CN109402727A - A kind of bio-photon crystal and preparation method thereof - Google Patents
A kind of bio-photon crystal and preparation method thereof Download PDFInfo
- Publication number
- CN109402727A CN109402727A CN201811433915.6A CN201811433915A CN109402727A CN 109402727 A CN109402727 A CN 109402727A CN 201811433915 A CN201811433915 A CN 201811433915A CN 109402727 A CN109402727 A CN 109402727A
- Authority
- CN
- China
- Prior art keywords
- bio
- raw material
- crystal
- photon
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of bio-photon crystal and preparation method thereof, first by the ingredient in proportion of the oxide raw material containing metal ions such as nickel magnesium calcium iron neodymium aluminium, calcination, drying are carried out to many oxide mixed raw material and weighed, by this raw material, it is pressed into fixed shape, raw material roasting is then synthesized into a kind of polycrystalline compounds crystal raw material;Then, roasting raw material is put into single crystal growing furnace with this method is lifted by pulling growth photonic crystal after material melts, will be used after the crystal boule grown up to cutting, obtains corresponding to more bio-photon frequency photonic crystals.Crystal of the present invention can not need any electric power load at normal temperature can generate the crystal photon radiation frequency to match with human-body biological photon radiation frequency.
Description
Technical field
The invention belongs to Material Fields, and in particular to a kind of crystal manufacture.
Background technique
Modern Pathological Physiology proposes: the generation of all diseases (including human senility) all with gene (i.e.DNA) damage have
It closes.Since bio-photon byDNA It generates, turnes back, bio-photon participates in againDNA Synthesis.Accordingly, bio-light is utilized
Son radiation is to repairDNA Damage, i.e. repair cell damage, until repair tissue, organ damage are possibly realized.One as a result,
Novel medicine——Bio-photon medicine (or bio-photon medical science of recovery therapy) is come into being!Countries in the world scientist is grinding
Study carefully, develop and find a kind of biophoton emission frequency spectrum that can be generated with human body match, directly itself can generate biology
The material of photon radiation, then, for human body diseases prevention and treatment and rehabilitation.
Summary of the invention
The invention discloses a kind of biophoton emission crystal, scientific matching prescription, can wide spectrum eradiation go out and human body
Itself transmitted spectrum matches.It can reach and occur with human-body biological photon frequency spectrum“It is relevant”, that is, generate“It tangles”, can be used for disease
In rehabilitation.
The present invention is first by the ingredient in proportion of the oxide raw material containing metal ions such as nickel magnesium calcium iron neodymium aluminium, to a variety of oxygen
Compound mixed raw material carries out calcination, drying and weighs, and by this raw material, is pressed into fixed shape, then roasts raw material and synthesizes
A kind of polycrystalline compounds crystal raw material;Then, roasting raw material is put into single crystal growing furnace to use and lifts this method for material melts
Pulling growth photonic crystal afterwards will use after the crystal boule grown up to cutting, obtain corresponding to more bio-photon frequency photons crystalline substances
Body.
A kind of preparation method of bio-photon crystal, the specific steps are as follows:
(1) metal oxide powder raw material of the purity more than or equal to 99.9995% are mixed and is added in alumina powder, every kind
The additive amount of metal oxide powder is the 0.1 ~ 1% of alumina powder quality;It is then pressed into bulk, at 700 ~ 1000 DEG C
Burn 9 ~ 15h under environment, suppressed again after cooling, after 6 ~ 10h is burnt in 1000 ~ 1300 DEG C, take out cooling stand-by;
(2) raw material are made in step (1) and are put into the lifting speed for using crystal pull furnace in Iridium Crucible according to 0.5-1.5mm/h
Degree, the revolving speed shape of 6-20r/min lift to form monocrystal;Cutting uses shape after taking-up.
Metal oxide of the present invention is nickel, magnesium, calcium, iron and neodymium oxides.
Preferably, the additive amount of every kind of metal oxide powder is the 0.2% of alumina powder quality in the present invention.
Preferably, in step (1) of the present invention, it is pressed into bulk, 12h is burnt in the environment of 900 DEG C, is pressed again after cooling
System, after burn 8h in 1200 DEG C, take out cooling stand-by.
Preferably, lumpy sizes are diameter 60cm thickness 2cm in step (1) of the present invention.
The invention also discloses the bio-photon crystal being prepared using the above method.
Beneficial effects of the present invention:
The present invention prepares photonic crystal by Multimetal oxide, and preferred nickel, magnesium, calcium, iron, neodymium and aluminum metal, optimization
The combination matching of each metal oxide makes its play optimal synergistic effect, it is burnt according to the compacting of best product performance
It is re-compacted burn after, the bio-photon crystal of the more bio-photon frequencies of the correspondence is obtained after lifting is handled.It is reacting
In the process, the non-uniform volatilization and absorption water for avoiding component participate in chemical reaction.Crystal of the present invention can not need at normal temperature
Any electric power load can generate the crystal photon radiation frequency to match with human-body biological photon radiation frequency.
Specific embodiment
Embodiment 1
A kind of preparation method of bio-photon crystal, the specific steps are as follows:
(1) nickel, magnesium, calcium, iron and the neodymium metal oxide powder raw material that purity is both greater than equal to 99.9995% mix addition
In alumina powder, the additive amount of every kind of metal oxide powder is the 0.2% of alumina powder quality;Bulk is then pressed into,
Burn 12h in the environment of 900 DEG C, suppressed again after cooling, after 8h is burnt in 1200 DEG C, take out cooling stand-by;
(2) step (1) obtained raw material are put into Iridium Crucible the pull rate with crystal pull furnace according to 1.0mm/h,
The revolving speed shape of 15r/min lifts to form monocrystal;Cutting uses shape after taking-up.
Embodiment 2
A kind of preparation method of bio-photon crystal, the specific steps are as follows:
(1) nickel by purity more than or equal to 99.9995%, magnesium, calcium, iron and neodymium metal oxide powder raw material, which mix, is added oxygen
Change in aluminium powder, the additive amount of every kind of metal oxide powder is the 0.1% of alumina powder quality;It is then pressed into bulk,
Burn 15h in the environment of 700 DEG C, suppressed again after cooling, after 10h is burnt in 1000 DEG C, take out cooling stand-by;
(2) raw material are made in step (1) to be put into Iridium Crucible with pull rate of the crystal pull furnace according to 0.5mm/h, 6r/
The revolving speed shape of min lifts to form monocrystal;Cutting uses shape after taking-up.
Embodiment 3
A kind of preparation method of bio-photon crystal, the specific steps are as follows:
(1) nickel by purity more than or equal to 99.9995%, magnesium, calcium, iron and neodymium metal oxide powder raw material, which mix, is added oxygen
Change in aluminium powder, the additive amount of every kind of metal oxide powder is the 1.0% of alumina powder quality;It is then pressed into bulk,
Burn 9h in the environment of 1000 DEG C, suppressed again after cooling, after 6h is burnt in 1300 DEG C, take out cooling stand-by;
(2) step (1) obtained raw material are put into Iridium Crucible the pull rate with crystal pull furnace according to 1.5mm/h,
The revolving speed shape of 20r/min lifts to form monocrystal;Cutting uses shape after taking-up.
Claims (6)
1. a kind of preparation method of bio-photon crystal, which is characterized in that specific step is as follows:
(1) metal oxide powder raw material of the purity more than or equal to 99.9995% are mixed and is added in alumina powder, every kind
The additive amount of metal oxide powder is the 0.1 ~ 1% of alumina powder quality;It is then pressed into bulk, at 700 ~ 1000 DEG C
Burn 9 ~ 15h under environment, suppressed again after cooling, after 6 ~ 10h is burnt in 1000 ~ 1300 DEG C, take out cooling stand-by;
(2) raw material are made in step (1) and are put into the lifting speed for using crystal pull furnace in Iridium Crucible according to 0.5-1.5mm/h
Degree, the revolving speed shape of 6-20r/min lift to form monocrystal;Cutting uses shape after taking-up.
2. the preparation method of bio-photon crystal according to claim 1, which is characterized in that the metal oxide is
Nickel, magnesium, calcium, iron and neodymium oxides.
3. the preparation method of bio-photon crystal according to claim 1, which is characterized in that every kind of metal oxide powder
Additive amount be alumina powder quality 0.2%.
4. the preparation method of bio-photon crystal according to claim 1, which is characterized in that briquet in step (1)
After shape, burn 12h in the environment of 900 DEG C, suppressed again after cooling, after 8h is burnt in 1200 DEG C, take out cooling stand-by.
5. the preparation method of bio-photon crystal according to claim 1, which is characterized in that lumpy sizes in step (1)
For diameter 60cm thickness 2cm.
6. a kind of bio-photon crystal being prepared using any one of claim 1-5 the method.