CN109483773A - A kind of polyvinyl chloride resin die processing method - Google Patents
A kind of polyvinyl chloride resin die processing method Download PDFInfo
- Publication number
- CN109483773A CN109483773A CN201811135901.6A CN201811135901A CN109483773A CN 109483773 A CN109483773 A CN 109483773A CN 201811135901 A CN201811135901 A CN 201811135901A CN 109483773 A CN109483773 A CN 109483773A
- Authority
- CN
- China
- Prior art keywords
- baking
- bed die
- laid
- polyvinyl chloride
- time
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of polyvinyl chloride resin die processing method, A, raw material mixing: polyvinyl chloride suspended particulate resin-oatmeal, PVC paste resin powder, dibutylester are mixed;B, it makes bed die: being laid with three layers of fiber filament in die surface, brush a calcium plaster before being laid with fiber filament every time;C, bed die baking, brushing: the bed die made is toasted for the first time, and the raw material slurry that one layer of step A is mixed up uniformly is brushed on bed die surface baked for the first time, and bed die carries out secondary baking, carries out secondary brushing after secondary baking after brushing;It repeats baking, brush 3-4 times;D, make glass fibre reinforced plastics casing: last baking after bed die on smear stabilizer, then be laid with layer of glass cloth, repeat smear stabilizer, be laid with glass fabric 4-5 times, obtain glass fibre reinforced plastics casing, high-temperature resin mold put on the shell to get.The mold features sense that the present invention makes was good, and energy angle is good, and demoulding is fast, and die life is long, up to 3 years or more.
Description
Technical field
The present invention relates to resin die processing technique fields, and in particular to a kind of polyvinyl chloride resin die processing method.
Background technique
Existing mold is to make mold with cement, and raw material are: cement, sand, glass fabric, 6 round bars.This raw material
The mold made is not only thick but also again, change into finished product will also brush release agent can take off, and the product poured out is rough, and trachoma is more, product
The lines sense taken off is poor, and energy differential seat angle, demoulding is slow, and the service life of mold can only be used 7 months or so.
Summary of the invention
The purpose of the present invention is to provide a kind of polyvinyl chloride resin die processing method, this method not only process it is simple,
It is suitble to industrial application, and the mold features sense made is good, energy angle was good, and demoulding is fast, and die life is long, up to 3 years or more.
In order to achieve the above objectives, the technical solution of the present invention is as follows:
Polyvinyl chloride resin die processing method of the invention, comprising the following steps:
A, raw material mixes: weigh 0.5-2 parts of polyvinyl chloride suspended particulate resin-oatmeal, 0.5-2 parts of PVC paste resin powder, and two
It 2-5 parts of fourth rouge, pours into container and is mixed, stirred evenly, it is spare;
B, it makes bed die: being laid with three layers of fiber filament in die surface, be laid with before fiber filament every time, uniformly brush a gypsum
Slurry can demould after standing 30-50min;
C, the bed die made bed die baking, brushing: is carried out first time baking, baking time 15- at 130-170 DEG C
20min;The raw material slurry that one layer of step A is mixed up uniformly is brushed on bed die surface baked for the first time, with each position in bed die surface
Being coated onto is advisable;Bed die carries out secondary baking after brushing, baking temperature is 400-500 DEG C, baking time 8-15min;It is secondary
Secondary brushing is carried out after baking, secondary brushing is with a thickness of 1.5-2.5mm;It repeats baking, brush 3-4 times;Last baking temperature
Degree is 250-350 DEG C, baking time 8-15min;
D, it makes glass fibre reinforced plastics casing: smearing stabilizer on the bed die after last baking, be then laid with layer of glass cloth, weight
Overcoating is smeared stabilizer, is laid with glass fabric 4-5 times, obtains glass fibre reinforced plastics casing, the high-temperature resin mold taken off is put on the shell,
To obtain the final product.
Further, in the step B, calcium plaster is mixed by gypsum and water according to the weight ratio of 2:1.
Further, in the step B, bed die is with a thickness of 2-3cm.
Further, the stabilizer is obtained by mixing by 191 resins, p-hydroxybenzenyl sulfonate and tetramethyl thiourea.
The invention has the benefit that
The resistance to drawing of the mold that the present invention makes, durable, good toughness, the product poured out is smooth, bright, resin die long service life,
Up to 3 years or more.
Specific embodiment
The present invention is described further with reference to embodiments.
Embodiment 1
Polyvinyl chloride resin die processing method of the invention, comprising the following steps:
A, raw material mixes: weighing polyvinyl chloride suspended particulate resin-oatmeal 0.5kg, PVC paste resin powder 0.5kg, dibutylester
2kg is poured into container and is mixed, and is stirred evenly, spare;
B, it makes bed die: being laid with three layers of fiber filament in die surface, be laid with before fiber filament every time, uniformly brush a gypsum
Slurry can demould after standing 30min;
C, the bed die made bed die baking, brushing: is carried out first time baking, baking time 15min at 130 DEG C;?
The raw material slurry that one layer of step A mix up uniformly is brushed on bed die surface baked for the first time, with each position in bed die surface be coated onto for
Preferably;Bed die carries out secondary baking after brushing, baking temperature is 400 DEG C, baking time 8min;Two are carried out after secondary baking
Secondary brushing, secondary brushing is with a thickness of 1.5mm;It repeats baking, brush 3 times;Last baking temperature is 250 DEG C, and baking time is
8min;
D, it makes glass fibre reinforced plastics casing: smearing stabilizer on the bed die after last baking, be then laid with layer of glass cloth, weight
Overcoating is smeared stabilizer, is laid with glass fabric 4 times, obtains glass fibre reinforced plastics casing, the high-temperature resin mold taken off is put on the shell, i.e.,
?.
In the step B, calcium plaster is mixed by gypsum and water according to the weight ratio of 2:1.
In the step B, bed die is with a thickness of 2cm.
The stabilizer is obtained by mixing by 191 resins, p-hydroxybenzenyl sulfonate and tetramethyl thiourea.
Embodiment 2
Polyvinyl chloride resin die processing method of the invention, comprising the following steps:
A, raw material mixes: polyvinyl chloride suspended particulate resin-oatmeal 1kg, PVC paste resin powder 1kg, dibutylester 3kg are weighed,
It pours into container and is mixed, stirred evenly, it is spare;
B, it makes bed die: being laid with three layers of fiber filament in die surface, be laid with before fiber filament every time, uniformly brush a gypsum
Slurry can demould after standing 40min;
C, the bed die made bed die baking, brushing: is carried out first time baking, baking time 18min at 150 DEG C;?
The raw material slurry that one layer of step A mix up uniformly is brushed on bed die surface baked for the first time, with each position in bed die surface be coated onto for
Preferably;Bed die carries out secondary baking after brushing, baking temperature is 450 DEG C, baking time 12min;It is carried out after secondary baking
Secondary brushing, secondary brushing is with a thickness of 2mm;It repeats baking, brush 3 times;Last baking temperature is 300 DEG C, and baking time is
12min;
D, it makes glass fibre reinforced plastics casing: smearing stabilizer on the bed die after last baking, be then laid with layer of glass cloth, weight
Overcoating is smeared stabilizer, is laid with glass fabric 5 times, obtains glass fibre reinforced plastics casing, the high-temperature resin mold taken off is put on the shell, i.e.,
?.
In the step B, calcium plaster is mixed by gypsum and water according to the weight ratio of 2:1.
In the step B, bed die is with a thickness of 2.5cm.
The stabilizer is obtained by mixing by 191 resins, p-hydroxybenzenyl sulfonate and tetramethyl thiourea.
Embodiment 3
Polyvinyl chloride resin die processing method of the invention, comprising the following steps:
A, raw material mixes: polyvinyl chloride suspended particulate resin-oatmeal 2kg, PVC paste resin powder 2kg, dibutylester 5kg are weighed,
It pours into container and is mixed, stirred evenly, it is spare;
B, it makes bed die: being laid with three layers of fiber filament in die surface, be laid with before fiber filament every time, uniformly brush a gypsum
Slurry can demould after standing 50min;
C, the bed die made bed die baking, brushing: is carried out first time baking, baking time 20min at 170 DEG C;?
The raw material slurry that one layer of step A mix up uniformly is brushed on bed die surface baked for the first time, with each position in bed die surface be coated onto for
Preferably;Bed die carries out secondary baking after brushing, baking temperature is 500 DEG C, baking time 15min;It is carried out after secondary baking
Secondary brushing, secondary brushing is with a thickness of 2.5mm;It repeats baking, apply 3-4 times;Last baking temperature is 350 DEG C, and baking time is
15min;
D, it makes glass fibre reinforced plastics casing: smearing stabilizer on the bed die after last baking, be then laid with layer of glass cloth, weight
Overcoating is smeared stabilizer, is laid with glass fabric 5 times, obtains glass fibre reinforced plastics casing, the high-temperature resin mold taken off is put on the shell, i.e.,
?.
In the step B, calcium plaster is mixed by gypsum and water according to the weight ratio of 2:1.
In the step B, bed die is with a thickness of 3cm.
The stabilizer is obtained by mixing by 191 resins, p-hydroxybenzenyl sulfonate and tetramethyl thiourea.
Claims (4)
1. a kind of polyvinyl chloride resin die processing method, which comprises the following steps:
A, raw material mixes: weigh 0.5-2 parts of polyvinyl chloride suspended particulate resin-oatmeal, 0.5-2 parts of PVC paste resin powder, and two
It 2-5 parts of fourth rouge, pours into container and is mixed, stirred evenly, it is spare;
B, it makes bed die: being laid with three layers of fiber filament in die surface, be laid with before fiber filament every time, uniformly brush a gypsum
Slurry can demould after standing 30-50min;
C, the bed die made bed die baking, brushing: is carried out first time baking, baking time 15- at 130-170 DEG C
20min;The raw material slurry that one layer of step A is mixed up uniformly is brushed on bed die surface baked for the first time, with each position in bed die surface
Being coated onto is advisable;Bed die carries out secondary baking after brushing, baking temperature is 400-500 DEG C, baking time 8-15min;It is secondary
Secondary brushing is carried out after baking, secondary brushing is with a thickness of 1.5-2.5mm;It repeats baking, brush 3-4 times;Last baking temperature
Degree is 250-350 DEG C, baking time 8-15min;
D, it makes glass fibre reinforced plastics casing: smearing stabilizer on the bed die after last baking, be then laid with layer of glass cloth, weight
Overcoating is smeared stabilizer, is laid with glass fabric 4-5 times, obtains glass fibre reinforced plastics casing, the high-temperature resin mold taken off is put on the shell,
To obtain the final product.
2. polyvinyl chloride resin die processing method according to claim 1, it is characterised in that: in the step B, stone
Cream slurry is mixed by gypsum and water according to the weight ratio of 2:1.
3. polyvinyl chloride resin die processing method according to claim 1, it is characterised in that: in the step B, bottom
Mould is with a thickness of 2-3cm.
4. polyvinyl chloride resin die processing method according to claim 1, it is characterised in that: the stabilizer by
191 resins, p-hydroxybenzenyl sulfonate and tetramethyl thiourea are obtained by mixing.