CN108659681A - A kind of environment-friendlyactive active carbon decorative paint - Google Patents

A kind of environment-friendlyactive active carbon decorative paint Download PDF

Info

Publication number
CN108659681A
CN108659681A CN201810485959.7A CN201810485959A CN108659681A CN 108659681 A CN108659681 A CN 108659681A CN 201810485959 A CN201810485959 A CN 201810485959A CN 108659681 A CN108659681 A CN 108659681A
Authority
CN
China
Prior art keywords
parts
powder
environment
decorative paint
nano
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201810485959.7A
Other languages
Chinese (zh)
Inventor
王宇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Qi Jia Polytron Technologies Inc
Original Assignee
Anhui Qi Jia Polytron Technologies Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Qi Jia Polytron Technologies Inc filed Critical Anhui Qi Jia Polytron Technologies Inc
Priority to CN201810485959.7A priority Critical patent/CN108659681A/en
Publication of CN108659681A publication Critical patent/CN108659681A/en
Withdrawn legal-status Critical Current

Abstract

A kind of environment-friendlyactive active carbon decorative paint, is made of the following raw material：Activated carbon, concave convex rod clay powder, zeolite granular, white cement, gesso, white carbon, calcium chloride, superfine silica gel powder, expanded perlite, nano silver-supported antibacterial powder, nano-titanium dioxide, sodium pyrophosphate, vinyl acetate, isopropanol, vinyl chloride, phosphotriester, lecithin, polyisobutene acid glyceride gel, methyltriethoxysilane, poly- isobutyl ester, aluminium hydroxide, antimony oxide, asbestos fibre, azo dicarbonamide, benzoyl peroxide, antifoaming agent, fire retardant.Beneficial effects of the present invention are：(1) present invention has the good adsorption function for harmful substances such as formaldehyde, while the nano silver-supported antibacterial powder added has good fungistatic effect；(2) while the decorative paint has good high temperature resistance and flame retardant property；(3) coating has not only acted as good decoration function, while also playing the effect to the environmental protection such as air purification.

Description

A kind of environment-friendlyactive active carbon decorative paint
Technical field
The invention belongs to energy conservation and environmental protection fields, and in particular to a kind of environment-friendlyactive active carbon decorative paint.
Background technology
Environment-friendly active charcoal is a kind of novel absorbent charcoal, specially applies to field of environment protection.It is net to be mainly used for industrial air Change and water process, this activated carbon are usually used for field of environment protection, so being referred to as " environment-friendly active charcoal " its maximum spy by people Point is that adsorption rate is fast, and pore structure prosperity can effectively handle exhaust gas, waste water.
Activated carbon is also known as activated carbon black, is black powder or bulk, graininess, cellular amorphous carbon, also there is row It arranges regular crystal carbon, also includes two class admixtures in activated carbon in addition to carbon：One kind is chemically combined element, mainly Oxygen and hydrogen, these elements be due to not completely charing and remain in charcoal, or in activation process, external non-carbon element It is combined with Surface Chemistry of Activated Carbon, when such as using steam activation, activated carbon surface is aoxidized or steam oxidation；Another kind of blending Object is ash content, it is the inorganic part of activated carbon.
In family's new house finishing, the improper use of wall paint can be such that harmful substance in air increases, and processing not in time can be right Human body causes damages.The appearance of environment-friendly active charcoal results in people and faces how environment-friendly active charcoal is applied to asking in wall paint Topic.
Invention content
Purpose of the invention is to overcome the shortcomings in the prior art, provides a kind of environment-friendlyactive active carbon decorative paint.
In order to solve the above technical problems, the technical scheme is that：
A kind of environment-friendlyactive active carbon decorative paint is made of following parts by weight raw material：10-16 parts of activated carbon, concave convex rod 5-7 parts of clay powder, 4-6 parts of zeolite granular, 10-14 parts of white cement, 9-13 parts of gesso, 6-8 parts of white carbon, calcium chloride 3-5 Part, 7-9 parts of superfine silica gel powder, 5-7 parts of expanded perlite, 2-4 parts of nano silver-supported antibacterial powder, 3-6 parts of nano-titanium dioxide, pyrophosphoric acid 2-4 parts of sodium, 5-10 parts of isopropanol, 1-3 parts of vinyl chloride, 2-4 parts of phosphotriester, 1-3 parts of lecithin, gathers 9-22 parts of vinyl acetate 18-24 parts of glyceryl methacrylate gel, 18-22 parts of methyltriethoxysilane, isobutyl ester 30-36 parts poly-, aluminium hydroxide 10- 14 parts, 9-11 parts of antimony oxide, 1-2 parts of asbestos fibre, 3-5 parts of azo dicarbonamide, 1-3 parts of benzoyl peroxide, antifoaming agent 2-4 parts, 2-4 parts of fire retardant.
Further, it is made of following parts by weight raw material：10 parts of activated carbon, 5 parts of concave convex rod clay powder, zeolite granular 4 Part, 10 parts of white cement, 9 parts of gesso, 6 parts of white carbon, 3 parts of calcium chloride, 7 parts of superfine silica gel powder, expanded perlite 5 part, nanometer 2 parts of Ag-carried antibacterial powder, 3 parts of nano-titanium dioxide, 2 parts of sodium pyrophosphate, 9 parts of vinyl acetate, 5 parts of isopropanol, 1 part of vinyl chloride, phosphorus Sour 2 parts of three ester, 1 part of lecithin, 18 parts of polyisobutene acid glyceride gel, 18 parts of methyltriethoxysilane, poly- isobutyl ester 30 Part, 10 parts of aluminium hydroxide, 9 parts of antimony oxide, 1 part of asbestos fibre, 3 parts of azo dicarbonamide, 1 part of benzoyl peroxide, defoaming 2 parts of agent, 2 parts of fire retardant.
Further, it is made of following parts by weight raw material：16 parts of activated carbon, 7 parts of concave convex rod clay powder, zeolite granular 6 Part, 14 parts of white cement, 13 parts of gesso, 8 parts of white carbon, 5 parts of calcium chloride, 9 parts of superfine silica gel powder, expanded perlite 7 part, nanometer 4 parts of Ag-carried antibacterial powder, 6 parts of nano-titanium dioxide, 4 parts of sodium pyrophosphate, 22 parts of vinyl acetate, 10 parts of isopropanol, 3 parts of vinyl chloride, 4 parts of phosphotriester, 3 parts of lecithin, 24 parts of polyisobutene acid glyceride gel, 22 parts of methyltriethoxysilane, poly- isobutyl ester 36 parts, 14 parts of aluminium hydroxide, 11 parts of antimony oxide, 2 parts of asbestos fibre, 5 parts of azo dicarbonamide, 3 parts of benzoyl peroxide, disappear 4 parts of infusion, 4 parts of fire retardant.
Further, it is made of following parts by weight raw material：13 parts of activated carbon, 6 parts of concave convex rod clay powder, zeolite granular 5 Part, 12 parts of white cement, 11 parts of gesso, 7 parts of white carbon, 4 parts of calcium chloride, 8 parts of superfine silica gel powder, expanded perlite 6 part, nanometer 3 parts of Ag-carried antibacterial powder, 5 parts of nano-titanium dioxide, 3 parts of sodium pyrophosphate, 15 parts of vinyl acetate, 7 parts of isopropanol, 2 parts of vinyl chloride, phosphorus Sour 3 parts of three ester, 2 parts of lecithin, 21 parts of polyisobutene acid glyceride gel, 20 parts of methyltriethoxysilane, poly- isobutyl ester 33 Part, 2 parts of benzoyl peroxide, disappears at 12 parts of aluminium hydroxide, 10 parts of antimony oxide, 1.5 parts of asbestos fibre, 4 parts of azo dicarbonamide 3 parts of infusion, 3 parts of fire retardant.
Further, the grain graininess of the activated carbon is 0.095-0.235mm.
Further, the nano-titanium dioxide grain size is 50-60nm.
Further, the fire retardant is at least one of ammonium polyphosphate, zinc borate.
Further, the antifoaming agent is polyoxyethylene polyoxypropylene pentaerythrite ether, polyoxyethylene polyoxy propyl alcohol amidogen ether At least one of weight.
Beneficial effects of the present invention are：(1) present invention has the good adsorption function for harmful substances such as formaldehyde, together The nano silver-supported antibacterial powder of Shi Tianjia has good fungistatic effect；(2) while the decorative paint has good heat-resisting quantity Energy and flame retardant property；(3) coating has not only acted as good decoration function, while also playing to the environmental protection such as air purification Effect.
Specific implementation mode
The effect of to make to structure feature of the invention and being reached, has a better understanding and awareness, to preferable Embodiment cooperation detailed description, is described as follows：
Embodiment 1
A kind of environment-friendlyactive active carbon decorative paint is made of following parts by weight raw material：10 parts of activated carbon, concave convex rod clay 5 parts of powder, 4 parts of zeolite granular, 10 parts of white cement, 9 parts of gesso, 6 parts of white carbon, 3 parts of calcium chloride, 7 parts of superfine silica gel powder, expansion 5 parts of perlite, 2 parts of nano silver-supported antibacterial powder, 3 parts of nano-titanium dioxide, 2 parts of sodium pyrophosphate, 9 parts of vinyl acetate, isopropanol 5 Part, 1 part of vinyl chloride, 2 parts of phosphotriester, 1 part of lecithin, 18 parts of polyisobutene acid glyceride gel, methyltriethoxysilane 18 parts, 30 parts of poly- isobutyl ester, 10 parts of aluminium hydroxide, 9 parts of antimony oxide, 1 part of asbestos fibre, 3 parts of azo dicarbonamide, peroxidating 1 part of benzoyl, 2 parts of antifoaming agent, 2 parts of fire retardant.
Wherein, the grain graininess of the activated carbon is 0.095mm, and the nano-titanium dioxide grain size is 50nm.The resistance Combustion agent is ammonium polyphosphate, and the antifoaming agent is polyoxyethylene polyoxypropylene pentaerythrite ether.
Embodiment 2
A kind of environment-friendlyactive active carbon decorative paint is made of following parts by weight raw material：16 parts of activated carbon, concave convex rod clay It is 7 parts of powder, 6 parts of zeolite granular, 14 parts of white cement, 13 parts of gesso, 8 parts of white carbon, 5 parts of calcium chloride, 9 parts of superfine silica gel powder, swollen 7 parts of swollen perlite, 4 parts of nano silver-supported antibacterial powder, 6 parts of nano-titanium dioxide, 4 parts of sodium pyrophosphate, 22 parts of vinyl acetate, isopropanol 10 parts, 3 parts of vinyl chloride, 4 parts of phosphotriester, 3 parts of lecithin, 24 parts of polyisobutene acid glyceride gel, methyltriethoxy silane 22 parts of alkane, 36 parts of poly- isobutyl ester, 14 parts of aluminium hydroxide, 11 parts of antimony oxide, 2 parts of asbestos fibre, 5 parts of azo dicarbonamide, mistake 3 parts of Benzoyl Oxide, 4 parts of antifoaming agent, 4 parts of fire retardant.
Wherein, the grain graininess of the activated carbon is 0.235mm, and the nano-titanium dioxide grain size is 60nm.The resistance Combustion agent is ammonium polyphosphate, and the antifoaming agent is polyoxyethylene polyoxypropylene pentaerythrite ether.
Embodiment 3
A kind of environment-friendlyactive active carbon decorative paint is made of following parts by weight raw material：13 parts of activated carbon, concave convex rod clay It is 6 parts of powder, 5 parts of zeolite granular, 12 parts of white cement, 11 parts of gesso, 7 parts of white carbon, 4 parts of calcium chloride, 8 parts of superfine silica gel powder, swollen 6 parts of swollen perlite, 3 parts of nano silver-supported antibacterial powder, 5 parts of nano-titanium dioxide, 3 parts of sodium pyrophosphate, 15 parts of vinyl acetate, isopropanol 7 parts, 2 parts of vinyl chloride, 3 parts of phosphotriester, 2 parts of lecithin, 21 parts of polyisobutene acid glyceride gel, methyltriethoxysilane 20 parts, 33 parts of poly- isobutyl ester, 12 parts of aluminium hydroxide, 10 parts of antimony oxide, 1.5 parts of asbestos fibre, 4 parts of azo dicarbonamide, mistake 2 parts of Benzoyl Oxide, 3 parts of antifoaming agent, 3 parts of fire retardant.
Wherein, the grain graininess of the activated carbon is 0.175mm, and the nano-titanium dioxide grain size is 55nm.The resistance Combustion agent is ammonium polyphosphate, and the antifoaming agent is polyoxyethylene polyoxypropylene pentaerythrite ether.
Environment-friendlyactive active carbon decorative paint and common wall coating obtained by above-described embodiment, with parts by weight and coated on same It is as shown in the table to survey its performance indicator within 30 days after wall under one environmental condition：
By above-mentioned as it can be seen that forming simultaneously environment-friendlyactive active carbon decorative paint obtained according to parts by weight raw material in embodiment 2 Have the effect of best wall fungistatic effect, absorption formaldehyde in air and excellent wall anti-flammability, belongs to best raw material Parts by weight form option, and more antibacterial than common coating for wall surface, formaldehyde adsorption effect is more preferable, and flame retardant property is more preferably.
Beneficial effects of the present invention are：(1) present invention has the good adsorption function for harmful substances such as formaldehyde, together The nano silver-supported antibacterial powder of Shi Tianjia has good fungistatic effect；(2) while the decorative paint has good heat-resisting quantity Energy and flame retardant property；(3) coating has not only acted as good decoration function, while also playing to the environmental protection such as air purification Effect.
The basic principles, main features and advantages of the present invention have been shown and described above.The technology of the industry Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and what is described in the above embodiment and the description is only the present invention Principle, various changes and improvements may be made to the invention without departing from the spirit and scope of the present invention, these variation and Improvement is both fallen in the range of claimed invention.The present invention claims protection domain by appended claims and its Equivalent defines.

Claims (8)

1. a kind of environment-friendlyactive active carbon decorative paint, it is characterised in that：It is made of following parts by weight raw material：Activated carbon 10-16 Part, 5-7 parts of concave convex rod clay powder, 4-6 parts of zeolite granular, 10-14 parts of white cement, 9-13 parts of gesso, 6-8 parts of white carbon, 3-5 parts of calcium chloride, 7-9 parts of superfine silica gel powder, 5-7 parts of expanded perlite, 2-4 parts of nano silver-supported antibacterial powder, nano-titanium dioxide 3-6 Part, 2-4 parts of sodium pyrophosphate, 9-22 parts of vinyl acetate, 5-10 parts of isopropanol, 1-3 parts of vinyl chloride, 2-4 parts of phosphotriester, lecithin 1-3 parts, 18-24 parts of polyisobutene acid glyceride gel, 18-22 parts of methyltriethoxysilane, isobutyl ester 30-36 parts poly-, hydrogen 10-14 parts of aluminium oxide, 9-11 parts of antimony oxide, 1-2 parts of asbestos fibre, 3-5 parts of azo dicarbonamide, benzoyl peroxide 1-3 Part, 2-4 parts of antifoaming agent, 2-4 parts of fire retardant.
2. a kind of environment-friendlyactive active carbon decorative paint according to claim 1, it is characterised in that：By following parts by weight original Material composition：10 parts of activated carbon, 5 parts of concave convex rod clay powder, 4 parts of zeolite granular, 10 parts of white cement, 9 parts of gesso, white carbon 6 Part, 3 parts of calcium chloride, 7 parts of superfine silica gel powder, 5 parts of expanded perlite, 2 parts of nano silver-supported antibacterial powder, 3 parts of nano-titanium dioxide, burnt phosphorus 2 parts of sour sodium, 9 parts of vinyl acetate, 5 parts of isopropanol, 1 part of vinyl chloride, 2 parts of phosphotriester, 1 part of lecithin, polyisobutene acid glycerol 18 parts of gels, 18 parts of methyltriethoxysilane, 30 parts of poly- isobutyl ester, 10 parts of aluminium hydroxide, 9 parts of antimony oxide, asbestos 1 part of fiber, 3 parts of azo dicarbonamide, 1 part of benzoyl peroxide, 2 parts of antifoaming agent, 2 parts of fire retardant.
3. a kind of environment-friendlyactive active carbon decorative paint according to claim 1, it is characterised in that：By following parts by weight original Material composition：16 parts of activated carbon, 7 parts of concave convex rod clay powder, 6 parts of zeolite granular, 14 parts of white cement, 13 parts of gesso, white carbon 8 Part, 5 parts of calcium chloride, 9 parts of superfine silica gel powder, 7 parts of expanded perlite, 4 parts of nano silver-supported antibacterial powder, 6 parts of nano-titanium dioxide, burnt phosphorus 4 parts of sour sodium, 22 parts of vinyl acetate, 10 parts of isopropanol, 3 parts of vinyl chloride, 4 parts of phosphotriester, 3 parts of lecithin, polyisobutene acid are sweet 24 parts of grease gel, 22 parts of methyltriethoxysilane, 36 parts of poly- isobutyl ester, 14 parts of aluminium hydroxide, 11 parts of antimony oxide, stone 2 parts of cotton fiber, 5 parts of azo dicarbonamide, 3 parts of benzoyl peroxide, 4 parts of antifoaming agent, 4 parts of fire retardant.
4. a kind of environment-friendlyactive active carbon decorative paint according to claim 1, it is characterised in that：By following parts by weight original Material composition：13 parts of activated carbon, 6 parts of concave convex rod clay powder, 5 parts of zeolite granular, 12 parts of white cement, 11 parts of gesso, white carbon 7 Part, 4 parts of calcium chloride, 8 parts of superfine silica gel powder, 6 parts of expanded perlite, 3 parts of nano silver-supported antibacterial powder, 5 parts of nano-titanium dioxide, burnt phosphorus 3 parts of sour sodium, 15 parts of vinyl acetate, 7 parts of isopropanol, 2 parts of vinyl chloride, 3 parts of phosphotriester, 2 parts of lecithin, polyisobutene acid glycerol 21 parts of gels, 20 parts of methyltriethoxysilane, 33 parts of poly- isobutyl ester, 12 parts of aluminium hydroxide, 10 parts of antimony oxide, asbestos 1.5 parts of fiber, 4 parts of azo dicarbonamide, 2 parts of benzoyl peroxide, 3 parts of antifoaming agent, 3 parts of fire retardant.
5. a kind of environment-friendlyactive active carbon decorative paint according to any one of claim 1 to 4, it is characterised in that：It is described The grain graininess of activated carbon is 0.095-0.235mm.
6. a kind of environment-friendlyactive active carbon decorative paint according to any one of claim 1 to 4, it is characterised in that：It is described Nano-titanium dioxide grain size is 50-60nm.
7. a kind of environment-friendlyactive active carbon decorative paint according to any one of claim 1 to 4, it is characterised in that：It is described Fire retardant is at least one of ammonium polyphosphate, zinc borate.
8. a kind of environment-friendlyactive active carbon decorative paint according to any one of claim 1 to 4, it is characterised in that：It is described Antifoaming agent is at least one of polyoxyethylene polyoxypropylene pentaerythrite ether, polyoxyethylene polyoxy propyl alcohol amidogen ether weight.
CN201810485959.7A 2018-05-21 2018-05-21 A kind of environment-friendlyactive active carbon decorative paint Withdrawn CN108659681A (en)