CN109554923A - A kind of digit printing fabric flame-proof antibiotic coating - Google Patents
A kind of digit printing fabric flame-proof antibiotic coating Download PDFInfo
- Publication number
- CN109554923A CN109554923A CN201811405242.3A CN201811405242A CN109554923A CN 109554923 A CN109554923 A CN 109554923A CN 201811405242 A CN201811405242 A CN 201811405242A CN 109554923 A CN109554923 A CN 109554923A
- Authority
- CN
- China
- Prior art keywords
- parts
- digit printing
- printing fabric
- proof antibiotic
- hexamethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The application belongs to fabric coating technology, specially a kind of digit printing fabric flame-proof antibiotic coating, raw material including following portions by weight, 20 parts of hydroxyethyl cellulose, 16 parts of chlorosulfonated polyethylene, 13 parts of trioctyl phosphate, 25 parts of hexamethylene alkylene pentylcyclohexanone, 30 parts of petroleum ether, 10 parts of stearate, 24 parts of sorbierite, 6 parts of hexamethylene, 18 parts of lauryl sodium sulfate, 25 parts of copper zinc pyrithione, 5 parts of imidazoline, 1000 parts of water, 5 parts of graphite powder, 15 parts of aluminium hydroxide, 25 parts of zirconium dioxide, 15 parts of bentonite, 5 parts of styrax, 5 parts of defoaming agent, 3 parts of dispersing agent, 2 parts of preservative.
Description
Technical field
The application belongs to fabric coating technology, specially a kind of preparation method of digit printing fabric flame-proof antibiotic coating.
Background technique
Digit printing is the stamp carried out with digital technology.Digital printing technology is as computer technology continues to develop
And a kind of new high-tech product for integrating machinery, computer machine electronic information technology gradually formed.And now with life
The raising of bioplasm amount, people more and more select outdoor sports, such as mountain-climbing, rock-climbing, and movement can generate a large amount of outdoors
Sweat, this requires fabrics to have antibacterial, fire-retardant excellent function.
Summary of the invention
In order to solve the above-mentioned technical problem, this application provides a kind of preparation sides of digit printing fabric flame-proof antibiotic coating
Method, the application are realized by following proposal:
A kind of digit printing fabric flame-proof antibiotic coating, 20 parts of hydroxyethyl cellulose, 16 parts of chlorosulfonated polyethylene, trioctyl phosphate
13 parts, 25 parts of hexamethylene alkylene pentylcyclohexanone, 30 parts of petroleum ether, 10 parts of stearate, 24 parts of sorbierite, 6 parts of hexamethylene, dodecane
18 parts of base sodium sulphate, 25 parts of copper zinc pyrithione, 5 parts of imidazoline, 1000 parts of water, 5 parts of graphite powder, 15 parts of aluminium hydroxide, titanium dioxide
25 parts of zirconium, 15 parts of bentonite, 5 parts of styrax, 5 parts of defoaming agent, 3 parts of dispersing agent, 2 parts of preservative.
Preferably, 18 parts of hydroxyethyl cellulose, 14 parts of chlorosulfonated polyethylene, 11 parts of trioctyl phosphate, hexamethylene alkylene basic ring
23 parts of hexanone, 28 parts of petroleum ether, 8 parts of stearate, 22 parts of sorbierite, 4 parts of hexamethylene, 16 parts of lauryl sodium sulfate, pyridine
23 parts of sulfidion copper zinc, 3 parts of imidazoline, 1000 parts of water, 4 parts of graphite powder, 13 parts of aluminium hydroxide, 23 parts of zirconium dioxide, 13 parts of bentonite,
4 parts of styrax, 4 parts of defoaming agent, 2 parts of dispersing agent, 1.5 parts of preservative.
Preferably, 16 parts of hydroxyethyl cellulose, 12 parts of chlorosulfonated polyethylene, 9 parts of trioctyl phosphate, hexamethylene alkylidene hexamethylene
20 parts of ketone, 22 parts of petroleum ether, 6 parts of stearate, 20 parts of sorbierite, 2 parts of hexamethylene, 13 parts of lauryl sodium sulfate, pyridine sulphur
20 parts of copper zinc, 3 parts of imidazoline, 1000 parts of water, 3 parts of graphite powder, 10 parts of aluminium hydroxide, 20 parts of zirconium dioxide, 11 parts of bentonite, peace
Breath is 2 parts, 2 parts of defoaming agent, 2 parts of dispersing agent, 1 part of preservative fragrant.
Preferably, the defoaming agent is BYK057.
Preferably, the dispersing agent is sodium tetrapolyphosphate, and the mixture of calgon and modified siloxane, described four is poly-
The mass ratio of sodium phosphate, calgon and modified siloxane is 1:2:1.
Preferably, the preservative be methylparaben, ethylparaben, propylben and butyl hydroxybenzoate, it is described
Methylparaben, ethylparaben, propylben and butyl hydroxybenzoate mass ratio be 1:4:2:3.
A kind of preparation method of digit printing fabric flame-proof antibiotic coating, (1) is by hydroxyethyl cellulose, the poly- second of chlorosulfonation
Alkene, trioctyl phosphate, hexamethylene alkylene pentylcyclohexanone, petroleum ether, stearate, sorbierite, hexamethylene, lauryl sodium sulfate,
Copper zinc pyrithione, imidazoline and water are placed in reaction kettle, and stir 3h at 55 DEG C;(2) continue that defoaming is added into reaction kettle
Agent, dispersing agent and preservative simultaneously stir 4h at 70 DEG C;(3) by graphite powder, aluminium hydroxide, zirconium dioxide and bentonite are in 500
Calcining 2h is placed on machinery spheroidal graphite 8h in spheroidal graphite tank and obtains premix at DEG C;(4) step (2) are added in premix obtained by step (3)
Reaction kettle at 60 DEG C stir 2h up to digit printing fabric flame-proof antibiotic coating.
Preferably, the revolving speed of the spheroidal graphite is 600r/min, and spheroidal graphite atmosphere is under neon atmosphere.
The application's, the utility model has the advantages that the application preparation process is simple, has high fire-retardance, high anti-microbial property, is suitble in face
Material field uses, and improves the performance of product.
Specific embodiment
Embodiment 1
A kind of digit printing fabric flame-proof antibiotic coating, 20 parts of hydroxyethyl cellulose, 16 parts of chlorosulfonated polyethylene, trioctyl phosphate
13 parts, 25 parts of hexamethylene alkylene pentylcyclohexanone, 30 parts of petroleum ether, 10 parts of stearate, 24 parts of sorbierite, 6 parts of hexamethylene, dodecane
18 parts of base sodium sulphate, 25 parts of copper zinc pyrithione, 5 parts of imidazoline, 1000 parts of water, 5 parts of graphite powder, 15 parts of aluminium hydroxide, titanium dioxide
25 parts of zirconium, 15 parts of bentonite, 5 parts of styrax, 5 parts of defoaming agent, 3 parts of dispersing agent, 2 parts of preservative.
Preferably, the defoaming agent is BYK057.
Preferably, the dispersing agent is sodium tetrapolyphosphate, and the mixture of calgon and modified siloxane, described four is poly-
The mass ratio of sodium phosphate, calgon and modified siloxane is 1:2:1.
Preferably, the preservative be methylparaben, ethylparaben, propylben and butyl hydroxybenzoate, it is described
Methylparaben, ethylparaben, propylben and butyl hydroxybenzoate mass ratio be 1:4:2:3.
A kind of preparation method of digit printing fabric flame-proof antibiotic coating, (1) is by hydroxyethyl cellulose, the poly- second of chlorosulfonation
Alkene, trioctyl phosphate, hexamethylene alkylene pentylcyclohexanone, petroleum ether, stearate, sorbierite, hexamethylene, lauryl sodium sulfate,
Copper zinc pyrithione, imidazoline and water are placed in reaction kettle, and stir 3h at 55 DEG C;(2) continue that defoaming is added into reaction kettle
Agent, dispersing agent and preservative simultaneously stir 4h at 70 DEG C;(3) by graphite powder, aluminium hydroxide, zirconium dioxide and bentonite are in 500
Calcining 2h is placed on machinery spheroidal graphite 8h in spheroidal graphite tank and obtains premix at DEG C;(4) step (2) are added in premix obtained by step (3)
Reaction kettle at 60 DEG C stir 2h up to digit printing fabric flame-proof antibiotic coating.
Preferably, the revolving speed of the spheroidal graphite is 600r/min, and spheroidal graphite atmosphere is under neon atmosphere.
Embodiment 2
A kind of digit printing fabric flame-proof antibiotic coating, 18 parts of hydroxyethyl cellulose, 14 parts of chlorosulfonated polyethylene, trioctyl phosphate
11 parts, 23 parts of hexamethylene alkylene pentylcyclohexanone, 28 parts of petroleum ether, 8 parts of stearate, 22 parts of sorbierite, 4 parts of hexamethylene, dodecane
16 parts of base sodium sulphate, 23 parts of copper zinc pyrithione, 3 parts of imidazoline, 1000 parts of water, 4 parts of graphite powder, 13 parts of aluminium hydroxide, titanium dioxide
23 parts of zirconium, 13 parts of bentonite, 4 parts of styrax, 4 parts of defoaming agent, 2 parts of dispersing agent, 1.5 parts of preservative.
Preferably, the defoaming agent is BYK057.
Preferably, the dispersing agent is sodium tetrapolyphosphate, and the mixture of calgon and modified siloxane, described four is poly-
The mass ratio of sodium phosphate, calgon and modified siloxane is 1:2:1.
Preferably, the preservative be methylparaben, ethylparaben, propylben and butyl hydroxybenzoate, it is described
Methylparaben, ethylparaben, propylben and butyl hydroxybenzoate mass ratio be 1:4:2:3.
A kind of preparation method of digit printing fabric flame-proof antibiotic coating, (1) is by hydroxyethyl cellulose, the poly- second of chlorosulfonation
Alkene, trioctyl phosphate, hexamethylene alkylene pentylcyclohexanone, petroleum ether, stearate, sorbierite, hexamethylene, lauryl sodium sulfate,
Copper zinc pyrithione, imidazoline and water are placed in reaction kettle, and stir 3h at 55 DEG C;(2) continue that defoaming is added into reaction kettle
Agent, dispersing agent and preservative simultaneously stir 4h at 70 DEG C;(3) by graphite powder, aluminium hydroxide, zirconium dioxide and bentonite are in 500
Calcining 2h is placed on machinery spheroidal graphite 8h in spheroidal graphite tank and obtains premix at DEG C;(4) step (2) are added in premix obtained by step (3)
Reaction kettle at 60 DEG C stir 2h up to digit printing fabric flame-proof antibiotic coating.
Preferably, the revolving speed of the spheroidal graphite is 600r/min, and spheroidal graphite atmosphere is under neon atmosphere.
Embodiment 3
A kind of digit printing fabric flame-proof antibiotic coating, 16 parts of hydroxyethyl cellulose, 12 parts of chlorosulfonated polyethylene, trioctyl phosphate
9 parts, 20 parts of hexamethylene alkylene pentylcyclohexanone, 22 parts of petroleum ether, 6 parts of stearate, 20 parts of sorbierite, 2 parts of hexamethylene, dodecyl
13 parts of sodium sulphate, 20 parts of copper zinc pyrithione, 3 parts of imidazoline, 1000 parts of water, 3 parts of graphite powder, 10 parts of aluminium hydroxide, zirconium dioxide
20 parts, 11 parts of bentonite, 2 parts of styrax, 2 parts of defoaming agent, 2 parts of dispersing agent, 1 part of preservative.
Preferably, the defoaming agent is BYK057.
Preferably, the dispersing agent is sodium tetrapolyphosphate, and the mixture of calgon and modified siloxane, described four is poly-
The mass ratio of sodium phosphate, calgon and modified siloxane is 1:2:1.
Preferably, the preservative be methylparaben, ethylparaben, propylben and butyl hydroxybenzoate, it is described
Methylparaben, ethylparaben, propylben and butyl hydroxybenzoate mass ratio be 1:4:2:3.
A kind of preparation method of digit printing fabric flame-proof antibiotic coating, (1) is by hydroxyethyl cellulose, the poly- second of chlorosulfonation
Alkene, trioctyl phosphate, hexamethylene alkylene pentylcyclohexanone, petroleum ether, stearate, sorbierite, hexamethylene, lauryl sodium sulfate,
Copper zinc pyrithione, imidazoline and water are placed in reaction kettle, and stir 3h at 55 DEG C;(2) continue that defoaming is added into reaction kettle
Agent, dispersing agent and preservative simultaneously stir 4h at 70 DEG C;(3) by graphite powder, aluminium hydroxide, zirconium dioxide and bentonite are in 500
Calcining 2h is placed on machinery spheroidal graphite 8h in spheroidal graphite tank and obtains premix at DEG C;(4) step (2) are added in premix obtained by step (3)
Reaction kettle at 60 DEG C stir 2h up to digit printing fabric flame-proof antibiotic coating.
Preferably, the revolving speed of the spheroidal graphite is 600r/min, and spheroidal graphite atmosphere is under neon atmosphere.
Performance measurement, the data obtained such as following table, fire protection flame retarding accreditation are carried out for embodiment 1-3 and certain commercial product
Using UL94 standard.
As it can be seen that the application has good corrosion-resistant, fire protection flame retarding, anti-mildew and antibacterial performance.
Claims (8)
1. kind of digit printing fabric flame-proof antibiotic coating, which is characterized in that 20 parts of hydroxyethyl cellulose, chlorosulfonated polyethylene 16
Part, 13 parts of trioctyl phosphate, 25 parts of hexamethylene alkylene pentylcyclohexanone, 30 parts of petroleum ether, 10 parts of stearate, 24 parts of sorbierite, ring
6 parts of hexane, 18 parts of lauryl sodium sulfate, 25 parts of copper zinc pyrithione, 5 parts of imidazoline, 1000 parts of water, 5 parts of graphite powder, hydroxide
15 parts of aluminium, 25 parts of zirconium dioxide, 15 parts of bentonite, 5 parts of styrax, 5 parts of defoaming agent, 3 parts of dispersing agent, 2 parts of preservative.
2. a kind of digit printing fabric flame-proof antibiotic coating as described in claim 1, which is characterized in that hydroxyethyl cellulose 18
Part, 14 parts of chlorosulfonated polyethylene, 11 parts of trioctyl phosphate, 23 parts of hexamethylene alkylene pentylcyclohexanone, 28 parts of petroleum ether, stearate 8
Part, 22 parts of sorbierite, 4 parts of hexamethylene, 16 parts of lauryl sodium sulfate, 23 parts of copper zinc pyrithione, 3 parts of imidazoline, 1000 parts of water,
4 parts of graphite powder, 13 parts of aluminium hydroxide, 23 parts of zirconium dioxide, 13 parts of bentonite, 4 parts of styrax, 4 parts of defoaming agent, dispersing agent 2
Part, 1.5 parts of preservative.
3. a kind of digit printing fabric flame-proof antibiotic coating as described in claim 1, which is characterized in that hydroxyethyl cellulose 16
Part, 12 parts of chlorosulfonated polyethylene, 9 parts of trioctyl phosphate, 20 parts of hexamethylene alkylene pentylcyclohexanone, 22 parts of petroleum ether, stearate 6
Part, 20 parts of sorbierite, 2 parts of hexamethylene, 13 parts of lauryl sodium sulfate, 20 parts of copper zinc pyrithione, 3 parts of imidazoline, 1000 parts of water,
3 parts of graphite powder, 10 parts of aluminium hydroxide, 20 parts of zirconium dioxide, 11 parts of bentonite, 2 parts of styrax, 2 parts of defoaming agent, dispersing agent 2
Part, 1 part of preservative.
4. a kind of digit printing fabric flame-proof antibiotic coating as described in claim 1, which is characterized in that the defoaming agent is
BYK057。
5. a kind of digit printing fabric flame-proof antibiotic coating as described in claim 1, which is characterized in that the dispersing agent is four
The mixture of polyphosphate sodium, calgon and modified siloxane, the sodium tetrapolyphosphate, calgon and modified siloxane
Mass ratio be 1:2:1.
6. a kind of digit printing fabric flame-proof antibiotic coating as described in claim 1, which is characterized in that the preservative is Buddhist nun
Moor tortoise beetle ester, ethylparaben, propylben and butyl hydroxybenzoate, the methylparaben, ethylparaben, nipalgin third
The mass ratio of ester and butyl hydroxybenzoate is 1:4:2:3.
7. a kind of preparation method of digit printing fabric flame-proof antibiotic coating as described in claim 1, which is characterized in that (1)
By hydroxyethyl cellulose, chlorosulfonated polyethylene, trioctyl phosphate, hexamethylene alkylene pentylcyclohexanone, petroleum ether, stearate, sorb
Alcohol, hexamethylene, lauryl sodium sulfate, copper zinc pyrithione, imidazoline and water are placed in reaction kettle, and stir 3h at 55 DEG C;
(2) continue that defoaming agent, dispersing agent and preservative are added into reaction kettle and stir 4h at 70 DEG C;(3) by graphite powder, hydroxide
Aluminium, zirconium dioxide and bentonite, which calcine 2h at 500 DEG C and be placed on machinery spheroidal graphite 8h in spheroidal graphite tank, obtains premix;(4) by step
(3) gained premix, which is added in the reaction kettle of step (2) at 60 DEG C, stirs 2h up to digit printing fabric flame-proof antibiotic coating.
8. a kind of preparation method of digit printing fabric flame-proof antibiotic coating as claimed in claim 7, which is characterized in that described
The revolving speed of spheroidal graphite is 600r/min, and spheroidal graphite atmosphere is under neon atmosphere.