CN109467855A - A kind of fluorubber of high temperature and pressure contracting ratio - Google Patents
A kind of fluorubber of high temperature and pressure contracting ratio Download PDFInfo
- Publication number
- CN109467855A CN109467855A CN201811342367.6A CN201811342367A CN109467855A CN 109467855 A CN109467855 A CN 109467855A CN 201811342367 A CN201811342367 A CN 201811342367A CN 109467855 A CN109467855 A CN 109467855A
- Authority
- CN
- China
- Prior art keywords
- fluorubber
- high temperature
- pressure contracting
- contracting ratio
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fluorubber of high temperature and pressure contracting ratio, according to parts by weight, the fluorubber is mainly process by 100 parts of crude fluororubber, 1~10 part of magnesia, 2~15 parts of highly basic, 0.5~6 part of vulcanizing agent, 1~10 part of multifunctional assistant LCA, 0.5~15 part of silicone oligomer, 1~6 part of processing aid, 0.2~2 part of promotor, 0~50 part of filler.The present invention increases the selection kind and type of raw material using being not limited to the highly basic of calcium hydroxide and be not limited to the vulcanizing agent of bisphenols, can be more flexible in production obtain extensive material source.It has selected LCA to improve the assembled scheme of not Concentrative crosslinking, has changed the performance of high temperature compressed cracking resistance.- 40 DEG C of black brittleness excellent properties below have been easily achieved using silicone oligomer.The mode of simple production process, realization is flexible, high-efficient, and low energy consumption, at low cost.
Description
Technical field
The present invention relates to a kind of fluorubber of high temperature and pressure contracting ratio, belong to technical field of rubber material.
Background technique
Fluorubber refers to the macromolecular elastomer that fluorine atom is connected on the carbon atom of molecular backbone or side chain.In fluorubber point
In minor structure, greatly, and fluorine atom covalent radius (0.064nm) is equivalent to C-C key key to the bond energy (435~485kJ/mol) of C-F key
Long half, C-C segment are protected well by fluorine atom, and therefore, fluorubber has the chemical stability of height and heat steady
It is qualitative, it is one kind that medium-resistance is best in current all elastic body, can be widely used for aerospace, automobile, machinery, petrochemical industry
Deng.
The high-temperature brake hose of usual automobile inflator pump connection needs high temperature resistant to 200 DEG C and -40 DEG C of low temperature, while wanting resistance to
Compressor oil and a small amount of water, vapor, and withstand 1.5MPa long-time service pressure below.Since automobile is in various complexity
Road conditions downward driving, the vibration of different frequency occurs, so hose needs very strong shock resistance.Generally also have using stainless steel
Bellows, ethylene propylene diene rubber braided steel wire pipe, polytetrafluoroethylene (PTFE) ripple steel wire woven tube etc.;But corrugated stainless steel tubing connects
Head weld is too thin, and under high-frequency vibration, solder joint is easy to crack, and accident rate is very high;The resistance to height of ethylene propylene diene rubber woven tube
Temperature is excessively poor, can only be to 150 DEG C, and compression resistant machine oil is excessively poor, so being easy to aging embrittlement in;Polytetrafluoroethylene (PTFE)
Ripple woven tube is since creep is very big, and especially high-temerature creep is more severe, so just will appear leakage after a period of use very
To the situation of de- head.
The automobile-used high temperature fluorubber air-brake coupling hose of Zhejiang iron-clad horses tubulation Co., Ltd application, the patent No. 200420036301.1
In, using fluorubber inner tube, outer volume steel wire by cutting ferrule, connector, is formed connected nut, and cutting ferrule and connector are connected in a manner of pressure by clamping
It connects.The technology uses general fluorubber, and hot tear crack is poor under high temperature;Simultaneously as being connected using pincers pressure mode, connect at high temperature
The fluororubber layer at the place of connecing is easy cracking and even falls off, and accident rate is very high, and safety is poor.
The fluorine rubber braking hose for vehicle use and its production technology of Zhejiang iron-clad horses tubulation Co., Ltd application, the patent No.
In 200410030386.7, magnesia, calcium hydroxide, carbon black, vulcanizing agent are equipped with using the raw rubber of vinylidene and hexafluoropropene
It is realized Deng the techniques such as steel core, primary and secondary vulcanization, customized cut-off are placed by mixing, slice, extrusion.It must be in the technology
Steel core is put in pipe, there are operating difficulties, tube lengths to be limited, and scraps the defects such as high, stress levels are low, and not to the pipe
Connection type is explained, if using pincers pressure etc. mechanical compression mode, the material there are under high temperature compression cracking and it is low temperature resistant
The problem of being not achieved 40 DEG C, it is difficult to guarantee that automobile high-temperature brake is flexible coupling using safe.
Summary of the invention
In view of the deficiencies of the prior art, the purpose of the present invention is by being added one in selecting wider fluorubber kind
Kind or a variety of vulcanizing agents for being not limited to bisphenols, and be added necessary to LCA, silicone oligomer and vulcanizable fluororubber and inhale
The processing aids such as sour agent, organic wax obtain high temperature and pressure contracting by general rubber processing and compare fluorubber.
The technical proposal for solving the technical problem of the invention is: a kind of fluorubber of high temperature and pressure contracting ratio, the fluorine
Rubber mainly by crude fluororubber, magnesia, highly basic, vulcanizing agent, promotor, multifunctional assistant LCA, silicone oligomer, plus
Work auxiliary agent, filler are process;
The content of each component, in parts by weight are as follows:
100 parts of crude fluororubber
1~10 part of magnesia
0.5~15 part of highly basic
1~6 part of processing aid
0.5~6 part of vulcanizing agent
0.2~2 part of promotor
0~50 part of filler
1~10 part of multifunctional assistant LCA
0.5~15 part of silicone oligomer.
Further, the content of each component, in parts by weight are as follows:
100 parts of crude fluororubber
2~10 parts of magnesia
2~10 parts of highly basic
1~4 part of processing aid
1~3 part of vulcanizing agent
0.2~1 part of promotor
1~30 part of filler
1~6 part of multifunctional assistant LCA;
1~10 part of silicone oligomer.
Further, the crude fluororubber includes three to be polymerized by vinylidene, tetrafluoroethene, perfluoropropene
First fluorubber, or the binary fluorine rubber being polymerized by vinylidene, perfluoropropene.
Further, the vulcanizing agent can be the group of bisphenols, phenol amine, one kind in amine curing agents or multiclass
It closes, is also possible to the combination of the vulcanizing agent of multiple and different structures in similar vulcanizing agent.
Further, the vulcanizing agent is phenol amine curing agents, and the phenol amine curing agents is to contain at least one
The compound of phenolic hydroxyl group and at least one amino;The phenol amine curing agents includes single phenol monoamine vulcanizing agent, polyphenol amine
The combination of vulcanizing agent, polyamines phenolic curative, one or more of them in the more amine curing agents of polyphenol.
Further, the phenol amine curing agents is preferred are as follows: to (1- aminohexane base) phenol, 5- amino -1,3-
Benzenediol, 6- amino -1,3,5- benzenetriol, 4- ethylamino -1,3- benzenediol, 5- ethylamino -1,3- benzenediol, 4- ethylamino -
Bis- (- 4 hydroxy benzenes of 3- amino of 1,3,5- benzenetriol, diaminophenol, 2,4- diaminophenol, 2,5- diaminophenol, 2,2-
Base)-hexafluoropropane, three (3,5- di-t-butyl -4- acrinyl) isocyanuric acid esters.
Further, the highly basic includes calcium hydroxide, hydrated sodium silicate+sodium metasilicate, hydrated sodium silicate+(inclined) aluminic acid
One of sodium, sodium metaaluminate or a variety of combinations.
Further, the hydrated sodium silicate+sodium metasilicate is by any combination water content of a water to nine water
The combination of the hydrated sodium silicate and sodium metasilicate of one of hydrated sodium silicate or a variety of combination water contents;The hydrated sodium silicate+
(inclined) sodium aluminate is by one of water to the hydrated sodium silicate of any combination water content of nine water or a variety of combination water
The combination of the hydrated sodium silicate of content and (inclined) sodium aluminate.
Further, in the hydrated sodium silicate+sodium metasilicate, the mass content of sodium metasilicate is not less than 5%;Described
In hydrated sodium silicate+(inclined) sodium aluminate, the mass content of (inclined) sodium aluminate is not less than 5%.
Further, the silicone oligomer refers to silanol class or silicone hydroxyl quasi-oligomer containing hydro carbons group
One of or a variety of combinations, the hydro carbons group include and be not limited to methyl, phenyl, ethyl, isopropyl;Described has
The molecular weight of machine silicon oligomer is within 50000;The form of the silicone oligomer can be liquid or solid-state.
Further, the processing aid be lubricity class release agent, including and be not limited to organic wax, palm wax,
One of ws280, Rhein 54, Rhein 25, Mo get Li 935P or a variety of combinations.
Further, the filler is compatibilization or reinforcing filler, including and is not limited to carbon black, diatomite, silicic acid
Calcium, tripoli, one of barium sulfate or a variety of combinations.
The fluorubber of above-mentioned high temperature and pressure contracting ratio is processed using general purpose rubber processing technology.The specific method is as follows: fluorubber
Raw rubber plasticates 1 in mixer~after five minutes, other raw materials are put into together, mixing is to after 80~120 degree, on a mill
Thin pass-out piece is cooling, after parking curing 24 hours or more, Bao Tong 3~8 times, and slice cooling packing.
The beneficial effects of the present invention are: compared with prior art, the present invention passes through fluorubber (vinylidene and tetrafluoro second
The binary fluorine rubber of alkene, the ternary fluororubber of hexafluoropropene monomer polymerization or vinylidene and hexafluoropropene polymerization) it replaces now
Some binary fluorine rubbers increase former material using being not limited to the highly basic of calcium hydroxide and be not limited to the vulcanizing agent of bisphenols
The selection kind and type of material, can be more flexible in production obtain extensive material source.LCA raising has been selected not concentrate friendship
The assembled scheme of connection changes the performance of high temperature compressed cracking resistance.Black brittleness-has been easily achieved using silicone oligomer
40 DEG C of excellent properties below.The mode of simple production process, realization is flexible, high-efficient, and low energy consumption, at low cost.
In the present invention, the highly basic of use is not limited to calcium hydroxide, more preferably hydrated sodium silicate+sodium metasilicate, hydration
Sodium metasilicate+(inclined) sodium aluminate and sodium metaaluminate, and above-mentioned highly basic can select one or several be applied in combination.Using no calcium
Vulcanizing system can greatly improve the physical mechanical property of fluorubber, especially elongation percentage and resilience, guarantee fluorubber product
Anti-cracking performance under high temperature environment, avoids that the tearing of traditional calcic vulcanizing system high temperature is poor, high compression is easy to crack well
The shortcomings that.
In the present invention, the vulcanizing agent of use is also not limited to bisphenols, amine curing agents, and more preferably phenol amine vulcanizes
Agent has hot tear crack performance more better than bis-phenol vulcanizing system, it is therefore prevented that Local Cracking caused by high speed is worn away, while also having
Compression set performance more better than amine curing agents, ensure that the longer service life of product.
Preferred phenol amine curing agents and hydrated sodium silicate or calcium hydroxide+sodium metaaluminate system, make fluorine rubber in the present invention
Hydrofluoric acid and hydrated sodium silicate or the sodium metaaluminate reaction generated in glue sulfidation, generates sodium fluoride, calcirm-fluoride and hydration two
Silica or hydrated alumina generate extra water and are oxidized magnesium absorption again, generate magnesium hydroxide;Without low point in whole process
Son be precipitated, ensure that product zero defect is not blistering, at the same hydrated SiO 2 or hydrated alumina in chemical reaction process from
It so is dispersed in fluorubber with nano shape in situ, this highly active band enriches the inorganic nano material and fluorine of hydroxyl
Rubber and its filler have stronger intermolecular force, play the role of in-situ reinforcement, improve the intensity of fluorubber and return
Elasticity, and then the hot tear crack and cracking resistance effect of fluorubber are improved to a certain extent.
Specific embodiment
Below with reference to embodiment, the invention will be further described.
Embodiment 1
A kind of fluorubber of high temperature and pressure contracting ratio, wherein the content of each component in the fluorubber, in parts by weight are as follows:
100 parts of binary fluorine rubber raw rubber F26
5 parts of acid absorbent (magnesia)
6 parts of calcium hydroxide
1 part of organic wax
2.5 parts of benzenediol of 2- amino -1,3-
0.4 part of promotor (bpp)
30 parts of filler (carbon black N990)
3 parts of LCA
The Changzhou phenyl polysiloxane PFS-8568(Chang Jihua work) 5 parts
It is prepared by 30 times of materials of above-mentioned fluorubber each component, the method is as follows:
Crude fluororubber is plasticated 3 minutes in mixer, and put into every other powder (can put into) mixing to 80~120 degree twice
Afterwards, thin pass-out piece is cooling on a mill, after parking curing 24 hours or more, Bao Tong 3~8 times, out thickness 8mm, 50mm's wide
Adhesive tape.
Embodiment 2
A kind of fluorubber of high temperature and pressure contracting ratio, calcium hydroxide changes SODIUM METASILICATE PENTAHYDRATE and inclined aluminium into each component of the fluorubber
Sour sodium (1:1 in mass ratio), 5.5 parts of dosage, 2- amino-Resorcinol changes 2 parts of bisphenol S into, and filler changes calcium silicates 35 into
Part, remaining component and preparation method are the same as embodiment 1.
Embodiment 3
A kind of fluorubber of high temperature and pressure contracting ratio, calcium hydroxide changes sodium metasilicate+nine water silicons acid into each component of the fluorubber
Sodium+sodium metaaluminate (1:1:1 in mass ratio), 6.5 parts of dosage, 2- amino-Resorcinol changes N, N- dicinnamylidene -1,6- into
Hexamethylene diamine, 2.8 parts of dosage, filler changes barium sulfate into, and 45 parts of dosage, organic wax changes palm wax into, and 1.2 parts of dosage, remaining component
With preparation method with embodiment 1.
Embodiment 4
A kind of fluorubber of high temperature and pressure contracting ratio, calcium hydroxide changes calcium hydroxide and meta-aluminic acid into each component of the fluorubber
2.5 parts of dosage of sodium (1:1 in mass ratio), 2- amino-Resorcinol change bis- (- 4 hydroxy phenyl of 3- the amino)-hexafluoros of 2,2- into
Propane, 2.5 parts of dosage, filler changes tripoli into, and 35 parts of dosage, organic wax changes Rhein 54 into, and dosage is constant, remaining component and preparation
Method is the same as embodiment 1.
Embodiment 5
A kind of fluorubber of high temperature and pressure contracting ratio, binary fluorine rubber raw rubber F26 changes F246, sulphur into each component of the fluorubber
Agent 2- amino-Resorcinol changes bis-phenol s into, and 2.3 parts of dosage, silicone oligomer changes Dow Corning Corporation into
XIAMETER RSN-6018,4.5 parts of dosage, filler changes diatomite into, and 32 parts of dosage, organic wax changes Rhein 25 into, and dosage is not
Become, remaining component and preparation method are the same as embodiment 1.
Embodiment 6
A kind of fluorubber of high temperature and pressure contracting ratio, calcium hydroxide changes sodium metaaluminate, dosage 3.5 into each component of the fluorubber
Part, 2- amino-Resorcinol changes bis- (- 4 hydroxy phenyl of 3- the amino)-hexafluoropropane of 2,2- and three (3,5- di-t-butyls-into
4- acrinyl) isocyanuric acid ester (1:2), 1.8 parts of dosage, filler changes calcium silicates and tripoli 1:1 into, and 35 parts of dosage, organic wax changes
At Mo get Li 935P, dosage is constant, remaining component and preparation method are the same as embodiment 1.
Embodiment 7
A kind of fluorubber of high temperature and pressure contracting ratio, calcium hydroxide changes sodium metaaluminate, dosage 4.5 into each component of the fluorubber
Part, 2- amino-Resorcinol changes bis- (- 4 hydroxy phenyl of 3- the amino)-hexafluoropropane of 2,2- and bis-phenol s(1:1 into) dosage 1.9
Part, filler changes barium sulfate and tripoli 1:1 into, and 40 parts of dosage, organic wax changes ws280 and Rhein 25 by 1:1, and dosage is constant,
Remaining component and preparation method are the same as embodiment 1.
Following table is the performance test results of the fluorubber of Examples 1 to 7.
Wherein, the test of 15*23 assembly requires project testing according to the 6 compressed-air hose assemblies of GB16897-2010,
Middle heat resistance test condition is increased to 260 DEG C of 168h, samples 100.Φ 30*5mm O-ring compression 35% 250 DEG C of * for 24 hours
Afterwards, it is cooled to room temperature, sheds pressure, whether there is or not fragmentations for observation product.The percentage that fragmentation quantity accounts for sum is crushing rate.Sampling
Quantity 100.
As it can be seen that the intensity of obtained each fluoro-rubber composite is high, according to automobile high-temperature brake hose from above embodiments
Examination criteria especially heat conditions are increased to 260 DEG C of * 168h by 100 DEG C of * 70h, and qualification rate reaches 99% or more.O-ring exists
At a temperature of 250 degree, decrement reaches 35%, crushing rate it is worst also 1%.
The above embodiments are only used to illustrate the present invention, and not limitation of the present invention, in relation to the common of technical field
Technical staff can also make various modifications and improvements, therefore all without departing from the spirit and scope of the present invention
Equivalent technical solution also belongs to scope of the invention, and scope of patent protection of the invention should be defined by the claims.
Claims (12)
1. a kind of fluorubber of high temperature and pressure contracting ratio, it is characterised in that: the fluorubber mainly by crude fluororubber, magnesia,
Highly basic, vulcanizing agent, promotor, multifunctional assistant LCA, silicone oligomer, processing aid, filler are process;
The content of each component, in parts by weight are as follows:
100 parts of crude fluororubber
1~10 part of magnesia
0.5~15 part of highly basic
1~6 part of processing aid
0.5~6 part of vulcanizing agent
0.2~2 part of promotor
0~50 part of filler
1~10 part of multifunctional assistant LCA
0.5~15 part of silicone oligomer.
2. a kind of fluorubber of high temperature and pressure contracting ratio according to claim 1, it is characterised in that: each component contains
Amount, in parts by weight are as follows:
100 parts of crude fluororubber
2~10 parts of magnesia
2~10 parts of highly basic
1~4 part of processing aid
1~3 part of vulcanizing agent
0.2~1 part of promotor
1~30 part of filler
1~6 part of multifunctional assistant LCA;
1~10 part of silicone oligomer.
3. a kind of fluorubber of high temperature and pressure contracting ratio according to claim 1, it is characterised in that: the crude fluororubber
Including the ternary fluororubber being polymerized by vinylidene, tetrafluoroethene, perfluoropropene, or by vinylidene, perfluor third
The binary fluorine rubber that alkene is polymerized.
4. a kind of fluorubber of high temperature and pressure contracting ratio according to claim 1, it is characterised in that: the vulcanizing agent can be with
It is the combination of bisphenols, phenol amine, one kind in amine curing agents or multiclass, is also possible to multiple and different in similar vulcanizing agent
The combination of the vulcanizing agent of structure.
5. a kind of fluorubber of high temperature and pressure contracting ratio according to claim 1 or 4, it is characterised in that: the vulcanizing agent
For phenol amine curing agents, the phenol amine curing agents is the compound containing at least one phenolic hydroxyl group He at least one amino;Institute
The phenol amine curing agents stated includes single phenol monoamine vulcanizing agent, polyphenol amine curing agents, polyamines phenolic curative, polyphenol polyamines class
The combination of one or more of them in vulcanizing agent.
6. a kind of fluorubber of high temperature and pressure contracting ratio according to claim 5, it is characterised in that: the phenol amine vulcanization
Agent is preferred are as follows: to (1- aminohexane base) phenol, 5- amino -1,3- benzenediol, 6- amino -1,3,5- benzenetriol, 4- ethylamino -
1,3- benzenediol, 5- ethylamino -1,3- benzenediol, 4- ethylamino -1,3,5- benzenetriol, diaminophenol, 2,4- diaminobenzene
Bis- (- 4 hydroxy phenyl of 3- the amino)-hexafluoropropane of phenol, 2,5- diaminophenol, 2,2-, three (3,5- di-t-butyl -4- hydroxyl benzyls
Base) isocyanuric acid ester.
7. a kind of fluorubber of high temperature and pressure contracting ratio according to claim 1, it is characterised in that: the highly basic includes hydrogen
One of calcium oxide, hydrated sodium silicate+sodium metasilicate, hydrated sodium silicate+(inclined) sodium aluminate, sodium metaaluminate or a variety of combinations.
8. a kind of fluorubber of high temperature and pressure contracting ratio according to claim 7, it is characterised in that: the hydrated sodium silicate+
Sodium metasilicate is by one of water to the hydrated sodium silicate of any combination water content of nine water or a variety of combination water contents
Hydrated sodium silicate and sodium metasilicate combination;The hydrated sodium silicate+(inclined) sodium aluminate is by any of a water to nine water
The combination of the hydrated sodium silicate of one of hydrated sodium silicate in conjunction with water content or a variety of combination water contents and (inclined) sodium aluminate.
9. a kind of fluorubber of high temperature and pressure contracting ratio according to claim 7 or 8, it is characterised in that: the hydration silicon
In sour sodium+sodium metasilicate, the mass content of sodium metasilicate is not less than 5%;In the hydrated sodium silicate+(inclined) sodium aluminate, (inclined) aluminic acid
The mass content of sodium is not less than 5%.
10. a kind of fluorubber of high temperature and pressure contracting ratio according to claim 1, it is characterised in that: the organosilicon is low
Polymers refers to one of the silanol class containing hydro carbons group or silicone hydroxyl quasi-oligomer or a variety of combinations, the hydro carbons
Group includes and is not limited to methyl, phenyl, ethyl, isopropyl;The molecular weight of the silicone oligomer is within 50000;
The form of the silicone oligomer can be liquid or solid-state.
11. a kind of fluorubber of high temperature and pressure contracting ratio according to claim 1, it is characterised in that: the processing aid
For lubricity class release agent, including and be not limited to organic wax, palm wax, ws280, Rhein 54, Rhein 25, in Mo get Li 935P
One or more combinations.
12. a kind of fluorubber of high temperature and pressure contracting ratio according to claim 1, it is characterised in that: the filler is to increase
Capacitive or reinforcing filler, including and it is not limited to carbon black, diatomite, calcium silicates, tripoli, one of barium sulfate or a variety of groups
It closes.