CN109437694A - A kind of pottery mud foaming composite type purifying plate - Google Patents
A kind of pottery mud foaming composite type purifying plate Download PDFInfo
- Publication number
- CN109437694A CN109437694A CN201811530144.2A CN201811530144A CN109437694A CN 109437694 A CN109437694 A CN 109437694A CN 201811530144 A CN201811530144 A CN 201811530144A CN 109437694 A CN109437694 A CN 109437694A
- Authority
- CN
- China
- Prior art keywords
- pottery mud
- pottery
- composite type
- type purifying
- board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of pottery mud foaming composite type purifying plates, are made of multiple pottery mud foamed composite boards being sequentially connected；The pottery mud foamed composite board includes pottery mud foamed board, and the two sides of pottery mud foamed board is equipped with galvanized sheet；Between the two neighboring pottery mud foamed board for card set it is connected, and it is fixed by rivet, pottery mud foaming composite type purifying plate of the invention, it is made of pottery mud foamed board and galvanized sheet, the primary raw material of pottery mud foamed board is ceramic powder, flyash and auxiliary additive, and be made up of chemical foaming technology；Pottery mud foamed board fire-protection rating after being made belongs to A grades of clean boards, and surfacing is beautiful, and fire resistance rating is high, can adhere to 90 minutes or more, and compression strength is good, good waterproof performance, and combustion process is non-toxic, no pyrolytic dropping, and environmental protection can be with the building same service life.
Description
Technical field
The invention belongs to purifying board technical fields, more particularly to one kind to be applied to electronics, pharmacy, food, biology, space flight boat
Empty, precision instrument manufacture and scientific research etc. require indoor environment the pottery mud foaming composite type purifying of harsh clean engineering field
Plate.
Background technique
The main composite type purifying plate of purifying board.Applied to hospital, laboratory, computer room etc. to the demanding area of clean environment
Domain.Composite type purifying plate is also known as purifying board, the composite plate by materials such as Coil Coating Products, stainless steels as plane materiel, is applied to electronics, system
Medicine, food, biology, space flight and aviation, precision instrument manufacture and scientific research etc. require indoor environment harsh clean engineering field.
Purifying board is mainly made of plate and core material, wherein rock wool, glass silk floss, paper honeycomb, pottery aluminium sheet, glass magnesium can be used
Seven kinds of core materials of paperboard bee, color steel plate, galvanized sheet, aluminum-zinc alloy tabula rasa, stainless steel, printed steel plate, aluminium-foil paper, PVC, three-ply board etc. ten
Several plates.
Existing purifying board mainly includes following several: 1. flame-retardant paper honeycomb clean boards: paper honeycomb core is by fire-retardant made of paper
At panel and another panel can be made of color steel plate, stainless steel plate, its anti-flammability is B1 grades, and only charing is not burnt, and not meet
Standard of check & acceptance；2. rock wool clean board: rock wool clean board is using color just contour plate as surface layer, and structure rock wool is sandwich layer, with special type
One kind " sandwich " structural slab that binder is combined, fire-protection rating belong to A1 clean board, finished product rock wool board surface smoothness,
Intensity difference, it is non-watertight, there is decomposition dropping, combustion process is toxic, not environmentally；3. glass magnesium clean board: glass magnesium board is non-burning
Material, fire resistance test detection of the fire-retardant rock wool purifying board of glass magnesium by national building engineering quality supervision inspection center, fire prevention etc.
Grade belongs to A1 clean board, and fire resistance rating is high, and compression strength is good, and surface smoothness is excellent, its raw material of glass magnesium are magnesium chloride, oxidation
Magnesium has greatly color steel plate surface corrosion, and finished product plate is heavier, and installation cost is high, and later period plate will appear large area and move back glue, especially
It expands with heat and contract with cold northern area is obvious.
Summary of the invention
It is beautiful that a kind of surfacing is provided the invention aims to overcome the deficiencies in the prior art, fire resistance rating height,
Compression strength and good waterproof performance, and the pottery mud foaming composite type purifying plate of environmental protection.
In order to achieve the above objectives, the technical solution adopted by the present invention is that: a kind of pottery mud foams composite type purifying plate, by it is multiple successively
Connected pottery mud foamed composite board is constituted；The pottery mud foamed composite board includes pottery mud foamed board, and the two sides of pottery mud foamed board is set
There is galvanized sheet.
Further, it sets connected between the two neighboring pottery mud foamed board, and is fixed by rivet for card.
Further, it is connected between the galvanized sheet and pottery mud foamed board by alite paste fastening.
Further, the galvanized sheet with a thickness of 0.5mm.
Further, the forming process of the pottery mud foamed board is as follows:
Stp1, it mixes the pottery powder of the cement of 40-50kg, the flyash of 10-20kg, 5-12kg to form mixture；
Stp2, the mixture in Stp1 is put into blender and stirs 1-6min, then be added into additive, stir 1-3min, and
Ensure that the above process carries out in the environment of temperature is 20-25 DEG C；
Stp3, the mixture in Stp2 is put into mold, above-mentioned mold is 2100:900:48's by multiple length, height and width
Three-dimensional mold is spliced, and is provided with feeding inlet in each mold；
Demoulding after Stp4,12-20h, conserves molding pottery mud foamed board；
Stp5, after 7 days factory carry out using.
Further, the additive is hydrogen peroxide.
Further, the maintenance is to be generated pottery mud foaming composite type purifying plate in forming process by cooling system
Heat send out, guarantee that pottery mud foaming composite type purifying plate is temperature-resistant in molding, between 20-25 DEG C.
Due to the application of the above technical scheme, compared with the prior art, the invention has the following advantages:
The pottery mud foaming composite type purifying plate of the present invention program, is made of, the master for mud foamed board of making pottery pottery mud foamed board and galvanized sheet
Wanting raw material is ceramic powder, flyash and auxiliary additive, and is made up of chemical foaming technology；Pottery mud foamed board after being made is anti-
Fiery grade belongs to A grades of clean boards, and surfacing is beautiful, and fire resistance rating is high, can adhere to 90 minutes or more, compression strength is good, waterproof
Property it is good, combustion process is non-toxic, no pyrolytic dropping, environmental protection, can be with the building same service life.
Detailed description of the invention
Technical scheme of the present invention is further explained with reference to the accompanying drawing:
Accompanying drawing 1 is the structural representation of the present invention；
Attached drawing 2 is the connected structural schematic diagram of two neighboring pottery mud foamed board；
Attached drawing 3 is the partial enlarged view in attached drawing 2；
Wherein: 1 pottery mud foamed board, 2 galvanized sheets.
Specific embodiment
Below in conjunction with the accompanying drawings and specific embodiment, the present invention is described in further details.
Refering to attached drawing 1-3, a kind of pottery mud foaming composite type purifying plate of the present invention, by multiple pottery mud being sequentially connected
Foamed composite board is constituted；The pottery mud foamed composite board includes pottery mud foamed board 1, and the two sides of pottery mud foamed board 1 is equipped with galvanized sheet
2。
As further embodiment, between the two neighboring pottery mud foamed board 1 for card set it is connected, and by rivet into
Row is fixed.
As further embodiment, it is connected between the galvanized sheet 2 and pottery mud foamed board 1 by alite paste fastening.
As further embodiment, the galvanized sheet with a thickness of 0.5mm.
Wherein the forming process of pottery mud foamed board includes various embodiments.
Implement one:
The forming process of pottery mud foamed board is as follows:
Stp1, it mixes the pottery powder of the cement of 40kg, the flyash of 10kg, 5kg to form mixture；
Stp2, the mixture in Stp1 is put into blender and stirs 1min, then be added into additive, stir 1min, and ensure
The above process is carried out in the case where temperature is 20 DEG C of environment；
Stp3, the mixture in Stp2 is put into mold, above-mentioned mold is 2100:900:48's by multiple length, height and width
Three-dimensional mold is spliced, and is provided with feeding inlet in each mold；
Demoulding after Stp4,12h, conserves molding pottery mud foamed board；
Stp5, after 7 days factory carry out using.
Implement two:
The forming process of pottery mud foamed board is as follows:
Stp1, it mixes the pottery powder of the cement of 50kg, the flyash of 20kg, 12kg to form mixture；
Stp2, the mixture in Stp1 is put into blender and stirs 6min, then be added into additive, stir 3min, and ensure
The above process is carried out in the case where temperature is 25 DEG C of environment；
Stp3, the mixture in Stp2 is put into mold, above-mentioned mold is 2100:900:48's by multiple length, height and width
Three-dimensional mold is spliced, and is provided with feeding inlet in each mold；
Demoulding after Stp4,20h, conserves molding pottery mud foamed board；
Stp5, after 7 days factory carry out using.
As further embodiment, the additive is hydrogen peroxide.
As further embodiment, the maintenance is to be formed pottery mud foaming composite type purifying plate by cooling system
The heat generated in the process is sent out, and is guaranteed that pottery mud foaming composite type purifying plate is temperature-resistant in molding, is in 20-25
Between DEG C.
Pottery mud foaming composite type purifying plate of the invention, is made of, the master for mud foamed board of making pottery pottery mud foamed board and galvanized sheet
Wanting raw material is ceramic powder, flyash and auxiliary additive, and is made up of chemical foaming technology；Pottery mud foamed board after being made is anti-
Fiery grade belongs to A grades of clean boards, and surfacing is beautiful, and fire resistance rating is high, can adhere to 90 minutes or more, compression strength is good, waterproof
Property it is good, combustion process is non-toxic, no pyrolytic dropping, environmental protection, can be with the building same service life.
The above is only specific application examples of the invention, are not limited in any way to protection scope of the present invention.All uses
Equivalent transformation or equivalent replacement and the technical solution formed, all fall within rights protection scope of the present invention.
Claims (7)
- The composite type purifying plate 1. a kind of pottery mud foams, it is characterised in that: be made of multiple pottery mud foamed composite boards being sequentially connected； The pottery mud foamed composite board includes pottery mud foamed board, and the two sides of pottery mud foamed board is equipped with galvanized sheet.
- The composite type purifying plate 2. pottery mud according to claim 1 foams, it is characterised in that: the two neighboring pottery mud foaming It sets for card connected between plate, and is fixed by rivet.
- The composite type purifying plate 3. pottery mud according to claim 1 foams, it is characterised in that: the galvanized sheet and pottery mud foaming It is fastened and is connected by alite paste between plate.
- The composite type purifying plate 4. pottery mud according to claim 1 foams, it is characterised in that: the galvanized sheet with a thickness of 0.5mm。
- The composite type purifying plate 5. pottery mud according to claim 1 foams, it is characterised in that: the molding of the pottery mud foamed board Process is as follows:Stp1, it mixes the pottery powder of the cement of 40-50kg, the flyash of 10-20kg, 5-12kg to form mixture；Stp2, the mixture in Stp1 is put into blender and stirs 1-6min, then be added into additive, stir 1-3min, and Ensure that the above process carries out in the environment of temperature is 20-25 DEG C；Stp3, the mixture in Stp2 is put into mold, above-mentioned mold is the vertical of 2100:900:48 by multiple length, height, width Mould is spliced, and is provided with feeding inlet in each mold；Demoulding after Stp4,12-20h, conserves molding pottery mud foamed board；Stp5, after 7 days factory carry out using.
- The composite type purifying plate 6. pottery mud according to claim 5 foams, it is characterised in that: the additive is hydrogen peroxide.
- The composite type purifying plate 7. pottery mud according to claim 5 foams, it is characterised in that: the maintenance is to pass through heat dissipation to be The system heat that generates in forming process of mud foaming composite type purifying plate that will make pottery is sent out, and guarantees that pottery mud foams composite type purifying Plate is temperature-resistant in molding, between 20-25 DEG C.