CN109423201A - It is a kind of to thicken waterproof and insulation integrated coating - Google Patents
It is a kind of to thicken waterproof and insulation integrated coating Download PDFInfo
- Publication number
- CN109423201A CN109423201A CN201710546205.3A CN201710546205A CN109423201A CN 109423201 A CN109423201 A CN 109423201A CN 201710546205 A CN201710546205 A CN 201710546205A CN 109423201 A CN109423201 A CN 109423201A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- waterproof
- insulation integrated
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Waterproof and insulation integrated coating is thickeied the invention discloses a kind of, belong to technical field of coatings, the raw material including following parts by weight: 10~40 parts of epoxy modified silicone resin, 25~55 parts of alcohol ester, 10~20 parts of dibutyl phthalate, 2~3 parts of ceramic microsphere and 1~3 part of attapulgite.The waterproof and insulation integrated coating of a kind of thickening of the invention, using epoxy modified silicone resin as film forming matter, and using vitreum earth silicon material, special ceramic materials, trbasic zinc phosphate, fibrous material as filler, insulation anticorrosive paint is made, a kind of waterproof heat insulation coating is made using raw materials such as elastic emulsion, hollow glass micropearl, diatomite, infrared reflection agent, asbestos wools, which, which only coats 2mm thickness, can reach good waterproof thermal-insulated effect.
Description
Technical field
The invention belongs to technical field of coatings, and in particular to a kind of to thicken waterproof and insulation integrated coating.
Background technique
In recent years, Chinese coating industry the real estate of fast growth, automobile, ship, etc. downstream industries promotion under, with
Speed higher than GDP5%-10% increases, and becomes the second big country of world's coating material production and consumption.
The 1-12 month in 2006, Chinese coating, ink, pigment and similar products manufacturing industry realize total cumulative output value of industry 191,
934,746 thousand yuan, increase by 26.19% than same period last year；Whole year realizes accumulative 185,825,254 thousand yuan of product sales revenue, than
Same period last year increases by 25.94%；Whole year realizes 12,513,338 thousand yuan of accumulated profit total value, increases by 25.7% than same period last year.
The 1-11 month in 2007, the accumulative present price total industrial output value of national 1985 coatings enterprises is 119,093,440,000 yuan, together
Than increasing by 27.5%, wherein new product output value 1-11 month to date is 5,288,430,000 yuan, increases by 39.2% on a year-on-year basis, same period coating sales volume
Also the impetus of rapid growth is kept.Coating industry all continues to increase rapidly for years, cancels from January 1st, 2006 related
The development of products export tariff, coating industry is further raised speed.
Coating products kind is more and more, and application range also constantly expands, and coatings industry has become in chemical industry one
Important independent production industrial department.The current coating yield in China is about 2,000,000 tons or more, and wherein industrial coating accounts for 60%, closely
Demand is increased over year with 3.4% average speed.
China's Coating Market supply and demand in 2008 substantially balances, but it is still necessary to optimize for structure.China's house ornamentations in 2008 and for building
Coating consumption figure will be in increase trend, and coating demand will be more than 2,550,000 tons.Wherein, about 900,000 tons of industrial coating, building coating
1150000 tons, 500,000 tons of sapecial coating and other functional coatings.Breed structure substantially presses industrial coating 35%~40%, building
Coating 45%~50%, sapecial coating 10%~15% are distributed.National about 2,600,000 tons of supply amount of coating in 2007, with demand
It is substantially close, it is in a basic balance.
Chinese coating yield in 2009 is up to 7,550,000 tons, and wherein car paint accounts for 6%, about 450,000 tons, and woodwork coating accounts for
10%, about 740,000 tons, marine paint account for 5%, about 400,000 tons, and powdery paints accounts for 11%, about 800,000 tons, and other industry apply
Material accounts for 33%, about 2,530,000 tons, and building coating accounts for 35%, about 2,640,000 tons.Calculated by annual output, China's coating industry oneself squeeze
Life experience circle most forefront.But coating dosage is still considerably less per capita, it is believed that in face of the market demand that is huge and just increasing rapidly,
It is extremely urgent to promote coating quality！
Summary of the invention
Goal of the invention: waterproof and insulation integrated coating is thickeied the purpose of the present invention is to provide a kind of.
Technical solution: for achieving the above object, the present invention adopts the following technical scheme:
It is a kind of to thicken waterproof and insulation integrated coating, the raw material including following parts by weight: epoxy modified silicone resin
10~40 parts, 25~55 parts of alcohol ester, 10~20 parts of dibutyl phthalate, 2~3 parts of ceramic microsphere and attapulgite 1~3
Part.
The raw material further includes the glass powder that parts by weight are 5~10 parts.
The raw material further includes the asbestos wool that parts by weight are 2~3 parts.
The raw material further includes the silica for the vitreum that parts by weight are 5~10 parts.
The raw material further includes the wollastonite in powder that parts by weight are 5~10 parts.
The utility model has the advantages that compared with prior art, the waterproof and insulation integrated coating of a kind of thickening of the invention, with epoxy-modified
Organic siliconresin is as film forming matter, and with vitreum earth silicon material, special ceramic materials, trbasic zinc phosphate, fibrous material
Insulation anticorrosive paint is made in filler, utilizes elastic emulsion, hollow glass micropearl, diatomite, infrared reflection agent, asbestos
A kind of waterproof heat insulation coating is made in the raw materials such as suede, which, which only coats 2mm thickness, can reach good waterproof thermal-insulated effect.
Specific embodiment
The present invention is described further With reference to embodiment.
Embodiment 1
It is a kind of to thicken waterproof and insulation integrated coating, the raw material including following parts by weight: epoxy modified silicone resin
10 parts, 25 parts of alcohol ester, 10 parts of dibutyl phthalate, 2 parts of ceramic microsphere and 1 part of attapulgite.
Raw material further includes the silica that parts by weight are 5 parts of glass powder, 2 parts of asbestos wool, 5 parts of vitreum.
Embodiment 2
It is a kind of to thicken waterproof and insulation integrated coating, the raw material including following parts by weight: epoxy modified silicone resin
40 parts, 55 parts of alcohol ester, 20 parts of dibutyl phthalate, 3 parts of ceramic microsphere and 3 parts of attapulgite.
Raw material further includes the silica that parts by weight are 10 parts of glass powder, 3 parts of asbestos wool, 10 parts of vitreum.
Embodiment 3
It is a kind of to thicken waterproof and insulation integrated coating, the raw material including following parts by weight: epoxy modified silicone resin
15 parts, 30 parts of alcohol ester, 12 parts of dibutyl phthalate, 2.2 parts of ceramic microsphere and 1.5 parts of attapulgite.
Raw material further includes the silica that parts by weight are 6 parts of glass powder, 2.5 parts of asbestos wool, 7 parts of vitreum.
Embodiment 4
It is a kind of to thicken waterproof and insulation integrated coating, the raw material including following parts by weight: epoxy modified silicone resin
30 parts, 25 parts of alcohol ester, 20 parts of dibutyl phthalate, 3 parts of ceramic microsphere and 1 part of attapulgite.
Raw material further includes the silica that parts by weight are 10 parts of glass powder, 3 parts of asbestos wool, 8 parts of vitreum.
Embodiment 5
It is a kind of to thicken waterproof and insulation integrated coating, the raw material including following parts by weight: epoxy modified silicone resin
40 parts, 55 parts of alcohol ester, 20 parts of dibutyl phthalate, 3 parts of ceramic microsphere and 1 part of attapulgite.
Raw material further includes the silica that parts by weight are 10 parts of glass powder, 3 parts of asbestos wool, 8 parts of vitreum.
To sum up:
(1) the coating selection epoxy silicone resin is as film forming matter so that coating has preferable heat resistance and soft
Toughness.
(2) ceramic on metal filler is selected so that there is macroscopic views to be combined between substrate and coating --- mechanical interlocking makes
It is good to obtain coating adhesion.And to form fine and close transition zone between coating and substrate so that anticorrosion with coat better performances.
(3) the lower vitreum silica of thermal coefficient is selected, the heat-proof quality of coating is enhanced.
(4) under the premise of not influencing the temperature tolerance of coating, suitable trbasic zinc phosphate is added, enhances coating adhesion.
(5) coating has preferable heat insulation in 115mm.
Claims (5)
1. a kind of thicken waterproof and insulation integrated coating, it is characterised in that: the raw material including following parts by weight: epoxy-modified to have
10~40 parts of machine silicone resin, 25~55 parts of alcohol ester, 10~20 parts of dibutyl phthalate, 2~3 parts of ceramic microsphere and concave convex rod
1~3 part of soil.
2. a kind of waterproof and insulation integrated coating of thickening according to claim 1, it is characterised in that: the raw material also wraps
Include the glass powder that parts by weight are 5~10 parts.
3. a kind of waterproof and insulation integrated coating of thickening according to claim 1, it is characterised in that: the raw material also wraps
Include the asbestos wool that parts by weight are 2~3 parts.
4. a kind of waterproof and insulation integrated coating of thickening according to claim 1, it is characterised in that: the raw material also wraps
Include the silica for the vitreum that parts by weight are 5~10 parts.
5. a kind of waterproof and insulation integrated coating of thickening according to claim 1, it is characterised in that: the raw material also wraps
Include the wollastonite in powder that parts by weight are 5~10 parts.