CN109466153A - A kind of processing technology and application of novel lighting fabric - Google Patents
A kind of processing technology and application of novel lighting fabric Download PDFInfo
- Publication number
- CN109466153A CN109466153A CN201811157705.9A CN201811157705A CN109466153A CN 109466153 A CN109466153 A CN 109466153A CN 201811157705 A CN201811157705 A CN 201811157705A CN 109466153 A CN109466153 A CN 109466153A
- Authority
- CN
- China
- Prior art keywords
- optical fiber
- fabric
- novel lighting
- processing
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of processing technologys of novel lighting fabric, belong to fabric manufacture field, include the following steps: step 1: first optical fiber being uniformly wrapped in acrylic template by sets requirement with winding machine；Step 2: cutting out bottom surface base fabric layer and surface top layer fabric by the dimensions of product requirement in advance；Step 3: mixing up soft Instant cement as required and bottom surface base fabric layer is sticked in the template for being tied with optical fiber, and reserve optical fiber and reserve silk processing region；Step 4: the bottom surface base fabric layer that optical fiber is stained under cutting out after certain time adhesive curing carries out the processing of surface dotting process；Step 5: being allowed to fixed with the compound upper layer of surface top layer fabric of transparent flexible glue after the completion of getting ready；Step 6: the process that optical fiber gathers warm set condenser tube ferrule is carried out to reserved silk region part；Step 7: can control various light-emitting modes after lamp bead controller is fixed in condenser tube ferrule.
Description
Technical field
The present invention relates to fabric processing technique field more particularly to the processing technologys and application of a kind of novel lighting fabric.
Background technique
China is added after International Trade Organization, and textile industry is faced with new opportunities and challenges.One side textile industry
Traditional product variety lacks new look, new function；The traditional Weaving device low efficiency in another aspect China, recruitment is more, adapts to
Property is poor, at high cost.
The existing fabric that can be shone, widespread practice is by textile technology optical fiber and silk on the market at present
Line is weaved together by textile machinery, and disadvantage of this is that textile threads material is limited larger, product illumination effect is bad,
It weaves at high cost, it is difficult to realize mass production.
In addition, Chinese patent CN2863827Y " Luminous textile fabric ", discloses one kind by power supply and LED light emitting diode
The light source and plastic optical fibre of composition are connected by connector, but are disadvantageous in that a part of optical fiber is exposed to woven face
Material outside is easy impaired fracture, influences luminous effect, and optical fiber is stretched out from one end of textile fabric, influences woven face
The quality of material and service life.
Summary of the invention
In view of the above-mentioned problems, the present invention provides a kind of processing technologys of novel lighting fabric comprising fabric body,
According to requiring technique to bond optical fiber wire in fabric body, setting light source after one end processing of optical fiber can knitted
The front of object shows the design configuration being made of the luminous point after getting ready, and the illumination effect for carrying out different mode is shown, can
Keep fabric cost of implementation lower, material selectivity is bigger, and product illumination effect is more preferable, is easier to realize the fabric system of mass production
Make technique.
In order to solve the above technical problems, the technical scheme adopted by the invention is that: a kind of processing work of novel lighting fabric
Skill, characterized by the following steps:
Step 1: first optical fiber being uniformly wrapped in acrylic template by sets requirement with winding machine；
Step 2: cutting out bottom surface base fabric layer and surface top layer fabric by the dimensions of product requirement in advance；
Step 3: mixing up soft Instant cement as required and bottom surface base fabric layer is sticked in the template for being tied with optical fiber, and stay
Optical fiber reserves silk processing region out；
Step 4: the bottom surface base fabric layer that optical fiber is stained under cutting out after certain time adhesive curing carries out surface dotting process
Processing；
Step 5: being allowed to fixed with the compound upper layer of surface top layer fabric of transparent flexible glue after the completion of getting ready；
Step 6: the process that optical fiber gathers warm set condenser tube ferrule is carried out to reserved silk region part；
Step 7: can control various light-emitting modes after lamp bead controller is fixed in condenser tube ferrule.
Preferably, the revolution of step 1 winding machine is 20r/min-30r/min, the gap densities between optical fiber
For 0.5mm-5mm, the tensile force of winding is in 3-6N.
Preferably, soft Instant cement common plasticizers and the allotment ratio of soft Instant cement are 1:17-1 in the step 3:
12, reserved optical fiber length has more 5-10cm than fabric product width under normal circumstances.
Preferably, at 3-5 minutes, the time was fully cured in 12-15 hour in the surface cure time in the step 4.
Preferably, in the step 5 curing time at 3-5 minutes.
Preferably, the temperature melted is gathered in the step 6 in 200-220 degree, condenser tube ferrule fixed temperature is in 150-180 degree.
Preferably, application of the novel lighting fabric in production collar domain.
By the above-mentioned description to structure of the invention it is found that compared to the prior art, the present invention has the advantage that
1, the textile threads material of existing emitting optical fiber fabric is limited larger, and product illumination effect is bad, and weaving is at high cost,
Volume production difficulty is high, either raw without that can be produced using complicated textile machinery after processing technology of the invention
Producing cost or fabric cost can greatly reduce, and due to that can make the restricted gender of material using attaching process more
It is small, it is no longer that can only be combined with fabric, moreover it is possible to and leather-like, tpu class setting metal material are combined, and are allowed to using material
More horn of plenty on material, and make product illumination effect more preferable, mass production is easier to realize.
Detailed description of the invention
The attached drawing constituted part of this application is used to provide further understanding of the present invention, schematic reality of the invention
It applies example and its explanation is used to explain the present invention, do not constitute improper limitations of the present invention.In the accompanying drawings:
Fig. 1 is the structural schematic diagram of the vamp of the embodiment of the present invention 4；
In figure: 1. bottom surface base fabric layers；2. intermediate fibres silk interlayer；3. surface top layer fabric.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, with reference to the accompanying drawings and embodiments, right
The present invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, and
It is not used in the restriction present invention.
Embodiment 1
A kind of processing technology of novel lighting fabric, includes the following steps: step 1: optical fiber wire hanging in rolls
On the bracket of winding machine, the density of optic fibre that requirement is then set in control system of machine exists in 0.5mm, winding revolving speed
20r/min, so that the speed of density and winding different between control machine adjustments optical fiber is gone, according to the demand of different product
It is after adjusting relevant parameter, coiled optical fiber is uniform with pre-set revolving speed progress helical form by winding machine
It is wrapped in the rectangular or cylinder type template polished of customization, the technique that winding while prepares lower one of cut-parts.Step 2: cutting out
Piece is exactly that different bottom surface base material and surface top layer material are selected according to different product demand, can include conventional clothes with material
The materials such as fabric, tpu material and metal are filled, chemical fiber plus material, cotton and tpu material are commonly selected, use sanction after choosing material
The dimensions shape bottom surface base fabric layer and surface top layer fabric product as required of bed batch carries out cutting setting treatment,
After winding machine winds the optical fiber fibril for completing to require, prepare the impregnation adhesion technique of next step.Step 3: impregnation
Adhesion technique is exactly to be matched not on year-on-year basis after selecting different bottom surface base fabric layers according to different products for product characteristic
The allotment ratio of the soft Instant cement of example ingredient, soft Instant cement common plasticizers and soft Instant cement is 1:17, is then being cut out
The soft Instant cement modulated is uniformly sprayed at using gluing machine by bottom surface base face on bottom surface base fabric layer after the completion of cutting
On material, and every smooth being attached to of bottom surface base fabric layer is wound on the acrylic plate for requiring density of optical fibers silk, is being bonded
During reserve reserved silk region, reserved optical fiber length has more 5-10cm than fabric product width under normal circumstances.With
Make subsequent fiber optic bundle trail processing technique, fitting carries out curing process after completing, and curing time at 3 minutes, is fully cured
Time carries out the surface dotting process processing of next step after 12 hour solidify completion.Step 4: optical fiber sandwich portion
It carrying out getting processing ready, different surface dotting process modes can be selected according to different product illumination effect requirements by getting processing ready,
The Integral luminous effect for making up to predetermined prod requirement can be carried out the processing of most surface top layer fabric combination process later.
Step 5: surface top layer fabric combination process is exactly to complete and then to the processing of optical fiber sandwiching surface illumination effect in optical fiber
The surface top layer fabric for cutting shape on silk interlayer in advance using one layer on rapid-curing cutback glue bond, after solidification after it is pre- to tail end again
A region is stayed to carry out optical fiber wire processing technique, curing time was at 3 minutes or so.Step 6: tail end optical fiber wire processing technique is exactly to refer to
Reserved silk part is carried out to gather bundles of one of process flow, first to the optical fiber to scatter in reserved silk region along product tail
End profile carry out away side it is fixed gather into it is a branch of, it is fixed gather into it is a branch of after cut off extra optical fiber, and use heated aluminum block
Tool to fiber optic bundle end face carry out it is poly- melts processing, so that melt between whole beam fiber optic bundle is not scattered, gather the temperature melted at 200 degree,
Condenser tube ferrule fixed temperature puts on condenser tube ferrule at 150 degree later；Step 7: lamp bead controller being mounted in i.e. controllable after condenser tube ferrule is fixed
Make various light-emitting modes.
Embodiment 2
A kind of processing technology of novel lighting fabric, includes the following steps: step 1: optical fiber wire hanging in rolls
On the bracket of winding machine, the density of optic fibre that requirement is then set in control system of machine exists in 3.5mm, winding revolving speed
25r/min, so that the speed of density and winding different between control machine adjustments optical fiber is gone, according to the demand of different product
It is after adjusting relevant parameter, coiled optical fiber is uniform with pre-set revolving speed progress helical form by winding machine
It is wrapped in the rectangular or cylinder type template polished of customization, the technique that winding while prepares lower one of cut-parts.Step 2: cutting out
Piece is exactly that different bottom surface base material and surface top layer material are selected according to different product demand, can include conventional clothes with material
The materials such as fabric, tpu material and metal are filled, chemical fiber plus material, cotton and tpu material are commonly selected, use sanction after choosing material
The dimensions shape bottom surface base fabric layer and surface top layer fabric product as required of bed batch carries out cutting setting treatment,
After winding machine winds the optical fiber fibril for completing to require, prepare the impregnation adhesion technique of next step.Step 3: impregnation
Adhesion technique is exactly to be matched not on year-on-year basis after selecting different bottom surface base fabric layers according to different products for product characteristic
The allotment ratio of the soft Instant cement of example ingredient, soft Instant cement common plasticizers and soft Instant cement is 1:14, is then being cut out
The soft Instant cement modulated is uniformly sprayed at using gluing machine by bottom surface base face on bottom surface base fabric layer after the completion of cutting
On material, and every smooth being attached to of bottom surface base fabric layer is wound on the acrylic plate for requiring density of optical fibers silk, is being bonded
During reserve reserved silk region, reserved optical fiber length has more 5-10cm than fabric product width under normal circumstances.With
Make subsequent fiber optic bundle trail processing technique, fitting carries out curing process after completing, and curing time at 4 minutes, is fully cured
Time carries out the surface dotting process processing of next step after 13 hour solidify completion.Step 4: optical fiber sandwich portion
It carrying out getting processing ready, different surface dotting process modes can be selected according to different product illumination effect requirements by getting processing ready,
The Integral luminous effect for making up to predetermined prod requirement can be carried out the processing of most surface top layer fabric combination process later.
Step 5: surface top layer fabric combination process is exactly to complete and then to the processing of optical fiber sandwiching surface illumination effect in optical fiber
The surface top layer fabric for cutting shape on silk interlayer in advance using one layer on rapid-curing cutback glue bond, after solidification after it is pre- to tail end again
A region is stayed to carry out optical fiber wire processing technique, curing time was at 4 minutes or so.Step 6: tail end optical fiber wire processing technique is exactly to refer to
Reserved silk part is carried out to gather bundles of one of process flow, first to the optical fiber to scatter in reserved silk region along product tail
End profile carry out away side it is fixed gather into it is a branch of, it is fixed gather into it is a branch of after cut off extra optical fiber, and use heated aluminum block
Tool to fiber optic bundle end face carry out it is poly- melts processing, so that melt between whole beam fiber optic bundle is not scattered, gather the temperature melted at 210 degree,
Condenser tube ferrule fixed temperature puts on condenser tube ferrule at 160 degree later；Step 7: lamp bead controller being mounted in i.e. controllable after condenser tube ferrule is fixed
Make various light-emitting modes.
Embodiment 3
A kind of processing technology of novel lighting fabric, includes the following steps: step 1: optical fiber wire hanging in rolls
On the bracket of winding machine, the density of optic fibre of requirement is then set in control system of machine in 5mm, winding revolving speed in 30r/
Min is adjusted to go the speed of density and winding different between control machine adjustments optical fiber according to the demand of different product
After good relevant parameter, coiled optical fiber is carried out helical form by winding machine with pre-set revolving speed and is uniformly wound
In the rectangular or cylinder type template polished of customization, technique that winding while prepares lower one of cut-parts.Step 2: cut-parts are just
It is to select different bottom surface base material and surface top layer material according to different product demand, can includes conventional garment face with material
The materials such as material, tpu material and metal commonly select chemical fiber plus material, cotton and tpu material, are criticized after choosing material using cutting
The dimensions shape bottom surface base fabric layer and surface top layer fabric product as required of amount carries out cutting setting treatment, is twining
After winding the optical fiber fibril for completing requirement around machine, prepare the impregnation adhesion technique of next step.Step 3: impregnation bonding
Technique is exactly after selecting different bottom surface base fabric layers according to different products, for product characteristic carry out proportion different proportion at
The allotment ratio of the soft Instant cement divided, soft Instant cement common plasticizers and soft Instant cement is 1:12, is then being cut
Uniformly the soft Instant cement modulated is sprayed on the base fabric layer of bottom surface using gluing machine on bottom surface base fabric layer after,
And every smooth being attached to of bottom surface base fabric layer is wound on the acrylic plate for requiring density of optical fibers silk, in the process of fitting
In reserve reserved silk region, reserved optical fiber length has more 5-10cm than fabric product width under normal circumstances.As subsequent
Fiber optic bundle trail processing technique, fitting carries out curing process after completing, and curing time, being fully cured the time existed at 5 minutes
15 hour solidify the surface dotting process processing for completing to carry out next step later.Step 4: optical fiber sandwich portion is beaten
Point processing, different surface dotting process modes can be selected according to different product illumination effect requirements by getting processing ready, be allowed to reach
The Integral luminous effect required to predetermined prod can be carried out the processing of most surface top layer fabric combination process later.Step 5:
Surface top layer fabric combination process is exactly to complete and then to the processing of optical fiber sandwiching surface illumination effect in optical fiber interlayer
On using one layer on rapid-curing cutback glue bond cut the surface top layer fabric of shape in advance, after solidification after silk area is reserved to tail end again
Domain carries out optical fiber wire processing technique, and curing time was at 5 minutes or so.Step 6: tail end optical fiber wire processing technique is exactly to refer to reserved
Silk part carries out gathering bundles of one of process flow, first to the optical fiber to scatter in reserved silk region along product tail end profile
Carry out away side it is fixed gather into it is a branch of, it is fixed gather into it is a branch of after cut off extra optical fiber, and use heated aluminum block tool pair
Fiber optic bundle end face carry out it is poly- melts processing, so that melt between whole beam fiber optic bundle is not scattered, gather the temperature melted at 220 degree, condenser tube ferrule
Fixed temperature puts on condenser tube ferrule in 180 degree later；Step 7: lamp bead controller can control after condenser tube ferrule fixation various
Light-emitting mode.
Embodiment 4
With reference to Fig. 1, a kind of novel lighting fabric production collar domain application, by taking luminous instep as an example, entire vamp master
It to be made of 3 parts, respectively bottom surface base fabric layer 1, intermediate fibres silk interlayer 2 and surface top layer fabric 3；By specifically twining
Silk adhering process is combined into 3 layer materials the Luminous shoe piece of whole piece requirement style.Specific step is as follows:
Step 1: first make 2 part of vamp intermediate fibres silk interlayer, by optical fiber wire it is coiled hang over wrapping machine
On the bracket of device, density of optic fibre is then being set in control system of machine between 0.5mm-2mm, is commonly used the density of 1mm, is twined
Around revolving speed in 20r/min-30r/min, commonly use 25r/min, thus go density different between control machine adjustments optical fiber and
Coiled optical fiber after adjusting parameter, is carried out helical form by winding machine and is uniformly wrapped in customization by the speed of winding
In the square template polished, the technique for preparing lower one of cut-parts while winding.
Step 2: shoes piece cut-parts technique, selecting the bottom surface base fabric layer 1 of vamp is polyester fabric, and surface top layer fabric 3 is
Grid polyester fabric is chosen after material using cutting batch bottom surface base fabric layer 1 and surface top layer fabric 3 by certain shoes
Chip size specification shape carries out cutting setting treatment, after winding machine winds the optical fiber fibril for completing to require, prepares
The impregnation adhesion technique of next step.
Step 3: shoes piece impregnation adhesion technique refers to that plasticizer and soft Instant cement are that 1:15 carries out allotment in proportion is mixed
It closes, then uniformly the soft Instant cement modulated is sprayed using gluing machine on the bottom surface base fabric layer 1 after the completion of cutting
On bottom surface base fabric layer 1, and every smooth being attached to of bottom surface base fabric layer 1 is wound the acrylic for requiring density of optical fibers silk
On plate, reserved silk region is reserved during the bonding process, reserves optical fiber length under normal circumstances than fabric product width
Have more the surplus of 5cm.As subsequent fiber optic bundle trail processing technique, fitting carries out curing process, curing time after completing
At 3-5 minutes, the surface dotting process processing of time progress next step after 12-15 hour solidifies completion is fully cured.
Step 4: dotting process processing in surface is exactly that a piece of stable leaded light substantially is formd after soft quick-drying adhesive curing
Fabric structure, and optical fiber is bonded according to the shape outer profile of bottom surface base fabric layer 1 and is cut together, then with getting pair of rollers ready
2 part of intermediate fibres silk interlayer carries out getting processing ready, is allowed to entire vamp and reaches illumination effect, can be carried out most surface later
The processing of 3 combination process of top layer fabric.
Step 5: 3 combination process of surface top layer fabric is exactly complete to intermediate 2 surface light emitting effect process of optical fiber interlayer
At and then cutting the surface top layer fabric of shape on intermediate fibres silk interlayer 2 in advance using one layer on rapid-curing cutback glue bond
3, after solidification after again to tail end reserve silk region carry out optical fiber wire processing technique, curing time was at 3-5 minutes or so.
Step 6: tail end optical fiber wire processing technique exactly refers to that reserving silk part to shoes piece carries out gathering bundles of one of technique
Process first carries out away side fixation along product tail end profile to the optical fiber to scatter in reserved silk region and gathers into a branch of, fixation
Gather into it is a branch of after cut off extra optical fiber, and using heated aluminum block tool to fiber optic bundle end face carry out it is poly- melt processing, make whole
Melt will not scatter between beam fiber optic bundle, and the poly- temperature melted is in 200-220 degree, and condenser tube ferrule fixed temperature is in 150-180 degree, later
Put on condenser tube ferrule.
Step 7: lamp bead controller, which is mounted in after condenser tube ferrule is fixed, can control various light-emitting modes.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Made any modifications, equivalent replacements, and improvements etc., should all be included in the protection scope of the present invention within mind and principle.
Claims (7)
1. a kind of processing technology of novel lighting fabric, characterized by the following steps:
Step 1: first optical fiber being uniformly wrapped in acrylic template by sets requirement with winding machine；
Step 2: cutting out bottom surface base fabric layer and surface top layer fabric by the dimensions of product requirement in advance；
Step 3: mixing up soft Instant cement as required and bottom surface base fabric layer is sticked in the template for being tied with optical fiber, and reserve light
Fibril reserves silk processing region；
Step 4: the bottom surface base fabric layer that optical fiber is stained under cutting out after certain time adhesive curing carries out the processing of surface dotting process；
Step 5: being allowed to fixed with the compound upper layer of surface top layer fabric of transparent flexible glue after the completion of getting ready；
Step 6: the process that optical fiber gathers warm set condenser tube ferrule is carried out to reserved silk region part；
Step 7: can control various light-emitting modes after lamp bead controller is fixed in condenser tube ferrule.
2. a kind of processing technology of novel lighting fabric according to claim 1, it is characterised in that: step 1 winding
The revolution of machine is 20r/min-30r/min, and the gap densities between optical fiber are 0.5mm-5mm, and the tensile force of winding is in 3-
6N。
3. a kind of processing technology of novel lighting fabric according to claim 1, it is characterised in that: soft in the step 3
Property Instant cement common plasticizers and soft Instant cement allotment ratio be 1:17-1:12, reserve optical fiber length under normal circumstances
5-10cm is had more than fabric product width.
4. a kind of processing technology of novel lighting fabric according to claim 1, it is characterised in that: table in the step 4
At 3-5 minutes, the time was fully cured in 12-15 hour in face curing time.
5. a kind of processing technology of novel lighting fabric according to claim 1, it is characterised in that: solid in the step 5
Change the time at 3-5 minutes.
6. a kind of processing technology of novel lighting fabric according to claim 1, it is characterised in that: gather in the step 6
The temperature melted is in 200-220 degree, and condenser tube ferrule fixed temperature is in 150-180 degree.
7. a kind of application of novel lighting fabric, it is characterised in that: application of the novel lighting fabric in production collar domain.