CN1095733A - Multicolor finish and preparation technology thereof - Google Patents
Multicolor finish and preparation technology thereof Download PDFInfo
- Publication number
- CN1095733A CN1095733A CN 93105085 CN93105085A CN1095733A CN 1095733 A CN1095733 A CN 1095733A CN 93105085 CN93105085 CN 93105085 CN 93105085 A CN93105085 A CN 93105085A CN 1095733 A CN1095733 A CN 1095733A
- Authority
- CN
- China
- Prior art keywords
- colored paint
- prepared
- straight
- final product
- dispersion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Multicolor finish involved in the present invention makes after by required mixed by two or more the straight-shade coating that is made of colored paint, dispersion liquid, and raw materials used is 22
#Resin liquid, dimethylbenzene, butanols, pigment, Synolac, dibutyl phthalate, Tritolyl Phosphate, Viscotrol C, nitro-cotton, butylacetate, methyl-isobutyl ethanol, DC dispersion agent, deionized water, octyl acetate etc., being prepared as of straight-shade coating wherein: 60 ℃ 60% colored paint added in 50 ℃ 40% the dispersion liquid, be stirred to desired particle size with dispersion machine and get final product, the present invention have color lucid and lively, bright and lustrous soft, can be made into multiple pattern, good decorating effect and prepare advantages such as simple.
Description
The present invention relates to a kind of coating and preparation thereof.
Coating mostly was paint etc. as finishing material in the past, if want to have in a kind of slurry the then difficult realization of multiple color lump, people always wish to have decorative effect variation, multicoloured coating, to reach better decorative effect.
The objective of the invention is to develop a kind of multicolor finish and preparation technology thereof.
Multicolor finish involved in the present invention makes after by required mixed by the straight-shade coating that is made of colored paint, dispersion liquid, and wherein the colored paint prescription is:
Base-material 54.95%
Mill base 23.15%
22# resin liquid 13.10%
The hot fat 3.10% of acetate
Dimethylbenzene 5.10%
Butanols 0.60%
It is prepared as: above-mentioned raw materials is put into the reactor stirring by formula rate got final product in about seven hours.
The prescription of aforementioned mill base is:
Pigment 53.84%
Synolac 28.85%
Dibutyl phthalate (DBP) 9.62%
Trimethylbenzene lipoprotein of phosphoric acid 1.92%
Castor oil 1.92%
Dimethylbenzene 3.85%
It is prepared as: after above-mentioned raw materials is pressed the formula rate mixing, stirred three hours, be ground to granularity and reach 20 microns and get final product on three-roll grinder, described pigment can select titanium dioxide, iron oxide red, carbon black, molybdenum red, lemon yellow, chrome green, the blue or green orchid of titanium etc. according to the requirement of color.
The prescription of aforementioned base-material is:
Nitro-cotton 10.15%
Dimethylbenzene 39.95%
Ethyl acetate 12.05%
Castor oil 1.30%
Dibutyl phthalate (DBP) 1.20%
The hot fat 25.30% of acetate
Methyl-isobutyl ethanol 10.05%
It is prepared as: earlier above-mentioned other raw materials except that nitro-cotton were put into the dissolution kettle stir about ten minutes, then the nitro-cotton gradation is added back stirring ten hours, get final product after even.
The prescription of aforementioned dispersion liquid is:
DC dispersion agent 1.55%
Deionized water 98.45%
It is prepared as: above-mentioned raw materials is pressed formula rate mix, the dissolving of DC dispersion agent is got final product.
Being prepared as of straight-shade coating: in the dispersion liquid with 50 ℃ 40% of 60 ℃ 60% colored paint adding, be stirred to desired particle size with dispersion machine and get final product.Wherein said granularity is fixed to the requirement of colored paint in the multicolor finish (color lump) size according to the user, promptly depends on the requirement of user to decorative effect.
With two or more straight-shade coating be mixed in proportion stir after, multicolor finish.Described ratio requires to decide to the density of each color lump according to the user.
The present invention have color lucid and lively, bright and lustrous soft, can be made into multiple pattern, good decorating effect and prepare advantages such as simple.
Claims (3)
1, a kind of multicolor finish is blended together by two or more straight-shade coating, and it is characterized in that: described straight-shade coating is made of colored paint and dispersion liquid, and the prescription of wherein said colored paint is:
Base-material 54.95%
Mill base 23.15%
22
#Resin liquid 13.10%
The hot fat 3.10% of acetate
Dimethylbenzene 5.10%
Butanols 0.60%
The prescription of described base-material is:
Nitro-cotton 10.15%
Dimethylbenzene 39.95%
Ethyl acetate 12.05%
Castor oil 1.30%
Dibutyl phthalate (DBP) 1.20%
The hot fat 25.30% of acetate
Methyl-isobutyl ethanol 10.05%
The prescription of described mill base is:
Pigment 53.84%
Synolac 28.85%
Dibutyl phthalate (DBP) 9.62%
Trimethylbenzene lipoprotein of phosphoric acid 1.92%
Castor oil 1.92%
Dimethylbenzene 3.85%
The prescription of described dispersion liquid is:
DC dispersion agent 1.55%
Deionized water 98.45%
2, multicolor finish according to claim 1 is characterized in that: described pigment is titanium dioxide, iron oxide red, carbon black, molybdenum red, lemon yellow, chrome green, the blue or green orchid of titanium etc.
3, a kind of technology for preparing claim 1 or 2 is mixed in proportion two or more straight-shade coating and stirs, and it is fixed that described ratio requires the density of each color lump according to the user, it is characterized in that:
Being prepared as of straight-shade coating: in the dispersion liquid with 50 ℃ 40% of 60 ℃ 60% colored paint adding, being stirred to desired particle size with dispersion machine gets final product, wherein said granularity is fixed to the requirement of colored paint in the multicolor finish (color lump) size according to the user, promptly depends on the requirement of user to decorative effect;
Being prepared as of described colored paint: raw material is put into reactor by proportioning stirred about seven hours; Being prepared as of base-material wherein: earlier above-mentioned other raw materials except that nitro-cotton were put into the dissolution kettle stir about ten minutes, then the nitro-cotton gradation is added back stirring ten hours, get final product after even; Being prepared as of mill base wherein: after raw material pressed formula rate and mix, stirred three hours, on three-roll grinder, be ground to granularity and reach 20 microns and get final product;
Being prepared as of described dispersion liquid: raw material is pressed formula rate mix, the dissolving of DC dispersion agent is got final product.