CN100355689C - High-intensity reflecting cement - Google Patents
High-intensity reflecting cement Download PDFInfo
- Publication number
- CN100355689C CN100355689C CNB2005100125690A CN200510012569A CN100355689C CN 100355689 C CN100355689 C CN 100355689C CN B2005100125690 A CNB2005100125690 A CN B2005100125690A CN 200510012569 A CN200510012569 A CN 200510012569A CN 100355689 C CN100355689 C CN 100355689C
- Authority
- CN
- China
- Prior art keywords
- cement
- present
- steel fiber
- glass beads
- white cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to high-strength reflecting cement which is formed by dryly stirring the following raw materials with the weight portions: 30-70 portions of white cement, 20-60 portions of glass beads and 5-10 portions of steel fiber. The present invention is formed by carefully compacting the white cement, the glass beads and the steel fiber; the accurate compatibility of the white cement and the glass beads in the raw materials ensures the reflex action to the light at night; when the present invention is applied to traffic roads, the present invention can guide and alarm the driver through the reflected light so as to prevent many traffic accidents from happening. When the present invention is applied to buildings such as storied buildings, etc., the present invention can beautify the environment at night. By the added steel fiber, the present invention also avoids the problems that the cement is loose, is low in strength, has no load bearing or poor load bearing performance, does not conform to the requirement of the building acceptance standard, and affects the service life of the building or results in great danger when the white cement and the glass beads are put together, so that the present invention ensures the strength of the cement and conforms to the requirement of the building construction engineering.
Description
Technical field
The present invention relates to a kind of high-intensity reflecting cement.
Background technology
In growing society, cement is more and more demonstrating its great, indispensable importance as a kind of important material of construction aspect communication, city-building, social needs or the like.But existing cement products is more single, does not possess other function, does not especially have a kind of cement that can be reflective to occur on the market as yet.
Summary of the invention
The technical problem to be solved in the present invention provides a kind of intensity height, can pass through the reflective high-intensity reflecting cement of light source irradiation at night.
The technical scheme that the present invention solves the problems of the technologies described above employing is: high-intensity reflecting cement, and it is made through doing to stir by following materials based on weight:
White cement 30-70 part, granulated glass sphere 20-60 part, steel fiber 5-10 part.
Above-mentioned high-intensity reflecting cement, the particle diameter of described granulated glass sphere are 0.02-0.6cm, and steel fiber length is 0.5-1.8cm.
Above-mentioned high-intensity reflecting cement, the model of described white cement are 32.5#-62.5#.
The technical progress that the present invention obtains is: the present invention adopts the meticulous compatibility of white cement, granulated glass sphere and steel fiber to form, the accurate compatibility of white cement in the raw material and granulated glass sphere has guaranteed that well night, it was to the reflection of light effect, as be applied on the traffic route, the driver can play good guiding and warning function by the light of reflection, thereby has avoided the generation of many traffic accidents.And if be applied on the buildingss such as building, again can it be to the effect of well beautifying the environment at night.And the adding of steel fiber, it is loose to have avoided above-mentioned two kinds of raw materials to put together the cement that causes again well, intensity is lower, not load-bearing or bearing are relatively poor, do not meet the requirement of building standard for acceptance and influenced the work-ing life of building or caused great danger, well guarantee cement intensity, met the requirement of construction engineering.
Embodiment
Embodiment one: cement prescription (parts by weight): white cement 30Kg, granulated glass sphere 20Kg, steel fiber 5Kg.The model of white cement is 32.5#, and the particle diameter of granulated glass sphere is 0.02cm, and steel fiber length is 0.5cm.
The preparation method:
The raw material of above-mentioned parts by weight is stirred under dry situation, during use, adds an amount of water, wait to need the operation of construction to finish after, the slighter polishing of body of cement is got final product.
As required, can in cement, add chemical additive red, orange, yellow, green, blue or green, blue, color purple, just make motley reflecting cement.
Embodiment two: cement prescription (parts by weight): white cement 50Kg, granulated glass sphere 40Kg, steel fiber 7.5Kg.The model of white cement is 47.5#, and the particle diameter of granulated glass sphere is 0.4cm, and steel fiber length is 1.2cm.
Its preparation method is with embodiment one.
Embodiment three: cement prescription (parts by weight): white cement 70Kg, granulated glass sphere 60Kg, steel fiber 10Kg.The model of white cement is 62.5#, and the particle diameter of granulated glass sphere is 0.6cm, and steel fiber length is 1.8cm.
Its preparation method is with embodiment one.
Claims (3)
1, high-intensity reflecting cement is characterized in that: it is made through doing to stir by following materials based on weight:
White cement 30-70 part, granulated glass sphere 20-60 part, steel fiber 5-10 part.
2, high-intensity reflecting cement according to claim 1 is characterized in that: the particle diameter of described granulated glass sphere is 0.02-0.6cm, and steel fiber length is 0.5-1.8cm.
3, high-intensity reflecting cement according to claim 1 is characterized in that: the model of described white cement is 32.5#-62.5#.