CN109401207A - A kind of environmental protection glass structure plate - Google Patents
A kind of environmental protection glass structure plate Download PDFInfo
- Publication number
- CN109401207A CN109401207A CN201811432782.0A CN201811432782A CN109401207A CN 109401207 A CN109401207 A CN 109401207A CN 201811432782 A CN201811432782 A CN 201811432782A CN 109401207 A CN109401207 A CN 109401207A
- Authority
- CN
- China
- Prior art keywords
- glass structure
- environmentally friendly
- structure plate
- environmental protection
- protection glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention is a kind of environmentally friendly glass structure plate, includes additive and carrier, the raw material in formula forms by weight percentage is respectively: 0.5~6% silane coupling agent, 10~35% thin base benzimidazoles, 1~10% 2-pyrrolidone-5-carboxylic acid's potassium, 0~3% damping additive, 0~2.5% refractory fibre, 5~20% vinyl ester resins, 10~20% germanium silicon optical fiber Bragg gratings, 30~60% environmentally friendly polyester, the product prepared by this method, possess preferable degradability, there is fabulous intensity.
Description
Technical field
The invention discloses a kind of environmentally friendly glass structure plates.
Background technique
In existing technology, structural slab possesses poor degradability, and structural slab is not easy to repair, once damage needs to change
New, bad structural slab can cause damages to environment.
Summary of the invention
In view of the above existing problems in the prior art, the present invention provides a kind of environmentally friendly glass structure plates, possess and preferably may be used
Degradability has fabulous intensity.
To achieve the goals above, the invention is realized by the following technical scheme: a kind of environmental protection glass structure plate, in formula
Raw material form by weight percentage and be respectively: 0.5~6% silane coupling agent, 10~35% thin base benzimidazoles, 1~10% pyrroles
Alkanone carboxylic acid potassium, 0~3% damping additive, 0~2.5% refractory fibre, 5~20% vinyl ester resins, 10~20% germanium silicon light
Fine Bragg grating, 30~60% environmentally friendly polyester.
The utility model has the advantages that the product prepared by this method, possesses preferable degradability, there is fabulous intensity.
Specific embodiment
Embodiment 1
A kind of environmental protection glass structure plate, the raw material in formula forms by weight percentage is respectively: 0.5% silane coupling agent, 10%
Dredge base benzimidazole, 1% 2-pyrrolidone-5-carboxylic acid's potassium, 1% damping additive, 1% refractory fibre, 5% vinyl ester resins, 10% germanium silicon
Fiber bragg grating, 30% environmentally friendly polyester, intensity is lower at this time.
Embodiment 2
A kind of environmental protection glass structure plate, the raw material in formula forms by weight percentage is respectively: 6% silane coupling agent, 35% dredges
Base benzimidazole, 10% 2-pyrrolidone-5-carboxylic acid's potassium, 3% damping additive, 2.5% refractory fibre, 20% vinyl ester resins, 20% germanium
Silicon optical fiber Bragg grating, 60% environmentally friendly polyester, degradability is bad at this time.
Embodiment 3
A kind of environmental protection glass structure plate, the raw material in formula forms by weight percentage is respectively: 4% silane coupling agent, 23% dredges
Base benzimidazole, 5% 2-pyrrolidone-5-carboxylic acid's potassium, 1.5% damping additive, 1.25% refractory fibre, 13% vinyl ester resins, 15%
Germanium silicon optical fiber Bragg grating, 45% environmentally friendly polyester, possesses preferable degradability at this time, there is fabulous intensity.
Claims (4)
1. a kind of environmental protection glass structure plate, includes additive and carrier, which is characterized in that the raw material in formula is by weight percentage
Composition is respectively: 0.5~6% silane coupling agent, 10~35% thin base benzimidazoles, 1~10% 2-pyrrolidone-5-carboxylic acid's potassium, 0~3% resistance
Buddhist nun's additive, 0~2.5% refractory fibre, 5~20% vinyl ester resins, 10~20% germanium silicon optical fiber Bragg gratings, 30~60%
Environmentally friendly polyester.
2. environmental protection glass structure plate according to claim 1, which is characterized in that the raw material group by weight percentage in formula
At being respectively: 0.5% silane coupling agent, 10% thin base benzimidazole, 1% 2-pyrrolidone-5-carboxylic acid's potassium, 1% damping additive, 1% fire resisting
Fiber, 5% vinyl ester resins, 10% germanium silicon optical fiber Bragg grating, 30% environmentally friendly polyester.
3. environmental protection glass structure plate according to claim 1, which is characterized in that the raw material group by weight percentage in formula
At being respectively: 6% silane coupling agent, 35% thin base benzimidazole, 10% 2-pyrrolidone-5-carboxylic acid's potassium, 3% damping additive, 2.5% fire resisting
Fiber, 20% vinyl ester resins, 20% germanium silicon optical fiber Bragg grating, 60% environmentally friendly polyester.
4. environmental protection glass structure plate according to claim 1, which is characterized in that the raw material group by weight percentage in formula
At being respectively: 4% silane coupling agent, 23% thin base benzimidazole, 5% 2-pyrrolidone-5-carboxylic acid's potassium, 1.5% damping additive, 1.25% is resistance to
Fiery fiber, 13% vinyl ester resins, 15% germanium silicon optical fiber Bragg grating, 45% environmentally friendly polyester.