CN109503105A - A kind of carbonaceous activity environment-friendly materials - Google Patents
A kind of carbonaceous activity environment-friendly materials Download PDFInfo
- Publication number
- CN109503105A CN109503105A CN201811582625.8A CN201811582625A CN109503105A CN 109503105 A CN109503105 A CN 109503105A CN 201811582625 A CN201811582625 A CN 201811582625A CN 109503105 A CN109503105 A CN 109503105A
- Authority
- CN
- China
- Prior art keywords
- parts
- carbonaceous
- friendly materials
- environment
- porous material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the preparation technical fields of building environment-friendly materials, and in particular to a kind of carbonaceous activity environment-friendly materials；Raw material including following parts by weight: 120-160 parts of carbonaceous porous material, 30-60 parts of diatomite, 20-40 parts of sepiolite, 5-10 parts of mica powder, 15-18 parts of magnesia, 10-15 parts of nano-titanium dioxide, 30-50 parts of epoxy resin, 25-30 parts of acrylate, 16-20 parts of wood fibre, 12-16 parts of ceramic fibre and 40-60 parts of waterglass；The present invention provides a kind of carbonaceous activity environment-friendly materials, environment-friendly materials of the invention, can thermal insulation property to carbonaceous activity environment-friendly materials and absorption property carry out different degrees of promotion, have wide range of applications；And simple production process of the present invention, controllable easy to operate, with good economic efficiency and application value, while consuming energy that relatively low, product stability is good, environmentally protective, at low cost, convenient and safety when using.
Description
Technical field
The present invention relates to the preparation technical fields of building environment-friendly materials, and in particular to a kind of carbonaceous activity environment-friendly materials.
Background technique
Construction material can be divided into structural material, ornament materials and certain proprietary materials.Structural material include timber, bamboo wood,
Stone material, cement, concrete, metal, brick and tile, ceramics, glass, engineering plastics, composite material etc.；Ornament materials includes various paintings
Material, paint, coating, veneer, assorted ceramic tile, the glass with special-effect etc.；Proprietary material refer to for waterproof, moisture-proof, anti-corrosion,
Fire prevention, fire-retardant, sound insulation, heat-insulated, heat preservation, sealing etc..
With the implementation and development of construction material, environment-friendly materials and product are increasingly valued by people.Environmental problem
Refer to environmental quality variation due to function of human activities caused by ambient enviroment and this variation to the production of the mankind,
It is influenced caused by life and health.For the mankind during nature remodeling environment and creation social environment, natural environment is still with it
The intrinsic natural law varies.On the one hand social environment is restricted by natural environment, also moved with its intrinsic rule.People
Class constantly influences each other and acts on environment, produces problem of environmental pollution.Problem of environmental pollution is that current social faces
One big problem, increasingly severe with problem of environmental pollution, environmentally friendly concept has been rooted in the hearts of the people, and the exploitation of environment-friendly materials and is made
With having a extensive future.Environment friendly decorative material refer to it is natural, itself without or few poisonous and hazardous substance, only carry out without pollution
The ornament materials of simple processing.As people's awareness of environmental protection continues to increase and the continuous improvement of living standard, and people are to residence
Firmly the requirement of environment is also higher and higher, and the existing fitment material for family played role in decoration merely has been unable to satisfy the demand of people.
Currently, the property for improving environment-friendly materials is also mostly concentrated in laboratory in the test in relation to carbonaceous activity environment-friendly materials
Can, but in terms of heat preservation and absorption property, still there is very big room for promotion, for this purpose, for a kind of carbonaceous activity environment-friendly materials, we
Need to provide a kind of new approaches.
Summary of the invention
In view of the deficiencies of the prior art, the present invention provides a kind of carbonaceous activity environment-friendly materials, environment-friendly materials of the invention,
Can thermal insulation property to carbonaceous activity environment-friendly materials and absorption property carry out different degrees of promotion, have wide range of applications；And
Simple production process of the present invention, controllable easy to operate, with good economic efficiency and application value, at the same consume energy it is relatively low,
Product stability is good, environmentally protective, at low cost, convenient and safety when using.
In order to achieve the above object, the present invention is achieved by the following technical programs:
A kind of carbonaceous activity environment-friendly materials, the raw material including following parts by weight: 120-160 parts of carbonaceous porous material, diatom
30-60 parts native, 20-40 parts of sepiolite, 5-10 parts of mica powder, 15-18 parts of magnesia, 10-15 parts of nano-titanium dioxide, asphalt mixtures modified by epoxy resin
30-50 parts of rouge, 25-30 parts of acrylate, 16-20 parts of wood fibre, 12-16 parts of ceramic fibre and 40-60 parts of waterglass.
Preferably, a kind of carbonaceous activity environment-friendly materials, the raw material including following parts by weight: 130 parts of carbonaceous porous material, silicon
30 parts of diatomaceous earth, 25 parts of sepiolite, 5 parts of mica powder, 17 parts of magnesia, 10 parts of nano-titanium dioxide, 30 parts of epoxy resin, acrylic acid
25 parts of ester resin, 16 parts of wood fibre, 14 parts of ceramic fibre and 40 parts of waterglass.
Preferably, a kind of carbonaceous activity environment-friendly materials, the raw material including following parts by weight: 120 parts of carbonaceous porous material, silicon
40 parts of diatomaceous earth, 30 parts of sepiolite, 8 parts of mica powder, 15 parts of magnesia, 14 parts of nano-titanium dioxide, 40 parts of epoxy resin, acrylic acid
27 parts of ester resin, 18 parts of wood fibre, 12 parts of ceramic fibre and 50 parts of waterglass.
Preferably, a kind of carbonaceous activity environment-friendly materials, the raw material including following parts by weight: 160 parts of carbonaceous porous material, silicon
35 parts of diatomaceous earth, 20 parts of sepiolite, 6 parts of mica powder, 16 parts of magnesia, 12 parts of nano-titanium dioxide, 50 parts of epoxy resin, acrylic acid
28 parts of ester resin, 17 parts of wood fibre, 15 parts of ceramic fibre and 55 parts of waterglass.
Preferably, a kind of carbonaceous activity environment-friendly materials, the carbonaceous porous material are active carbon, activated carbon fibre, charcoal gas
One of gel, activated coke or active carbocoal or any combination.
A kind of preparation method of carbonaceous activity environment-friendly materials, comprising the following steps:
S1, the epoxy resin of above-mentioned specific gravity is heated to 115-135 DEG C, be added the diatomite of above-mentioned specific gravity, magnesia and
Wood fibre carries out insulated and stirred 3-5h under conditions of revolving speed is 350-650r/min, obtains mixed component A；
S2, mixed component A obtained in above-mentioned S1 is cooled to 85-105 DEG C, the Hai Pao of above-mentioned specific gravity is added thereto
Stone, mica powder, nano-titanium dioxide, acrylate and ceramic fibre stir under conditions of revolving speed is 260-560r/min
Mixing 1-3h is mixed, room temperature is cooled to after mixing, obtains mixed component B；
S3, the carbonaceous porous material and waterglass of above-mentioned specific gravity are added into mixed component B obtained in above-mentioned S2,
Revolving speed is stirred after 20-60min under conditions of being 580-980r/min to get environment-friendly materials.
The invention has the following advantages:
Since above-mentioned carbonaceous porous material has porous structure, the venomous injurant of formaldehyde etc. in air can be adsorbed
Matter；Diatomite has natural micropore structure, can be realized breathing damping, while it can also adsorb formaldehyde etc. in air
Poisonous and harmful substance；Sepiolite has the performances such as extremely strong absorption, decoloration and dispersion, also there is high thermal stability；Mica powder
With the characteristics such as good elasticity, toughness, insulating properties, high temperature resistant, acid and alkali-resistance, corrosion-resistant, adhesive force is strong；Magnesia has lightweight
The advantages such as high-strength, fire-proof and thermal-insulation, energy conservation and environmental protection；Nano-titanium dioxide has sterilization, antifouling, deodorization, nontoxic and performance stable
Feature；Lignocellulosic specific gravity is small, large specific surface area, has excellent heat preservation, heat-insulated, sound insulation, insulation and permeability, heat swollen
Swollen do not flake uniformly is not cracked, higher wet film intensity and coverage effect；With excellent flexibility and dispersibility, shape after mixing
At tridimensional network, the support force and endurance of system are enhanced, the stability of system, intensity, compactness and can be improved
Evenness；Ceramic fibre have light, high temperature resistant, thermal stability is good, fire resistance is good, heat insulation property is good and the spy of high mechanical strength
Point；The present invention, as addition base-material, using diatomite, sepiolite, mica powder, magnesia, receives by using carbonaceous porous material
Rice titanium dioxide, epoxy resin, acrylate, wood fibre, ceramic fibre and waterglass are significantly improved as auxiliary material
The thermal insulation property and absorption property of environment-friendly materials, can effectively remove indoor benzene, formaldehyde, sulfide, ammonia and stink substances, and
With sterilizing function.
Carbonaceous activity environment-friendly materials of the invention, by adjusting carbonaceous porous material, diatomite, sepiolite, mica powder, oxygen
Change the ratio volume of magnesium, nano-titanium dioxide, epoxy resin, acrylate, wood fibre, ceramic fibre and waterglass etc.
And technological parameter, can thermal insulation property to carbonaceous activity environment-friendly materials and absorption property carry out different degrees of promotion, using model
It encloses extensively；And it is simple production process of the present invention, controllable easy to operate, with good economic efficiency and application value consumes simultaneously
Can it is relatively low, product stability is good, environmentally protective, at low cost, convenient and safety when using.
Specific embodiment
In order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below in conjunction with the embodiment of the present invention,
Technical scheme in the embodiment of the invention is clearly and completely described, it is clear that described embodiment is the present invention one
Divide embodiment, instead of all the embodiments.Based on the embodiments of the present invention, those of ordinary skill in the art are not making
Every other embodiment obtained, shall fall within the protection scope of the present invention under the premise of creative work.
Embodiment 1:
A kind of carbonaceous activity environment-friendly materials, the raw material including following parts by weight: 120-160 parts of carbonaceous porous material, diatom
30-60 parts native, 20-40 parts of sepiolite, 5-10 parts of mica powder, 15-18 parts of magnesia, 10-15 parts of nano-titanium dioxide, asphalt mixtures modified by epoxy resin
30-50 parts of rouge, 25-30 parts of acrylate, 16-20 parts of wood fibre, 12-16 parts of ceramic fibre and 40-60 parts of waterglass.
Preferably, a kind of carbonaceous activity environment-friendly materials, the raw material including following parts by weight: 130 parts of carbonaceous porous material, silicon
30 parts of diatomaceous earth, 25 parts of sepiolite, 5 parts of mica powder, 17 parts of magnesia, 10 parts of nano-titanium dioxide, 30 parts of epoxy resin, acrylic acid
25 parts of ester resin, 16 parts of wood fibre, 14 parts of ceramic fibre and 40 parts of waterglass.
Preferably, a kind of carbonaceous activity environment-friendly materials, the carbonaceous porous material are active carbon, activated carbon fibre, charcoal gas
One of gel, activated coke or active carbocoal or any combination.
A kind of preparation method of carbonaceous activity environment-friendly materials, comprising the following steps:
S1, the epoxy resin of above-mentioned specific gravity is heated to 115-135 DEG C, be added the diatomite of above-mentioned specific gravity, magnesia and
Wood fibre carries out insulated and stirred 3-5h under conditions of revolving speed is 350-650r/min, obtains mixed component A；
S2, mixed component A obtained in above-mentioned S1 is cooled to 85-105 DEG C, the Hai Pao of above-mentioned specific gravity is added thereto
Stone, mica powder, nano-titanium dioxide, acrylate and ceramic fibre stir under conditions of revolving speed is 260-560r/min
Mixing 1-3h is mixed, room temperature is cooled to after mixing, obtains mixed component B；
S3, the carbonaceous porous material and waterglass of above-mentioned specific gravity are added into mixed component B obtained in above-mentioned S2,
Revolving speed is stirred after 20-60min under conditions of being 580-980r/min to get environment-friendly materials.
Embodiment 2:
A kind of carbonaceous activity environment-friendly materials, the raw material including following parts by weight: 120-160 parts of carbonaceous porous material, diatom
30-60 parts native, 20-40 parts of sepiolite, 5-10 parts of mica powder, 15-18 parts of magnesia, 10-15 parts of nano-titanium dioxide, asphalt mixtures modified by epoxy resin
30-50 parts of rouge, 25-30 parts of acrylate, 16-20 parts of wood fibre, 12-16 parts of ceramic fibre and 40-60 parts of waterglass.
Preferably, a kind of carbonaceous activity environment-friendly materials, the raw material including following parts by weight: 120 parts of carbonaceous porous material, silicon
40 parts of diatomaceous earth, 30 parts of sepiolite, 8 parts of mica powder, 15 parts of magnesia, 14 parts of nano-titanium dioxide, 40 parts of epoxy resin, acrylic acid
27 parts of ester resin, 18 parts of wood fibre, 12 parts of ceramic fibre and 50 parts of waterglass.
Preferably, a kind of carbonaceous activity environment-friendly materials, the carbonaceous porous material are active carbon, activated carbon fibre, charcoal gas
One of gel, activated coke or active carbocoal or any combination.
A kind of preparation method of carbonaceous activity environment-friendly materials, comprising the following steps:
S1, the epoxy resin of above-mentioned specific gravity is heated to 115-135 DEG C, be added the diatomite of above-mentioned specific gravity, magnesia and
Wood fibre carries out insulated and stirred 3-5h under conditions of revolving speed is 350-650r/min, obtains mixed component A；
S2, mixed component A obtained in above-mentioned S1 is cooled to 85-105 DEG C, the Hai Pao of above-mentioned specific gravity is added thereto
Stone, mica powder, nano-titanium dioxide, acrylate and ceramic fibre stir under conditions of revolving speed is 260-560r/min
Mixing 1-3h is mixed, room temperature is cooled to after mixing, obtains mixed component B；
S3, the carbonaceous porous material and waterglass of above-mentioned specific gravity are added into mixed component B obtained in above-mentioned S2,
Revolving speed is stirred after 20-60min under conditions of being 580-980r/min to get environment-friendly materials.
Embodiment 3:
A kind of carbonaceous activity environment-friendly materials, the raw material including following parts by weight: 120-160 parts of carbonaceous porous material, diatom
30-60 parts native, 20-40 parts of sepiolite, 5-10 parts of mica powder, 15-18 parts of magnesia, 10-15 parts of nano-titanium dioxide, asphalt mixtures modified by epoxy resin
30-50 parts of rouge, 25-30 parts of acrylate, 16-20 parts of wood fibre, 12-16 parts of ceramic fibre and 40-60 parts of waterglass.
Preferably, a kind of carbonaceous activity environment-friendly materials, the raw material including following parts by weight: 160 parts of carbonaceous porous material, silicon
35 parts of diatomaceous earth, 20 parts of sepiolite, 6 parts of mica powder, 16 parts of magnesia, 12 parts of nano-titanium dioxide, 50 parts of epoxy resin, acrylic acid
28 parts of ester resin, 17 parts of wood fibre, 15 parts of ceramic fibre and 55 parts of waterglass.
Preferably, a kind of carbonaceous activity environment-friendly materials, the carbonaceous porous material are active carbon, activated carbon fibre, charcoal gas
One of gel, activated coke or active carbocoal or any combination.
A kind of preparation method of carbonaceous activity environment-friendly materials, comprising the following steps:
S1, the epoxy resin of above-mentioned specific gravity is heated to 115-135 DEG C, be added the diatomite of above-mentioned specific gravity, magnesia and
Wood fibre carries out insulated and stirred 3-5h under conditions of revolving speed is 350-650r/min, obtains mixed component A；
S2, mixed component A obtained in above-mentioned S1 is cooled to 85-105 DEG C, the Hai Pao of above-mentioned specific gravity is added thereto
Stone, mica powder, nano-titanium dioxide, acrylate and ceramic fibre stir under conditions of revolving speed is 260-560r/min
Mixing 1-3h is mixed, room temperature is cooled to after mixing, obtains mixed component B；
S3, the carbonaceous porous material and waterglass of above-mentioned specific gravity are added into mixed component B obtained in above-mentioned S2,
Revolving speed is stirred after 20-60min under conditions of being 580-980r/min to get environment-friendly materials.
Embodiment 4:
A kind of carbonaceous activity environment-friendly materials, the raw material including following parts by weight: 120-160 parts of carbonaceous porous material, diatom
30-60 parts native, 20-40 parts of sepiolite, 5-10 parts of mica powder, 15-18 parts of magnesia, 10-15 parts of nano-titanium dioxide, asphalt mixtures modified by epoxy resin
30-50 parts of rouge, 25-30 parts of acrylate, 16-20 parts of wood fibre, 12-16 parts of ceramic fibre and 40-60 parts of waterglass.
Preferably, a kind of carbonaceous activity environment-friendly materials, the raw material including following parts by weight: 150 parts of carbonaceous porous material, silicon
60 parts of diatomaceous earth, 40 parts of sepiolite, 9 parts of mica powder, 18 parts of magnesia, 13 parts of nano-titanium dioxide, 45 parts of epoxy resin, acrylic acid
30 parts of ester resin, 20 parts of wood fibre, 16 parts of ceramic fibre and 45 parts of waterglass.
Preferably, a kind of carbonaceous activity environment-friendly materials, the carbonaceous porous material are active carbon, activated carbon fibre, charcoal gas
One of gel, activated coke or active carbocoal or any combination.
A kind of preparation method of carbonaceous activity environment-friendly materials, comprising the following steps:
S1, the epoxy resin of above-mentioned specific gravity is heated to 115-135 DEG C, be added the diatomite of above-mentioned specific gravity, magnesia and
Wood fibre carries out insulated and stirred 3-5h under conditions of revolving speed is 350-650r/min, obtains mixed component A；
S2, mixed component A obtained in above-mentioned S1 is cooled to 85-105 DEG C, the Hai Pao of above-mentioned specific gravity is added thereto
Stone, mica powder, nano-titanium dioxide, acrylate and ceramic fibre stir under conditions of revolving speed is 260-560r/min
Mixing 1-3h is mixed, room temperature is cooled to after mixing, obtains mixed component B；
S3, the carbonaceous porous material and waterglass of above-mentioned specific gravity are added into mixed component B obtained in above-mentioned S2,
Revolving speed is stirred after 20-60min under conditions of being 580-980r/min to get environment-friendly materials.
Embodiment 5:
A kind of carbonaceous activity environment-friendly materials, the raw material including following parts by weight: 120-160 parts of carbonaceous porous material, diatom
30-60 parts native, 20-40 parts of sepiolite, 5-10 parts of mica powder, 15-18 parts of magnesia, 10-15 parts of nano-titanium dioxide, asphalt mixtures modified by epoxy resin
30-50 parts of rouge, 25-30 parts of acrylate, 16-20 parts of wood fibre, 12-16 parts of ceramic fibre and 40-60 parts of waterglass.
Preferably, a kind of carbonaceous activity environment-friendly materials, the raw material including following parts by weight: 140 parts of carbonaceous porous material, silicon
50 parts of diatomaceous earth, 35 parts of sepiolite, 10 parts of mica powder, 17 parts of magnesia, 15 parts of nano-titanium dioxide, 35 parts of epoxy resin, propylene
29 parts of acid ester resin, 19 parts of wood fibre, 13 parts of ceramic fibre and 60 parts of waterglass.
Preferably, a kind of carbonaceous activity environment-friendly materials, the carbonaceous porous material are active carbon, activated carbon fibre, charcoal gas
One of gel, activated coke or active carbocoal or any combination.
A kind of preparation method of carbonaceous activity environment-friendly materials, comprising the following steps:
S1, the epoxy resin of above-mentioned specific gravity is heated to 115-135 DEG C, be added the diatomite of above-mentioned specific gravity, magnesia and
Wood fibre carries out insulated and stirred 3-5h under conditions of revolving speed is 350-650r/min, obtains mixed component A；
S2, mixed component A obtained in above-mentioned S1 is cooled to 85-105 DEG C, the Hai Pao of above-mentioned specific gravity is added thereto
Stone, mica powder, nano-titanium dioxide, acrylate and ceramic fibre stir under conditions of revolving speed is 260-560r/min
Mixing 1-3h is mixed, room temperature is cooled to after mixing, obtains mixed component B；
S3, the carbonaceous porous material and waterglass of above-mentioned specific gravity are added into mixed component B obtained in above-mentioned S2,
Revolving speed is stirred after 20-60min under conditions of being 580-980r/min to get environment-friendly materials.
Gained environment-friendly materials in above-described embodiment 1-5 are tested for the property, performance test data is as shown in the table:
It should be noted that, in this document, relational terms such as first and second and the like are used merely to a reality
Body or operation are distinguished with another entity or operation, are deposited without necessarily requiring or implying between these entities or operation
In any actual relationship or order or sequence.Moreover, the terms "include", "comprise" or its any other variant are intended to
Non-exclusive inclusion, so that the process, method, article or equipment including a series of elements is not only wanted including those
Element, but also including other elements that are not explicitly listed, or further include for this process, method, article or equipment
Intrinsic element.In the absence of more restrictions, the element limited by sentence "including a ...", it is not excluded that
There is also other identical elements in process, method, article or equipment including element.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations；Although with reference to the foregoing embodiments
Invention is explained in detail, those skilled in the art should understand that: it still can be to aforementioned each implementation
Technical solution documented by example is modified or equivalent replacement of some of the technical features；And these modification or
Replacement, the spirit and scope for technical solution of various embodiments of the present invention that it does not separate the essence of the corresponding technical solution.
Claims (6)
1. a kind of carbonaceous activity environment-friendly materials, which is characterized in that the raw material including following parts by weight: carbonaceous porous material 120-
160 parts, 30-60 parts of diatomite, 20-40 parts of sepiolite, 5-10 parts of mica powder, 15-18 parts of magnesia, nano-titanium dioxide 10-
15 parts, 30-50 parts of epoxy resin, 25-30 parts of acrylate, 16-20 parts of wood fibre, 12-16 parts of ceramic fibre and water
40-60 parts of glass.
2. a kind of carbonaceous activity environment-friendly materials according to claim 1, which is characterized in that the original including following parts by weight
Material: 130 parts of carbonaceous porous material, 30 parts of diatomite, 25 parts of sepiolite, 5 parts of mica powder, 17 parts of magnesia, nano-titanium dioxide
10 parts, 30 parts of epoxy resin, 25 parts of acrylate, 16 parts of wood fibre, 14 parts of ceramic fibre and 40 parts of waterglass.
3. a kind of carbonaceous activity environment-friendly materials according to claim 1, which is characterized in that the original including following parts by weight
Material: 120 parts of carbonaceous porous material, 40 parts of diatomite, 30 parts of sepiolite, 8 parts of mica powder, 15 parts of magnesia, nano-titanium dioxide
14 parts, 40 parts of epoxy resin, 27 parts of acrylate, 18 parts of wood fibre, 12 parts of ceramic fibre and 50 parts of waterglass.
4. a kind of carbonaceous activity environment-friendly materials according to claim 1, which is characterized in that the original including following parts by weight
Material: 160 parts of carbonaceous porous material, 35 parts of diatomite, 20 parts of sepiolite, 6 parts of mica powder, 16 parts of magnesia, nano-titanium dioxide
12 parts, 50 parts of epoxy resin, 28 parts of acrylate, 17 parts of wood fibre, 15 parts of ceramic fibre and 55 parts of waterglass.
5. a kind of carbonaceous activity environment-friendly materials according to claim 1, it is characterised in that: the carbonaceous porous material is to live
One of property charcoal, activated carbon fibre, charcoal-aero gel, activated coke or active carbocoal or any combination.
6. a kind of preparation method of carbonaceous activity environment-friendly materials as described in claim 1-5 any one, which is characterized in that packet
Include following steps:
S1, the epoxy resin of above-mentioned specific gravity is heated to 115-135 DEG C, the diatomite of above-mentioned specific gravity, magnesia and wooden is added
Fiber carries out insulated and stirred 3-5h under conditions of revolving speed is 350-650r/min, obtains mixed component A；
S2, mixed component A obtained in above-mentioned S1 is cooled to 85-105 DEG C, sepiolite, the cloud of above-mentioned specific gravity is added thereto
Female powder, nano-titanium dioxide, acrylate and ceramic fibre are stirred under conditions of revolving speed is 260-560r/min
1-3h is cooled to room temperature after mixing, obtains mixed component B；
S3, the carbonaceous porous material and waterglass of above-mentioned specific gravity are added into mixed component B obtained in above-mentioned S2, in revolving speed
To be stirred under conditions of 580-980r/min after 20-60min to get environment-friendly materials.