CN109439851A - A kind of Metal Surface Heat Treatment - Google Patents
A kind of Metal Surface Heat Treatment Download PDFInfo
- Publication number
- CN109439851A CN109439851A CN201811579431.2A CN201811579431A CN109439851A CN 109439851 A CN109439851 A CN 109439851A CN 201811579431 A CN201811579431 A CN 201811579431A CN 109439851 A CN109439851 A CN 109439851A
- Authority
- CN
- China
- Prior art keywords
- heat treatment
- parts
- metal surface
- surface heat
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Metal Surface Heat Treatment, which is successively put into metal plate to be heated after firing 10-15 minutes in heating furnace and takes out, with spare the following steps are included: heating furnace is heated up to 1050-1200 DEG C by S1.；S2. above-mentioned thermally treated metal plate was realized that metal surface heat treatment derusted by aqueous solution soaking 10-20 minute of the deionized water mixed preparing of the ethyl alcohol of 10-15 parts by weight, the sodium hydroxide of 20-30 parts by weight and 15-25 parts by weight.The heat treatment process have the characteristics that it is easy to operate, at low cost, can quick derusting, allomeric function is perfect, practical.
Description
Technical field
The present invention relates to technical field of metal heat treatment, more specifically, it relates to a kind of Metal Surface Heat Treatment.
Background technique
Currently, existing Metal Surface Heat Treatment is cumbersome, at high cost, urgently its those skilled in the art is developed
A kind of new Metal Surface Heat Treatment.
Summary of the invention
It is an object of the invention to overcome the deficiencies in the prior art described above, a kind of Metal Surface Heat Treatment is provided,
The heat treatment process have the characteristics that it is easy to operate, at low cost, being capable of quick derusting.
In order to solve the above technical problems, the object of the present invention is achieved like this: a kind of metal watch according to the present invention
Face heat treatment process, the Metal Surface Heat Treatment the following steps are included:
S1. heating furnace is heated up to 1050-1200 DEG C, successively metal plate to be heated is put into heating furnace and is fired
It is taken out after 10-15 minutes, with spare；
S2. above-mentioned thermally treated metal plate is passed through into the ethyl alcohol of 10-15 parts by weight, the hydroxide of 20-30 parts by weight
The aqueous solution soaking of the deionized water mixed preparing of sodium and 15-25 parts by weight 10-20 minutes realizes that metal surface heat treatment removes
Rust.
The present invention is further arranged to, and the temperature of the heating furnace is set as 1120 DEG C.
The present invention is further arranged to, and the aqueous solution includes that the raw material cooperation of following weight parts is made: 12 parts of ethyl alcohol, hydrogen
25 parts of sodium oxide molybdena, 15 parts of deionized water.
In conclusion the invention has the following advantages: Metal Surface Heat Treatment according to the present invention, uses
Heating furnace is heated up to 1050-1200 DEG C, successively metal plate to be heated is put into after being fired 10-15 minutes in heating furnace and is taken
Out, with spare；Above-mentioned thermally treated metal plate is passed through into the ethyl alcohol of 10-15 parts by weight, the sodium hydroxide of 20-30 parts by weight
And the aqueous solution soaking of the deionized water mixed preparing of 15-25 parts by weight 10-20 minutes, realize that metal surface heat treatment removes
Rust, it is easy to operate, at low cost, can quick derusting, allomeric function is perfect, practical.
Specific embodiment
Below with reference to preferred embodiment, the present invention is further described.
Embodiment 1
A kind of Metal Surface Heat Treatment involved in the present embodiment, the Metal Surface Heat Treatment include following step
It is rapid:
S1. heating furnace is heated up to 1050-1200 DEG C, successively metal plate to be heated is put into heating furnace and is fired
It is taken out after 10-15 minutes, with spare；
S2. above-mentioned thermally treated metal plate is passed through into the ethyl alcohol of 10-15 parts by weight, the hydroxide of 20-30 parts by weight
The aqueous solution soaking of the deionized water mixed preparing of sodium and 15-25 parts by weight 10-20 minutes realizes that metal surface heat treatment removes
Rust.
The present invention is further arranged to, and the temperature of the heating furnace is set as 1120 DEG C.
The present invention is further arranged to, and the aqueous solution includes that the raw material cooperation of following weight parts is made: 12 parts of ethyl alcohol, hydrogen
25 parts of sodium oxide molybdena, 15 parts of deionized water.
Embodiment 2
A kind of Metal Surface Heat Treatment involved in the present embodiment, the Metal Surface Heat Treatment include following step
It is rapid:
S1. heating furnace is heated up to 1120 DEG C, successively metal plate to be heated is put into heating furnace and fires 10-15 points
It is taken out after clock, with spare；
S2. by above-mentioned thermally treated metal plate by the ethyl alcohol of 12 parts by weight, 25 parts by weight sodium hydroxide and
The aqueous solution soaking of the deionized water mixed preparing of 15 parts by weight 10-20 minutes realizes metal surface heat treatment derusting.
The preferred embodiment of the present invention has been described in detail above.It should be appreciated that those skilled in the art without
It needs creative work according to the present invention can conceive and makes many modifications and variations.Therefore, all technologies in the art
Personnel are available by logical analysis, reasoning, or a limited experiment on the basis of existing technology under this invention's idea
Technical solution, all should be within the scope of protection determined by the claims.
Claims (3)
1. a kind of Metal Surface Heat Treatment, which is characterized in that the Metal Surface Heat Treatment the following steps are included:
S1. heating furnace is heated up to 1050-1200 DEG C, successively metal plate to be heated is put into heating furnace and fires 10-15
It is taken out after minute, with spare；
S2. by above-mentioned thermally treated metal plate by the sodium hydroxide of the ethyl alcohol of 10-15 parts by weight, 20-30 parts by weight with
And the aqueous solution soaking of the deionized water mixed preparing of 15-25 parts by weight 10-20 minutes, realize metal surface heat treatment derusting.
2. Metal Surface Heat Treatment according to claim 1, which is characterized in that the temperature of the heating furnace is set as
1120℃。
3. Metal Surface Heat Treatment according to claim 1, which is characterized in that the aqueous solution includes following weight
The raw material cooperation of part is made: 12 parts of ethyl alcohol, 25 parts of sodium hydroxide, 15 parts of deionized water.