CN109505116A - A kind of production method of medical cotton ball - Google Patents
A kind of production method of medical cotton ball Download PDFInfo
- Publication number
- CN109505116A CN109505116A CN201811320544.0A CN201811320544A CN109505116A CN 109505116 A CN109505116 A CN 109505116A CN 201811320544 A CN201811320544 A CN 201811320544A CN 109505116 A CN109505116 A CN 109505116A
- Authority
- CN
- China
- Prior art keywords
- cotton
- production method
- medical
- completion
- thimerosal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production method of medical cotton ball, production method steps are as follows: a. selects first-class rayon balls first, then carries out weighing its weight, the thimerosal prepared is then selected to be measured again；B. after the completion of step a, then weighed rayon balls and the thimerosal that has measured is put into container and impregnated, needs carry out under sterile environment when immersion；C. after the completion of step b, then soaked cotton balls is put under ultraviolet light the sterilization that carries out disinfection, its 2-3 cotton balls is then taken to be detected again；D. the cotton balls that will test qualification again, which is encased in bottle, is sealed preservation.The present invention effectively removes ash content, protein, organic matter and impurity in medical cotton ball, both medical cotton ball quality had been can guarantee, it can guarantee that noresidue or residue index comply with standard in medical cotton ball again, improve safety when patient uses, and the medical cotton ball sterilization effect is good, to human body be not easy allergy and to skin it is non-stimulated.
Description
Technical field
The present invention relates to medical cotton ball technical field, specially a kind of production method of medical cotton ball.
Background technique
Medical cotton ball is to draw medicinal alcohol by the rayon balls of sterilized processing to be made, and has and disappears to human skin
Poison prevents the effect of infecting.People are by test repeatedly, and the alcohol sterilizing power for learning that concentration is 75% is most strong, so medical
Ethanol for disinfection is typically all to contain 75% absolute alcohol and 25% water.
Existing medical cotton ball is usually medicining liquid dipping rayon balls, medical by intensified glutaraldehyde, antirust agent, buffer
It is dehydrated after being impregnated in medical fluid made of distilled water configuration and cotton swab immerses the tincture of iodine, the method for alcohol is made.It is impregnated in the tincture of iodine
Medical cotton ball obtained is because idodine has stronger irritation to human skin, therefore, clinically general again with alcoholic
Cotton balls carries out second and wipes, to dilute the iodine number on skin, normally referred to as de- iodine, to reduce stimulation of the iodine to human skin
Effect, but since iodide ion is extremely active, oxidability is strong, distils quickly after meeting light, meets other materials, and it is heavy also easily to generate
It forms sediment, after being especially formed into cotton balls, the effect tool of sterilizing significantly decreases, and can contain in existing medical cotton ball
A small amount of impurity reduces safety when patient uses, and sterilization effect is more general, is easy easy allergy and right to human body
Skin can generate stimulation.
Summary of the invention
The purpose of the present invention is to provide a kind of production methods of medical cotton ball, solve and ask proposed in background technique
Topic.
To achieve the above object, the invention provides the following technical scheme: a kind of production method of medical cotton ball, production method
Steps are as follows:
A. first-class rayon balls is selected first, is then carried out weighing its weight, is then selected the thimerosal prepared again
It is measured；
B. after the completion of step a, then weighed rayon balls is put into container with the thimerosal measured and is carried out
It impregnates, needs when immersion to carry out under sterile environment；
C. after the completion of step b, then soaked cotton balls is put under ultraviolet light the sterilization that carries out disinfection, then takes it again
2-3 cotton balls are detected；
D. after the completion of step c, then it will test qualified cotton balls and be encased in bottle and be sealed preservation.
As a kind of preferred embodiment of the invention, the step a rayon balls is needed when weighing with high-precision electricity
Sub- scale is weighed, and the thimerosal needs to measure using the graduated cylinder of 100mL when measuring.
As a kind of preferred embodiment of the invention, the proportion of rayon balls and thimerosal is 1:10 in the step b,
The time of immersion is 60-80min.
As a kind of preferred embodiment of the invention, rayon balls preparation step is as follows in the step a:
S1. first the cotton piece for taking out ash content, protein, organic matter and fat is put into bleaching medical fluid, is removed in cotton piece
Pigment, whiteness needed for reaching product；
S2. after the completion of step S1, then by the cotton piece after bleaching be placed in concentration be 85% the concentrated sulfuric acid in, remove cotton
Piece remaining alkaline matter when processing；
S3. after the completion of step S2, then by the cotton piece after neutralization be placed in concentration be 15% dilute sulfuric acid in, remove cotton
Impurity in piece；
S4. after the completion of step S3, then to cotton piece into cleaning, and the moisture in cotton piece is dried；
S5. after the completion of step S4, then the cotton piece to complete is cut into small pieces later and is packed, complete degreasing
The production of cotton.
As a kind of preferred embodiment of the invention, cotton piece is placed in bleaching medical fluid in the step S2, will be floated
Baiyao liquid is warming up to 120 DEG C~140 DEG C, and keeps the temperature 30min~40min, and cotton piece, which is placed in after the concentrated sulfuric acid, will heat up to 70 DEG C
~80 DEG C, and keep the temperature 10min~20min.
As a kind of preferred embodiment of the invention, 60 are warming up to after cotton piece is placed in dilute sulfuric acid in the step S3
DEG C, and keep the temperature 10min~20min.
As a kind of preferred embodiment of the invention, the preparation step of the thimerosal is as follows:
K1. raw material is chosen first；
K2. then the raw material chosen is put into blender again and is stirred, temperature when stirring is 20 DEG C~30
DEG C, the time of stirring is 10min~15min；
K3. the thimerosal of preparation is put into container again seal it is spare.
As a kind of preferred embodiment of the invention, the raw material of the step K1 be respectively basic thimerosal, sterile water,
Fresh water pearl powder, neopelex and potassium iodide.
Compared with prior art, beneficial effects of the present invention are as follows:
The present invention effectively removes ash content, protein, organic matter and impurity in medical cotton ball, both can guarantee medical cotton ball
Quality, and can guarantee that noresidue or residue index comply with standard in medical cotton ball, improve safety when patient uses
Property, and the medical cotton ball sterilization effect is good, to human body be not easy allergy and to skin it is non-stimulated.
Detailed description of the invention
Upon reading the detailed description of non-limiting embodiments with reference to the following drawings, other feature of the invention,
Objects and advantages will become more apparent upon:
Fig. 1 is a kind of flow chart of the production method of medical cotton ball of the present invention.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.
Referring to Fig. 1, the present invention provides a kind of technical solution: a kind of production method of medical cotton ball, production method steps
It is as follows:
A. first-class rayon balls is selected first, is then carried out weighing its weight, is then selected the thimerosal prepared again
It is measured；
B. after the completion of step a, then weighed rayon balls is put into container with the thimerosal measured and is carried out
It impregnates, needs when immersion to carry out under sterile environment；
C. after the completion of step b, then soaked cotton balls is put under ultraviolet light the sterilization that carries out disinfection, then takes it again
2-3 cotton balls are detected；
D. after the completion of step c, then it will test qualified cotton balls and be encased in bottle and be sealed preservation.
Further, it needs to be weighed with high-precision electronic scale when the step a rayon balls weighs, the thimerosal
It needs to measure using the graduated cylinder of 100mL when measurement.
Further, the proportion of rayon balls and thimerosal is 1:10 in the step b, and the time of immersion is 60-80min.
Further, rayon balls preparation step is as follows in the step a:
S1. first the cotton piece for taking out ash content, protein, organic matter and fat is put into bleaching medical fluid, is removed in cotton piece
Pigment, whiteness needed for reaching product；
S2. after the completion of step S1, then by the cotton piece after bleaching be placed in concentration be 85% the concentrated sulfuric acid in, remove cotton
Piece remaining alkaline matter when processing；
S3. after the completion of step S2, then by the cotton piece after neutralization be placed in concentration be 15% dilute sulfuric acid in, remove cotton
Impurity in piece；
S4. after the completion of step S3, then to cotton piece into cleaning, and the moisture in cotton piece is dried；
S5. after the completion of step S4, then the cotton piece to complete is cut into small pieces later and is packed, complete degreasing
The production of cotton.
Further, cotton piece is placed in bleaching medical fluid in the step S2, bleaching medical fluid is warming up to 120 DEG C~140
DEG C, and keep the temperature 30min~40min, cotton piece, which is placed in after the concentrated sulfuric acid, will heat up to 70 DEG C~80 DEG C, and keep the temperature 10min~
20min。
Further, cotton piece is placed in after dilute sulfuric acid in the step S3 and is warming up to 60 DEG C, and keep the temperature 10min~20min.
Further, the preparation step of the thimerosal is as follows:
K1. raw material is chosen first；
K2. then the raw material chosen is put into blender again and is stirred, temperature when stirring is 20 DEG C~30
DEG C, the time of stirring is 10min~15min；
K3. the thimerosal of preparation is put into container again seal it is spare.
Further, the raw material of the step K1 is basic thimerosal, sterile water, fresh water pearl powder, detergent alkylate respectively
Sodium sulfonate and potassium iodide.
In conclusion the present invention effectively removes ash content, protein, organic matter and impurity in medical cotton ball, Ji Nengbao
Medical cotton ball quality is demonstrate,proved, and can guarantee that noresidue or residue index comply with standard in medical cotton ball, improving patient makes
The safety of used time, and the medical cotton ball sterilization effect is good, to human body be not easy allergy and to skin it is non-stimulated.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention, for this field skill
For art personnel, it is clear that invention is not limited to the details of the above exemplary embodiments, and without departing substantially from spirit of the invention or
In the case where essential characteristic, the present invention can be realized in other specific forms.Therefore, in all respects, should all incite somebody to action
Embodiment regards exemplary as, and is non-limiting, the scope of the present invention by appended claims rather than on state
Bright restriction, it is intended that including all changes that fall within the meaning and scope of the equivalent elements of the claims in the present invention
It is interior.Any reference signs in the claims should not be construed as limiting the involved claims.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (8)
1. a kind of production method of medical cotton ball, it is characterised in that: production method steps are as follows:
A. first-class rayon balls is selected first, then carries out weighing its weight, and the thimerosal prepared is then selected to carry out again
It measures；
B. after the completion of step a, then weighed rayon balls is put into container with the thimerosal measured and is impregnated,
It needs to carry out under sterile environment when immersion；
C. after the completion of step b, then soaked cotton balls is put under ultraviolet light the sterilization that carries out disinfection, then take again its 2-3
A cotton balls is detected；
D. after the completion of step c, then it will test qualified cotton balls and be encased in bottle and be sealed preservation.
2. a kind of production method of medical cotton ball according to claim 1, it is characterised in that: the step a rayon balls
It needs to be weighed with high-precision electronic scale when weighing, the thimerosal needs to be surveyed using the graduated cylinder of 100mL when measuring
Amount.
3. a kind of production method of medical cotton ball according to claim 1, it is characterised in that: absorbent cotton in the step b
The proportion of ball and thimerosal is 1:10, and the time of immersion is 60-80min.
4. a kind of production method of medical cotton ball according to claim 1, it is characterised in that: absorbent cotton in the step a
Ball preparation step is as follows:
S1. first the cotton piece for taking out ash content, protein, organic matter and fat is put into bleaching medical fluid, removes the color in cotton piece
Element, whiteness needed for reaching product；
S2. after the completion of step S1, then the cotton piece after bleaching is placed in concentration and is added in 85% concentrated sulfuric acid, to remove cotton piece
Working hour remaining alkaline matter；
S3. after the completion of step S2, then by the cotton piece after neutralization be placed in concentration be 15% dilute sulfuric acid in, remove cotton piece in
Impurity；
S4. after the completion of step S3, then to cotton piece into cleaning, and the moisture in cotton piece is dried；
S5. after the completion of step S4, then the cotton piece to complete is cut into small pieces later and is packed, complete absorbent cotton
Production.
5. a kind of production method of medical cotton ball according to claim 4, it is characterised in that: by cotton piece in the step S2
It is placed in bleaching medical fluid, bleaching medical fluid is warming up to 120 DEG C~140 DEG C, and keep the temperature 30min~40min, cotton piece is placed in
It is will heat up after the concentrated sulfuric acid to 70 DEG C~80 DEG C, and keeps the temperature 10min~20min.
6. a kind of production method of medical cotton ball according to claim 4, it is characterised in that: by cotton piece in the step S3
60 DEG C are warming up to after being placed in dilute sulfuric acid, and keeps the temperature 10min~20min.
7. a kind of production method of medical cotton ball according to claim 1, it is characterised in that: the preparation of the thimerosal walks
It is rapid as follows:
K1. raw material is chosen first；
K2. then the raw material chosen is put into blender again and is stirred, temperature when stirring is 20 DEG C~30 DEG C, is stirred
The time mixed is 10min~15min；
K3. the thimerosal of preparation is put into container again seal it is spare.
8. a kind of production method of medical cotton ball according to claim 7, it is characterised in that: the raw material of the step K1 point
It Wei not basic thimerosal, sterile water, fresh water pearl powder, neopelex and potassium iodide.