CN109575862A - A kind of anti-flammability binder - Google Patents
A kind of anti-flammability binder Download PDFInfo
- Publication number
- CN109575862A CN109575862A CN201811503171.0A CN201811503171A CN109575862A CN 109575862 A CN109575862 A CN 109575862A CN 201811503171 A CN201811503171 A CN 201811503171A CN 109575862 A CN109575862 A CN 109575862A
- Authority
- CN
- China
- Prior art keywords
- parts
- flammability
- binder
- agent
- alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anti-flammability binder, the anti-flammability binder is made from the following raw materials in parts by weight: 17~26 parts of aluminum oxide, 15~20 parts halogen-free of epoxy resin, 8~15 parts of 3- ethoxyl ethyl propionate；6~9 parts of alcohol-soluble acrylic resin, 15~18 parts of organophosphorus compound, 3~6 parts of curing accelerator, 5~8 parts of fire retardant, 7~12 parts of curing agent, 7~13 parts of antismoke agent, 4~9 parts of ultraviolet absorbing agent.The anti-flammability binder high temperature resistant, good flame retardation effect, security performance high pollution object is few, and quality is stablized.
Description
Technical field
The present invention relates to a kind of field of material technology more particularly to a kind of anti-flammability binders.
Background technique
Binder is the intermediate for connecting two kinds of materials, is mostly occurred with aqua, and fine chemistry industry class is belonged to, many kinds of, mainly
Classified with sizing, physical aspect, method for curing and adherend material.Especially in field of circuit boards, used bonding
Agent has higher requirement to temperature, and binder function used at present is relatively simple, poor fire, and reliability is high, safety
It can be low.
Summary of the invention
In view of the above existing problems in the prior art, the present invention provides a kind of anti-flammability binder, the anti-flammability binders
High temperature resistant, good flame retardation effect, security performance high pollution object is few, and quality is stablized.
To achieve the goals above, the present invention proposes a kind of anti-flammability binder, and the anti-flammability binder is by following heavy
The raw material of amount part is made: 17~26 parts of aluminum oxide, 15~20 parts halogen-free of epoxy resin, 3- ethoxyl ethyl propionate 8
~15 parts；6~9 parts of alcohol-soluble acrylic resin, 15~18 parts of organophosphorus compound, 3~6 parts of curing accelerator, fire retardant 5
~8 parts, 7~12 parts of curing agent, 7~13 parts of antismoke agent, 4~9 parts of ultraviolet absorbing agent.
Preferably, the anti-flammability binder is made from the following raw materials in parts by weight: 17 parts of aluminum oxide, halogen-free
15 parts of epoxy resin, 8 parts of 3- ethoxyl ethyl propionate；6 parts of alcohol-soluble acrylic resin, 15 parts of organophosphorus compound, solidification
3 parts of promotor, 5 parts of fire retardant, 7 parts of curing agent, 7 parts of antismoke agent, 4 parts of ultraviolet absorbing agent.
Preferably, the anti-flammability binder is made from the following raw materials in parts by weight: 26 parts of aluminum oxide, halogen-free
20 parts of epoxy resin, 15 parts of 3- ethoxyl ethyl propionate；9 parts of alcohol-soluble acrylic resin, 18 parts of organophosphorus compound, solidification
6 parts of promotor, 8 parts of fire retardant, 12 parts of curing agent, 13 parts of antismoke agent, 9 parts of ultraviolet absorbing agent.
Preferably, the anti-flammability binder is made from the following raw materials in parts by weight: 22 parts of aluminum oxide, halogen-free
18 parts of epoxy resin, 11 parts of 3- ethoxyl ethyl propionate；8 parts of alcohol-soluble acrylic resin, 16 parts of organophosphorus compound, solidification
4 parts of promotor, 6 parts of fire retardant, 9 parts of curing agent, 10 parts of antismoke agent, 7 parts of ultraviolet absorbing agent.
The beneficial effects of the present invention are: the anti-flammability binder high temperature resistant, good flame retardation effect, security performance high pollution object
Few, quality is stablized.
Specific embodiment
The invention will be further described below.
Embodiment 1:
A kind of anti-flammability binder provided by the invention, the anti-flammability binder are made from the following raw materials in parts by weight:
17 parts of aluminum oxide, 15 parts halogen-free of epoxy resin, 8 parts of 3- ethoxyl ethyl propionate；6 parts of alcohol-soluble acrylic resin,
15 parts of organophosphorus compound, 3 parts of curing accelerator, 5 parts of fire retardant, 7 parts of curing agent, 7 parts of antismoke agent, ultraviolet absorbing agent 4
Part.
Embodiment 2
A kind of anti-flammability binder provided by the invention, the anti-flammability binder are made from the following raw materials in parts by weight:
26 parts of aluminum oxide, 20 parts halogen-free of epoxy resin, 15 parts of 3- ethoxyl ethyl propionate；9 parts of alcohol-soluble acrylic resin,
18 parts of organophosphorus compound, 6 parts of curing accelerator, 8 parts of fire retardant, 12 parts of curing agent, 13 parts of antismoke agent, ultraviolet absorbing agent
9 parts.
Embodiment 3
A kind of anti-flammability binder provided by the invention, the anti-flammability binder are made from the following raw materials in parts by weight:
22 parts of aluminum oxide, 18 parts halogen-free of epoxy resin, 11 parts of 3- ethoxyl ethyl propionate；8 parts of alcohol-soluble acrylic resin,
16 parts of organophosphorus compound, 4 parts of curing accelerator, 6 parts of fire retardant, 9 parts of curing agent, 10 parts of antismoke agent, ultraviolet absorbing agent 7
Part.
The beneficial effects of the present invention are: the anti-flammability binder high temperature resistant, good flame retardation effect, security performance high pollution object
Few, quality is stablized.
Although the embodiments of the present invention has been shown and described above, it is to be understood that above-described embodiment is example
Property, it is not considered as limiting the invention, those skilled in the art within the scope of the invention can be to above-mentioned
Embodiment is changed, modifies, replacement and variant.
Claims (4)
1. a kind of anti-flammability binder, which is characterized in that the anti-flammability binder is made from the following raw materials in parts by weight: three oxygen
Change 17~26 parts of two aluminium, 15~20 parts halogen-free of epoxy resin, 8~15 parts of 3- ethoxyl ethyl propionate；Alcohol-soluble acrylic acid
6~9 parts of resin, 15~18 parts of organophosphorus compound, 3~6 parts of curing accelerator, 5~8 parts of fire retardant, curing agent 7~12
Part, 7~13 parts of antismoke agent, 4~9 parts of ultraviolet absorbing agent.
2. anti-flammability binder according to claim 1, which is characterized in that the anti-flammability binder is by following parts by weight
Raw material be made: 17 parts of aluminum oxide, 15 parts halogen-free of epoxy resin, 8 parts of 3- ethoxyl ethyl propionate；Alcohol-soluble propylene
It is 6 parts of acid resin, 15 parts of organophosphorus compound, 3 parts of curing accelerator, 5 parts of fire retardant, 7 parts of curing agent, 7 parts of antismoke agent, ultraviolet
4 parts of light absorbers.
3. anti-flammability binder according to claim 1, which is characterized in that the anti-flammability binder is by following parts by weight
Raw material be made: 26 parts of aluminum oxide, 20 parts halogen-free of epoxy resin, 15 parts of 3- ethoxyl ethyl propionate；Alcohol-soluble third
9 parts of olefin(e) acid resin, 18 parts of organophosphorus compound, 6 parts of curing accelerator, 8 parts of fire retardant, 12 parts of curing agent, 13 parts of antismoke agent,
9 parts of ultraviolet absorbing agent.
4. anti-flammability binder according to claim 1, which is characterized in that the anti-flammability binder is by following parts by weight
Raw material be made: 22 parts of aluminum oxide, 18 parts halogen-free of epoxy resin, 11 parts of 3- ethoxyl ethyl propionate；Alcohol-soluble third
8 parts of olefin(e) acid resin, 16 parts of organophosphorus compound, 4 parts of curing accelerator, 6 parts of fire retardant, 9 parts of curing agent, 10 parts of antismoke agent,
7 parts of ultraviolet absorbing agent.