CN109571714A - The preparation method of interior/exterior decoration papery watt and the interior/exterior decoration papery watt thus prepared - Google Patents

The preparation method of interior/exterior decoration papery watt and the interior/exterior decoration papery watt thus prepared Download PDF

Info

Publication number
CN109571714A
CN109571714A CN201810436199.0A CN201810436199A CN109571714A CN 109571714 A CN109571714 A CN 109571714A CN 201810436199 A CN201810436199 A CN 201810436199A CN 109571714 A CN109571714 A CN 109571714A
Authority
CN
China
Prior art keywords
watt
papery
preparation
mentioned
interior
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810436199.0A
Other languages
Chinese (zh)
Inventor
韩泽永
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Publication of CN109571714A publication Critical patent/CN109571714A/en
Pending legal-status Critical Current

Abstract

The present invention relates to the preparation method of following interior/exterior decoration papery watt and thus the interior/exterior decoration papery watt prepared: due to using industry waste paper, resource can be re-used, since weight can be greatly reduced, workability can be improved and shorten the activity duration, due to easily prepared, product cost can be reduced significantly to ensure economy and product competitiveness.According to the present invention, the preparation method of following interior/exterior decoration papery watt is provided, that is, the preparation method of above-mentioned interior/exterior decoration papery watt includes: raw material preparation step, in order to form papery watt, prepares the raw material comprising paper powder end;Raw mixture preparation process prepares raw mixture with requirement ratio mixing above-mentioned raw materials;Whipping step mixes above-mentioned raw materials mixture with water to prepare stirring thing;Maturation step makes above-mentioned stirring thing maturation carry out quick lime;Forming step carries out molding preparation using above-mentioned stirring thing of watt shaping frame to institute's maturation;And drying steps, molding molding in above-mentioned forming step is dried to complete.

Description

The preparation method of interior/exterior decoration papery watt and the interior/exterior decoration thus prepared are used Papery watt
Technical field
The present invention relates to the preparation method of interior/exterior decoration papery watt and thus the interior/exterior decoration papery watt prepared, In more detail, the interior/exterior decoration papery for being related to the preparation method of following interior/exterior decoration papery watt and thus preparing Watt: since resource can be re-used using industry waste paper, since weight can be greatly reduced, workability can be improved and shorten and make The industry time can reduce product cost significantly due to easily prepared to ensure economy and product competitiveness.
Background technique
In general, cover Korea Spro room roof watt during, spread on the upside of the cover board for being stamped rafter after viscosity on it Plain tile and circle watt are covered, at this point, paving in a manner of opening along longitudinal overlap 2 to 3 watt, along transverse direction with the both ends of plain tile Adjacent mode is paved watt side by side, covers circle watt by clay in the upside of the adjacent part in above-mentioned plain tile both ends.
This previous Korea Spro's roofing tile is to pinch native (kaolin, clay etc.) to form plain tile, circle watt one by one, therefore, is inhaled Wet effect is good and the weak and easy breakage of hardness, and therefore, rainy day can leak, and needs often to repair, and due to very heavy, inconvenience is carried, It is constructed in a manner of being overlapped enumerate individual watt one by one, therefore, it is necessary to many labours and times, on the roof constructed In, if watt by summer solar heat heat, due to watt be thickness soil plate, accumulation heat and shape room in conduction, to make interior Heating, due to problem as described above, be not appropriate for by decorate for the purpose of performance with watt.
In view of problem as described above, recently, the metal tile by the molding bone plate form of iron plate is disclosed, this tool There are outstanding application property and waterproofness, still, this metal tile is to carry out die mould to metal plate to form, to expression such as Korea Spro's roofing tile The deep thin plain tile of paddy, circle watt shape, then need a large amount of iron plates, not only without economy, when molded, be bent Platform part it is not easily molded.In particular, electric leakage and lightning stroke are not avoided that when being constructed, not with the intrinsic shape of such as Korea Spro's roofing tile Shape construction, therefore avoid constructing, this is also not suitable for performance use watt of decorative purpose.
Existing technical literature
Patent document
(patent document 1) (document 1) Korean Patent Laid 10-1986-0001266 (on February 24th, 1986 open)
(patent document 2) (document 2) South Korea discloses utility model bulletin 20-1998-0008338 (on 04 30th, 1998 It is open)
(patent document 3) (document 3) Korean Patent Laid 10-1997-0027001 (on 06 24th, 1997 open)
(patent document 4) (document 4) South Korea discloses utility model bulletin 20-1998-0008341 (on 04 30th, 1998 It is open)
(patent document 5) (document 5) Korean granted utility model bulletin 20-0370373 (bulletin on December 20th, 2004)
Summary of the invention
Therefore, for solve conventional problems as described above the object of the present invention is to provide following indoor and outdoors The preparation method of decoration paper matter watt and the interior/exterior decoration papery watt thus prepared: due to that can weigh using industry waste paper Resource is newly utilized, since weight can be greatly reduced, workability can be improved and the shortening activity duration can be significant due to easily prepared Product cost is reduced to ensure economy and product competitiveness.
Problem of the invention is not limited to content set forth above, and those of ordinary skill can be defined by following record Understand the other problems not proposed.
According to the viewpoint of the invention for realizing the purpose of aforementioned present invention and other features, following interior is provided The preparation method of external decoration papery watt, that is, the preparation method of above-mentioned interior/exterior decoration papery watt includes: raw material preparation step Suddenly, in order to form papery watt, prepare the raw material comprising paper powder end;Raw mixture preparation process is mixed above-mentioned with requirement ratio Raw material prepares raw mixture;Whipping step mixes above-mentioned raw materials mixture with water to prepare stirring thing;Maturation step, Above-mentioned stirring thing maturation is set to carry out quick lime;Forming step is carried out using above-mentioned stirring thing of watt shaping frame to institute's maturation Molding preparation;And drying steps, molding molding in above-mentioned forming step is dried to complete.
A viewpoint according to the present invention, above-mentioned raw materials may include paper powder end, lime powder, compression cement or mortar, loess Powder and powder-type fire retardant.
A viewpoint according to the present invention, for each above-mentioned raw materials, the range of shared content is as follows: paper powder end accounts for 30 Weight percent~60 weight percent, as lime powder cement account for 18 weight percent~22 weight percent, compression Cement or mortar account for 8 weight percent~15 weight percent, loess powder accounts for 5 weight percent~10 weight percent, resistance Combustion powder accounts for 3 weight percent~8 weight percent, and above-mentioned raw materials also include liquid phase waterproofing agent, relative to the upper of 100 parts by weight Paper powder end is stated, the above-mentioned liquid phase waterproofing agent of 6 parts by weight~30 parts by weight is mixed.
A viewpoint according to the present invention, it is preferable that in above-mentioned maturation step, given birth to maturation in 1 hour~3 hours Calcification, maturation carry out to the external condensed water in stirring thing being divided into only.
Another viewpoint according to the present invention provides the preparation of the interior/exterior decoration papery watt according to a viewpoint as described above Method is come the interior/exterior decoration papery watt that is prepared.
The preparation method of interior/exterior decoration present invention as described above papery watt and the interior/exterior decoration thus prepared Have the effect of with papery watt as follows.
First, therefore the present invention can re-use resource using industry waste paper.
Second, the present invention can greatly reduce weight, therefore, workability can be improved and shorten the activity duration, due to being easy to make It is standby, product cost can be reduced significantly to ensure economy and product competitiveness.
Traditional Korean style watt as traditional Korean Architecture object grace factor can be suitable for interior/exterior decoration by third, the present invention Works therefore can be to the tradition beauty of domestic and international publicity South Korea.
Effect of the invention is not limited to content set forth above, and those of ordinary skill can be defined by following record Understand the other problems not proposed.
Detailed description of the invention
Fig. 1 is the flow chart for showing the preparation process of interior/exterior decoration papery watt of the invention.
Fig. 2 be show by interior/exterior decoration papery watt of the invention preparation method preparation watt in a structural element Plain tile figure.
Fig. 3 be show by interior/exterior decoration papery watt of the invention preparation method preparation watt in a structural element Plain tile side view.
Fig. 4 be show by interior/exterior decoration papery watt of the invention preparation method preparation watt in a structural element Round eaves-tile ornament figure.
Fig. 5 be the preparation method preparation by interior/exterior decoration papery watt of the invention watt in a structural element The figure of one end (rear section) observation of round eaves-tile ornament.
Fig. 6 be show by interior/exterior decoration papery watt of the invention preparation method preparation watt in a structural element The figure worked as of plain tile.
Fig. 7 be show by interior/exterior decoration papery watt of the invention preparation method preparation watt in a structural element Solid watt of figure.
The explanation of appended drawing reference
S100: raw material preparation step
S200: raw mixture preparation process
S300: whipping step
S400: maturation step
S500: forming step
S600: drying steps
Specific embodiment
Addition objects, features and advantages of the invention can be expressly understood that by detailed description below and attached drawing.
Before the present invention is described in detail, it should be appreciated that the present invention can carry out numerous variations, and can have Various embodiments, the illustration for being illustrated and being shown in the accompanying drawings in the following do not limit the invention to specific reality Mode is applied, is included in the having altered of thought and technical scope of the invention, equivalent technical solutions to replacing technical solution to belong to In the present invention.
When proposing a structural element with another structural element " being connected " or " being connected ", not only can be understood as The two is directly connected to or directly couples, it is understood that there is other structures element between the two.On the contrary, when proposing a knot When structure element is with another structural element " being directly connected to " or " directly coupling ", it should be understood that among the two, there is no other structures Element.
Term used in the present specification is merely to illustrate specific embodiment, does not limit the present invention.Unless in text Difference is explicitly indicated that on arteries and veins, then singular expression includes the expression of plural number.In the present specification, it should be appreciated that " comprising " Or the term of " having " etc. for it is specified in the description documented by feature, number, step, movement, structural element, component or The presence of their combination, rather than other one or more features or number, step, movement, structure are excluded in advance The presence or additional possibility of element, component or their combination.
Also, the term of " ... portion " documented by the description, " ... unit ", " ... module " etc. means to locate In at least one function or the unit of movement, this being implemented in combination with by hardware or software or hardware and software.
Also, during being described with reference to the accompanying drawings, independently with appended drawing reference, identical structural element is assigned Identical appended drawing reference will be omitted to this repeat description.In the course of describing the present invention, if think to it is relevant Related illustrate of well-known technique unnecessarily obscures the gist of the invention, then description is omitted.
Hereinafter, being made referring to attached drawing to the preparation method of the interior/exterior decoration papery watt of the preferred embodiment of the present invention and thus Standby interior/exterior decoration papery watt is described in detail.
Firstly, the preparation method of interior/exterior decoration of the invention papery watt is described in detail referring to Figure 1 to Figure 7. Fig. 1 is the flow chart for showing the preparation process of interior/exterior decoration papery watt of the invention, and Fig. 2 is to show by interior of the invention External decoration papery watt preparation method preparation watt in a structural element plain tile figure, Fig. 3 be Fig. 2 plain tile side view Figure, Fig. 4 be show by interior/exterior decoration papery watt of the invention preparation method preparation watt in a structural element circle The figure of eaves tile, Fig. 5 are in the figure of one end (rear section) observation of the round eaves-tile ornament of Fig. 4, and Fig. 6 is to show by indoor exterior of the invention The preparation method preparation of decorations papery watt watt in a structural element the figure worked as of plain tile, Fig. 7 is to show by room of the invention The preparation method preparation of internal and external ornament papery watt watt in a structural element solid watt of figure.
As shown in Figure 1, the preparation method of interior/exterior decoration papery watt of the invention includes: raw material preparation step S100, Prepare the raw material for being used to form papery watt;Raw mixture preparation process S200 is blended in above-mentioned raw materials with requirement ratio and prepares The raw material for preparing in step S100 prepares raw mixture;Whipping step S300 makes in above-mentioned raw materials mixture preparation process The raw mixture prepared in S200 mixes to prepare stirring thing with the water of specified amount;Maturation step S400, makes in above-mentioned stirring The stirring thing maturation for preparing in step S300 carries out quick lime;Forming step S500, using a watt shaping frame (mold) to institute The above-mentioned stirring thing of maturation carries out molding preparation;And drying steps S600, in above-mentioned forming step S500 it is molding at Type object is spontaneously dried to complete.
The raw material prepared in above-mentioned raw materials preparation process S100 includes paper powder end, lime powder, compression cement or sand Slurry, loess powder and powder-type fire retardant.
Above-mentioned paper powder end is formed by the paper powder end formed by specified process, it is preferable that by the paper powder end shape using waste paper At above-mentioned lime powder is cement (for example, a kind of cement), compresses the aggregate and aggregate of cement or mortar blended cement and sand etc. It is formed with organic/inorganic binder, above-mentioned fire retardant can be formed by inorganic based flame retardant or organic based flame retardant.
Wherein, above-mentioned raw materials preparation process S100 also may include waterproofing agent (preferably liquid phase waterproofing agent), to improve most The waterproofness of finished product.Above-mentioned waterproofing agent is mixed with mortar or concrete to block its gap, Lai Tigao watertightness plays anti- Water, damp proof effect, can by sodium metasilicate (waterglass) class, silicic acid powdery type, fatty acid, pitch, paraffin, polymer substance cream The formation such as turbid.
Later, in above-mentioned raw materials mixture preparation process S200, allotment ratio is adjusted to deploy according to field condition The each above-mentioned raw materials prepared, are mixed using blender etc., can be with 30 weight percent~60 weight percent Paper powder end (waste paper powder), 18 weight percent~22 weight percent lime powder (cement), 8 weight percent~15 weights The compression cement or mortar, 5 weight percent~10 weight percent loess powder of amount percentage and 3 weight percent~8 It is deployed in the range of the fire-retardant powder (powder-type fire retardant) of weight percent.
Preferably, each above-mentioned raw materials are with the paper powder of 55 weight percent last (waste paper powder), the stone of 22 weight percent Grey powder (cement), the compression cement of 10 weight percent or the loess powder and 3 weight percent of mortar, 10 weight percent Fire-retardant powder (powder-type fire retardant) allotment.
Also, when above-mentioned raw materials also include waterproofing agent (liquid phase waterproofing agent), relative to the paper powder end of 100 parts by weight, packet Containing 6 parts by weight~30 parts by weight waterproofing agent, that is, include 5%~20% waterproofing agent.
The present inventor is by research repeatedly and preproduction to weight, rigidity, mouldability (processability), waterproofness Etc. being tested as a result, having confirmed that, above-mentioned numberical range is optimal values.
Also, the present invention also may include pigment, make above-mentioned raw materials that can assign beautiful color to final products.
Later, it in above-mentioned whipping step S300, is stirred using blender etc., the stirring thing stirred is above-mentioned Pass through 1 hour~3 hours in maturation step S400, it is preferable that 2 hours or so maturation processes carry out quick lime, above-mentioned The external condensed water of stirring thing, which is divided into, only carries out maturation.
Later, it in above-mentioned forming step S500, is carried out after the stirring thing of institute's maturation is filled to the shaping frame of hydraulic press Molding, at this point, shaping frame according to watt type include plain tile shaping frame, round eaves-tile ornament shaping frame, plain tile when shaping frame, consolidate watt at Type frame.
Wherein, as shown in Figures 2 and 3, above-mentioned plain tile shaping frame using make molding plain tile one end one side (preferably, with the outside of the radial direction of the plain tile of arc-shaped formation) be formed with the plain tile of specified altitude boss outstanding at Type frame.
Also, as shown in fig. 6, above-mentioned plain tile when shaping frame also using make the one side of one end worked as of molding plain tile (preferably, with the outside of the radial direction in the plain tile portion of arc-shaped formation) is formed with the plain tile of specified altitude boss outstanding Work as shaping frame.
As described above, forming boss in plain tile peace eaves tile, there is following problem in the past, that is, tail portion is overlapped It is constructed in a manner of collapsing, since ponding generates backflow phenomena caused by stagnation behavior, the present invention can prevent this phenomenon.
Also, as shown in figure 4, in the case where above-mentioned round eaves-tile ornament shaping frame, it is preferable that when from length direction institute at When one end (the decorative pattern formation opposite end) of the round eaves-tile ornament of type, the terminal surface of semiorbicular end be formed with have with plain tile and The round eaves-tile ornament for the inclined cross section that the upper side (round eaves-tile ornament mounting surface) that plain tile is worked as meets.
Then, it is preferable that the molding molding of institute need to be spontaneously dried in above-mentioned forming step S500.
According to the preparation method of the interior/exterior decoration of aforementioned present invention papery watt and thus the interior/exterior decoration prepared is used Papery watt has the following advantages, that is, due to that can re-use resource using industry waste paper, due to that can greatly reduce weight Amount can be improved workability and shorten the activity duration, due to being easy preparation, can reduce product cost significantly to ensure economy and production Product competitiveness.
Also, traditional Korean style watt as the element of the traditional architecture object of South Korea's beauty can be suitable for indoor exterior by the present invention Works is adornd, it therefore, can be to the tradition beauty of domestic and international publicity South Korea.
Only illustratively explanation is contained in technical idea of the invention to embodiment and attached drawing in the present specification A part.Therefore, embodiment disclosed in this description is for illustrating technical idea of the invention, rather than limits this The technical idea of invention, therefore, it is obvious that the range of technical idea of the invention, which is not limited to above-described embodiment,.It answers When understanding, those of ordinary skill simply leads in the range of being included in the technical idea of specification and attached drawing of the invention Variation and specific embodiment out belongs to interest field of the invention.

Claims (4)

1. a kind of preparation method of interior/exterior decoration papery watt characterized by comprising
Raw material preparation step prepares to form papery watt comprising paper powder end, lime powder, compression cement or mortar, loess powder Last, powder-type fire retardant raw material;
Raw mixture preparation process prepares raw mixture with requirement ratio mixing above-mentioned raw materials;
Whipping step mixes above-mentioned raw materials mixture with water to prepare stirring thing;
Maturation step makes above-mentioned stirring thing maturation carry out quick lime;
Forming step carries out molding preparation using above-mentioned stirring thing of watt shaping frame to institute's maturation;And
Drying steps are dried molding molding in above-mentioned forming step to complete.
2. the preparation method of interior/exterior decoration papery watt according to claim 1, which is characterized in that
For each above-mentioned raw materials, the range of shared content is as follows: paper powder end accounts for 30 weight percent~60 weight percents Than, as lime powder cement account for 18 weight percent~22 weight percent, compression cement or mortar account for 8 weight percent ~15 weight percent, loess powder account for 5 weight percent~10 weight percent, fire-retardant powder accounts for 3 weight percent~8 weights Percentage is measured,
Above-mentioned raw materials also include liquid phase waterproofing agent,
Relative to the above-mentioned paper powder end of 100 parts by weight, the above-mentioned liquid phase waterproofing agent of 6 parts by weight~30 parts by weight is mixed.
3. the preparation method of interior/exterior decoration papery watt according to claim 1, which is characterized in that walked in above-mentioned maturation In rapid, quick lime was carried out with maturation in 1 hour~3 hours, maturation carries out to the external condensed water in stirring thing being divided into only.
4. a kind of interior/exterior decoration papery watt, which is characterized in that interior according to any one of claims 1 to 3 The preparation method of external decoration papery watt is prepared.
CN201810436199.0A 2017-09-29 2018-05-09 The preparation method of interior/exterior decoration papery watt and the interior/exterior decoration papery watt thus prepared Pending CN109571714A (en)