CN104441845A - High-flame retardance glass fiber knitted fabric - Google Patents
High-flame retardance glass fiber knitted fabric Download PDFInfo
- Publication number
- CN104441845A CN104441845A CN201410699779.0A CN201410699779A CN104441845A CN 104441845 A CN104441845 A CN 104441845A CN 201410699779 A CN201410699779 A CN 201410699779A CN 104441845 A CN104441845 A CN 104441845A
- Authority
- CN
- China
- Prior art keywords
- glass fiber
- cloth
- flame retardant
- glass fibre
- flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses high-flame retardance glass fiber knitted fabric, and belongs to the technical field of flame-retardant fabric. The high-flame retardance glass fiber knitted fabric comprises glass fiber base cloth, and is characterized in that a flame-retardant rubber layer is arranged on the surface of one outward side of the glass fiber base cloth in a using state; non-woven fabric is combined on the surface of the flame-retardant rubber layer; the glass fiber base cloth is in plain weave; the kilometer weight of glass fibers forming the glass fiber base cloth is 10-3000TEX. The glass fiber base cloth has an inherent flame-retardant effect of an inorganic non-metallic material, so that high-flame retardance glass fiber knitted fabric can play a flame-retardant function lastingly; the glass non-woven fabric is combined on one side surface of the fiber base cloth, so that requirements of bedroom supplies and car inner decorations can be met; the non-woven fabric is combined with the glass fiber base cloth, so that a natural resilience problem of the non-woven fabric can be made up.
Description
Technical field
The invention belongs to inflaming retarding fabric technical field, be specifically related to a kind of high flame retardant glass fibre knitting cloth.
Background technology
The flame retardant effect of the inflaming retarding fabric in prior art is mostly by embodying adding fire retardant in the finishing process of fabric, although this inflaming retarding fabric has certain flame retardant effect, but because fire retardant is attached on fabric (i.e. base cloth) with artificial addition manner, base cloth self does not exist and the anti-flaming function had, and due to the quality of flame retardant effect and the characteristic of fire retardant and relevant with the adhesion of base cloth, thus As time goes on particularly the increase flame retardant effect of washing times fails and even better than nothing gradually.Perhaps based on this factor, this inflaming retarding fabric gradually suffers people's cold reception, though have the heart of improvement at present, but there is no the plan of reply.
Chinese invention patent Authorization Notice No. CN101696549B recommends to be had " a kind of flame retardant glass fiber mesh ", it impregnated in fire retardant glue using the glass fiber mesh as base cloth, fire-retardant surface layer is formed on the surface of glass fiber mesh, this flame retardant glass fiber mesh is applicable to industry and civil buildings, can not use as bedroom dress product and automobile interior product.
Chinese invention patent Authorization Notice No. CN101886339B provides " glass fiber flame retardant silica gel cloth and preparation method thereof ", this patent is exactly in conjunction with anti-corrosion flame-retardant layer at least one side surface of the glass fabric as base cloth, this anti-corrosion flame-retardant layer is made up of the raw material of following parts by weight: melting silicone rubber 60-70 part, fire retardant 25-30 part, colorant 2-5 part and vulcanizing agent 0.1-0.5 part, wherein: fire retardant is one or more the combination in aluminium hydroxide, magnesium hydroxide, antimony oxide, deca-BDE.The glass fibre silicone fabric that this patent formula provides is mainly used in flexibly connecting and sealing of Aero-Space navigation, the production of oil medication chemistry, traffic, generating, HVAC and Architectural Equipment and electric plant equipment, namely use as the cloth that is flexible coupling, can not get into bed dress product and automobile interior trim product be used as equally.
" flame retardant knitted cloth " that Chinese utility model patent Authorization Notice No. CN202482595U introduces is made into by fire resistance fibre yarn, fire resistance fibre yarn is formed by least two strands of single thread twisteds, fire-retardant single thread is flame-resistant terylene monofilament or flame-retardant acrylic fibre monofilament, and this flame retardant knitted cloth can be used as getting into bed dress articles for use and can be used for vehicle interior trim.But as is known in the industry, flame-resistant terylene silk or flame-retardant acrylic fibre silk are that the phosphorus flame retardant adding such as red phosphorus, phosphate or halogenated phosphate and so in spinning process obtains, be not terylene, the fire resistance that innately has of acrylic fibers, thus as aforementioned, along with the increase of passage of time and washing times, flame retardant effect can be faded.Especially the flame retardant knitted cloth that obtains of this patent is large due to natural resilience, thus can affect result of use.
For above-mentioned prior art, be necessary to be improved, the applicant has done useful design for this reason, defines technical scheme described below, and is taking to the experiment proved that it is practicable under secrecy provision.
Summary of the invention
Task of the present invention is to provide a kind of high flame retardant glass fibre knitting cloth contributing to ensureing lasting flame retardant effect and be conducive to eliminating nature resilience and use the instructions for use meeting get into bed dress articles for use and automotive upholstery.
Task of the present invention has been come like this, a kind of high flame retardant glass fibre knitting cloth, comprise fiberglass-based cloth, be characterised in that: under described fiberglass-based cloth using state, a side surface is toward the outside provided with fire-retardant glue-line, non-woven fabrics is had at the surface conjunction of fire-retardant glue-line, described fiberglass-based cloth be organized as plain weave, and the km weight forming the glass fibre of fiberglass-based cloth is 10-3000TEX.
In a specific embodiment of the present invention, described fiberglass-based cloth is the fiberglass-based cloth that acquisition is weaved in weft knitting.
In another specific embodiment of the present invention, the grammes per square metre of described fiberglass-based cloth is 200-300g/ ㎡.
In another specific embodiment of the present invention, the grammes per square metre of described non-woven fabrics is 20-30g/ ㎡.
In another specific embodiment of the present invention, the thickness of described fire-retardant glue-line is 30-60 μm.
Also have in a specific embodiment of the present invention, described non-woven fabrics is the non-woven fabrics obtained through needing machine acupuncture by chemical fibre.
More of the present invention and in a specific embodiment, described chemical fibre is polyster fibre, acrylic fiber or the third fiberoptic fiber.
In an of the present invention and then specific embodiment, described fire-retardant glue-line is flame-proof environmental protection water-based compound adhesive.
Technical scheme provided by the invention has the intrinsic flame retardant effect of Inorganic Non-metallic Materials due to fiberglass-based cloth, thus can play anti-flaming function enduringly; Because the side surface conjunction at fiberglass-based cloth has non-woven fabrics, the requirement of get into bed dress articles for use and automobile interior trim thus can be met; Because non-woven fabrics combines with fiberglass-based cloth, the natural resilience problem of non-woven fabrics thus can be made up.
Accompanying drawing explanation
Fig. 1 is embodiments of the invention structure chart.
Detailed description of the invention
Embodiment 1:
Refer to Fig. 1, figure 1 illustrates and weave by weft knitting the fiberglass-based cloth 1 namely being weaved acquisition by weft-knitted machinery, the fabric tissue of this fiberglass-based cloth 1 is plain weave, and grammes per square metre is 200g/ ㎡, in the present embodiment, the km weight of the glass fibre of fiberglass-based cloth 1 is 3000TEX.Under fiberglass-based cloth 1 using state, a side surface toward the outside preferably adopts applicator roll to be coated with fire-retardant glue-line 11, the thickness of fire-retardant glue-line 11 is 60 μm, this fire-retardant glue-line 11 is environment-friendly water-based compound adhesive, and preferably use produced by Jiangsu Province, China Zhangjagang City Yong Li adhesive Co., Ltd and be ZJJ-II A type adhesive at the trade mark of market public offering before the present invention proposes.Also show the non-woven fabrics 2 on the surface being incorporated into foregoing flame retardant glue-line 11 in Fig. 1, this non-woven fabrics 2 is obtained by the needing machine acupuncture of polyster fibre through Nonwoven Machinery category, and grammes per square metre is 20g/ ㎡.
Embodiment 2:
Only change the grammes per square metre of fiberglass-based cloth 1 into 300g/ ㎡, the km Change Weight To 1500TEX of glass fibre, the thickness of fire-retardant glue-line 11 changes 45 μm into, and the grammes per square metre of non-woven fabrics 2 changes 30g/ ㎡ into, the fiber of non-woven fabrics 2 changes acrylic fiber into, and all the other are all with the description to embodiment 1.
Embodiment 3:
Only change the grammes per square metre of fiberglass-based cloth 1 into 250g/ ㎡, the km Change Weight To 20TEX of glass fibre, the thickness of fire-retardant glue-line 11 changes 30 μm into, and the grammes per square metre of non-woven fabrics 2 changes 25g/ ㎡ into, the fiber of non-woven fabrics 2 changes polypropylene fiber into, and all the other are all with the description to embodiment 1.
Claims (8)
1. a high flame retardant glass fibre knitting cloth, comprise fiberglass-based cloth (1), it is characterized in that: under described fiberglass-based cloth (1) using state, a side surface is toward the outside provided with fire-retardant glue-line (11), non-woven fabrics (2) is had at the surface conjunction of fire-retardant glue-line (11), described fiberglass-based cloth (1) be organized as plain weave, and the km weight forming the glass fibre of fiberglass-based cloth (1) is 10-3000TEX.
2. high flame retardant glass fibre knitting cloth according to claim 1, is characterized in that described fiberglass-based cloth (1) is the fiberglass-based cloth that acquisition is weaved in weft knitting.
3. high flame retardant glass fibre knitting cloth according to claim 1 and 2, is characterized in that the grammes per square metre of described fiberglass-based cloth (1) is 200-300g/ ㎡.
4. high flame retardant glass fibre knitting cloth according to claim 1, is characterized in that the grammes per square metre of described non-woven fabrics (2) is 20-30g/ ㎡.
5. high flame retardant glass fibre knitting cloth according to claim 1, is characterized in that the thickness of described fire-retardant glue-line (11) is 30-60 μm.
6. the high flame retardant glass fibre knitting cloth according to claim 1 or 4, is characterized in that described non-woven fabrics (2) is the non-woven fabrics obtained through needing machine acupuncture by chemical fibre.
7. high flame retardant glass fibre knitting cloth according to claim 6, is characterized in that described chemical fibre is polyster fibre, acrylic fiber or the third fiberoptic fiber.
8. high flame retardant glass fibre knitting cloth according to claim 1 or 5, is characterized in that described fire-retardant glue-line (11) is for flame-proof environmental protection water-based compound adhesive.