CN109439118A - Functional coating varnish and its preparation method and application - Google Patents
Functional coating varnish and its preparation method and application Download PDFInfo
- Publication number
- CN109439118A CN109439118A CN201811355078.XA CN201811355078A CN109439118A CN 109439118 A CN109439118 A CN 109439118A CN 201811355078 A CN201811355078 A CN 201811355078A CN 109439118 A CN109439118 A CN 109439118A
- Authority
- CN
- China
- Prior art keywords
- coating varnish
- agent
- varnish according
- amino modified
- functionality
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
This application involves a kind of functional coating varnishes and its preparation method and application, the functionality coating varnish, in terms of mass percentage, mainly it is prepared by 10%~50% amino modified AA emulsion, 2%~4% thickener, 0.2%~0.6% dispersing agent, 0.5%~1.1% wetting agent, 3%~5% coalescing agent, 1%~4% antifreezing agent, 0.2%~0.5% defoaming agent, 0.1%~0.3% preservative, 0.1%~0.5% mould inhibitor and 39%~80% water.Above-mentioned functionality coating varnish, can long-acting purifying formaldehyde, dust-proof resistant, antimildew and antibacterial.
Description
Technical field
The present invention relates to technical field of coatings, more particularly to a kind of functional coating varnish and preparation method thereof and answer
With.
Background technique
Indoors in fitment process, coating varnish has extremely strong decoration effect because having many advantages, such as high glaze, the high grade of transparency
Fruit can be used for various substrate surfaces, have both protection and decoration functions, is widely used.However, with indoor decorating and refurnishing materials
Increasingly diversified, a large amount of synthetic material such as glue, plate etc. is used, so that indoor content of formaldehyde is tight after the completion of finishing
Weight is exceeded, is exposed in this environment, can cause damages to the health of human body for a long time.With people's environmental consciousness and health perception
Gradually increase, the content of indoor formaldehyde increasingly attracts people's attention.Since formaldehyde volatilizees from finishing material, there are weeks
Phase is long, the features such as persistently volatilizing, previous purifying formaldehyde technology, such as plant purification, physical absorption, photocatalytic conversion are deposited mostly
It is palliative the disadvantages of purification efficiency is low, clean-up effect is unstable.And current conventional coating varnish on the market, mostly
It can only play the role of protection and decoration, the effect of without having both purifying formaldehyde.
Summary of the invention
Based on this, it is necessary to provide a kind of functional coating varnish of long-acting purifying formaldehyde of energy, concrete scheme is as follows:
It is a kind of functionality coating varnish be mainly prepared from the following materials in terms of mass percentage:
Above-mentioned functionality coating varnish, using amino modified AA emulsion as emulsion system, amino can be with
Nucleophilic addition or Mannich (Mannich) reaction occur for formaldehyde, reach the mesh of consumption formaldehyde, long-acting purification formaldehyde in air
's.By amino modified AA emulsion and thickener, dispersing agent, wetting agent, coalescing agent, antifreezing agent, defoaming agent, prevent
Rotten agent, mould inhibitor and hydroscience combination, the functional coating varnish being prepared not only have the effect of long-acting purifying formaldehyde,
And have many advantages, such as dust-proof resistant, antimildew and antibacterial.
In addition, above-mentioned functionality coating varnish, has excellent environmental-protecting performance, meet " HJ2537-2014 environmental mark production
Product technical requirements water paint " mark;Meet standard " JC/T 1074-2008 function of purifying indoor air coating material purification property
Can " standard, for purification efficiency higher than 75%, purification persistence is higher than 60%.
The mass percentage of the amino modified AA emulsion is 25% in one of the embodiments,.
The purifying formaldehyde efficiency of above-mentioned functionality coating varnish increases with the dosage of amino modified AA emulsion
Add and promoted, but after lotion dosage is more than 25%, purifying formaldehyde improved efficiency is slower, takes into account lotion dosage cost, amino
The optimum amount of modified acrylic acid terpolymer lotion is 25%.
In one of the embodiments, the viscosity of the amino modified AA emulsion be 600mPas~
1000mPas, the glass transition temperature of the amino modified AA emulsion are 30 DEG C~40 DEG C.
The viscosity and glass transition temperature for controlling amino modified AA emulsion are more advantageous to itself and other originals
Material combination makes the functional coating varnish of preparation not only have the effect of long-acting purifying formaldehyde, but also dry be more suitable for
Dry speed.
The amino modified AA emulsion is by methyl methacrylate, propylene in one of the embodiments,
Sour N-butyl, isobornyl methacrylate and function monomer are copolymerized, and the function monomer is selected from acrylamide, N- hydroxyl first
At least one of base acrylamide, N- butoxy methyl acrylamide, crotonamide, ethernamine and amylene amide;It is described
The dosage of function monomer is prepare monomer gross mass used in the amino modified AA emulsion 15%~25%.
Above-mentioned amino modified AA emulsion, by by methyl methacrylate, n-butyl acrylate, methyl-prop
Olefin(e) acid isobornyl thiocyanoacetate and function monomer copolymerization, introduce AA emulsion by chemical modification for the amino in function monomer
In, then compound with other raw materials, make the functional coating varnish of preparation that not only there is the protection of conventional coating varnish, decoration effect
Fruit, and have the effect of long-term purifying formaldehyde.
Thickener is hydrophobically modified polyurethane thickener in one of the embodiments,.
The dispersing agent is polyacrylic acid sodium salt aqueous dispersion in one of the embodiments,;The wetting agent is different
Structure alcohol polyoxyethylene ether wetting agent;The coalescing agent is alcohol ester 12;The antifreezing agent is selected from ethylene glycol, propylene glycol and high score
At least one of sub- antifreeze auxiliary agent of polyalcohols;The defoaming agent is siliceous class defoaming agent.
The preservative is selected from least one in Kathon CG and 2- benzisothiazole (BIT) in one of the embodiments,
Kind;The mould inhibitor is selected from iodopropynyl butyl formate (IPBC), methyl formate (BCM) and the different thiophene of 2- n-octyl -4-
At least one of oxazoline -3- ketone (OIT).
The mould inhibitor is that iodopropynyl butyl formate and 2- n-octyl -4- are different in one of the embodiments,
The combination of thiazoline -3- ketone.
Above-mentioned functionality coating varnish, when mould inhibitor is the combination of IPBC and OIT, anti-mold effect is best.
The application also provides a kind of preparation method of above-mentioned functional coating varnish, and concrete scheme is as follows:
A kind of preparation method of functional coating varnish described in any of the above embodiments, comprising the following steps:
Part water, dispersing agent, wetting agent, defoaming agent, antifreezing agent and coalescing agent are mixed 3~5 minutes;
Amino modified AA emulsion is added, mixes 3~5 minutes;
Thickener and another part water is added, mixes 3~5 minutes;
Preservative and mould inhibitor are sequentially added, is mixed 3~5 minutes, remaining water is added, mixes 3~5 minutes, obtains institute
State functional coating varnish.
Further, mixed rate is no more than 400r/min.
It is above-mentioned functionality coating varnish preparation method, simple possible, by by water, dispersing agent, wetting agent, defoaming agent,
Antifreezing agent and coalescing agent first mix, and obtain the more suitable system of viscosity, add amino modified AA emulsion,
Demulsifying phenomenon caused by being directly added into lotion is prevented, makes the functional coating varnish of preparation that can not only keep coating varnish
Characteristic, and the effect of long-acting purifying formaldehyde can be had both;Preparing functional coating varnish by substep can be improved yield rate.
The application also provides a kind of application of above-mentioned functional coating varnish, and concrete scheme is as follows:
A kind of functional coating varnish described in any of the above embodiments is preparing the application in construction wall decorative layer.
Specific embodiment
To facilitate the understanding of the present invention, below will to invention is more fully described, and give it is of the invention compared with
Good embodiment.But the invention can be realized in many different forms, however it is not limited to embodiment described herein.Phase
Instead, purpose of providing these embodiments is makes the disclosure of the present invention more thorough and comprehensive.
Unless otherwise defined, all technical and scientific terms used herein and belong to technical field of the invention
The normally understood meaning of technical staff is identical.Term as used herein in the specification of the present invention is intended merely to description tool
The purpose of the embodiment of body, it is not intended that in the limitation present invention.Term as used herein "and/or" includes one or more phases
Any and all combinations of the listed item of pass.
It should be noted that raw materials used in following embodiment and comparative example is commercially available common product, water is deionization
Water.
It is formulated according to table 1, the functional coating varnish of comparative example 1~2 and Examples 1 to 6 is prepared respectively, according to JC/T
1074-2008 " function of purifying indoor air coating material purifying property ", confrontation formaldehyde performance are evaluated.
Table 1
As shown in Table 1, the coating varnish of conventional emulsions preparation does not have purifying formaldehyde function, the functional Lacquer finish of the application
Varnish purifying formaldehyde effect is obvious, and the purifying formaldehyde efficiency of the functional coating varnish of the application is with amino modified acrylic acid
Copolymer emulsion dosage increases and is promoted, after base modified acrylic acid terpolymer lotion dosage is more than 25%, functional Lacquer finish
The promotion speed of the purifying formaldehyde efficiency of varnish slows down and enters plateau, considers the increase of lotion dosage cost, amino modified
The optimum amount of AA emulsion is 25%.
It is formulated according to table 2, the functional coating varnish of embodiment 7~12 is prepared respectively, by GB/T 1741-2007 " paint film
Milk mycotic measuring method " described in test method, fungicidal properties is evaluated.
Table 2
As can be seen from Table 2, above-mentioned functional coating varnish is prevented when the combination using IPBC and OIT is as mould inhibitor
Mould effect is best.
Each technical characteristic of embodiment described above can be combined arbitrarily, for simplicity of description, not to above-mentioned reality
It applies all possible combination of each technical characteristic in example to be all described, as long as however, the combination of these technical characteristics is not deposited
In contradiction, all should be considered as described in this specification.
The embodiments described above only express several embodiments of the present invention, and the description thereof is more specific and detailed, but simultaneously
It cannot therefore be construed as limiting the scope of the patent.It should be pointed out that coming for those of ordinary skill in the art
It says, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to protection of the invention
Range.Therefore, the scope of protection of the patent of the invention shall be subject to the appended claims.
Claims (10)
1. a kind of functionality coating varnish, which is characterized in that in terms of mass percentage, be mainly prepared from the following materials:
2. functionality coating varnish according to claim 1, which is characterized in that the amino modified acrylic copolymer cream
The mass percentage of liquid is 25%.
3. functionality coating varnish according to claim 1 or 2, which is characterized in that the amino modified acrylic acid copolymer
The viscosity of object lotion is 600mPas~1000mPas, the glass transition of the amino modified AA emulsion
Temperature is 30 DEG C~40 DEG C.
4. functionality coating varnish according to claim 3, which is characterized in that the amino modified acrylic copolymer cream
Liquid is copolymerized by methyl methacrylate, n-butyl acrylate, isobornyl methacrylate and function monomer, the function
Monomer is selected from acrylamide, N hydroxymethyl acrylamide, N- butoxy methyl acrylamide, crotonamide, ethernamine and penta
At least one of acrylamide;The dosage of the function monomer is to prepare list used in the amino modified AA emulsion
The 15%~25% of body gross mass.
5. functionality coating varnish according to claim 1, which is characterized in that the thickener is hydrophobically modified polyurethane
Thickener.
6. functionality coating varnish according to claim 1, which is characterized in that the dispersing agent is Sodium Polyacrylate salt water
Property dispersing agent;The wetting agent is isomeric alcohol polyethenoxy ether wetting agent;The coalescing agent is alcohol ester 12;The antifreezing agent
Selected from least one of ethylene glycol, propylene glycol and the antifreeze auxiliary agent of macromolecular multi-component alcohols;The defoaming agent is the defoaming of siliceous class
Agent.
7. the functional coating varnish according to right 1, which is characterized in that the preservative is selected from Kathon CG and 2- benzisothia
At least one of azoles beautiful jade;It is different that the mould inhibitor is selected from iodopropynyl butyl formate, methyl formate and 2- n-octyl -4-
At least one of thiazoline -3- ketone.
8. functionality coating varnish according to claim 7, which is characterized in that the mould inhibitor is iodopropynyl
The combination of butyl formate and Kathon.
9. a kind of preparation method of functional coating varnish according to any one of claims 1 to 8, which is characterized in that including with
Lower step:
Part water, dispersing agent, wetting agent, defoaming agent, antifreezing agent and coalescing agent are mixed 3~5 minutes;
Amino modified AA emulsion is added, mixes 3~5 minutes;
Thickener and another part water is added, mixes 3~5 minutes;
Preservative and mould inhibitor are sequentially added, is mixed 3~5 minutes, remaining water is added, mixes 3~5 minutes, obtains the function
It can property coating varnish.
10. a kind of functional coating varnish according to any one of claims 1 to 8 is preparing answering in construction wall decorative layer
With.