CN108859566A - A kind of antibacterial steady type decoration leather and preparation method thereof - Google Patents
A kind of antibacterial steady type decoration leather and preparation method thereof Download PDFInfo
- Publication number
- CN108859566A CN108859566A CN201810674758.1A CN201810674758A CN108859566A CN 108859566 A CN108859566 A CN 108859566A CN 201810674758 A CN201810674758 A CN 201810674758A CN 108859566 A CN108859566 A CN 108859566A
- Authority
- CN
- China
- Prior art keywords
- substrate layer
- decorative layer
- layer
- skeleton
- antibacterial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of antibacterial steady type decoration leathers and preparation method thereof, including substrate layer, skeleton, decorative layer, binding material；The present invention obtains novel decorative of the invention by the preparation of substrate layer and fluting, the preparation of decorative layer and fluting, hot pressing fitting, the preparation of skeleton, perfusion binding material step and removes from office；The present invention is sufficiently merged zinc oxide with the other components of decorative layer as carrier using silica white, ensure that antibacterial uniformity while ensure that fungistatic effect.
Description
Technical field
The present invention relates to novel decoratives to remove from office field more particularly to antibacterial steady type decoration leather and preparation method thereof.
Background technique
With the continuous development of society, living standards of the people increasingly improve, and requirement of the people for living environment is also increasingly
It improves.Currently, indoor wall decoration is mainly with decoration wallpaper and natural leather.Wallpaper is not moisture resistance, light fugitive, cracky, difficult
To reach high-grade decorative effect.For natural leather, due to being restricted by natural conditions, while the whole world is to the meaning of protection animal
Knowledge is gradually reinforced, and natural leather is reduced year by year.Currently, the Household ornament synthetic leather developed in the market, generally comprises decoration
Layer and substrate layer, decorative layer and substrate layer mix various modifying agent by polyvinyl chloride resin and are kneaded, then by decorative layer and substrate
Layer carries out hot pressing fitting, and still, the fungistatic effect of such decoration leather is poor, hygroscopicity is poor, decorative layer and substrate layer are bonded loosely
Gu, intensity it is not high.
Summary of the invention
In view of the deficiencies of the prior art mentioned above, problems solved by the invention is：Improve a kind of good antimicrobial effect, moisture absorption
Property good, decorative layer and substrate layer fitting securely, intensity is high, antibacterial steady type decoration leather with long service life and preparation method thereof.
To solve the above problems, the technical solution adopted by the present invention is as follows：
A kind of antibacterial steady type decoration leather, including substrate layer, skeleton, decorative layer, binding material；The substrate layer each component and
Parts by weight are as follows：100 parts of polyvinyl chloride resin, 4 to 5 parts of stabilizer, 3 to 4 parts of foaming agent, 30 to 40 parts of calcium carbonate；The decorative layer
Each component and parts by weight are as follows：100 parts of polyvinyl chloride resin, 40 to 50 parts of plasticizer, 10 to 20 parts of color cake, 10 to 20 parts of zinc oxide,
10 to 20 parts of silica white；The skeleton includes multiple twisted fibres silks；The twisted fibres silk include glass fiber and
Mo Daer fiber filament；The glass fiber and Mo Daer fiber filament is twisted to form twisted fibres silk；The substrate layer and
Decorative layer is fitted and connected by hot pressing；The upper surface of the substrate layer is equipped with multiple substrate layer mounting grooves；The decoration
The lower end surface of layer is equipped with multiple decorative layer mounting grooves；Multiple substrate layer mounting grooves and multiple decorative layers install groove location
It corresponds to and multiple skeleton mounting grooves is formed to patch；Binding material is perfused in the skeleton mounting groove；Each skeleton installation
It is worn in binding material in slot and connects one twisted fibres silk of bonding.
Further, the mass ratio of zinc oxide and silica white is 1 in the decorative layer:1.
Further, the twisted fibres silk is by 1000 to 1200 Gen Modaer fiber filaments and 1200 to 1400 glass fibers
Dimension silk is twisted to be formed；The filametntary diameter of glass fiber and Mo Daer is 15 to 20 microns.
Further, the binding material is adhesive mortar.
Further, the polyvinyl chloride resin is three type polyvinyl chloride resins.
A kind of preparation method of antibacterial steady type decoration leather, steps are as follows：
S1, the preparation of substrate layer and fluting：Each group in substrate layer is distributed into blender and is stirred；The base that will be stirred
The each component of material layer is kneaded, mill, calendering, obtains substrate layer initial material；Then by groover the one of substrate layer initial material
It slots on side, is cut into multiple substrate layer mounting grooves；
S2, the preparation of decorative layer and fluting：First by decorative layer zinc oxide and silica white put into and filled into blender
Divide and be mixed, mixing time is 20 to 30min, and then the other components in decorative layer are sent into blender and are stirred；
The each component for the substrate layer being stirred is kneaded, mill, calendering, obtains decorative layer initial material；Then it is being filled by groover
It adorns on the one side of layer initial material and slots, be cut into multiple decorative layer mounting grooves；
S3, hot pressing fitting：By substrate layer and decorative layer as on compounding machine, by preheating, flattening, fitting, cooling process, simultaneously
It keeps substrate layer mounting groove and decorative layer mounting groove to form multiple skeleton mounting grooves to patch, forms decoration leather preform；
The preparation of S4, skeleton：More glass fibers and more Gen Modaer fiber filaments are twisted together and form twisted fibres silk；
S5, perfusion binding material：Binding material is perfused in the multiple skeleton mounting grooves formed in step s3, then pacifies in each skeleton
It is inserted into a twisted fibres silk in binding material in tankage, is then heating and curing, is cooled and shaped, obtain decoration leather.
Further, the temperature that blender is controlled in the step S1 is 170 to 180 DEG C.
Further, the temperature that blender is controlled in the step S2 is 180 to 190 DEG C.
Further, by 1000~1200 Gen Modaer fiber filaments and 1200~1400 glass fibres in the step S4
Silk is twisted to be formed.
Further, heating temperature is 80 to 100 DEG C in the step S5, and heating time is 20 to 30min.
Beneficial effects of the present invention
The present invention joined zinc oxide in decorative layer in order to improve the fungistatic effect of decorative layer, but due to the change of zinc oxide
The other components amalgamation of characteristic, zinc oxide and decorative layer is not high, therefore the present invention first carries out zinc oxide and silica white in advance
Mixing, carries out evenly dispersed absorption for zinc oxide using the adsorptivity of silica white, using silica white as carrier by zinc oxide and
The other components of decorative layer are sufficiently merged, and ensure that antibacterial uniformity while ensure that fungistatic effect；The present invention exists
It is bonded at substrate layer and the binding face of decorative layer by skeleton, in order to guarantee that skeleton is fitted and connected with substrate layer and decorative layer
Fastness be then inserted into one in the binding material in each skeleton mounting groove by the way that binding material is perfused in skeleton mounting groove
A twisted fibres silk, so that substrate layer, decorative layer, the fastness of skeleton connection are realized, simultaneously because skeleton of the present invention includes
Multiple twisted fibres silks, twisted fibres silk include glass fiber and Mo Daer fiber filament, glass fiber and Mo Daer fiber
Silk is twisted to form twisted fibres silk, and the intensity of glass fiber is high, stiffness is good, and Mo Daer fiber filament is with soft well
Property and excellent hygroscopicity, by glass fiber and Mo Daer it is filametntary it is twisted form skeleton, to not only increase dress
The intensity and stiffness of dressing leather, while improving the hygroscopicity of decoration leather.
Detailed description of the invention
Fig. 1 is schematic cross-sectional view of the invention.
Fig. 2 is section view fractionation structural representation of the present invention.
Specific embodiment
The content of present invention is described in further detail with reference to the accompanying drawing.
Embodiment 1
As illustrated in fig. 1 and 2, a kind of antibacterial steady type decoration leather, including substrate layer 2, skeleton, decorative layer 1, binding material 4.Substrate layer
2 each components and parts by weight are as follows：100 parts of polyvinyl chloride resin, 4 parts of stabilizer, 3 parts of foaming agent, 30 parts of calcium carbonate；The decoration
1 each component of layer and parts by weight are as follows：100 parts of polyvinyl chloride resin, 40 parts of plasticizer, 10 parts of color cake, 10 parts of zinc oxide, silica white 10
Part；Plasticizer is preferably DOP dioctyl phthalate.The skeleton includes multiple twisted fibres silks 5；Described is twisted
Fiber filament 5 includes glass fiber and Mo Daer fiber filament；The glass fiber and Mo Daer fiber filament is twisted to form twirl
Condensating fiber silk 5；Twisted fibres silk 5 is twisted together with 1400 glass fibers by 1000 Gen Modaer fiber filaments and is formed；Glass fibre
Silk and the filametntary diameter of Mo Daer are 15 microns.The substrate layer 2 and decorative layer 1 is fitted and connected by hot pressing；Described
The upper surface of substrate layer 2 is equipped with multiple substrate layer mounting grooves 21；The lower end surface of the decorative layer 1 is equipped with multiple decorative layers
Mounting groove 11；Multiple substrate layer mounting grooves 21 and multiple 11 positions of decorative layer mounting groove are corresponding and form multiple bones to patch
Frame mounting groove 3；Binding material 4 is perfused in the skeleton mounting groove 3；Binding material 4 is preferably adhesive mortar.Each bone
It is worn in binding material 4 in frame mounting groove 3 and connects one twisted fibres silk 5 of bonding.Polyvinyl chloride resin of the invention can be preferably three type PVC
Resin.
A kind of preparation method of antibacterial steady type decoration leather, steps are as follows：
S1, the preparation of substrate layer and fluting：Each group in substrate layer is distributed into blender and is stirred, blender is controlled
Temperature is 170 DEG C；The each component for the substrate layer being stirred is kneaded, mill, calendering, obtains substrate layer initial material；Then lead to
It crosses groover to slot on the one side of substrate layer initial material, is cut into multiple substrate layer mounting grooves；
S2, the preparation of decorative layer and fluting：First by decorative layer zinc oxide and silica white put into and filled into blender
Divide and be mixed, then the other components in decorative layer are sent into blender and are stirred by mixing time 30min, stir
Time is 30min, and controlling the temperature in blender is 180 DEG C；The each component for the substrate layer being stirred is kneaded, mill,
Calendering, obtains decorative layer initial material；Then it is slotted on the one side of decorative layer initial material by groover, is cut into multiple decorative layers
Mounting groove；
S3, hot pressing fitting：By substrate layer and decorative layer as on compounding machine, by preheating, flattening, fitting, cooling process, simultaneously
It keeps substrate layer mounting groove and decorative layer mounting groove to form multiple skeleton mounting grooves to patch, forms decoration leather preform；
The preparation of S4, skeleton：More glass fibers and more Gen Modaer fiber filaments are twisted together and form twisted fibres silk；By 1000
Gen Modaer fiber filament is twisted together with 1400 glass fibers and forms；
S5, perfusion binding material：Binding material is perfused in the multiple skeleton mounting grooves formed in step s3, then pacifies in each skeleton
It is inserted into a twisted fibres silk in binding material in tankage, is then heating and curing, is cooled and shaped, obtain decoration leather；Heating
Temperature is 80 DEG C, heating time 30min.
Embodiment 2
As illustrated in fig. 1 and 2, a kind of antibacterial steady type decoration leather, including substrate layer 2, skeleton, decorative layer 1, binding material 4.Substrate layer
2 each components and parts by weight are as follows：100 parts of polyvinyl chloride resin, 4.5 parts of stabilizer, 3.5 parts of foaming agent, 35 parts of calcium carbonate；Described
1 each component of decorative layer and parts by weight are as follows：100 parts of polyvinyl chloride resin, 45 parts of plasticizer, 15 parts of color cake, 15 parts of zinc oxide, silica gel
15 parts of powder；Plasticizer is preferably DOP dioctyl phthalate.The skeleton includes multiple twisted fibres silks 5；Described
Twisted fibres silk 5 includes glass fiber and Mo Daer fiber filament；The glass fiber and Mo Daer fiber filament is twisted together shape
At twisted fibres silk 5；Twisted fibres silk 5 is twisted together with 1300 glass fibers by 1100 Gen Modaer fiber filaments and is formed；Glass
Fiber filament and the filametntary diameter of Mo Daer are 18 microns.The substrate layer 2 and decorative layer 1 is fitted and connected by hot pressing；Institute
The upper surface for the substrate layer 2 stated is equipped with multiple substrate layer mounting grooves 21；The lower end surface of the decorative layer 1 is equipped with multiple dresses
Adorn layer mounting groove 11；Multiple substrate layer mounting grooves 21 and multiple 11 positions of decorative layer mounting groove are corresponding and more to patch formation
A skeleton mounting groove 3；Binding material 4 is perfused in the skeleton mounting groove 3；Binding material 4 is preferably adhesive mortar.Described is every
It is worn in binding material 4 in a skeleton mounting groove 3 and connects one twisted fibres silk 5 of bonding.Polyvinyl chloride resin of the invention can be preferably three types
Polyvinyl chloride resin.
A kind of preparation method of antibacterial steady type decoration leather, steps are as follows：
S1, the preparation of substrate layer and fluting：Each group in substrate layer is distributed into blender and is stirred, is controlled in blender
Temperature be 175 DEG C；The each component for the substrate layer being stirred is kneaded, mill, calendering, obtains substrate layer initial material；Then
It is slotted on the one side of substrate layer initial material by groover, is cut into multiple substrate layer mounting grooves；
S2, the preparation of decorative layer and fluting：First by decorative layer zinc oxide and silica white put into and filled into blender
Divide and be mixed, then the other components in decorative layer are sent into blender and are stirred by mixing time 25min, stir
Time is 25min, and controlling the temperature in blender is 185 DEG C；The each component for the substrate layer being stirred is kneaded, mill,
Calendering, obtains decorative layer initial material；Then it is slotted on the one side of decorative layer initial material by groover, is cut into multiple decorative layers
Mounting groove；
S3, hot pressing fitting：By substrate layer and decorative layer as on compounding machine, by preheating, flattening, fitting, cooling process, simultaneously
It keeps substrate layer mounting groove and decorative layer mounting groove to form multiple skeleton mounting grooves to patch, forms decoration leather preform；
The preparation of S4, skeleton：More glass fibers and more Gen Modaer fiber filaments are twisted together and form twisted fibres silk；By 1100
Gen Modaer fiber filament is twisted together with 1300 glass fibers and forms；
S5, perfusion binding material：Binding material is perfused in the multiple skeleton mounting grooves formed in step s3, then pacifies in each skeleton
It is inserted into a twisted fibres silk in binding material in tankage, is then heating and curing, is cooled and shaped, obtain decoration leather.Heating
Temperature is 90 DEG C, heating time 25min.
Embodiment 3
As illustrated in fig. 1 and 2, a kind of antibacterial steady type decoration leather, including substrate layer 2, skeleton, decorative layer 1, binding material 4.Substrate layer
2 each components and parts by weight are as follows：100 parts of polyvinyl chloride resin, 5 parts of stabilizer, 4 parts of foaming agent, 40 parts of calcium carbonate；The decoration
1 each component of layer and parts by weight are as follows：100 parts of polyvinyl chloride resin, 50 parts of plasticizer, 20 parts of color cake, 20 parts of zinc oxide, silica white 20
Part；Plasticizer is preferably DOP dioctyl phthalate.The skeleton includes multiple twisted fibres silks 5；Described is twisted
Fiber filament 5 includes glass fiber and Mo Daer fiber filament；The glass fiber and Mo Daer fiber filament is twisted to form twirl
Condensating fiber silk 5；Twisted fibres silk 5 is twisted together with 1200 glass fibers by 1200 Gen Modaer fiber filaments and is formed；Glass fibre
Silk and the filametntary diameter of Mo Daer are 20 microns.The substrate layer 2 and decorative layer 1 is fitted and connected by hot pressing；Described
The upper surface of substrate layer 2 is equipped with multiple substrate layer mounting grooves 21；The lower end surface of the decorative layer 1 is equipped with multiple decorative layers
Mounting groove 11；Multiple substrate layer mounting grooves 21 and multiple 11 positions of decorative layer mounting groove are corresponding and form multiple bones to patch
Frame mounting groove 3；Binding material 4 is perfused in the skeleton mounting groove 3；Binding material 4 is preferably adhesive mortar.Each bone
It is worn in binding material 4 in frame mounting groove 3 and connects one twisted fibres silk 5 of bonding.Polyvinyl chloride resin of the invention can be preferably three type PVC
Resin.
A kind of preparation method of antibacterial steady type decoration leather, steps are as follows：
S1, the preparation of substrate layer and fluting：Each group in substrate layer is distributed into blender and is stirred, is controlled in blender
Temperature be 180 DEG C；The each component for the substrate layer being stirred is kneaded, mill, calendering, obtains substrate layer initial material；Then
It is slotted on the one side of substrate layer initial material by groover, is cut into multiple substrate layer mounting grooves；
S2, the preparation of decorative layer and fluting：First by decorative layer zinc oxide and silica white put into and filled into blender
Divide and be mixed, mixing time is 20 min, and then the other components in decorative layer are sent into blender and are stirred, and is stirred
Time is 20 min, and controlling the temperature in blender is 190 DEG C；The each component for the substrate layer being stirred is kneaded, mill,
Calendering, obtains decorative layer initial material；Then it is slotted on the one side of decorative layer initial material by groover, is cut into multiple decorative layers
Mounting groove；
S3, hot pressing fitting：By substrate layer and decorative layer as on compounding machine, by preheating, flattening, fitting, cooling process, simultaneously
It keeps substrate layer mounting groove and decorative layer mounting groove to form multiple skeleton mounting grooves to patch, forms decoration leather preform；
The preparation of S4, skeleton：More glass fibers and more Gen Modaer fiber filaments are twisted together and form twisted fibres silk；By 1200
Gen Modaer fiber filament is twisted together with 1200 glass fibers and forms；
S5, perfusion binding material：Binding material is perfused in the multiple skeleton mounting grooves formed in step s3, then pacifies in each skeleton
It is inserted into a twisted fibres silk in binding material in tankage, is then heating and curing, is cooled and shaped, obtain decoration leather.Heating
Temperature is 100 DEG C, and heating time is 20 min.
The present invention joined zinc oxide in decorative layer in order to improve the fungistatic effect of decorative layer, but due to zinc oxide
Chemical characteristic, the other components amalgamation of zinc oxide and decorative layer is not high, thus the present invention first by zinc oxide and silica white into
Row premixing, carries out evenly dispersed absorption for zinc oxide using the adsorptivity of silica white, will be aoxidized using silica white as carrier
Zinc is sufficiently merged with the other components of decorative layer, ensure that antibacterial uniformity while ensure that fungistatic effect；This hair
It is bright to be bonded at substrate layer and the binding face of decorative layer by skeleton, in order to guarantee that skeleton is bonded with substrate layer and decorative layer
Then the fastness of connection is inserted by the way that binding material is perfused in skeleton mounting groove in the binding material in each skeleton mounting groove
Enter a twisted fibres silk, so that substrate layer, decorative layer, the fastness of skeleton connection are realized, simultaneously because skeleton of the present invention
Including multiple twisted fibres silks, twisted fibres silk includes glass fiber and Mo Daer fiber filament, glass fiber and Mo Daer
Fiber filament is twisted to form twisted fibres silk, and the intensity of glass fiber is high, stiffness is good, and Mo Daer fiber filament has well
Flexibility and excellent hygroscopicity form skeleton by filametntary be twisted together of glass fiber and Mo Daer, to not only improve
The intensity and stiffness of decoration leather, while improving the hygroscopicity of decoration leather.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Within mind and principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (10)
1. a kind of antibacterial steady type decoration leather, which is characterized in that including substrate layer, skeleton, decorative layer, binding material；The base
Material layer each component and parts by weight are as follows：100 parts of polyvinyl chloride resin, 4 to 5 parts of stabilizer, 3 to 4 parts of foaming agent, calcium carbonate 30 to 40
Part；The decorative layer each component and parts by weight are as follows：100 parts of polyvinyl chloride resin, 40 to 50 parts of plasticizer, 10 to 20 parts of color cake,
10 to 20 parts of zinc oxide, 10 to 20 parts of silica white；The skeleton includes multiple twisted fibres silks；The twisted fibres silk packet
Include glass fiber and Mo Daer fiber filament；The glass fiber and Mo Daer fiber filament is twisted to form twisted fibres silk；
The substrate layer and decorative layer is fitted and connected by hot pressing；It is installed equipped with multiple substrate layers the upper surface of the substrate layer
Slot；The lower end surface of the decorative layer is equipped with multiple decorative layer mounting grooves；Multiple substrate layer mounting grooves and multiple dresses
Decorations layer installation groove location is corresponding and forms multiple skeleton mounting grooves to patch；Binding material is perfused in the skeleton mounting groove；It is described
Each skeleton mounting groove in binding material in wear connect bonding one twisted fibres silk.
2. antibacterial steady type decoration leather according to claim 1, which is characterized in that zinc oxide and silicon in the decorative layer
The mass ratio of rubber powder is 1:1.
3. antibacterial steady type decoration leather according to claim 1, which is characterized in that the twisted fibres silk by 1000 to
1200 Gen Modaer fiber filaments are twisted together with 1200 to 1400 glass fibers and form；The glass fiber and Mo Daer are fine
The diameter for tieing up silk is 15 to 20 microns.
4. antibacterial steady type decoration leather according to claim 1, which is characterized in that the binding material is adhesive mortar.
5. antibacterial steady type decoration leather according to claim 1, which is characterized in that the polyvinyl chloride resin is three type PVC trees
Rouge.
6. one kind is according to claim 1 to the preparation method of antibacterial steady type decoration leather described in 5 any one, feature exists
In steps are as follows：
S1, the preparation of substrate layer and fluting：Each group in substrate layer is distributed into blender and is stirred；The base that will be stirred
The each component of material layer is kneaded, mill, calendering, obtains substrate layer initial material；Then by groover the one of substrate layer initial material
It slots on side, is cut into multiple substrate layer mounting grooves；
S2, the preparation of decorative layer and fluting：First by decorative layer zinc oxide and silica white put into and filled into blender
Divide and be mixed, mixing time is 20 to 30min, and then the other components in decorative layer are sent into blender and are stirred；
The each component for the substrate layer being stirred is kneaded, mill, calendering, obtains decorative layer initial material；Then it is being filled by groover
It adorns on the one side of layer initial material and slots, be cut into multiple decorative layer mounting grooves；
S3, hot pressing fitting：By substrate layer and decorative layer as on compounding machine, by preheating, flattening, fitting, cooling process, simultaneously
It keeps substrate layer mounting groove and decorative layer mounting groove to form multiple skeleton mounting grooves to patch, forms decoration leather preform；
The preparation of S4, skeleton：More glass fibers and more Gen Modaer fiber filaments are twisted together and form twisted fibres silk；
S5, perfusion binding material：Binding material is perfused in the multiple skeleton mounting grooves formed in step s3, then pacifies in each skeleton
It is inserted into a twisted fibres silk in binding material in tankage, is then heating and curing, is cooled and shaped, obtain decoration leather.
7. the preparation method of antibacterial steady type decoration leather according to claim 6, which is characterized in that in the step S1
The temperature for controlling blender is 170 to 180 DEG C.
8. the preparation method of antibacterial steady type decoration leather according to claim 6, which is characterized in that in the step S2
The temperature for controlling blender is 180 to 190 DEG C.
9. the preparation method of antibacterial steady type decoration leather according to claim 6, which is characterized in that in the step S4
1000~1200 Gen Modaer fiber filaments are twisted together with 1200~1400 glass fibers and are formed.
10. the preparation method of antibacterial steady type decoration leather according to claim 6, which is characterized in that the step S5
Middle heating temperature is 80 to 100 DEG C, and heating time is 20 to 30min.