CN109483927A - A kind of moisture-proof phone housing manufacture craft - Google Patents
A kind of moisture-proof phone housing manufacture craft Download PDFInfo
- Publication number
- CN109483927A CN109483927A CN201811412109.0A CN201811412109A CN109483927A CN 109483927 A CN109483927 A CN 109483927A CN 201811412109 A CN201811412109 A CN 201811412109A CN 109483927 A CN109483927 A CN 109483927A
- Authority
- CN
- China
- Prior art keywords
- grams
- manufacture craft
- moisture
- proof
- vinyl chloride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of moisture-proof phone housing manufacture craft, formula includes olefin polymer, vinyl chloride tree and fireproofed paper, and the olefin polymer is the first covering surface, and second covering surface is vinyl chloride resin, and the third level is fireproofed paper;Its manufacture craft is the following steps are included: using common painting dyeing method, using brush brushing, roll-type applies dye device and paints, then the heat drying in 150 DEG C of heating furnaces, and foaming agent is added in the composition, it is coated on first coating with one vinyl chloride copolymer solvent of surface treating agent acrylate, then the vinyl chloride resin constituent for screen printer or print intaglio press the print coating liquid that can print predetermined pattern is utilized, and it is heated in 200 DEG C of heating furnace, foaming, pattern layer weight per cm is 40-100 grams, and antimony trichloride is added in papermaking, using being pasted on mobile phone for scraps of paper material, can effectively provide fire prevention and it is moisture-proof, and the material production of the scraps of paper can reduce the weight of mobile phone, and it can be convenient for changing at any time, better visual effect can be provided.
Description
Technical field
A kind of fire-proof and damp-proof manufacture craft especially designs a kind of moisture-proof phone housing manufacture craft.
Background technique
Common mobile phone shell can make mobile phone appearance more and more beautiful, and more and more mobile phone shells are with various
Function, but the heat dissipation of existing mobile phone shell is difficult, and is easy to produce mobile phone overheat, causes dangerous and excessively moist in region
Place, dampness and infiltration, keep its service life too short, do not give mobile phone maximum meating and use.
Summary of the invention
The purpose of the present invention is to provide a kind of moisture-proof phone housing manufacture crafts, and overall structure is simple, at low cost, application
Range is wide, practical.
In order to achieve the above object, the invention provides the following technical scheme:
A kind of moisture-proof phone housing manufacture craft, formula include olefin polymer, vinyl chloride tree and fireproofed paper, feature
Be: the olefin polymer is the first covering surface, and second covering surface is vinyl chloride resin, the third level
For fireproofed paper;Its manufacture craft the following steps are included:
S1: using common painting dyeing method, and using brush brushing, roll-type applies dye device and paints, and then heats at 150 DEG C
Heat drying in furnace, and foaming agent is added in the composition, form alkene froth bed;
One vinyl chloride copolymer solvent of surface treating agent acrylate is coated on S2: the first covering surface, then utilization can print
The vinyl chloride resin constituent of screen printer or print intaglio press the print coating liquid of predetermined pattern processed, and at 200 DEG C
It heats, foams in heating furnace, pattern layer weight per cm is 40-100 grams, and adds antimony trichloride in papermaking.
Preferably, the material composition of the olefin polymer are as follows: 20 grams of vinyl monomer polymerization object, sticks 30 grams of calcium carbonate
Native 40 grams, 10 grams of titanium oxide, and 20 grams of foaming agent are added with, which is azo
Two 10 grams of ureas, 10 grams of ten pentamethylene of dinitro, four ammonium, 10 grams and 20 grams of sodium bicarbonate of two benzene sulfonyl hydrazide of P-P oxygen.
Preferably, Corvic addition dioctyl phthalate and two urea of azo, fire resisting plasticizer, nothing
Machine additive, stabilizer, fireproof agent.
Preferably, the fire resisting plasticizer is silicon carbide.
Preferably, the stabilizer is carboxylic esterification polyvinyl alcohol.
Preferably, the fireproofed paper composition is paper pulp and antimony trichloride.
Present invention employs composite materials to be made, and using being pasted on mobile phone for scraps of paper material, can effectively provide
It prevents fires and moisture-proof, and the material production of the scraps of paper can reduce the weight of mobile phone, and can be convenient for changing at any time, can mention
For better visual effect.
Specific embodiment
Embodiments of the present invention will be described for preferred embodiment below.
A kind of moisture-proof phone housing manufacture craft, formula includes olefin polymer, vinyl chloride tree and fireproofed paper, described
Olefin polymer is the first covering surface, and ingredient is as follows: every square metre of weight is 80 to 270 grams, and second covering surface is
Vinyl chloride resin, the third level be fireproofed paper, manufacture craft the following steps are included:
S1: using common painting dyeing method, and using brush brushing, roll-type applies dye device and paints, and then heats at 150 DEG C
Heat drying in furnace, and foaming agent is added in the composition, form alkene froth bed;
One vinyl chloride copolymer solvent of surface treating agent acrylate is coated on S2: the first covering surface, then utilization can print
The vinyl chloride resin constituent of screen printer or print intaglio press the print coating liquid of predetermined pattern processed, and at 200 DEG C
It heats, foams in heating furnace, pattern layer weight per cm is 40-100 grams, and adds antimony trichloride in papermaking.
The material of the olefin polymer forms are as follows: 20 grams of vinyl monomer polymerization object, 30 grams of calcium carbonate, 40 grams of clay,
10 grams of titanium oxide and the above are additives, and 20 grams of foaming agent are added with, which is 10 grams of two urea of azo, dinitro
10 grams of ten pentamethylene of base, four ammonium, 10 grams and 20 grams of sodium bicarbonate of two benzene sulfonyl hydrazide of P-P oxygen.
Two urea of azo of 50 grams of dioctyl phthalates with 3-15 grams is added in every 100 grams of Corvic, and is added
Add 10 grams of fire resisting plasticizer, 15 grams of inorganic additive, 10 grams of stabilizer, 5 grams of fireproof agent.
The fireproofed paper composition is paper pulp 70% and antimony trichloride 30%.
Its manufacture craft the following steps are included:
Using common painting dyeing method, using brush brushing, roll-type applies dye device and paints, then in 150 DEG C of heating furnaces
Middle heat drying, and foaming agent is added in the composition, form alkene froth bed.It coats on first coating with surface treating agent
Then one vinyl chloride copolymer solvent of acrylate utilizes the screen printer or print intaglio press that can print predetermined pattern
The vinyl chloride resin constituent of coating liquid is printed, and is heated in 200 DEG C of heating furnace, is foamed, pattern layer weight per cm is
40-100 grams.
Fireproofed paper utilizes medium paper pulp, and the fire prevention such as antimony trichloride is added in papermaking.
Present invention employs composite materials to be made, and using being pasted on mobile phone for scraps of paper material, can effectively provide
It prevents fires and moisture-proof, and the material production of the scraps of paper can reduce the weight of mobile phone, and can be convenient for changing at any time, can mention
For better visual effect.
It, for the ordinary skill in the art, can be with although having shown and having described the embodiment of the present invention
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And deformation, the scope of the present invention is defined by the appended.
Claims (6)
1. a kind of moisture-proof phone housing manufacture craft, formula includes that olefin polymer, vinyl chloride tree and fireproofed paper, feature exist
In: the olefin polymer is the first covering surface, and second covering surface is vinyl chloride resin, and the third level is
Fireproofed paper;Its manufacture craft the following steps are included:
S1: using common painting dyeing method, and using brush brushing, roll-type applies dye device and paints, then in 150 DEG C of heating furnaces
Heat drying, and foaming agent is added in the composition, form alkene froth bed;
One vinyl chloride copolymer solvent of surface treating agent acrylate is coated on S2: the first covering surface, then utilization can print rule
Determine the screen printer of pattern or the vinyl chloride resin constituent of print intaglio press print coating liquid, and in 200 DEG C of heating
It heats, foams in furnace, pattern layer weight per cm is 40-100 grams, and adds antimony trichloride in papermaking.
2. a kind of moisture-proof phone housing manufacture craft according to claim 1, it is characterised in that: the olefin polymer
Material composition are as follows: 20 grams of vinyl monomer polymerization object, 30 grams of calcium carbonate, 40 grams of clay, 10 grams of titanium oxide, and be added with foaming agent
20 grams, which is 10 grams of two urea of azo, 10 grams of ten pentamethylene of dinitro, four ammonium, 10 grams of two benzene sulfonyl hydrazide of P-P oxygen
With 20 grams of sodium bicarbonate.
3. a kind of moisture-proof phone housing manufacture craft according to claim 1, it is characterised in that: the polyvinyl chloride tree
Rouge adds dioctyl phthalate and two urea of azo, fire resisting plasticizer, inorganic additive, stabilizer, fireproof agent.
4. a kind of moisture-proof phone housing manufacture craft according to claim 3, it is characterised in that: the fire resisting plasticizer
For silicon carbide.
5. a kind of moisture-proof phone housing manufacture craft according to claim 3, it is characterised in that: the stabilizer is carboxylic
Esterification polyvinyl alcohol.
6. fire-proof and damp-proof according to claim 1 pastes phone housing manufacture craft, it is characterised in that: the fireproofed paper at
Part is paper pulp and antimony trichloride.