CN109466127A - A kind of environment-friendly composite fabric lining - Google Patents

A kind of environment-friendly composite fabric lining Download PDF

Info

Publication number
CN109466127A
CN109466127A CN201811176661.4A CN201811176661A CN109466127A CN 109466127 A CN109466127 A CN 109466127A CN 201811176661 A CN201811176661 A CN 201811176661A CN 109466127 A CN109466127 A CN 109466127A
Authority
CN
China
Prior art keywords
parts
flame retardant
precoat
retardant coating
environment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811176661.4A
Other languages
Chinese (zh)
Inventor
张振天
黄龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Xicheng New Mstar Technology Ltd
Original Assignee
Jiangsu Xicheng New Mstar Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Xicheng New Mstar Technology Ltd filed Critical Jiangsu Xicheng New Mstar Technology Ltd
Priority to CN201811176661.4A priority Critical patent/CN109466127A/en
Publication of CN109466127A publication Critical patent/CN109466127A/en
Pending legal-status Critical Current

Abstract

The present invention discloses a kind of environment-friendly composite fabric lining, including the first precoat and the second precoat being stacked, it is bonded between first precoat and second precoat by retardant adhesive layer, first precoat is mutually woven by aramid fiber warp and aramid fiber weft, second precoat is mutually woven by antibiotic cotton fiber warp and antibiotic cotton fiber weft, flame retardant coating is additionally provided on first precoat and second precoat, the flame retardant coating includes the first flame retardant coating and the second flame retardant coating；Wherein, first flame retardant coating includes the composition of following parts by weight: 80~100 parts of oiliness polyurethane, 5~15 parts of phosphate flame retardant, 10~30 parts of ethyl acetate, 1~5 part of aluminium powder, 0.1~1 part of thickener；Second flame retardant coating includes the composition of following parts by weight: 80~100 parts of oiliness polyurethane, 10~20 parts of phosphate flame retardant, 20~50 parts of ethyl acetate, 5~10 parts of aluminium powder, 0.1~1 part of thickener.Fabric in the present invention has excellent flame retardant property, good environmental protection.

Description

A kind of environment-friendly composite fabric lining
Technical field
The present invention relates to technical field of textile fabric, more particularly to a kind of environment-friendly composite fabric lining.
Background technique
Autumn and winter day dry is dry, and fabric belongs to extremely fire-hazardous special article, easily develops once encountering star igniting At fire disaster, great security risk is brought to people's lives.Existing fabric flame retardant property is poor, meets fiery inflammable, peace Full property is lower.
For this reason, it is necessary to be able to solve the prior art in view of the above-mentioned problems, propose a kind of environment-friendly composite fabric lining The problem of.
Summary of the invention
The purpose of the present invention is to provide a kind of environment-friendly composite fabric linings, to overcome deficiency in the prior art.
To achieve the above object, the invention provides the following technical scheme:
A kind of environment-friendly composite fabric lining, including the first precoat and the second precoat being stacked, described first It is bonded between precoat and second precoat by retardant adhesive layer, first precoat is by aramid fiber warp and virtue Synthetic fibre weft mutually weaves, second precoat mutually woven by antibiotic cotton fiber warp and antibiotic cotton fiber weft and At being additionally provided with flame retardant coating on first precoat and second precoat, the flame retardant coating includes the first fire-retardant painting Layer and the second flame retardant coating；Wherein, first flame retardant coating includes the composition of following parts by weight: oiliness polyurethane 80~100 Part, 5~15 parts of phosphate flame retardant, 10~30 parts of ethyl acetate, 1~5 part of aluminium powder, 0.1~1 part of thickener；Second resistance Combustion coating includes the composition of following parts by weight: 80~100 parts of oiliness polyurethane, 10~20 parts of phosphate flame retardant, and ethyl acetate 20~50 parts, 5~10 parts of aluminium powder, 0.1~1 part of thickener.
Preferably, first precoat is equipped with one or both of the first flame retardant coating, the second flame retardant coating, institute The second precoat is stated equipped with one or both of the first flame retardant coating, the second flame retardant coating.
Preferably, each aramid fiber warp and each aramid fiber weft are formed by 2~3 aramid fiber twistings.
Preferably, each antibiotic cotton fiber warp and each antibiotic cotton fiber weft are by 2~3 antibacterial cottons Fiber twisting forms.
Preferably, the antibiotic cotton fiber warp and the antibiotic cotton fiber weft are made of nanometer silver antimicrobial cotton fiber.
Preferably, the adhesive layer is polyvinyl alcohol environmental protection glue.
Preferably, the adhesive layer with a thickness of 0.10~0.15mm.
Preferably, first flame retardant coating includes the composition of following parts by weight: 90 parts of oiliness polyurethane, organic phosphate flame-retardant 10 parts of agent, 20 parts of ethyl acetate, 3 parts of aluminium powder, 0.5 part of thickener；Second flame retardant coating includes the composition of following parts by weight: 90 parts of oiliness polyurethane, 15 parts of phosphate flame retardant, 35 parts of ethyl acetate, 7.5 parts of aluminium powder, 0.5 part of thickener.
Compared with the prior art, the advantages of the present invention are as follows: terylene-spandex composite material in the present invention has excellent Flame retardant property, the dry dry autumn and winter in day can give the protection of people's safety, have a good application prospect, be worthy to be popularized.
Specific embodiment
The present invention is described further by the following example: according to following embodiments, the present invention may be better understood. However, as it will be easily appreciated by one skilled in the art that specific material ratio, process conditions and its result described in embodiment are only used In illustrating the present invention, without the present invention described in detail in claims should will not be limited.
The present invention discloses a kind of environment-friendly composite fabric lining, including the first precoat and the second fabric being stacked Layer, be bonded between first precoat and second precoat by retardant adhesive layer, first precoat by Aramid fiber warp and aramid fiber weft mutually weave, and second precoat is by antibiotic cotton fiber warp and antibiotic cotton fiber weft It mutually weaves, is additionally provided with flame retardant coating on first precoat and second precoat, the flame retardant coating includes First flame retardant coating and the second flame retardant coating；Wherein, first flame retardant coating includes the composition of following parts by weight: the poly- ammonia of oiliness 80~100 parts of ester, 5~15 parts of phosphate flame retardant, 10~30 parts of ethyl acetate, 1~5 part of aluminium powder, 0.1~1 part of thickener；Institute State the composition that the second flame retardant coating includes following parts by weight: 80~100 parts of oiliness polyurethane, 10~20 parts of phosphate flame retardant, 20~50 parts of ethyl acetate, 5~10 parts of aluminium powder, 0.1~1 part of thickener.
It is following that environmentally friendly composite fibre fabric is illustrated in the present invention with specifically embodiment.
Embodiment 1
A kind of environment-friendly composite fabric lining, including the first precoat and the second precoat being stacked, described first It is bonded between precoat and second precoat by retardant adhesive layer, first precoat is twisted by 2 or 3 aramid fibers Weft made of warp made of system and 2 or 3 aramid fiber twistings mutually weaves, and second precoat is by 2 or 3 antibacterials Warp made of cotton fiber twisting and the weft as made of 2 or 3 antibiotic cotton fiber twistings mutually weave, first face The bed of material is equipped with one or both of the first flame retardant coating, the second flame retardant coating, and second precoat is equipped with the first resistance Fire one or both of coating, second flame retardant coating.
Wherein, first flame retardant coating includes the composition of following parts by weight: 80 parts of oiliness polyurethane, phosphate flame retardant 5 parts, 10 parts of ethyl acetate, 1 part of aluminium powder, 0.1 part of thickener；Second flame retardant coating includes the composition of following parts by weight: oil 80 parts of polyurethane, 10 parts of phosphate flame retardant, 20 parts of ethyl acetate, 5 parts of aluminium powder, 0.1 part of thickener of property.
Embodiment 2
A kind of environment-friendly composite fabric lining, including the first precoat and the second precoat being stacked, described first It is bonded between precoat and second precoat by retardant adhesive layer, first precoat is twisted by 2 or 3 aramid fibers Weft made of warp made of system and 2 or 3 aramid fiber twistings mutually weaves, and second precoat is by 2 or 3 antibacterials Warp made of cotton fiber twisting and the weft as made of 2 or 3 antibiotic cotton fiber twistings mutually weave, first face The bed of material is equipped with one or both of the first flame retardant coating, the second flame retardant coating, and second precoat is equipped with the first resistance Fire one or both of coating, second flame retardant coating.
Wherein, first flame retardant coating includes the composition of following parts by weight: 90 parts of oiliness polyurethane, phosphate flame retardant 10 parts, 20 parts of ethyl acetate, 3 parts of aluminium powder, 0.5 part of thickener；Second flame retardant coating includes the composition of following parts by weight: oil 90 parts of polyurethane, 15 parts of phosphate flame retardant, 35 parts of ethyl acetate, 7.5 parts of aluminium powder, 0.5 part of thickener of property.
Embodiment 3
A kind of environment-friendly composite fabric lining, including the first precoat and the second precoat being stacked, described first It is bonded between precoat and second precoat by retardant adhesive layer, first precoat is twisted by 2 or 3 aramid fibers Weft made of warp made of system and 2 or 3 aramid fiber twistings mutually weaves, and second precoat is by 2 or 3 antibacterials Warp made of cotton fiber twisting and the weft as made of 2 or 3 antibiotic cotton fiber twistings mutually weave, first face The bed of material is equipped with one or both of the first flame retardant coating, the second flame retardant coating, and second precoat is equipped with the first resistance Fire one or both of coating, second flame retardant coating.
Wherein, first flame retardant coating includes the composition of following parts by weight: 100 parts of oiliness polyurethane, organic phosphate flame-retardant 15 parts of agent, 30 parts of ethyl acetate, 5 parts of aluminium powder, 1 part of thickener；Second flame retardant coating includes the composition of following parts by weight: oil 100 parts of polyurethane, 20 parts of phosphate flame retardant, 50 parts of ethyl acetate, 10 parts of aluminium powder, 1 part of thickener of property.
Environment-friendly composite fabric lining in the present invention, which passes through, uses first precoat and second precoat Retardant adhesive layer is bonded, so that the environment-friendly composite fabric lining has certain flame retardant effect；Meanwhile by described Flame retardant coating is set on first precoat and second precoat, so that the flame retardant property of the fabric greatly improves, in the Heavenly Stems Object dry autumn and winter can give the protection of people's safety, have a good application prospect.
By the test for carrying out flame retardant property to the environment-friendly composite fabric lining in the present invention, the results showed that, the limit Oxygen index (OI) is 28.5~29.8.
Finally, it is to be noted that, the terms "include", "comprise" or its any other variant be intended to it is non-exclusive Property include so that include a series of elements process, method, article or equipment not only include those elements, but also Further include other elements that are not explicitly listed, or further include for this process, method, article or equipment it is intrinsic Element.

Claims (8)

1. a kind of environment-friendly composite fabric lining, which is characterized in that including the first precoat and the second precoat being stacked, It is bonded between first precoat and second precoat by retardant adhesive layer, first precoat is by aramid fiber Warp and aramid fiber weft mutually weave, and second precoat is mutual by antibiotic cotton fiber warp and antibiotic cotton fiber weft It weaves, flame retardant coating is additionally provided on first precoat and second precoat, the flame retardant coating includes first Flame retardant coating and the second flame retardant coating；Wherein, first flame retardant coating includes the composition of following parts by weight: oiliness polyurethane 80 ~100 parts, 5~15 parts of phosphate flame retardant, 10~30 parts of ethyl acetate, 1~5 part of aluminium powder, 0.1~1 part of thickener；Described Two flame retardant coatings include the composition of following parts by weight: 80~100 parts of oiliness polyurethane, 10~20 parts of phosphate flame retardant, and acetic acid 20~50 parts of ethyl ester, 5~10 parts of aluminium powder, 0.1~1 part of thickener.
2. environment-friendly composite fabric lining according to claim 1, which is characterized in that first precoat is equipped with the One or both of one flame retardant coating, second flame retardant coating, second precoat are equipped with the first flame retardant coating, the second resistance Fire one or both of coating.
3. environment-friendly composite fabric lining according to claim 1, which is characterized in that each aramid fiber warp and each The aramid fiber weft is formed by 2~3 aramid fiber twistings.
4. environment-friendly composite fabric lining according to claim 1, which is characterized in that each antibiotic cotton fiber warp It is formed with each antibiotic cotton fiber weft by 2~3 antibiotic cotton fiber twistings.
5. environment-friendly composite fabric lining according to claim 1 or 4, which is characterized in that the antibiotic cotton fiber warp It is made with the antibiotic cotton fiber weft of nanometer silver antimicrobial cotton fiber.
6. environment-friendly composite fabric lining according to claim 1, which is characterized in that the adhesive layer is polyvinyl alcohol ring Protect glue.
7. environment-friendly composite fabric lining according to claim 1, which is characterized in that the adhesive layer with a thickness of 0.10 ~0.15mm.
8. environment-friendly composite fabric lining according to claim 1, which is characterized in that first flame retardant coating include with The composition of lower parts by weight: 90 parts of oiliness polyurethane, 10 parts of phosphate flame retardant, 20 parts of ethyl acetate, 3 parts of aluminium powder, thickener 0.5 Part；Second flame retardant coating includes the composition of following parts by weight: 90 parts of oiliness polyurethane, 15 parts of phosphate flame retardant, and acetic acid 35 parts of ethyl ester, 7.5 parts of aluminium powder, 0.5 part of thickener.
CN201811176661.4A 2018-10-10 2018-10-10 A kind of environment-friendly composite fabric lining Pending CN109466127A (en)