CN109486360A - A kind of aqueous one-component organic zinc-rich paint and its preparation method and application - Google Patents
A kind of aqueous one-component organic zinc-rich paint and its preparation method and application Download PDFInfo
- Publication number
- CN109486360A CN109486360A CN201811527080.0A CN201811527080A CN109486360A CN 109486360 A CN109486360 A CN 109486360A CN 201811527080 A CN201811527080 A CN 201811527080A CN 109486360 A CN109486360 A CN 109486360A
- Authority
- CN
- China
- Prior art keywords
- aqueous
- rich paint
- zinc
- component organic
- organic zinc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of aqueous one-component organic zinc-rich paint and its preparation method and application, the aqueous one-component organic zinc-rich paint includes 10 ~ 20 parts of water-base resin, modified 70 ~ 100 parts of zinc powder, 0.5 ~ 1 part of fumed silica, 5 ~ 8 parts of cosolvent, 0.9 ~ 2.5 part of auxiliary agent, 0.5 ~ 2 part of corrosion inhibiter;The modified zinc powder is corrosion-resistant modified zinc powder;The corrosion inhibiter is the combination solution of 2-[4-morpholinodithio sulfosuccinate and molybdate.The present invention is by selecting modified zinc powder and sulfur-bearing high-efficient corrosion inhibitor, collocation other components, aqueous one-component organic zinc-rich paint is successfully prepared, aqueous one-component organic zinc-rich paint obtained has good storage stability, construction convenient, and has good early stage corrosion resistance.
Description
Technical field
The present invention relates to organic zinc-rich paint technical fields, apply more particularly, to a kind of organic zinc-rich of aqueous one-component
Material and its preparation method and application.
Background technique
In heavy antisepsis field, aqueous double-component zinc-rich paint is widely used because of its excellent antiseptic property.Mesh
Before, it the use of most common aqueous double-component zinc-rich paint is double-component aqueous epoxy zinc-enriched paint, double-component aqueous epoxy zinc-rich
Coating is generally included by the component A that forms of part such as liquid epoxies, zinc powder, dispersing agent, anti-settling agent, solvent and aqueous solid
The B component of agent composition.Aqueous double-component zinc-rich paint needs two components to mix in the construction process, rapid construction, working life
Later, coating fails.The working life of aqueous double-component zinc-rich paint is shorter, is unfavorable for subsequent construction, improves the time of construction
It is required that increasing the difficulty of construction.
And aqueous one-component organic zinc-rich paint then can preferably solve being applicable in for aqueous double-component organic zinc-rich paint
Phase short problem.But the high activity of zinc powder limits application of the zinc powder in aqueous one-component coating.Common zinc powder can be with
Moisture reacts, and generates hydrogen, causes coating to be easy flatulence during storage, is unfavorable for single-component water-based zinc-rich paint
Storage stability.So current few aqueous one-component zinc-rich paint.
Moreover, in actual application, the early stage corrosion resistance of organic zinc-rich paint is an important index, need
It takes in.However, the early stage corrosion resistance of existing organic zinc-rich paint is insufficient, it is difficult to meet requirement.
Therefore, it is necessary to develop with good storage stability, the organic richness of one-component of good early stage corrosion resistance
Spelter coating.
Summary of the invention
The present invention be overcome aqueous double-component organic zinc-rich paint working life described in the above-mentioned prior art it is short, construction not
Just, the insufficient defect of the early stage corrosion resistance of one-component organic zinc-rich paint poor storage stability and organic zinc-rich paint, mentions
For a kind of aqueous one-component organic zinc-rich paint, the aqueous one-component organic zinc-rich paint provided has good stable storing
Property, construction it is convenient, and have good early stage corrosion resistance.
Another object of the present invention is to provide the preparation methods of above-mentioned aqueous one-component organic zinc-rich paint.
A further purpose of the present invention is to provide the application of above-mentioned aqueous one-component organic zinc-rich paint.
In order to solve the above technical problems, the technical solution adopted by the present invention is that:
A kind of aqueous one-component organic zinc-rich paint, including 10~20 parts of water-base resin, modified 70~100 parts of zinc powder, gas phase two
0.5~1 part of silica, 5~8 parts of cosolvent, 0.9~2.5 part of auxiliary agent, 0.5~2 part of corrosion inhibiter;
The modified zinc powder is corrosion-resistant modified zinc powder;
The corrosion inhibiter is the combination solution of 2-[4-morpholinodithio sulfosuccinate and molybdate.The molybdate can be conventional
Molybdate corrosion inhibiter, such as sodium molybdate, zinc molybdate.
Modifying agent in modified zinc powder can contact of the exclusion of water with zinc powder, delay reacting for zinc powder and water, be aqueous single group
The storage stability of part zinc-rich paint provides guarantee.There is fine and close clad on the surface of modified zinc powder, and coating storage stage can hinder
Sealing is directly contacted with zinc powder;After paint film is made, zinc powder is released, and plays the role of cathodic protection to metal base.On
Aqueous one-component organic zinc-rich paint is stated while keeping the strong corrosion resistant of current zinc-rich paint, greatly improves zinc-rich
The easy construction of coating.
Above-mentioned corrosion inhibiter is sulfur-bearing high-efficient corrosion inhibitor, which is generally 45% left side
The right side is free of sodium nitrite, and water resistance is good, can effectively slow down the corrosion of metal base, especially provide in early stage for zinc rich primer
Good rust quality.Inventor the study found that the sulfur-bearing high-efficient corrosion inhibitor on substrate by molecular layer adsorption and passivation,
The early stage corrosion resistance of zinc rich primer is greatly improved, inhibition efficiency is high, and will not cause the side effects such as blistering, migration surface, tool
There is good storage stability.
Early stage corrosion resistance refers to corrosion resistance of the coating that do not do solid work in corrosive environment.And simple zinc-rich coating
Because early stage is dry, not exclusively coating is not fine and close enough, and often water resistance is poor for corrosion inhibiter commonly used in the art, is easy blistering,
Or be easy to be precipitated, so corrosion inhibiter commonly used in the art is difficult to play the role of corrosion-resistant, lead to the early stage corrosion resistance of coating
It is poor.The corrosion inhibiter of this field routine is generally used for long-effective corrosion, ineffective for early stage corrosion-resistant.And the present invention is by adding
The sulfur-bearing high-efficient corrosion inhibitor added can play antisepsis in paint film early stage.
The present invention combines special sulfur-bearing high-efficient corrosion inhibitor and other components by selecting corrosion-resistant modified zinc powder, at
Function is prepared with good storage stability, construction is convenient and has the aqueous one-component of good early stage corrosion resistance
Organic zinc-rich paint.
Preferably, in the corrosion inhibiter, 2-[4-morpholinodithio sulfosuccinate and molybdate equimolar ratio are compounded, wherein molybdenum
The molar concentration of hydrochlorate is 0.09mol/L.
Preferably, the modified zinc powder is obtained by modifying agent cladding zinc powder, and the modifying agent is rare-earth modifier.
Preferably, the rare-earth modifier is lanthanum salt solution.
Preferably, the auxiliary agent includes wetting dispersing agent, anti-settling agent and defoaming agent.
Preferably, the aqueous one-component organic zinc-rich paint includes 10~20 parts of resin aqueous emulsion, modified zinc powder 70
~100 parts, 5~8 parts of cosolvent, 0.5~1 part of fumed silica, 0.5~1 part of wetting dispersing agent, anti-settling agent 0.5~1.5
Part, 0.1~0.5 part of defoaming agent, 0.5~2 part of corrosion inhibiter.
Preferably, the water-base resin is resin aqueous emulsion.
Preferably, the resin aqueous emulsion is aqueous polyurethane emulsion, watersoluble modified epoxy resin latex or aqueous third
One or more of olefin(e) acid lotion.The watersoluble modified epoxy resin latex is aqueous one-component epoxy resin latex.
Preferably, the cosolvent is one or more of propylene glycol monomethyl ether, dipropylene, propandiol butyl ether.
Preferably, the wetting dispersing agent is non-ionic polyalcohol dispersing agent.
Preferably, the wetting dispersing agent is Tech-6208.The Tech-6208 is the profound new ADDITOL VXW in the U.S.
6208。
Preferably, the anti-settling agent is bentonite.Bentonite, thixotropy is strong, prevents zinc powder from precipitating.
Preferably, the defoaming agent is organic silicon defoamer.Organic silicon defoamer defoaming and deaeration ability are strong.
The present invention protects the preparation method of above-mentioned aqueous one-component organic zinc-rich paint simultaneously, and the preparation method includes such as
Lower step:
Include the following steps:
S1. cosolvent, auxiliary agent, fumed silica are added in tank, high-speed stirred is uniformly mixed;
S2. continue that water-base resin is added into tank, moderate-speed mixer, be uniformly mixed;
S3. it is subsequently added into modified zinc powder, leads to cooling water, high-speed stirred makes zinc powder scatter;
S4. it is eventually adding corrosion inhibiter, moderate-speed mixer is uniformly mixed, then filters, sealed package.
Preferably, in step S1. and S3., high-speed stirred is to stir 10~20 minutes under 1500~2000r/min revolving speed.
Preferably, in step S2., moderate-speed mixer is to stir 5~10 minutes under 1000~1200r/min revolving speed.
Preferably, in step S4., moderate-speed mixer is to stir 15 minutes under 1000~1200r/min revolving speed.
Specifically, the preparation method includes the following steps:
S1. 5~8 parts of cosolvents, 0.5~1 part of wetting dispersing agent, 0.5~1.5 portion of anti-settling agent, 0.1~0.5 part are added in tank
Defoaming agent, 0.5~1 part of fumed silica, high speed (1500~2000r/min) stir 10~20 minutes;
S2. continue that 10~20 parts of aqueous one-component epoxy resin latexes are added into tank, middling speed (1000~1200r/min) stirring
It 5~10 minutes, is uniformly mixed;
S3. 70~100 parts of modified zinc powders are subsequently added into, cooling water is led to, high speed (1500~2000r/min) stirs 15~20 points
Clock makes zinc powder scatter, no precipitating and conglomeration;
S4. it is eventually adding 0.5~2 part of corrosion inhibiter, middling speed (1000~1200r/min) is stirred 15 minutes, then filtered, sealing packet
Dress.
The present invention also protects application of the above-mentioned aqueous one-component organic zinc-rich paint in iron matrix or steel matrix anti-corrosion.
Compared with prior art, the beneficial effects of the present invention are:
For the present invention by selecting corrosion-resistant modified zinc powder and sulfur-bearing high-efficient corrosion inhibitor, water is successfully prepared in other components of arranging in pairs or groups
Property one-component organic zinc-rich paint, aqueous one-component organic zinc-rich paint obtained have good storage stability, construction just
Victory, and there is good early stage corrosion resistance.
Specific embodiment
The present invention is further illustrated With reference to embodiment.
The equal cocoa of raw material in embodiment is by being commercially available;
Unless stated otherwise, the present invention uses reagent, method and apparatus is the art conventional reagents, method and apparatus.
The sulfur-bearing high-efficient corrosion inhibitor of embodiment by 2-[4-morpholinodithio sulfosuccinate and sodium molybdate equimolar ratio compounding and
At wherein the molar concentration of sodium molybdate is 0.09mol/L.
Embodiment 1
A kind of aqueous one-component organic zinc-rich paint, component are as follows:
15 parts of aqueous one-component epoxy resin latex, 6 parts of propylene glycol monomethyl ether, 1 part of bentonite, 0.5 part of Tech-6208 dispersing agent,
1 part of fumed silica, 80 parts of rare earth modified zinc powder, 0.3 part of organic silicon defoamer, 2 parts of sulfur-bearing high-efficient corrosion inhibitor, 10 parts of water.
Preparation method:
S1. 6 parts of propylene glycol monomethyl ethers, 0.3 part of wetting dispersing agent, 1 part of bentonite, 0.3 part of organic silicon defoamer, 1 are added in tank
Part fumed silica, part water, high speed (1500~2000r/min) stir 10~20 minutes;
S2. continue that 15 parts of aqueous epoxy emulsions are added into tank, middling speed (1000~1200r/min) stirs 5~10 minutes, mixing
Uniformly;
S3. 80 parts of modified zinc powders are subsequently added into, cooling water is led to, high speed (1500~2000r/min) stirs 15~20 minutes, makes zinc
Powder scatter, no precipitating and conglomeration;
S4. it is eventually adding 1 part of corrosion inhibiter and remaining water, middling speed (1000~1200r/min) is stirred 15 minutes, then filtered, close
Package dress.
Embodiment 2
A kind of aqueous one-component organic zinc-rich paint, component are as follows:
10 parts of aqueous one-component epoxy resin latex, 5 parts of propylene glycol monomethyl ether, 0.5 part of bentonite, Tech-6208 dispersing agent 0.5
Part, 0.5 part of fumed silica, 70 parts of rare earth modified zinc powder, 0.5 part of organic silicon defoamer, 1 part of sulfur-bearing high-efficient corrosion inhibitor, water
10 parts.
The step of preparation method, is same as Example 1.
Embodiment 3
A kind of aqueous one-component organic zinc-rich paint, component are as follows:
20 parts of aqueous one-component epoxy resin latex, 8 parts of propylene glycol monomethyl ether, 1.5 parts of bentonite, Tech-6208 dispersing agent 0.8
Part, 1 part of fumed silica, 100 parts of rare earth modified zinc powder, 0.1 part of organic silicon defoamer, 0.5 part of sulfur-bearing high-efficient corrosion inhibitor,
10 parts of water.
The step of preparation method, is same as Example 1.
Comparative example 1
This comparative example the difference from embodiment 1 is that, rare earth modified zinc powder is replaced using common zinc powder, additional amount is constant;
Other raw materials and step are same as Example 1.
Comparative example 2
This comparative example the difference from embodiment 1 is that, sulfur-bearing high-efficient corrosion inhibitor is replaced using common anti-flash rusting agent AMP-95, is added
It measures constant;AMP-95 is 2-amino-2-methyl-1-propanol;
Other raw materials and step are same as Example 1.
Comparative example 3
This comparative example the difference from embodiment 1 is that, the additional amount of sulfur-bearing high-efficient corrosion inhibitor is 0.25 part;
Other raw materials and step are same as Example 1.
Performance test
1. storage stability is tested
By the regulation of GB3186-82 " samplings of coating products ", representative sample is taken out, is fitted into the paint can that container is 0.3L, lid
Tight lid stores 7d under the conditions of normal temperature (50 ± 2) DEG C, checks its can opening state.
2. adhesive force is tested
By GB/T 9286-1998 standard testing.
3. impact resistance is tested
By GB/T 1732-1993 standard testing.
4. early stage corrosion resistance is tested
The template for being coated with paint film is toasted into 30min in 60 DEG C of baking ovens, then naturally cools to room temperature;Then by the sample after edge sealing
Plate is vacantly placed in 50 DEG C of warm water, is exposed to paint film in heated steam, sees whether to generate rust spot.
5. resistance to neutral salt spray test
It is taken out after the template for being coated with paint film is toasted 30min in 60 DEG C of baking ovens, natural cooling 7d, then by the template after edge sealing
It is placed in neutral salt spray test case, observation paint film variation.
Test result
The performance test results of Examples 1 to 3 and comparative example 1~3 are as shown in table 1.
The performance test results of 1 Examples 1 to 3 of table and comparative example 1~3
Within the scope of the claims, properties meet actual requirement to example 1~3, and early stage anti-corrosive properties and storage stability are good
It is good, and comparative example 1 uses common zinc powder, poor storage stability, comparative example 2 leads to zinc-rich paint only with general anti-flash rusting agent
Early stage rust-preventing characteristic it is poor, while anti-flash rusting agent is easy migration, also affects resistance to neutral salt spray performance, and comparative example 3 is because of sulfur-bearing
High-efficient corrosion inhibitor usage amount is inadequate, causes early stage Corrosion Protection bad, but does not influence resistance to neutral salt spray.
Obviously, the above embodiment of the present invention be only to clearly illustrate example of the present invention, and not be pair
The restriction of embodiments of the present invention.For those of ordinary skill in the art, may be used also on the basis of the above description
To make other variations or changes in different ways.There is no necessity and possibility to exhaust all the enbodiments.It is all this
Made any modifications, equivalent replacements, and improvements etc., should be included in the claims in the present invention within the spirit and principle of invention
Protection scope within.
Claims (10)
1. a kind of aqueous one-component organic zinc-rich paint, which is characterized in that including 10 ~ 35 parts of water-base resin, modification zinc powder 70 ~
100 parts, 0.5 ~ 1 part of fumed silica, 5 ~ 8 parts of cosolvent, 0.9 ~ 2.5 part of auxiliary agent, 0.5 ~ 2 part of corrosion inhibiter;
The modified zinc powder is corrosion-resistant modified zinc powder;
The corrosion inhibiter is the combination solution of 2-[4-morpholinodithio sulfosuccinate and molybdate.
2. aqueous one-component organic zinc-rich paint according to claim 1, which is characterized in that in the corrosion inhibiter, 2- benzene
And thiazole sulfosuccinate and molybdate equimolar ratio compound, wherein the molar concentration of molybdate is 0.09mol/L.
3. aqueous one-component organic zinc-rich paint according to claim 1, which is characterized in that the modified zinc powder is by being modified
Agent cladding zinc powder obtains, and the modifying agent is rare-earth modifier.
4. aqueous one-component organic zinc-rich paint according to claim 1, which is characterized in that the auxiliary agent includes wetting point
Powder, anti-settling agent and defoaming agent.
5. aqueous one-component organic zinc-rich paint according to claim 1, which is characterized in that the water-base resin is aqueous
Resin emulsion.
6. aqueous one-component organic zinc-rich paint according to claim 5, which is characterized in that the resin aqueous emulsion is
One or more of aqueous polyurethane emulsion, watersoluble modified epoxy resin latex or aqueous acrylic emulsion.
7. aqueous one-component organic zinc-rich paint according to claim 1, which is characterized in that the cosolvent is propylene glycol
One or more of methyl ether, dipropylene, propandiol butyl ether.
8. aqueous one-component organic zinc-rich paint according to claim 1, which is characterized in that the wetting dispersing agent is non-
Ionic polymeric dispersant.
9. the preparation method of any one of the claim 1 ~ 8 aqueous one-component organic zinc-rich paint, which is characterized in that including such as
Lower step:
S1. cosolvent, auxiliary agent, fumed silica are added in tank, high-speed stirred is uniformly mixed;
S2. continue that water-base resin is added into tank, moderate-speed mixer, be uniformly mixed;
S3. it is subsequently added into modified zinc powder, leads to cooling water, high-speed stirred makes zinc powder scatter;
S4. it is eventually adding corrosion inhibiter, moderate-speed mixer is uniformly mixed, then filters, sealed package.
10. any one of claim 1 ~ 8 aqueous one-component organic zinc-rich paint the answering in iron matrix or steel matrix anti-corrosion
With.