CN106220142A - Artificial jade based on granite mine tailing and preparation method thereof - Google Patents

Artificial jade based on granite mine tailing and preparation method thereof Download PDF

Info

Publication number
CN106220142A
CN106220142A CN201610552769.3A CN201610552769A CN106220142A CN 106220142 A CN106220142 A CN 106220142A CN 201610552769 A CN201610552769 A CN 201610552769A CN 106220142 A CN106220142 A CN 106220142A
Authority
CN
China
Prior art keywords
mine tailing
artificial jade
granite mine
granite
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610552769.3A
Other languages
Chinese (zh)
Inventor
黄聿新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenzhen Super Technology Development Co Ltd
Original Assignee
Shenzhen Super Technology Development Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenzhen Super Technology Development Co Ltd filed Critical Shenzhen Super Technology Development Co Ltd
Priority to CN201610552769.3A priority Critical patent/CN106220142A/en
Publication of CN106220142A publication Critical patent/CN106220142A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of artificial jade based on granite mine tailing and preparation method thereof, artificial jade calculates by weight percentage, including following component: granite mine tailing 10 85%, clay 5 20%, aluminium oxide or aluminium hydroxide 5 20%, zirconium oxide 5 15%, Pulvis Talci 2 10%, sodium carbonate 5 15%, titanium dioxide 1 5%, Borax 5 15%, inorganic color 0 10%, each constituent content percent sum is 100%.By weighing each raw material, broken, mixing during preparation.Pressing mold, sinter, cool down, polish, the step such as polishing prepares artificial jade.The artificial jade of the present invention not only environmental protection, and preparation technology is simple, and the artificial jade obtained has high intensity, high tenacity, color is various and the feature of high refractive index, and without Organic substance, be unlikely to deform, the most inflammable, aging resistance hole corrosivity is strong, has great application prospect.

Description

Artificial jade based on granite mine tailing and preparation method thereof
Technical field
The present invention relates to the synthetic field of jade, be specifically related to a kind of artificial jade based on granite mine tailing and Preparation method.
Background technology
Beautiful exquisite quality is tough and tensile, and color and luster is gentle soft, the most very popular, but, natural output Beautiful resource-constrained, and expensive, it is impossible to meet the needs that people are growing, thus people use synthetic technology system Make jade material.Artificial jade's product in the market is most with Organic substance and aluminium hydroxide for raw material manufacture, and it is in outward appearance And far away from natural jade in performance, and the most aging, yielding, the most fire-resistant.
Summary of the invention
For overcoming above-mentioned technical problem, it is an object of the invention to provide a kind of have high intensity, high tenacity based on Artificial jade of granite mine tailing and preparation method thereof.
The technical scheme used is:
A kind of artificial jade based on granite mine tailing, calculates, by weight percentage including following component:
Granite mine tailing 10-85%, clay 5-20%, aluminium oxide or aluminium hydroxide 5-20%, zirconium oxide 5-15%, Talcum Powder 2-10%, sodium carbonate 5-15%, titanium dioxide 1-5%, Borax 5-15%, inorganic color 0-10%, each constituent content percentage Number sum is 100%.
Preferably, calculate by weight percentage, including following component:
Granite mine tailing 40-60%, clay 5-20%, aluminium oxide or aluminium hydroxide 5-20%, zirconium oxide 5-15%, Talcum Powder 2-10%, sodium carbonate 5-15%, titanium dioxide 1-5%, Borax 5-15%, inorganic color 0-10%.
Preferably, calculate by weight percentage, including following component:
Granite mine tailing 45-55%, clay 5-10%, aluminium oxide or aluminium hydroxide 5-10%, zirconium oxide 5-10%, Talcum Powder 2-8%, sodium carbonate 5-10%, titanium dioxide 1-5%, Borax 5-10%, inorganic color 0-10%.
Described inorganic color such as ferrum oxide, zinc yellow or white carbon black etc., select to add according to actual needs.
The preparation method of the artificial jade based on granite mine tailing of the present invention, comprises the steps:
(1) press the formula of artificial jade based on granite mine tailing in such scheme, weigh various raw material；
(2) sieve broken for various raw materials；
(3) various raw materials are put into mix homogeneously in stirring container；
(4) material being stirred is passed through molding press pressing mold molding, obtain base substrate；
(5) base substrate is at room temperature put into sintering furnace, be warming up to 900-1500 DEG C with stove, be incubated 1-3h；
(6) product cools to room temperature with the furnace, takes out from stove, through polishing, polishing, finally gives artificial jade.
Preferably, in step (5), it is incubated 2h.
The beneficial effects of the present invention is:
The present invention utilize granite mine tailing for primary raw material, not only environmental protection, and preparation technology is simple, the people obtained Make jade and there is high intensity, high tenacity, color is various and the feature of high refractive index, and without Organic substance, be unlikely to deform, The most inflammable, aging resistance hole corrosivity is strong, has great application prospect.
The bulk density of the artificial jade of the present invention is 300-1500Kg/m3, comprcssive strength >=5MPa, rupture strength >= 3MPa。
Detailed description of the invention
Below by specific embodiment, the present invention is described in detail, but the purposes of these exemplary embodiments and Purpose is only used for enumerating the present invention, and not the real protection scope to the present invention constitutes any type of any restriction, more non-general Protection scope of the present invention is confined to this.
It addition, unless stated otherwise, below percentage ratio used by component be all weight percentage.
Embodiment 1
A kind of artificial jade based on granite mine tailing, including following component:
Granite mine tailing 40%, clay 10%, aluminium oxide or aluminium hydroxide 10%, zirconium oxide 10%, Pulvis Talci 6%, carbon Acid sodium 10%, titanium dioxide 4%, Borax 10%.
Preparation method is as follows:
(1) press the formula of artificial jade based on granite mine tailing in such scheme, weigh various raw material；
(2) sieve broken for various raw materials；
(3) various raw materials are put into mix homogeneously in stirring container；
(4) material being stirred is passed through molding press pressing mold molding, obtain base substrate；
(5) base substrate is at room temperature put into sintering furnace, be warming up to 900-1500 DEG C with stove, be incubated 2h；
(6) product cools to room temperature with the furnace, takes out from stove, through polishing, polishing, finally gives artificial jade.
Embodiment 2
A kind of artificial jade based on granite mine tailing, including following component:
Granite mine tailing 45%, clay 10%, aluminium oxide or aluminium hydroxide 5%, zirconium oxide 10%, Pulvis Talci 5%, carbonic acid Sodium 10%, titanium dioxide 5%, Borax 5%, inorganic color 5%.
Preparation method is with reference to embodiment 1.
Embodiment 3
A kind of artificial jade based on granite mine tailing, including following component:
Granite mine tailing 50%, clay 10%, aluminium oxide or aluminium hydroxide 5%, zirconium oxide 5%, Pulvis Talci 7%, carbonic acid Sodium 5%, titanium dioxide 3%, Borax 10%, inorganic color 5%.
Preparation method is with reference to embodiment 1.
Embodiment 4
A kind of artificial jade based on granite mine tailing, including following component:
Granite mine tailing 60%, clay 5%, aluminium oxide or aluminium hydroxide 5%, zirconium oxide 5%, Pulvis Talci 8%, sodium carbonate 5%, titanium dioxide 2%, Borax 5%, inorganic color 5%.
Preparation method is with reference to embodiment 1.
The artificial jade that embodiment 1-embodiment 4 prepares being tested, test result sees table 1 below.
Table 1
Should be appreciated that the purposes of these embodiments is merely to illustrate the present invention and is not intended to limit the protection model of the present invention Enclose.Additionally, it will also be appreciated that after the technology contents having read the present invention, the present invention can be made respectively by those skilled in the art Planting change, amendment and/or modification, all these equivalent form of value falls within the guarantor that the application appended claims is limited equally Within the scope of protecting.

Claims (5)

1. an artificial jade based on granite mine tailing, it is characterised in that calculate by weight percentage, including following component:
Granite mine tailing 10-85%, clay 5-20%, aluminium oxide or aluminium hydroxide 5-20%, zirconium oxide 5-15%, Pulvis Talci 2- 10%, sodium carbonate 5-15%, titanium dioxide 1-5%, Borax 5-15%, inorganic color 0-10%, each constituent content percent it With for 100%.
Artificial jade based on granite mine tailing the most according to claim 1, it is characterised in that calculate by weight percentage, Including following component:
Granite mine tailing 40-60%, clay 5-20%, aluminium oxide or aluminium hydroxide 5-20%, zirconium oxide 5-15%, Pulvis Talci 2- 10%, sodium carbonate 5-15%, titanium dioxide 1-5%, Borax 5-15%, inorganic color 0-10%.
Artificial jade based on granite mine tailing the most according to claim 1, it is characterised in that calculate by weight percentage, Including following component:
Granite mine tailing 45-55%, clay 5-10%, aluminium oxide or aluminium hydroxide 5-10%, zirconium oxide 5-10%, Pulvis Talci 2- 8%, sodium carbonate 5-10%, titanium dioxide 1-5%, Borax 5-10%, inorganic color 0-10%.
4. the preparation method of an artificial jade based on granite mine tailing, it is characterised in that comprise the steps:
(1) by the formula of the arbitrary described artificial jade based on granite mine tailing of claim 1-3, various raw material is weighed；
(2) sieve broken for various raw materials；
(3) various raw materials are put into mix homogeneously in stirring container；
(4) material being stirred is passed through molding press pressing mold molding, obtain base substrate；
(5) base substrate is at room temperature put into sintering furnace, be warming up to 900-1500 DEG C with stove, be incubated 1-3h；
(6) product cools to room temperature with the furnace, takes out from stove, through polishing, polishing, finally gives artificial jade.
The preparation method of artificial jade based on granite mine tailing the most according to claim 4, it is characterised in that
In step (5), it is incubated 2h.
CN201610552769.3A 2016-07-13 2016-07-13 Artificial jade based on granite mine tailing and preparation method thereof Pending CN106220142A (en)