CN109553974A - Improved organic silicon-type composite flame-retardant agent - Google Patents
Improved organic silicon-type composite flame-retardant agent Download PDFInfo
- Publication number
- CN109553974A CN109553974A CN201710877615.6A CN201710877615A CN109553974A CN 109553974 A CN109553974 A CN 109553974A CN 201710877615 A CN201710877615 A CN 201710877615A CN 109553974 A CN109553974 A CN 109553974A
- Authority
- CN
- China
- Prior art keywords
- parts
- type composite
- organic silicon
- composite flame
- improved organic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of improved organic silicon-type composite flame-retardant agents, according to parts by weight, it includes 44-65 parts of dimethyl silicone polymer, 37-42 parts of silicon ester resin, 22-29 parts of stearate, 16-20 parts of zinc borate, 11-16 parts of calcium carbonate, 5-9 parts of aluminium hydroxide, 2-4 parts of silica, 1-2 parts of antimony oxide.Easy processing of the present invention, good flame retardation effect.
Description
Technical field
The invention belongs to chemical products fields, and in particular to a kind of composite flame-retardant agent.
Background technique
With the development of Macromolecular materials industry, plastics are applied to the every field of production and life more and more extensively.
At the same time, the fire due to caused by the combustibility of plastics has also led to heavy casualties to people and has caused huge
Economic loss, some industrially developed country start to produce and using flame retardant plastics.With electric appliance, electronics, machinery, automobile, ship
The development of oceangoing ship, aerospace, it is also higher and higher to the flame-retardancy requirements of product material, be fire retardant and fire proofing development,
Production and popularization and application are rapidly developed.Due to the expansion of fire proofing application field and the demand of environment for human survival, nothing
Halogen, low cigarette, less toxic new flame retardant are the developing direction of the following fire retardant.
Summary of the invention
Goal of the invention: purpose of the invention is to overcome the shortcomings in the prior art, provides a kind of easy processing, fire-retardant effect
The good improved organic silicon-type composite flame-retardant agent of fruit.
Technical solution: in order to solve the above-mentioned technical problem, improved organic silicon-type composite flame-retardant agent of the present invention is pressed
Parts by weight meter, it includes following components,
(1) dimethyl silicone polymer 44-65 parts;
(2) silicon ester resin 37-42 parts;
(3) stearate 22-29 parts;
(4) zinc borate 16-20 parts;
(5) calcium carbonate 11-16 parts;
(6) aluminium hydroxide 5-9 parts;
(7) silica 2-4 parts;
(8) antimony oxide 1-2 parts.
Preferably, the improved organic silicon-type composite flame-retardant agent, according to parts by weight, it includes following components,
(1) 58 parts of dimethyl silicone polymer;
(2) 38 parts of silicon ester resin;
(3) 26 parts of stearate;
(4) 19 parts of zinc borate;
(5) 13 parts of calcium carbonate;
(6) 7 parts of aluminium hydroxide;
(7) 3 parts of silica;
(8) 1.2 parts of antimony oxide.
The utility model has the advantages that compared with prior art, the present invention its remarkable advantage is: the present invention passes through accurate component proportion,
Each component interpenetrates, and makes product good flame retardation effect, and this product stability is good, and easy processing meets actual operation requirements.
Specific embodiment
Below with reference to embodiment, the present invention is further illustrated.
Improved organic silicon-type composite flame-retardant agent of the present invention, according to parts by weight, it includes following components,
(1) 60 parts of dimethyl silicone polymer;
(2) 38 parts of silicon ester resin;
(3) 23 parts of stearate;
(4) 17 parts of zinc borate;
(5) 12 parts of calcium carbonate;
(6) 6 parts of aluminium hydroxide;
(7) 2.4 parts of silica;
(8) 1.6 parts of antimony oxide.
The present invention is interpenetrated by accurate component proportion, each component, makes product good flame retardation effect, this product stability
Good, easy processing meets actual operation requirements.
The present invention provides a kind of thinking and methods, and there are many method and the approach for implementing the technical solution, the above institute
Stating is only the preferred embodiment of the present invention, it is noted that for those skilled in the art, is not being departed from
Under the premise of the principle of the invention, several improvements and modifications can also be made, these improvements and modifications also should be regarded as guarantor of the invention
Range is protected, all undefined components in this embodiment can be implemented in the prior art.
Claims (2)
1. improved organic silicon-type composite flame-retardant agent, it is characterised in that: according to parts by weight, it includes following components,
(1) dimethyl silicone polymer 44-65 parts;
(2) silicon ester resin 37-42 parts;
(3) stearate 22-29 parts;
(4) zinc borate 16-20 parts;
(5) calcium carbonate 11-16 parts;
(6) aluminium hydroxide 5-9 parts;
(7) silica 2-4 parts;
(8) antimony oxide 1-2 parts.
2. improved organic silicon-type composite flame-retardant agent according to claim 1, it is characterised in that: according to parts by weight, it
Including following components,
(1) 58 parts of dimethyl silicone polymer;
(2) 38 parts of silicon ester resin;
(3) 26 parts of stearate;
(4) 19 parts of zinc borate;
(5) 13 parts of calcium carbonate;
(6) 7 parts of aluminium hydroxide;
(7) 3 parts of silica;
(8) 1.2 parts of antimony oxide.