CN107903543A - One kind is used for flame-proof abrasion-resistant chemical resistance sizing material - Google Patents
One kind is used for flame-proof abrasion-resistant chemical resistance sizing material Download PDFInfo
- Publication number
- CN107903543A CN107903543A CN201711211553.1A CN201711211553A CN107903543A CN 107903543 A CN107903543 A CN 107903543A CN 201711211553 A CN201711211553 A CN 201711211553A CN 107903543 A CN107903543 A CN 107903543A
- Authority
- CN
- China
- Prior art keywords
- sizing material
- flame
- chemical resistance
- proof abrasion
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides one kind to be used for flame-proof abrasion-resistant chemical resistance sizing material.For the sizing material using 26 type fluorubber as main material, resorcinol binder resin, precipitated silica, bisphenol AF, accelerant B PP, be main auxiliary material, is made with certain be kneaded.The advantages of this rubber is:The sizing material is fire-retardant, wear-resisting, resistant to chemical etching with the high and energy with aromatic polyamide cord bonding strength.
Description
Technical field
The present invention relates to high molecular material, is specifically that one kind is used for flame-proof abrasion-resistant chemical resistance sizing material.
Background technology
The framework material that existing protection adhesive plaster uses is not pure aramid fabric.It is the court head to do framework material using aramid fabric
Wound, while rubber compound that is high performance, having been bonded with aramid fiber framework material is equipped with, and our company initiates.Flame-proof abrasion-resistant resistance toization
Learn corrosivity protection adhesive plaster and use aramid fabric as framework material, with many advantages, such as intensity is high, heat endurance is good, but at the same time
The shortcomings that aramid fabric with rubber there is being not easy to bond.
The content of the invention
The invention aims to provide one kind to be used for flame-proof abrasion-resistant chemical resistance sizing material.
Realizing the technical solution of the object of the invention is:One kind is used for flame-proof abrasion-resistant chemical resistance sizing material, the sizing material with
26 type fluorubber are main material, resorcinol binder resin, precipitated silica, bisphenol AF, accelerant B PP, for main auxiliary
Material, is made with being kneaded.Specific materials and materials weight are:
Further, preferred solution of the invention is:
The 26 type fluorubber have the characteristics that strength and extension property height, good combination property;Resorcinol binder resin is in rubber
It can react in glue sizing material, so as to play the role of bonding;The use occasion of fluorubber needs flame-proof abrasion-resistant resistant to chemical etching,
Select the spray carbon black that heat is low, performance is stablized to make reinforcing agent in sizing compound formula, in this way, can not only increase loading, reduce
Cost, and also preferable processing performance;Activated magnesia and calcium hydroxide combined system is selected to have as sour accepting agent
Effect ground neutralizes the hydrogen fluoride during vulcanizable fluororubber, moreover it is possible to promotes the raising of crosslink density, it is steady to assign the preferable heat of vulcanizate
It is qualitative.
It is an advantage of the invention that:The sizing material has high, flame-proof abrasion-resistant chemical resistance with aromatic polyamide cord bonding strength
Performance advantage.
Embodiment
Performance is as follows after tested for this sizing material:
Claims (2)
1. one kind is used for flame-proof abrasion-resistant chemical resistance sizing material, it is characterized in that by following raw materials by weight ratio through being kneaded
Form:
2. sizing material according to claim 1, it is characterized in that:Materials and materials weight are: