CN109535945A - A kind of open air salt spray resistance powdery paints - Google Patents
A kind of open air salt spray resistance powdery paints Download PDFInfo
- Publication number
- CN109535945A CN109535945A CN201811572055.4A CN201811572055A CN109535945A CN 109535945 A CN109535945 A CN 109535945A CN 201811572055 A CN201811572055 A CN 201811572055A CN 109535945 A CN109535945 A CN 109535945A
- Authority
- CN
- China
- Prior art keywords
- polyaniline
- salt spray
- spray resistance
- coating
- powdery paints
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of outdoor salt spray resistance powdery paints, are made of the component of following mass percent: polyester resin 56-65%, hydroxy alkyl amide curing agents 3-3.5%, smooth degasifier 1-1.5%, levelling agent 1-1.5%, polyaniline 1-5%, pigments and fillers 23.5-38%.Contain a certain amount of polyaniline in powder coating formulation prepared by the present invention, in acid condition, anodic oxidation reactions occur, form surface passivation layer, even if corrosive deposit immerses, passivation layer can be used as the second barrier, also the generation of corrosion can be hindered, it ensure that the salt spray resistance of coating, simultaneously using polyester resin as matrix resin in dope preparing process, due to polyester resin wetability with higher, it can sufficiently be mixed with polyaniline, so that polyaniline is evenly dispersed in coating, a small amount of polyaniline, which is added, can be realized coating salt spray resistance, and it does not pollute the environment.
Description
Technical field
The invention belongs to coating preparation fields, are related to a kind of outdoor salt spray resistance powdery paints.
Background technique
In coating spraying process organic solvent volatilization be always air pollution one of main source, especially at present I
The haze weather that state various regions frequently occur even more proposes a urgent demand to coating industry.Relative to liquid coating
Speech, powdery paints do not use solvent, solvent-free volatilization in application process, and high, the easy to operate, productivity with recovery utilization rate
It the advantages that height, coating fast drying, therefore, is widely adopted in fields such as automobile, household electrical appliance, machinery, building, ships, to replace
For liquid coating.
Currently, the coating that the powdery paints of common HAA powder coating formulation is formed, has many advantages, such as nontoxic, good weatherability,
But when use environment slightly becomes more harsh, for example, being exposed under corrosive environment for a long time than high temperature and humidity, such as acid
Rain, haze, coastal climate etc. can all be obviously shortened the useful life time of coating, accelerate coating corrosion failure, appearance and performance
It runs down, is generallyd use in existing dope preparing process and directly add polyphenyl amine hardener in epoxy resin, realize coating
Salt spray resistance, but the mobility of epoxy resin is smaller, be easy to cause dispersing polyaniline uneven in mixed process, and
And the coating thermal stability of preparation is lower, and pollution environment is easy when polyaniline additional amount is larger.
Summary of the invention
The purpose of the present invention is to provide a kind of outdoor salt spray resistance powdery paints, contain in the powder coating formulation a certain amount of
Polyaniline, in acid condition, occur anodic oxidation reactions, formed surface passivation layer, even if corrosive deposit immerse, passivation layer
It can be used as the second barrier, the generation of corrosion can be also hindered, ensure that the salt spray resistance of coating, while in dope preparing process
It using polyester resin as matrix resin, due to polyester resin wetability with higher, can sufficiently be mixed with polyaniline, so that poly-
Aniline is evenly dispersed in coating, and a small amount of polyaniline, which is added, can be realized coating salt spray resistance, and not pollute the environment.
The purpose of the present invention can be achieved through the following technical solutions:
A kind of open air salt spray resistance powdery paints, is made of the component of following mass percent:
Preferably, the polyester resin acid value is 28-32mgKOH/g;
Preferably, the smooth degasifier is synthesis microwax;
Preferably, the levelling agent is acrylate copolymer;
Preferably, the polyaniline is conductive state, conductivity is greater than 2S/cm, and partial size is less than 30 μm.
Beneficial effects of the present invention:
Contain a certain amount of polyaniline in powder coating formulation of the present invention, in acid condition, anodic oxidation reactions occur,
Surface passivation layer is formed, even if corrosive deposit immerses, passivation layer can be used as the second barrier, can also hinder the generation of corrosion, guarantee
The salt spray resistance of coating, while using polyester resin as matrix resin in dope preparing process, since polyester resin has
Higher wetability can be mixed sufficiently with polyaniline, so that polyaniline is evenly dispersed in coating, a small amount of polyaniline is added
Coating salt spray resistance can be realized, and do not pollute the environment.
Powdery paints of the present invention using safety, low toxicity beta-hydroxy alkylamide as curing agent, therefore have it is safe,
The features such as environmentally friendly.
Specific embodiment
Embodiment 1
A kind of open air salt spray resistance powdery paints, including following components by weight percent raw material:
Polyester resin 56%
Hydroxy alkyl amide curing agents 3%
Smooth degasifier 1%
Levelling agent 1%
Polyaniline 1%
Filler 25%
Pigment 13%
Polyester resin: Anhui Shenjian New Material Co., Ltd. SJ5122;
Beta-hydroxy alkylamide: the prompt sensible new material Co., Ltd SA3120 of six peaces;
Smooth degasifier: the prompt sensible new material Co., Ltd SA500 of six peaces;
Levelling agent: the PV88 of German moral letter benefit chemistry;
Polyaniline: Jiaxing Nan Jian biomaterial Co., Ltd product;
Blanc fixe: the blanc fixe of Shaanxi enrichment chemical industry Co., Ltd;
Titanium dioxide: Jiangsu Zhentai Chemical Industry Co., Ltd. ZR940+;
Raw material are put into together according to aforementioned proportion carry out being pre-mixed in compounding jar → extruder extrusion → tabletting →
Crushing → sieving → finished product.
Comparative example 1
The preparation process of the present embodiment is with embodiment 1, the difference is that not adding polyaniline in formula.
Embodiment 2
A kind of open air salt spray resistance powdery paints, including following components by weight percent raw material:
Polyester resin 60%
Hydroxy alkyl amide curing agents 3.3%
Smooth degasifier 1.3%
Levelling agent 1.3%
Polyaniline 3%
Filler 20%
Pigment 11.1%
Polyester resin: Anhui Shenjian New Material Co., Ltd. SJ5122;
Beta-hydroxy alkylamide: the prompt sensible new material Co., Ltd SA3120 of six peaces;
Smooth degasifier: the prompt sensible new material Co., Ltd SA500 of six peaces;
Levelling agent: the PV88 of German moral letter benefit chemistry;
Polyaniline: Jiaxing Nan Jian biomaterial Co., Ltd product;
Blanc fixe: the blanc fixe of Shaanxi enrichment chemical industry Co., Ltd;
Titanium dioxide: Jiangsu Zhentai Chemical Industry Co., Ltd. ZR940+;
Raw material are put into together according to aforementioned proportion carry out being pre-mixed in compounding jar → extruder extrusion → tabletting →
Crushing → sieving → finished product.
Comparative example 2
The preparation process of the present embodiment is with embodiment 2, the difference is that not adding polyaniline in formula.
Embodiment 3
A kind of open air salt spray resistance powdery paints, including following components by weight percent raw material:
Polyester resin 65%
Hydroxy alkyl amide curing agents 3.5%
Smooth degasifier 1.5%
Levelling agent 1.5%
Polyaniline 5%
Filler 15%
Pigment 8.5%
Polyester resin: Anhui Shenjian New Material Co., Ltd. SJ5122;
Beta-hydroxy alkylamide: the prompt sensible new material Co., Ltd SA3120 of six peaces;
Smooth degasifier: the prompt sensible new material Co., Ltd SA500 of six peaces;
Levelling agent: the PV88 of German moral letter benefit chemistry;
Polyaniline: Jiaxing Nan Jian biomaterial Co., Ltd product;
Blanc fixe: the blanc fixe of Shaanxi enrichment chemical industry Co., Ltd;
Titanium dioxide: Jiangsu Zhentai Chemical Industry Co., Ltd. ZR940+;
Raw material are put into together according to aforementioned proportion carry out being pre-mixed in compounding jar → extruder extrusion → tabletting →
Crushing → sieving → finished product.
Comparative example 3
The preparation process of the present embodiment is with embodiment 3, the difference is that not adding polyaniline in formula.
The method that finished product obtained by 1-3 grades of comparative example 1-3 of above-described embodiment is electrostatically sprayed is sprayed on stainless steel respectively
On plate, toasted 10 minutes at 200 DEG C, finally obtaining dried film thickness is 90um, the performance test of film is carried out to each formula respectively,
The various performance indicators of film obtained by above-described embodiment and comparative example are tested, test result is as shown in table 1:
Table 1: the various performance indicators of film obtained by embodiment 1-3 and comparative example 1-3
As shown in Table 1, the coating is using polyester resin as matrix resin, have after being solidified by hydroxy alkyl amide curing agents compared with
High impact resistant strength and hardness, and its glossiness reaches 90 or more.
Salt spray corrosion resistance measurement:
According to national standards the measurement of the resistance to neutral salt spray performance of GB/T 1771-2007 paint and varnish to embodiment 1-3 and
Comparative example 1-3 carries out the measurement of salt spray corrosion resistance, minute 250 hours, intersects scratch, away from edge 20mm, knot
Fruit is as shown in table 2:
Table 2: resisting salt fog corrosion experimental result
As shown in Table 2, after directly adding polyaniline in coating, the coating of preparation without discoloration, without blistering, without fall off, nothing
Therefore situations such as getting rusty directly adds a small amount of polyaniline, so that coating salt spray resistance with higher, and coating
Intensity, glossiness and impact resistance do not reduce.
Present invention disclosed above preferred embodiment is only intended to help to illustrate the present invention.There is no detailed for preferred embodiment
All details are described, are not limited the invention to the specific embodiments described.Obviously, according to the content of this specification,
It can make many modifications and variations.These embodiments are chosen and specifically described to this specification, is in order to better explain the present invention
Principle and practical application, so that skilled artisan be enable to better understand and utilize the present invention.The present invention is only
It is limited by claims and its full scope and equivalent.
Claims (5)
1. a kind of open air salt spray resistance powdery paints, which is characterized in that be made of the component of following mass percent:
2. a kind of outdoor salt spray resistance powdery paints according to claim 1, which is characterized in that the polyester resin acid value
For 28-32mgKOH/g.
3. a kind of outdoor salt spray resistance powdery paints according to claim 1, which is characterized in that the smooth degasifier is to close
At microwax.
4. a kind of outdoor salt spray resistance powdery paints according to claim 1, which is characterized in that the levelling agent is acrylic acid
Ester copolymer.
5. a kind of outdoor salt spray resistance powdery paints according to claim 1, which is characterized in that the polyaniline is conduction
State, conductivity are greater than 2S/cm, and partial size is less than 30 μm.