CN109465934A - A kind of mobile phone shell manufacture craft - Google Patents
A kind of mobile phone shell manufacture craft Download PDFInfo
- Publication number
- CN109465934A CN109465934A CN201811412131.5A CN201811412131A CN109465934A CN 109465934 A CN109465934 A CN 109465934A CN 201811412131 A CN201811412131 A CN 201811412131A CN 109465934 A CN109465934 A CN 109465934A
- Authority
- CN
- China
- Prior art keywords
- bamboo wood
- mobile phone
- main body
- thermal grease
- bamboo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of mobile phone shell manufacture crafts, manufacture craft including bamboo wood main body and bamboo wood main body, the bamboo wood body surfaces are bleaching colouring processing, the back side of the bamboo wood main body is equipped with pad and sets thermal grease, and the production of the bamboo wood main body is prepared by the raw material of following mass percent: bleaching agent solution 0.5-1.5%, acetum 4-6%, buck 75-85%, sulfur dioxide 4-6%, phenolic resin glue 8-10% and bamboo wood surplus.Present invention employs bamboo woods to be made; further reducing plastics is to use; bamboo wood memory by being cut into item by the invention; processing and fabricating is carried out, then carries out being designed assembly according to mobile phone shape, and the mobile phone protecting case of bamboo wood production is adhered to phone housing by thermal grease; the bonding of thermal grease can more preferably radiate to mobile phone; and thermal grease cleaning is easy, and prevents from being adhered to mobile phone being difficult to clear up, the setting directly bonded can make to assemble and disassemble more convenient.
Description
Technical field
The present invention relates to mobile phone shell fields, and in particular to a kind of mobile phone shell manufacture craft.
Background technique
Mobile phone increasingly becomes one of the requirement of modern life, makees under the various situations such as the modern life, work contact
With more and more important, therefore, the aesthetics of mobile phone, the robustness of handset shell, the factors such as cost of buying mobile phone are required
Producer constantly improve, and the manufacturing cost of the especially metal shell of mobile phone directly affects the totle drilling cost of mobile phone.
Mobile phone shell employed in society is all made of the phone housing of sleeve type now, and this mobile phone can be with effective protection hand
Outside machine, and this sleeve type mobile phone shell can carry out the change of a variety of styles on the outside, make mobile phone appearance more beautiful, but
Be in the market used by mobile phone shell be all made of plastics carry out processing and fabricating, and the mobile phone shell of plastic production not environmentally except,
It is also easy to heated denaturalization and oxidation stain, and some mobile phone shells plastics harder using the quality of bite type now, still
Such phone housing dismounting trouble, causes certain trouble.
Summary of the invention
The processing is simple and low-cost mobile phone shell manufacture craft there is provided one kind for an object of the present invention.
A kind of mobile phone shell manufacture craft, the manufacture craft including bamboo wood main body and bamboo wood main body, which is characterized in that institute
The bamboo wood body surfaces stated are bleaching colouring processing, and the back side of the bamboo wood main body is equipped with pad and sets thermal grease, the bamboo
The production of material main body is prepared by the raw material of following mass percent: bleaching agent solution 0.5-1.5%, acetum 4-6%,
Buck 75-85%, sulfur dioxide 4-6%, phenolic resin glue 8-10% and bamboo wood surplus,
Preferably, the bamboo wood main body production the following steps are included:
(1) cutting bamboo wood is 1.2 millimeters of thickness or more, and a number of bamboo wood is put in 8 millimeters of width or more of bar shaped
Out in reaction kettle, bleaching is carried out to bamboo wood and is taken out, bamboo wood is placed and is dried on dryer, carries out passing through heat after drying
Handle thermal grease be adhered to processing on the outside of mobile phone.
(2) bleaching process for bamboo material: bamboo wood is put into Eusol and is impregnated 1 hour, impregnates and pulls out later, it is molten to put acetic acid into
Impregnate 30 minutes, cleaned finally by clear water, and be placed to dry in liquid, the bamboo wood be placed to dry in be put into sealing container,
And sulfur dioxide gas is injected, place 4 hours.
(3) painting methods of bamboo wood: bamboo wood is placed in buck and is boiled 5 minutes, taking-up is placed to dry, and finally places phenolic aldehyde
It is impregnated in resin glue.
Preferably, thermal grease production is prepared by the raw material of following mass percent: silane coupling agent 35-
45%, silica 1 4-16%, cumyl peroxide 25-27%, reinforcing agent 10-13%, plasticizer surplus.
Preferably, the production method of thermal grease production are as follows: by silane coupling agent, silica, peroxidating two
Isopropylbenzene, reinforcing agent, plasticizer pour into blender together and are stirred, and coating is in the bamboo wood main body one after mixing evenly
Side.
Present invention employs bamboo woods to be made, and further reducing plastics is to use, which passes through bamboo wood memory
It is cut into item, carries out processing and fabricating, then carry out being designed assembly according to mobile phone shape, and the mobile phone protecting case of bamboo wood production
It is adhered to phone housing by thermal grease, the bonding of thermal grease can more preferably radiate to mobile phone, and thermal grease
Cleaning is easy, and prevents from being adhered to mobile phone being difficult to clear up, the setting directly bonded can make to assemble and disassemble more convenient.
Specific embodiment
Specific implementation case 1: a kind of mobile phone shell manufacture craft, the manufacture craft including bamboo wood main body and bamboo wood main body,
It is characterized in that, the bamboo wood body surfaces are bleaching colouring processing, the back side of the bamboo wood main body is equipped with pad and sets heat dissipation
The production of silica gel, the bamboo wood main body is prepared by the raw material of following mass percent: bleaching agent solution 0.5%, acetic acid
Solution 4%, buck 75%, sulfur dioxide 4%, phenolic resin glue 8% and bamboo wood surplus,
Preferably, the bamboo wood main body production the following steps are included:
(1) cutting bamboo wood is 1.2 millimeters of thickness or more, and a number of bamboo wood is put in 8 millimeters of width or more of bar shaped
Out in reaction kettle, bleaching is carried out to bamboo wood and is taken out, bamboo wood is placed and is dried on dryer, carries out passing through heat after drying
Handle thermal grease be adhered to processing on the outside of mobile phone.
(2) bleaching process for bamboo material: bamboo wood is put into Eusol and is impregnated 0.5 hour, impregnates and pulls out later, put acetic acid into
Impregnate 30 minutes, cleaned finally by clear water, and be placed to dry in solution, the bamboo wood be placed to dry in be put into sealing hold
Device, and sulfur dioxide gas is injected, place 3 hours.
(3) painting methods of bamboo wood: bamboo wood is placed in buck and is boiled 4 minutes, taking-up is placed to dry, and finally places phenolic aldehyde
It is impregnated in resin glue.
Preferably, thermal grease production is prepared by the raw material of following mass percent: silane coupling agent
35%, silica 1 4%, cumyl peroxide 25%, reinforcing agent 10%, plasticizer surplus.
The production method of the described thermal grease production are as follows: by silane coupling agent, silica, cumyl peroxide,
Reinforcing agent, plasticizer pour into blender together and are stirred, and coating is in the bamboo wood body side after mixing evenly.
Specific implementation case 2: a kind of mobile phone shell manufacture craft, the manufacture craft including bamboo wood main body and bamboo wood main body,
It is characterized in that, the bamboo wood body surfaces are bleaching colouring processing, the back side of the bamboo wood main body is equipped with pad and sets heat dissipation
The production of silica gel, the bamboo wood main body is prepared by the raw material of following mass percent: bleaching agent solution 1%, acetic acid are molten
Liquid 5%, buck 80%, sulfur dioxide 5%, phenolic resin glue 9% and bamboo wood surplus,
The production of the bamboo wood main body the following steps are included:
(1) cutting bamboo wood is 1.2 millimeters of thickness or more, and a number of bamboo wood is put in 8 millimeters of width or more of bar shaped
Out in reaction kettle, bleaching is carried out to bamboo wood and is taken out, bamboo wood is placed and is dried on dryer, carries out passing through heat after drying
Handle thermal grease be adhered to processing on the outside of mobile phone.
(2) bleaching process for bamboo material: bamboo wood is put into Eusol and is impregnated 1 hour, impregnates and pulls out later, it is molten to put acetic acid into
Impregnate 30 minutes, cleaned finally by clear water, and be placed to dry in liquid, the bamboo wood be placed to dry in be put into sealing container,
And sulfur dioxide gas is injected, place 4 hours.
(3) painting methods of bamboo wood: bamboo wood is placed in buck and is boiled 5 minutes, taking-up is placed to dry, and finally places phenolic aldehyde
It is impregnated in resin glue.
The thermal grease production is prepared by the raw material of following mass percent: silane coupling agent 40%, dioxy
SiClx 15%, cumyl peroxide 26%, reinforcing agent 12%, plasticizer surplus.
The production method of the described thermal grease production are as follows: by silane coupling agent, silica, cumyl peroxide,
Reinforcing agent, plasticizer pour into blender together and are stirred, and coating is in the bamboo wood body side after mixing evenly.
Specific implementation case 3: a kind of mobile phone shell manufacture craft, the manufacture craft including bamboo wood main body and bamboo wood main body,
It is characterized in that, the bamboo wood body surfaces are bleaching colouring processing, the back side of the bamboo wood main body is equipped with pad and sets heat dissipation
The production of silica gel, the bamboo wood main body is prepared by the raw material of following mass percent: bleaching agent solution 1.5%, acetic acid
Solution 4%, buck 85%, sulfur dioxide 4%, phenolic resin glue 8% and bamboo wood surplus,
The production of the bamboo wood main body the following steps are included:
(1) cutting bamboo wood is 1.2 millimeters of thickness or more, and a number of bamboo wood is put in 8 millimeters of width or more of bar shaped
Out in reaction kettle, bleaching is carried out to bamboo wood and is taken out, bamboo wood is placed and is dried on dryer, carries out passing through heat after drying
Handle thermal grease be adhered to processing on the outside of mobile phone.
(2) bleaching process for bamboo material: bamboo wood is put into Eusol and is impregnated 1.5 hours, impregnates and pulls out later, put acetic acid into
Impregnate 50 minutes, cleaned finally by clear water, and be placed to dry in solution, the bamboo wood be placed to dry in be put into sealing hold
Device, and sulfur dioxide gas is injected, place 5 hours.
(3) painting methods of bamboo wood: bamboo wood is placed in buck and is boiled 10 minutes, taking-up is placed to dry, and finally places phenol
It is impregnated in urea formaldehyde glue.
The thermal grease production is prepared by the raw material of following mass percent: silane coupling agent 45%, dioxy
SiClx 16%, cumyl peroxide 27%, reinforcing agent 13%, plasticizer surplus.
The production method of the described thermal grease production are as follows: by silane coupling agent, silica, cumyl peroxide,
Reinforcing agent, plasticizer pour into blender together and are stirred, and coating is in the bamboo wood body side after mixing evenly.
Present invention employs bamboo woods to be made, and further reducing plastics is to use, which passes through bamboo wood memory
It is cut into item, carries out processing and fabricating, then carry out being designed assembly according to mobile phone shape, and the mobile phone protecting case of bamboo wood production
It is adhered to phone housing by thermal grease, the bonding of thermal grease can more preferably radiate to mobile phone, and thermal grease
Cleaning is easy, and prevents from being adhered to mobile phone being difficult to clear up, the setting directly bonded can make to assemble and disassemble more convenient.
It, for the ordinary skill in the art, can be with although having shown and having described the embodiment of the present invention
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And deformation, the scope of the present invention is defined by the appended.
Claims (4)
1. a kind of mobile phone shell manufacture craft, the manufacture craft including bamboo wood main body and bamboo wood main body, which is characterized in that described
Bamboo wood body surfaces are bleaching colouring processing, and the back side of the bamboo wood main body is equipped with pad and sets thermal grease, the bamboo wood master
The production of body is prepared by the raw material of following mass percent: bleaching agent solution 0.5-1.5%, acetum 4-6%, buck
75-85%, sulfur dioxide 4-6%, phenolic resin glue 8-10% and bamboo wood surplus.
2. a kind of mobile phone shell manufacture craft according to claim 1, which is characterized in that the production packet of the bamboo wood main body
Include following steps:
(1) cutting bamboo wood is 1.2 millimeters of thickness or more, 8 millimeters of width or more of bar shaped, a number of bamboo wood is released anti-
It answers in kettle, bleaching is carried out to bamboo wood and is taken out, bamboo wood is placed and is dried on dryer, is carried out after drying through hot pressing handle
Thermal grease be adhered to processing on the outside of mobile phone.
(2) bleaching process for bamboo material: bamboo wood is put into Eusol and is impregnated 1 hour, impregnates and pulls out later, put into acetum
Impregnate 30 minutes, cleaned finally by clear water, and be placed to dry, the bamboo wood be placed to dry in be put into sealing container, and infuse
Enter sulfur dioxide gas, places 4 hours.
(3) painting methods of bamboo wood: bamboo wood is placed in buck and is boiled 5 minutes, taking-up is placed to dry, and finally places phenolic resin
It is impregnated in glue.
3. a kind of mobile phone shell manufacture craft according to claim 1, which is characterized in that the described thermal grease production by with
The raw material of lower mass percent is prepared: silane coupling agent 35-45%, silica 1 4-16%, cumyl peroxide
25-27%, reinforcing agent 10-13%, plasticizer surplus.
4. a kind of mobile phone shell manufacture craft according to claim 1, which is characterized in that the system of the thermal grease production
Make method are as follows: silane coupling agent, silica, cumyl peroxide, reinforcing agent, plasticizer are poured into blender together and carried out
Stirring, coating is in the bamboo wood body side after mixing evenly.