillation, in 0,4,6,8,12, sample for 24 hours, pour into culture medium, 30 DEG C of incubation 48h take out, and calculate mildew number and simultaneously calculate
Mould proof rate, mould proof rate a=(A0—At)/A0× 100%, in formula: A0For initial mildew number;AtFor mildew number after the th of interval.
4, test result:
Test result is as shown in table 3.
Table 3: the fungicidal properties test result of the multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion
As can be seen from Table 3,4h, 6h, 8h, 12h, for 24 hours when, be used for made from embodiment 1, embodiment 2 and embodiment 3
The mould proof rate of the multi-functional moxa fiber of low frequency electromagnetic physiotherapy cushion is apparently higher than comparative example 1 and comparative example 2 is obtained for low frequency
The multi-functional moxa fiber of electromagnetic physiotherapy pad.This explanation, the multi-functional moxa produced by the present invention for low frequency electromagnetic physiotherapy cushion
Fiber has significant anti-mold effect.
Claims (10)
1. a kind of multi-functional moxa fiber for low frequency electromagnetic physiotherapy cushion, which is characterized in that including following components and its weight
Number: 9-12 parts of moxa, 2-4 parts of sodium alginate, 2-4 parts of carboxymethyl chitosan, 0.5-1 parts of composite mineral matter, glycerol 0.2-0.4
Part and deionized water 500-600 parts.
2. being used for the multi-functional moxa fiber of low frequency electromagnetic physiotherapy cushion as described in claim 1, which is characterized in that including following
Component and its parts by weight: 10 parts of moxa, 3 parts of sodium alginate, 2.5 parts of carboxymethyl chitosan, 0.6 part of composite mineral matter, glycerol
0.3 part and 550 parts of deionized water.
3. being used for the multi-functional moxa fiber of low frequency electromagnetic physiotherapy cushion as claimed in claim 1 or 2, which is characterized in that described
Composite mineral matter by weight percentage, is grouped as by following group: attapulgite 30-40%, chlorite 25-35%, sepiolite
8-14% and hydroxyapatite 11-37%.
4. being used for the multi-functional moxa fiber of low frequency electromagnetic physiotherapy cushion as claimed in claim 3, which is characterized in that described compound
Minerals by weight percentage, are grouped as by following group: attapulgite 35%, chlorite 30%, sepiolite 12% and hydroxyl
Apatite 23%.
5. being used for the multi-functional moxa fiber of low frequency electromagnetic physiotherapy cushion as claimed in claim 3, which is characterized in that described compound
Minerals the preparation method comprises the following steps: by attapulgite, chlorite, sepiolite and hydroxyapatite mix, be put into nanoscale grinder
Middle grinding, be ground to gained fine powder partial size be 5-10 μm to get.
6. the preparation method of the multi-functional moxa fiber as described in any one in claim 1-5 for low frequency electromagnetic physiotherapy cushion,
Characterized by comprising the following steps:
Moxa is put into nanoscale grinder and grinds by S1, and the partial size for being ground to gained fine powder is 10-20 μm, obtains moxa
Powder;
S2 mixes sodium alginate and carboxymethyl chitosan, and deionized water is added, and stirring is filtered to being completely dissolved, removed insoluble
Object obtains filtrate, and above-mentioned filtrate is stood 10-14h, obtains mixed liquor;
Moxa powder obtained by composite mineral matter and step S1 is added in mixed liquor obtained by step S2 by S3, stirring, and mixing speed is
Glycerol is added in 3000-4000r/min, mixing time 15-25min, continues to stir 2-5min, deaeration obtains spinning solution;
Spinning solution obtained by step S3 is squeezed out spinneret orifice and enters coagulating bath by S4, solution coagulation forming, is further drawn in air bath
Stretch, draw ratio be 4-6 to get.
7. the preparation method for the multi-functional moxa fiber of low frequency electromagnetic physiotherapy cushion, feature exist as claimed in claim 6
In the partial size that the step S1 is ground to gained fine powder is 15 μm.
8. the preparation method for the multi-functional moxa fiber of low frequency electromagnetic physiotherapy cushion, feature exist as claimed in claim 6
In above-mentioned filtrate is stood 13h by the step S2.
9. the preparation method for the multi-functional moxa fiber of low frequency electromagnetic physiotherapy cushion, feature exist as claimed in claim 6
In the step S3 mixing speed is 3600r/min, mixing time 23min, and glycerol is added, and continues to stir 3min.
10. the preparation method for the multi-functional moxa fiber of low frequency electromagnetic physiotherapy cushion, feature exist as claimed in claim 6
In the step S4 draw ratio is 5.