CN109457483A - A kind of preparation method of high-strength and waterproofing Ventilate cloth - Google Patents
A kind of preparation method of high-strength and waterproofing Ventilate cloth Download PDFInfo
- Publication number
- CN109457483A CN109457483A CN201811170213.3A CN201811170213A CN109457483A CN 109457483 A CN109457483 A CN 109457483A CN 201811170213 A CN201811170213 A CN 201811170213A CN 109457483 A CN109457483 A CN 109457483A
- Authority
- CN
- China
- Prior art keywords
- cloth
- degree
- raw material
- parts
- waterproofing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation methods of high-strength and waterproofing Ventilate cloth, it is characterized in that, include the following steps: pretreatment of raw material, soft finish, washing drying, padding finishing, lamination treatment and raw material printing and dyeing, pretreatment of raw material is that raw material is placed on to the impurity that the attachment of raw material surface is removed in cloth de-burring machine, soft finish is according to mass fraction meter, 5-10 parts of polyether silicone oils are added in 10-20 parts of ethyl alcohol, practical blender is stirred, rotating speed of agitator is 100 rpms, whipping temp control is in 40-45 degree, add 120-150 parts of water, 50 degree are warming up to 2 degree of heating rates per minute, 2 parts of glacial acetic acid are added, continue to examine according to 1 degree of heating rate per minute and is warming up to 55 degree, the preparation method of this high-strength and waterproofing Ventilate cloth is existed using the operation mode of continuous warming The original structure that cloth is utmostly protected under the premise of cloth treatment process is completed, so that product of the cloth in the later period is the perfect of guarantee quality.
Description
Technical field
The invention belongs to cloth preparation technical field, spy is involved a kind of preparation method of high-strength and waterproofing Ventilate cloth.
Background technique
The most resource consumption of the preparation method of traditional cloth is big, and batch prepares and is difficult effectively to guarantee every cloth
Quality, and traditional cloth waterproof and breathable performance is more general, needs to design a kind of system of high-strength and waterproofing Ventilate cloth to this
Preparation Method.
Summary of the invention:
The object of the invention is that in order to solve the problems, such as to be previously mentioned in above-mentioned background technique, and provide a kind of high-strength anti-
The preparation method of water Ventilate cloth solves the problems, such as of the existing technology.
To solve the above-mentioned problems, the present invention provides a kind of technical solutions: a kind of preparation of high-strength and waterproofing Ventilate cloth
Method, which comprises the steps of: pretreatment of raw material, soft finish, washing drying, padding finishing, lamination treatment and
Raw material printing and dyeing；
Preferably, the pretreatment of raw material is to be placed on raw material to remove the miscellaneous of raw material surface attachment in cloth de-burring machine
Matter.
Preferably, the soft finish is that 5-10 parts of polyether silicone oils are added 10-20 parts according to mass fraction meter
In ethyl alcohol, practical blender is stirred, and rotating speed of agitator is 100 rpms, and whipping temp control is spent 40-45, then plus
Enter 120-150 parts of water, be warming up to 50 degree with 2 degree of heating rates per minute, 2 parts of glacial acetic acid are added, continues according to 1 degree every point
The heating rate of clock is examined and is warming up to 55 degree, and 1-3 parts of lecithin are added, this process blender is kept stirring, to be mixed uniform
Afterwards, finishing fluid is obtained, will be put into truth liquid by pretreated raw material, continues to heat up according to 2 degree of heating rates per minute
To 65 degree, constant temperature impregnates 3 hours, spare.
Preferably, the washing drying is will to be put into cleaning machine to clean into the raw material after soft finish excessively, water temperature control
For system at 40 degree, washing time is 10 minutes, and raw material is put into 0.8-0.9MPa after washing, and 50-55 degree are lower to carry out vacuum
Drying.
Preferably, the padding finishing is stirred evenly, at the beginning of water temperature in the water for put into 2-3 parts of sodium fluoborates 80 parts
Beginning temperature is 50 degree, is warming up to 70 degree according to 2 degree of heating rates per minute, adds 10 to 12 parts of water-base fluorocarbon emulsion,
Be again stirring for uniformly, then by by washing drying after to raw material be put into carry out padding finishing operation.
Preferably, the lamination treatment is to carry out lamination realization using PTFE (polytetrafluoroethylene (PTFE)) film and raw material,
PTFE (polytetrafluoroethylene (PTFE)) film spreading glue between raw material merges operation in 70 to 80 at a temperature of progress glue, needs
By washing several times, part glue is washed away, can be increased with hole, Air permenbility rises；Meanwhile the clothes that the fabric is made into may be used also
To block the invading into the heat for preventing wind from distributing stature through cloth is taken away, and feels stature because of the forfeiture of heat of cold wind
To air-cooled.
Preferably, the raw material printing and dyeing are including scouringing and bleaching, dyeing, four steps of stamp and arrangement, concrete operations are as follows:
A, scouring and bleaching-original cloth tested, turn over cloth, in batches, branch mailbox, printing and margin to seam, then into crossing operation of singing, burning-off
Villus on original cloth surface, so that the bright and clean beauty of cloth surface, the slurry in original cloth can be used alkali desizing and carry out desizing operation, by it
It is stripped from fabric, caustic soda and other kierings assistant agent and pectic substance, waxy substance, nitrogen substance, cotton seed hulls is recycled to occur
Chemical degradation reaction, Swelling Functions, strips impurity from original cloth after washing at emulsification, will be into crossing the original cloth after kiering
Bleaching operation is carried out using peroxide passivation, finally at low temperature by original cloth, under the premise of direction of warp and weft actuates power, with dense
Soda bath processing, improves original cloth performance；
B, dyeing-by the cloth after scouringing and bleaching 120-130 degree temperature environment and 4.7 to 5.2 PH value under plus
Enter dyeing assistant and carries out dyeing operation；
C, stamp-elder generation prints the resist agent that can prevent contaminating on dyestuff on cloth, then pad dyeing background color, is printed at decorative pattern
It can prevent from contaminating on background color；
D, it arranges-finally needs to carry out cloth sanding according to actual processing, press polish, embossing, flocking, coating, answers
It conjunction, gold stamping, stamp, clipping and carving, napping and crumples.
Beneficial effects of the present invention: the present invention relates to a kind of preparation methods of high-strength and waterproofing Ventilate cloth, have printing and dyeing high
The characteristics of effect, quality ensures, it is specific in use, compared with the preparation method of traditional high-strength and waterproofing Ventilate cloth and
Speech, the preparation method of this high-strength and waterproofing Ventilate cloth is using the operation mode of continuous warming in the premise for completing cloth treatment process
Under utmostly protect the original structure of cloth so that product of the cloth in the later period is guarantee quality perfect.
Detailed description of the invention:
Detailed description will be given by the following detailed implementation and drawings by the present invention for ease of explanation,.
Fig. 1 is present invention production processing process schematic diagram；
Specific embodiment:
As shown in Figure 1, present embodiment uses a kind of following technical scheme: preparation side of high-strength and waterproofing Ventilate cloth
Method, which comprises the steps of: pretreatment of raw material, soft finish, washing drying, padding finishing, lamination treatment and original
Material printing and dyeing；
Wherein, the pretreatment of raw material is that raw material is placed on to the impurity that the attachment of raw material surface is removed in cloth de-burring machine.
Wherein, the soft finish is that 10-20 parts of ethyl alcohol are added in 5-10 parts of polyether silicone oils according to mass fraction meter
In, practical blender is stirred, and rotating speed of agitator is 100 rpms, and whipping temp control is added in 40-45 degree
120-150 parts of water are warming up to 50 degree with 2 degree of heating rates per minute, and 2 parts of glacial acetic acid are added, and continue according to 1 degree per minute
Heating rate examine be warming up to 55 degree, add 1-3 parts of lecithin, this process blender is kept stirring, it is to be mixed uniformly after,
Finishing fluid is obtained, will be put into truth liquid by pretreated raw material, continues to be warming up to 65 according to 2 degree of heating rates per minute
Degree, constant temperature impregnates 3 hours, spare.
Wherein, the washing drying is will to be put into cleaning machine to clean into the raw material after soft finish excessively, and water temperature control exists
40 degree, washing time is 10 minutes, and raw material is put into 0.8-0.9MPa after washing, and 50-55 degree are lower to carry out vacuum drying.
Wherein, the padding finishing is stirred evenly, water temperature is initially warm in the water for put into 2-3 parts of sodium fluoborates 80 parts
Degree is 50 degree, is warming up to 70 degree according to 2 degree of heating rates per minute, adds 10 to 12 parts of water-base fluorocarbon emulsion, again
Stir evenly, then by by washing drying after to raw material be put into carry out padding finishing operation.
Wherein, the lamination treatment is to carry out lamination realization using PTFE (polytetrafluoroethylene (PTFE)) film and raw material, in PTFE
(polytetrafluoroethylene (PTFE)) film spreading glue between raw material, 70 to 80 at a temperature of carry out glue merge operation, need by
It washes several times, part glue is washed away, can be increased with hole, Air permenbility rises；Meanwhile the clothes that the fabric is made into can also block
Resistance cold wind is invaded into the heat for preventing wind from distributing stature through cloth is taken away, and stature is made not feel wind because of the forfeiture of heat
It is cold.
Wherein, raw material printing and dyeing include scouringing and bleaching, dyeing, stamp and arranging four steps, and concrete operations are as follows:
A, scouring and bleaching-original cloth tested, turn over cloth, in batches, branch mailbox, printing and margin to seam, then into crossing operation of singing, burning-off
Villus on original cloth surface, so that the bright and clean beauty of cloth surface, the slurry in original cloth can be used alkali desizing and carry out desizing operation, by it
It is stripped from fabric, caustic soda and other kierings assistant agent and pectic substance, waxy substance, nitrogen substance, cotton seed hulls is recycled to occur
Chemical degradation reaction, Swelling Functions, strips impurity from original cloth after washing at emulsification, will be into crossing the original cloth after kiering
Bleaching operation is carried out using peroxide passivation, finally at low temperature by original cloth, under the premise of direction of warp and weft actuates power, with dense
Soda bath processing, improves original cloth performance；
B, dyeing-by the cloth after scouringing and bleaching 120-130 degree temperature environment and 4.7 to 5.2 PH value under plus
Enter dyeing assistant and carries out dyeing operation；
C, stamp-elder generation prints the resist agent that can prevent contaminating on dyestuff on cloth, then pad dyeing background color, is printed at decorative pattern
It can prevent from contaminating on background color；
D, it arranges-finally needs to carry out cloth sanding according to actual processing, press polish, embossing, flocking, coating, answers
It conjunction, gold stamping, stamp, clipping and carving, napping and crumples.
Beneficial effects of the present invention: the present invention relates to a kind of preparation methods of high-strength and waterproofing Ventilate cloth, have printing and dyeing high
The characteristics of effect, quality ensures, it is specific in use, compared with the preparation method of traditional high-strength and waterproofing Ventilate cloth and
Speech, the preparation method of this high-strength and waterproofing Ventilate cloth is using the operation mode of continuous warming in the premise for completing cloth treatment process
Under utmostly protect the original structure of cloth so that product of the cloth in the later period is guarantee quality perfect.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention, the technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention, the claimed scope of the invention by appended claims and its
Effect object defines.
Claims (7)
1. a kind of preparation method of high-strength and waterproofing Ventilate cloth, which comprises the steps of: pretreatment of raw material, softness
It arranges, wash drying, padding finishing, lamination treatment and raw material printing and dyeing.
2. a kind of preparation method of high-strength and waterproofing Ventilate cloth according to claim 1, it is characterised in that: the raw material is pre-
Processing is that raw material is placed on to the impurity that the attachment of raw material surface is removed in cloth de-burring machine.
3. a kind of preparation method of high-strength and waterproofing Ventilate cloth according to claim 1, it is characterised in that: the softness is whole
Reason is 5-10 parts of polyether silicone oils to be added in 10-20 parts of ethyl alcohol, practical blender is stirred, and is stirred according to mass fraction meter
Mix paddle revolving speed be 100 rpms, whipping temp control 40-45 degree, add 120-150 parts of water, with 2 degree per minute
Heating rate is warming up to 50 degree, is added 2 parts of glacial acetic acid, continues to be warming up to 55 degree according to 1 degree heating rate per minute is careful, then plus
Enter 1-3 parts of lecithin, this process blender is kept stirring, it is to be mixed uniformly after, obtain finishing fluid, pretreated original will be passed through
Material is put into truth liquid, continues to be warming up to 65 degree according to 2 degree of heating rates per minute, constant temperature impregnates 3 hours, spare.
4. a kind of preparation method of high-strength and waterproofing Ventilate cloth according to claim 1, it is characterised in that: the washing is dried
Dry is that will be put into cleaning machine to clean into the raw material after soft finish excessively, and water temperature control is at 40 degree, and washing time is 10 minutes, water
Raw material is put into 0.8-0.9MPa after washing, 50-55 degree are lower to carry out vacuum drying.
5. a kind of preparation method of high-strength and waterproofing Ventilate cloth according to claim 1, it is characterised in that: it is described pad it is whole
Reason is stirred evenly in the water for put into 2-3 parts of sodium fluoborates 80 parts, and water temperature initial temperature is 50 degree, per minute according to 2 degree
Heating rate be warming up to 70 degree, add 10 to 12 parts of water-base fluorocarbon emulsion, be again stirring for uniformly, then will by washing dry
After dry to raw material be put into and carry out padding finishing operation.
6. a kind of preparation method of high-strength and waterproofing Ventilate cloth according to claim 1, it is characterised in that: at the lamination
Reason is to carry out lamination realization using PTFE (polytetrafluoroethylene (PTFE)) film and raw material, PTFE (polytetrafluoroethylene (PTFE)) film in raw material it
Between spreading glue, 70 to 80 at a temperature of carry out glue and merge operation, need to wash away part glue by washing several times,
It can be increased with hole, Air permenbility rises；Meanwhile the clothes that are made into of the fabric can also block the invading into preventing wind from penetrating of cold wind
The heat that cloth distributes stature is taken away, and stature is made not feel air-cooled because of the forfeiture of heat.
7. a kind of preparation method of high-strength and waterproofing Ventilate cloth according to claim 1, it is characterised in that: the raw material print
It contaminates including scouringing and bleaching, dyeing, four steps of stamp and arrangement, concrete operations are as follows:
A, scouring and bleaching-original cloth tested, turn over cloth, in batches, branch mailbox, printing and margin to seam, then into crossing operation of singing, burning-off original cloth
Villus on surface, so that the bright and clean beauty of cloth surface, the slurry in original cloth can be used alkali desizing and carry out desizing operation, by it from knitting
It is stripped on object, recycles caustic soda and other kierings assistant agent and pectic substance, waxy substance, nitrogen substance, cotton seed hulls that chemistry occurs
Degradation reaction or emulsification, strip impurity from original cloth after washing at Swelling Functions, will use into the original cloth after kiering excessively
Peroxide passivation carries out bleaching operation, finally at low temperature by original cloth, under the premise of direction of warp and weft actuates power, with dense caustic soda
Solution processing, improves original cloth performance；
B, dyeing-by the cloth after scouringing and bleaching 120-130 degree temperature environment and 4.7 to 5.2 pH value under be added dye
Auxiliary agent carries out dyeing operation；
C, stamp-elder generation prints the resist agent that can prevent contaminating on dyestuff on cloth, then pad dyeing background color, and being printed at decorative pattern can prevent
Only contaminated on background color；
D, arrange-finally need to carry out cloth sanding, press polish, embossing, flocking, coating, compound, boiling hot according to actual processing
It gold, stamp, clipping and carving, napping and crumples.