CN109456669A - High-strength water-based woodwork coating and its manufacturing method - Google Patents
High-strength water-based woodwork coating and its manufacturing method Download PDFInfo
- Publication number
- CN109456669A CN109456669A CN201811147017.4A CN201811147017A CN109456669A CN 109456669 A CN109456669 A CN 109456669A CN 201811147017 A CN201811147017 A CN 201811147017A CN 109456669 A CN109456669 A CN 109456669A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- stage
- obtains
- adhesive force
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of high-strength water-based woodwork coating and its manufacturing methods, the water-borne wood coating is using urethane acrylate grafted acrylate, starch graft acrylic acid sodium, water-soluble alkali, aluminium borate whisker, carborundum powder, CF carbon fiber, the tackifier from extracting in cornu caprae hircus part, blocked isocyanate, polyether siloxane copolymers, the aqueous adhesive force promotor extracted from peach branch as raw material, using deionized water as medium, sufficiently reaction is obtained at 70 DEG C -85 DEG C;Wherein the preparation process of tackifier includes infiltration, pelletizing, simmers, purifies, being concentrated;The preparation process of aqueous adhesive force promotor is including being soaked, microorganism broken wall, collagen discharge and activation, concentration.The present invention have specially suitable for woodenware surface, it is aqueous, do not hurt the good technical effect of wooden, high-intensitive, high abrasion, surface lubrication, texture.
Description
Technical field
The present invention relates to woodwork coating field more particularly to a kind of high-strength water-based woodwork coating and its manufacturing methods.
Background technique
Currently, the generally existing wooden implements in our life, surface lacquer water has significant limitations: easy to aging,
Peel off, mostly organic polymer is high containing formaldehyde, makes a general survey of domestic entire woodenware paint market, and kind is more, but mostly with have protect,
Based on closing, decoration functions, functional paint has water resistance, alkali resistance, stain resistant and better simply flame retardant property mostly
Coating, and most of is organic group coating, contains the composition being harmful to the human body;There is obvious closing energy in a small amount of water based paint
Power difference or poor defect in conjunction with woodenware.
It is poly- as initiator, alkyl phenol frequently with persulfate or organic peroxide in current technology customary in the art
For ethylene oxide ether as emulsifier, bromide fire retardant as fire retardant, these three materials are universally acknowledged poisonous and harmful substance.
In the related patents applied at home, patent " a kind of aqueous acrylic acid series wooden ware sealing paint and its dedicated cream
The preparation method of liquid " (application number: 201010159689.4, publication date: 2010.09.01), a kind of wooden ware sealing is disclosed with third
The copolymer emulsion of olefin(e) acid class, closed performance is excellent, but without the addition of enhancing sexual function object, binding force is poor, is also easy
It is worn, flakes;In addition, the other main material constituents of the invention are in high temperature poisonous and harmful substance easily generated.Patent " aqueous wooden ware
Paint lotion " (application number: 200810081974.1, publication date: 2009.09.09), disclose a kind of cream of fire resistant water resistant erosion
Liquid obtains stable silicon oxygen bond by adding silica solution, to improve the high temperature resistance of lotion, but its solid content is high, easily
It is dry and cracked;Meanwhile the auxiliary agent of adhesive force promotion functions is also had without adding, binding force is poor.
Therefore need in the market it is a kind of be specially suitable for woodenware surface, it is aqueous, do not hurt wooden, high-intensitive, high abrasion, surface
The good woodwork coating of lubrication, texture.
Summary of the invention
To solve drawbacks described above existing in the prior art, the present invention is intended to provide a kind of be specially suitable for woodenware surface, water
Property, do not hurt wooden, high-intensitive, high abrasion, the high-strength water-based woodwork coating that surface lubrication, texture are good.
In order to achieve the above-mentioned object of the invention, the invention adopts the following technical scheme: a kind of high-strength water-based woodwork coating
Manufacturing method, comprising the following steps:
1) raw material prepare
1. raw material prepare: preparation 70 parts -80 parts of urethane acrylate grafted acrylate, starch-grafted by weight
15 parts -18 parts of sodium acrylate, 1 part -1.5 parts of water-soluble alkali, 0.2 part -0.3 part of aluminium borate whisker, 1 part -2 parts of carborundum powder, CF
5 parts -8 parts of carbon fiber, 30 parts -35 parts of cornu caprae hircus, 2 parts -3 parts of blocked isocyanate, 0.2 part of polyether siloxane copolymers -
0.3 part, 8 parts -10 parts of peach branch;
2. auxiliary material prepares: preparing Enough Dl water, enough Cytophaga microbial inoculums, enough collagen activation enzyme aquas;
2) tackifier synthesize
1. by the stage 1) cornu caprae hircus that 1. prepares of step is bathed in the stage 1) made of the deionized water that 2. prepares of step
In mixture of ice and water, continue holdings temperature on the rocks after mixing evenly and stablize, kept for -8 days 6 days, clean up and remove aqueous with
Infiltration is obtained after blood matter without blood cutin;
2. 1. infiltration that step obtains to be chopped into the particle of partial size 2mm-5mm without blood cutin machinery, angle to be processed is obtained
Matter;
3. 2. cutin to be processed that step obtains is uniformly mixed with 2 times -3 times of its weight of deionized water be placed on it is closed
, simmer in the environment of vapour pressure 0.35MPa-0.4MPa, simmer 120 DEG C of temperature
- 125 DEG C, 2.5h-3h is kept the temperature, uses 200 meshes to filter out Solid content after removing aqueous surface offscum, obtains pre-prepared colloid
Liquid;
4. repeating step 3. 3 times -5 times, the prefabricated glue of acquisition is uniformly mixed, crude glue is obtained;
5. 4. crude glue that step is obtained gradually steams from moisture content to glue the kinematic viscosity at 20 DEG C -25 DEG C
100mm2/s-120mm2/ s, that is, tackifier needed for obtaining;
3) prepared by aqueous adhesive force promotor
1. by the stage 1) the peach branch that 1. obtains of step is immersed in the water, is soaked after -2 days 1 day, takes out Solid content using mechanical
Mode break into slag obtains original slurry material;
2. by 2. original slurry material that step obtains addition water and being tuned into paste, the stage 1 is implanted into paste) 2. step prepares
Cytophaga microbial inoculum, control temperature be not higher than 25 DEG C, with stir per hour 1min regular intervals stir -8 days 5 days, obtain
Protoplasm release matrix;
3. the stage 1 is added in 2. protoplasm release matrix that step obtains) the collagen activation enzyme aqua that 2. obtains of step, and
It is mixed evenly, processing then is sealed to mixture, kept for -8 days 5 days;
4. the mixture 3. step is sealed after takes out, after filtering out Solid content, solution is slowly dried using 40 DEG C -50 DEG C
It is dry, until solution kinematic viscosity 40mm at 20 DEG C -25 DEG C2/s-60mm2/ s, i.e. acquisition aqueous adhesive force promotor;
4) whole water-borne wood coating processed
1. by the stage 2) tackifier that obtain, stage 3) the aqueous adhesive force promotor that obtains and stage 1) 1. step prepares
Urethane acrylate grafted acrylate, starch graft acrylic acid sodium, water-soluble alkali, aluminium borate whisker, carborundum powder, CF
Carbon fiber, blocked isocyanate, polyether siloxane copolymers add mixture quality 30%- after being mixed and stirred for uniformly
35% deionized water is sufficiently reacted at 70 DEG C -85 DEG C, that is, high-strength water-based woodwork coating needed for obtaining.
In the manufacturing method of above-mentioned high-strength water-based woodwork coating, the water-soluble alkali is potassium hydroxide, sodium hydroxide
Or one of ammonium hydroxide or their compositions.
According to the high-strength water-based woodwork coating that the above method manufactures, the water-borne wood coating is with polyurethane by weight
70 parts -80 parts of acrylic ester grafted acrylate, 15 parts -18 parts of starch graft acrylic acid sodium, 1 part -1.5 parts of water-soluble alkali, boron
0.2 part -0.3 part of sour al whisker, 5 parts -8 parts of CF carbon fiber, is extracted from 30 parts -35 parts of cornu caprae hircus 1 part -2 parts of carborundum powder
Tackifier, 2 parts -3 parts of blocked isocyanate, 0.2 part -0.3 part of polyether siloxane copolymers, from peach branch 8 parts -10 parts in
The aqueous adhesive force promotor of extraction is raw material, and using deionized water as medium, sufficiently reaction is obtained at 70 DEG C -85 DEG C;Wherein increase
The preparation process of stick includes infiltration, pelletizing, simmers, purifies, being concentrated;The preparation process of aqueous adhesive force promotor includes bubble
Hair, the release of microorganism broken wall, collagen and activation, concentration.
Compared with prior art, by adopting the above-described technical solution, the invention has the following advantages that (1) is of the invention
The CF carbon fiber especially selected, is a kind of substance different from enhancing additive glass fibre in routine techniques, and this substance is
High-intensitive, high modulus fibre new fiber materials, it is by organic fibers such as flake graphites along fiber axial direction heap
It builds, through microcrystalline graphite material obtained from carbonization and graphitization processing;Carbon fiber " soft outside but hard inside ", quality compare metallic aluminium
Gently, but intensity is higher than steel, and has corrosion-resistant, high-modulus characteristic, it not only has the intrinsic intrinsic spy of carbon material
Property, and have both the soft machinability of textile fabric, intensity of the invention, ductility and filming performance can be significantly improved.(2) originally
Invention is different from directlying adopt in the prior art for the wearability and binding force that improve lacquer painting chemically synthesized organic matter as adding
Add agent, but sterol, polypeptide, colloid extracted from cornu caprae hircus etc. is respectively adopted as tackifier, wood glue is extracted from peach branch
The vegetalitas surface adhesion force promotor of (peach gum) as natural nuisance-free, on the one hand takes full advantage of in routine techniques and does not answer
Waste (goat's horn be different from deer horn and ox horn, by the reason of composition in the inner substantially without medical value, cannot be such as deer
Angle, ox horn are equally used as medicine, also due to its geomery is limited, can not be processed as the objects such as craftwork or daily necessity such as horn comb
Part, therefore be typically also directly to be discarded as waste;And peach branch is different from peach trunk there are also other effects, in people day
Often plantation peach during also otherwise it is open close cross trimming branch come maintain peach shape and produce fruit rate, trim the branch to get off
One without used in, also can only waste treatment, but it is in fact also dry equally containing a large amount of Collagen materials abundant with peach in peach branch,
Only because not excessive and go out be inconvenient to pick edible) the natural free of contamination additive source of conduct, not only saved cost but also
Environmental-protecting performance and functionality of the invention are improved, intensity of the invention, wearability and the adhesive force with wood surface are improved.
(3) peach gum extracted from peach branch itself has hydrophilic radical, it can uses as aqueous additive, in enclosed type isocyanide
Acid esters effect is lower outstanding with acrylic based resin coating binding force of the invention, since peach gum is inherently extracted from wooden object
, thus the binding force of itself and wooden device surface is also very outstanding;More simultaneous peach gum itself plays the role of desinsection degerming
Although (relatively slight), the probability and the speed for reducing corruption that woodenware is damaged by insects can be reduced to a certain extent, is promoted and uses the longevity
Life.(4) present invention uses the experience (mainly deer horn medicine product etc.) of horn using cornu caprae hircus colloid composition and people for many years,
It is (non-by simmering the sterol endured out in cornu caprae hircus, amino acid, peptide matters and colloid composition after pressurization (making the elevation of boiling point of water)
Water-soluble keratin, guanidine substance etc. are removed with separation of solid and liquid), the sicker of acquisition kinematic viscosity superelevation, and by
In these substances be all water-soluble, small molecule, thus it is good with acrylic based resin binding force of the invention, also easily penetrate into wood
Device surface, thus it is very outstanding as tackifier and matching of the present invention, it is also convenient for brushing the film forming at woodenware surface and mentions film
Self-bonding power and intensity.(5) it is different from leaning on resin itself entirely in conjunction with the organic resins such as the glass fibre in routine techniques and ABS
Internal bond fix, peach gum of the invention, angle glue are the adhesivity substance of high kinematic viscosity, can effectively increase matrix resin
Internal bond, keep internal bond of the present invention stronger, intensity, surface hardness are higher.(6) in addition to CF in all compositions of the invention
Outside a small amount of additive such as carbon fiber, aluminium borate and carborundum powder, other compositions are water-soluble substances, on the one hand environmental protection, to people
It is harmless, it is applied widely, it is deployed when on the other hand convenient to use, easy to use, good economy performance.(7) due to self-adhesion of the invention
Even intensity is higher than conventional coating in the prior art in the case where being added to two kinds of colloids (peach gum, angle glue), and the present invention is also
Enough viscosity surplus additions function composition completely immiscible with acrylic based resin of the present invention: it is obviously improved lubrication of the present invention
The CF carbon fiber of property and integral hardness, the aluminium borate for being obviously improved intensity of the present invention, the carbon for being obviously improved wear-resisting property of the present invention
SiClx powder directly improves wearability and lubricity of the invention, and the dicoration for improving coating of the present invention is (translucent
Opaque aluminium borate and silicon carbide existing for multiclass colloid and disperse) with feel (feel as a variety of cured class ambers of colloid and
Hard and stroke gently feel with lubricator bring).Therefore the present invention have specially be suitable for woodenware surface, it is aqueous, do not hurt it is wooden,
The good characteristic of high intensity, high abrasion, surface lubrication, texture, there is excellent comprehensive performance.
Specific embodiment
Embodiment 1:
A kind of high-strength water-based woodwork coating, the water-borne wood coating is with the grafting of urethane acrylate by weight third
Olefin(e) acid ester 70Kg, starch graft acrylic acid sodium 18Kg, potassium hydroxide 1.5Kg, aluminium borate whisker 0.3Kg, carborundum powder 2Kg, CF
Carbon fiber 8Kg, the tackifier extracted from cornu caprae hircus 35Kg, blocked isocyanate 3Kg, polyether siloxane copolymers
0.3Kg, the aqueous adhesive force promotor extracted from peach branch 10Kg are raw material, using deionized water as medium, at 80 DEG C -85 DEG C
Sufficiently reaction obtains;Wherein the preparation process of tackifier includes infiltration, pelletizing, simmers, purifies, being concentrated;Aqueous adhesive force promotes
The preparation process of agent is including being soaked, microorganism broken wall, collagen discharge and activation, concentration.
A kind of manufacturing method of high-strength water-based woodwork coating, comprising the following steps:
1) raw material prepare
1. raw material prepare: preparation urethane acrylate grafted acrylate 70Kg, starch-grafted propylene by weight
Sour sodium 18Kg, potassium hydroxide 1.5Kg, aluminium borate whisker 0.3Kg, carborundum powder 2Kg, CF carbon fiber 8Kg, cornu caprae hircus 35Kg, envelope
Closed form isocyanates 3Kg, polyether siloxane copolymers 0.3Kg, peach branch 10Kg;
2. auxiliary material prepares: preparing Enough Dl water, enough Cytophaga microbial inoculums, enough collagen activation enzyme aquas;
2) tackifier synthesize
1. by the stage 1) cornu caprae hircus that 1. prepares of step is bathed in the stage 1) made of the deionized water that 2. prepares of step
In mixture of ice and water, continues holding temperature on the rocks after mixing evenly and stablize, kept for 6 days, clean up and remove aqueous and blood matter
Infiltration is obtained afterwards without blood cutin;
2. 1. infiltration that step obtains to be chopped into the particle of partial size 2mm-5mm without blood cutin machinery, angle to be processed is obtained
Matter;
3. 2. cutin to be processed that step obtains is uniformly mixed with 2 times of its weight of deionized water be placed on it is closed,
It is simmered in the environment of vapour pressure 0.35MPa-0.4MPa, simmers 120 DEG C -125 DEG C of temperature, keep the temperature 2.5h, it is floating to remove aqueous surface
Solid content is filtered out using 200 meshes after foam, obtains prefabricated glue;
4. repeating step 3. 3 times, the prefabricated glue of acquisition is uniformly mixed, crude glue is obtained;
5. 4. crude glue that step is obtained gradually steams from moisture content to glue the kinematic viscosity at 20 DEG C -25 DEG C
100mm2/s-120mm2/ s, that is, tackifier needed for obtaining;
3) prepared by aqueous adhesive force promotor
1. by the stage 1) step 1. obtain peach branch be immersed in the water, be soaked after 1 day, take out Solid content use mechanical system
Break into slag obtains original slurry material;
2. by 2. original slurry material that step obtains addition water and being tuned into paste, the stage 1 is implanted into paste) 2. step prepares
Cytophaga microbial inoculum, control temperature be not higher than 25 DEG C, with stir per hour 1min regular intervals stir 5 days, obtain protoplasm
Release matrix;
3. the stage 1 is added in 2. protoplasm release matrix that step obtains) the collagen activation enzyme aqua that 2. obtains of step, and
It is mixed evenly, processing then is sealed to mixture, kept for 5 days;
4. the mixture 3. step is sealed after takes out, after filtering out Solid content, solution is slowly dried using 40 DEG C -50 DEG C
It is dry, until solution kinematic viscosity 40mm at 20 DEG C -25 DEG C2/s-60mm2/ s, i.e. acquisition aqueous adhesive force promotor;
4) whole water-borne wood coating processed
1. by the stage 2) tackifier that obtain, stage 3) the aqueous adhesive force promotor that obtains and stage 1) 1. step prepares
Urethane acrylate grafted acrylate, starch graft acrylic acid sodium, water-soluble alkali, aluminium borate whisker, carborundum powder, CF
Addition mixture quality 30% goes after carbon fiber, blocked isocyanate, polyether siloxane copolymers are mixed and stirred for uniformly
Ionized water sufficiently reacts at 80 DEG C -85 DEG C, that is, high-strength water-based woodwork coating needed for obtaining.
Embodiment 2
It is whole consistent with embodiment 1, it is in place of difference:
A kind of high-strength water-based woodwork coating, the water-borne wood coating is with the grafting of urethane acrylate by weight third
Olefin(e) acid ester 80Kg, starch graft acrylic acid sodium 15Kg, ammonium hydroxide 1Kg, aluminium borate whisker 0.2Kg, carborundum powder 1Kg, CF carbon
Fiber 5Kg, the tackifier extracted from cornu caprae hircus 30Kg, blocked isocyanate 2Kg, polyether siloxane copolymers 0.2Kg,
The aqueous adhesive force promotor extracted from peach branch 8Kg is raw material, sufficiently anti-at 70 DEG C -75 DEG C using deionized water as medium
It should obtain;Wherein the preparation process of tackifier includes infiltration, pelletizing, simmers, purifies, being concentrated;The system of aqueous adhesive force promotor
Standby process is including being soaked, microorganism broken wall, collagen discharge and activation, concentration.
A kind of manufacturing method of high-strength water-based woodwork coating, comprising the following steps:
1) raw material prepare
1. raw material prepare: preparation urethane acrylate grafted acrylate 80Kg, starch-grafted propylene by weight
Sour sodium 15Kg, ammonium hydroxide 1Kg, aluminium borate whisker 0.2Kg, carborundum powder 1Kg, CF carbon fiber 5Kg, cornu caprae hircus 30Kg, closing
Type isocyanates 2Kg, polyether siloxane copolymers 0.2Kg, peach branch 8Kg;
2) tackifier synthesize
1. by the stage 1) cornu caprae hircus that 1. prepares of step is bathed in the stage 1) made of the deionized water that 2. prepares of step
In mixture of ice and water, continues holding temperature on the rocks after mixing evenly and stablize, kept for 8 days, clean up and remove aqueous and blood matter
Infiltration is obtained afterwards without blood cutin;
3. 2. cutin to be processed that step obtains is uniformly mixed with 3 times of its weight of deionized water be placed on it is closed,
It is simmered in the environment of vapour pressure 0.35MPa-0.4MPa, simmers 120 DEG C -125 DEG C of temperature, keep the temperature 3h, remove aqueous surface offscum
Solid content is filtered out using 200 meshes afterwards, obtains prefabricated glue;
4. repeating step 3. 5 times, the prefabricated glue of acquisition is uniformly mixed, crude glue is obtained;
3) prepared by aqueous adhesive force promotor
1. by the stage 1) step 1. obtain peach branch be immersed in the water, be soaked after 2 days, take out Solid content use mechanical system
Break into slag obtains original slurry material;
2. by 2. original slurry material that step obtains addition water and being tuned into paste, the stage 1 is implanted into paste) 2. step prepares
Cytophaga microbial inoculum, control temperature be not higher than 25 DEG C, with stir per hour 1min regular intervals stir 8 days, obtain protoplasm
Release matrix;
3. the stage 1 is added in 2. protoplasm release matrix that step obtains) the collagen activation enzyme aqua that 2. obtains of step, and
It is mixed evenly, processing then is sealed to mixture, kept for 8 days;
4) whole water-borne wood coating processed
1. by the stage 2) tackifier that obtain, stage 3) the aqueous adhesive force promotor that obtains and stage 1) 1. step prepares
Urethane acrylate grafted acrylate, starch graft acrylic acid sodium, water-soluble alkali, aluminium borate whisker, carborundum powder, CF
Addition mixture quality 35% goes after carbon fiber, blocked isocyanate, polyether siloxane copolymers are mixed and stirred for uniformly
Ionized water sufficiently reacts at 70 DEG C -75 DEG C, that is, high-strength water-based woodwork coating needed for obtaining.
Embodiment 3
It is whole consistent with embodiment 1, it is in place of difference:
A kind of high-strength water-based woodwork coating, the water-borne wood coating is with the grafting of urethane acrylate by weight third
Olefin(e) acid ester 75Kg, starch graft acrylic acid sodium 16Kg, sodium hydroxide 0.6Kg, ammonium hydroxide 0.5Kg, aluminium borate whisker 0.25Kg,
Carborundum powder 1.5Kg, CF carbon fiber 6Kg, the tackifier extracted from cornu caprae hircus 32Kg, blocked isocyanate 2.5g, polyethers-
Silicone copolymers 0.25Kg, the aqueous adhesive force promotor extracted from peach branch 9Kg are raw material, are to be situated between with deionized water
Matter, sufficiently reaction obtains at 75 DEG C -80 DEG C;Wherein the preparation process of tackifier includes infiltration, pelletizing, simmers, purifies, being concentrated;
The preparation process of aqueous adhesive force promotor is including being soaked, microorganism broken wall, collagen discharge and activation, concentration.
A kind of manufacturing method of high-strength water-based woodwork coating, comprising the following steps:
1) raw material prepare
1. raw material prepare: preparation aqueous polyurethane acrylate grafted acrylate 75Kg, starch-grafted by weight
Sodium acrylate 16Kg, sodium hydroxide 0.6Kg, ammonium hydroxide 0.5Kg, aluminium borate whisker 0.25Kg, carborundum powder 1.5Kg, CF carbon
Fiber 6Kg, cornu caprae hircus 32Kg, blocked isocyanate 2.5g, polyether siloxane copolymers 0.25Kg, peach branch 9Kg;
2) tackifier synthesize
4. repeating step 3. 4 times, the prefabricated glue of acquisition is uniformly mixed, crude glue is obtained;
3) prepared by aqueous adhesive force promotor
1. by the stage 1) step 1. obtain peach branch be immersed in the water, be soaked after 2 days, take out Solid content use mechanical system
Break into slag obtains original slurry material;
4) whole water-borne wood coating processed
1. by the stage 2) tackifier that obtain, stage 3) the aqueous adhesive force promotor that obtains and stage 1) 1. step prepares
Urethane acrylate grafted acrylate, starch graft acrylic acid sodium, water-soluble alkali, aluminium borate whisker, carborundum powder, CF
Addition mixture quality 30% goes after carbon fiber, blocked isocyanate, polyether siloxane copolymers are mixed and stirred for uniformly
Ionized water sufficiently reacts at 75 DEG C -80 DEG C, that is, high-strength water-based woodwork coating needed for obtaining.
The foregoing description of the disclosed embodiments, only for can be realized professional and technical personnel in the field or use this
Invention.Various modifications to these embodiments will be readily apparent to those skilled in the art, institute herein
The General Principle of definition can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore,
The present invention will not be limited to the embodiments shown herein, and is to fit to special with principles disclosed herein and novelty
The consistent widest scope of point.
Claims (3)
1. a kind of manufacturing method of high-strength water-based woodwork coating, it is characterised in that the following steps are included:
1) raw material prepare
1. raw material prepare: preparation 70 parts -80 parts of urethane acrylate grafted acrylate, starch-grafted propylene by weight
15 parts -18 parts of sour sodium, 1 part -1.5 parts of water-soluble alkali, 0.2 part -0.3 part of aluminium borate whisker, 1 part -2 parts of carborundum powder, CF carbon fiber
Dimension 5 parts -8 parts, 30 parts -35 parts of cornu caprae hircus, 2 parts -3 parts of blocked isocyanate, 0.2 part -0.3 part of polyether siloxane copolymers,
8 parts -10 parts of peach branch;
2. auxiliary material prepares: preparing Enough Dl water, enough Cytophaga microbial inoculums, enough collagen activation enzyme aquas;
2) tackifier synthesize
1. by the stage 1) cornu caprae hircus that 1. prepares of step is bathed in the stage 1) ice water made of the deionized water that 2. prepares of step
In mixture, continues holding temperature on the rocks after mixing evenly and stablize, kept for -8 days 6 days, clean up and remove aqueous and blood matter
Infiltration is obtained afterwards without blood cutin;
2. 1. infiltration that step obtains to be chopped into the particle of partial size 2mm-5mm without blood cutin machinery, cutin to be processed is obtained;
3. 2. cutin to be processed that step obtains is uniformly mixed with 2 times -3 times of its weight of deionized water be placed on it is closed,
It is simmered in the environment of vapour pressure 0.35MPa-0.4MPa, simmers 120 DEG C -125 DEG C of temperature, keep the temperature 2.5h-3h, remove aqueous surface
Solid content is filtered out using 200 meshes after offscum, obtains prefabricated glue;
4. repeating step 3. 3 times -5 times, the prefabricated glue of acquisition is uniformly mixed, crude glue is obtained;
5. 4. crude glue that step is obtained gradually steams from moisture content to glue the kinematic viscosity 100mm at 20 DEG C -25 DEG C2/s-
120mm2/ s, that is, tackifier needed for obtaining;
3) prepared by aqueous adhesive force promotor
1. by the stage 1) step 1. obtain peach branch be immersed in the water, be soaked after -2 days 1 day, take out Solid content use mechanical system
Break into slag obtains original slurry material;
2. by 2. original slurry material that step obtains addition water and being tuned into paste, the stage 1 is implanted into paste) biting of 2. preparing of step
Fiber bacteria agent, control temperature are not higher than 25 DEG C, are stirred -8 days 5 days with stirring the regular intervals of 1min per hour, obtain protoplasm
Release matrix;
3. the stage 1 is added in 2. protoplasm release matrix that step obtains) the collagen activation enzyme aqua that 2. obtains of step, and mix
It stirs evenly, processing then is sealed to mixture, kept for -8 days 5 days;
4. the mixture 3. step is sealed after takes out, after filtering out Solid content, by solution using 40 DEG C -50 DEG C slowly drying, until
Solution kinematic viscosity 40mm at 20 DEG C -25 DEG C2/s-60mm2/ s, i.e. acquisition aqueous adhesive force promotor;
4) whole water-borne wood coating processed
1. by the stage 2) tackifier that obtain, stage 3) the aqueous adhesive force promotor that obtains and stage 1) and step 1. prepare it is poly-
Urethane acrylate grafted acrylate, starch graft acrylic acid sodium, water-soluble alkali, aluminium borate whisker, carborundum powder, CF carbon fiber
Addition mixture quality 30%-35% after dimension, blocked isocyanate, polyether siloxane copolymers are mixed and stirred for uniformly
Deionized water is sufficiently reacted at 70 DEG C -85 DEG C, that is, high-strength water-based woodwork coating needed for obtaining.
2. the manufacturing method of high-strength water-based woodwork coating according to claim 1, it is characterised in that: wherein described water-soluble
Property alkali be one of potassium hydroxide, sodium hydroxide or ammonium hydroxide or their compositions.
3. a kind of high-strength water-based woodwork coating, it is characterised in that: the water-borne wood coating is with polyurethane propylene by weight
70 parts -80 parts of acid esters grafted acrylate, 15 parts -18 parts of starch graft acrylic acid sodium, 1 part -1.5 parts of water-soluble alkali, aluminium borate
0.2 part -0.3 part of whisker, 1 part -2 parts of carborundum powder, 5 parts -8 parts of CF carbon fiber, the thickening extracted from 30 parts -35 parts of cornu caprae hircus
Agent, 2 parts -3 parts of blocked isocyanate, 0.2 part -0.3 part of polyether siloxane copolymers, from peach branch 8 parts -10 parts in extract
Aqueous adhesive force promotor be raw material, using deionized water as medium, at 70 DEG C -85 DEG C sufficiently reaction obtain;Wherein tackifier
Preparation process include infiltration, pelletizing, simmer, purify, being concentrated;The preparation process of aqueous adhesive force promotor includes being soaked, being micro-
Biological wall breaking, collagen release and activation, concentration.