CN109397787A - A kind of antibacterial light and thin fabric - Google Patents
A kind of antibacterial light and thin fabric Download PDFInfo
- Publication number
- CN109397787A CN109397787A CN201811202313.XA CN201811202313A CN109397787A CN 109397787 A CN109397787 A CN 109397787A CN 201811202313 A CN201811202313 A CN 201811202313A CN 109397787 A CN109397787 A CN 109397787A
- Authority
- CN
- China
- Prior art keywords
- fiber
- layer
- antibacterial
- cotton crepe
- frivolous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of antibacterial light and thin fabric, including frivolous layer and antibiotic layer, the frivolous layer is pasted and fixed on antibiotic layer upper surface by antimicrobial adhesive, and compared with prior art, the present invention has the function of following the utility model has the advantages that realizing bilayer, improve warming effect, and have the advantages that elasticity is high, it is not easy to be pulled bad, and also improve antibacterial effect, health-care effect is improved, and aesthetics is also improved by the design of luminescent material.
Description
Technical field
The present invention is a kind of antibacterial light and thin fabric, belongs to fabric technical field.
Background technique
Existing light and thin fabric functionality is single, does not have warming function not only, and elasticity is poor, is easily pulled bad, and
Antibacterial effect is poor, therefore, continues a kind of antibacterial light and thin fabric to solve the above problems.
Summary of the invention
In view of the deficienciess of the prior art, it is an object of the present invention to provide a kind of antibacterial light and thin fabric, to solve above-mentioned back
The problem of being proposed in scape technology.
To achieve the goals above, the present invention is to realize by the following technical solutions: a kind of antibacterial light and thin fabric, packet
Frivolous layer and antibiotic layer are included, the frivolous layer is pasted and fixed on antibiotic layer upper surface, including following system by antimicrobial adhesive
Standby process:
Firstly, choosing the Down Fiber that becomes mildewed, the cotton crepe fiber of 32-70 parts by weight and the bamboo charcoal of 100 parts by weight of 30-68 parts by weight
Fiber;
Then, by plush fibrous raw material at 85-100 DEG C with methyl morpholine oxide mixed dissolution, stir 15-35min, obtain
Become mildewed Down Fiber stoste;Cotton crepe fiber raw material is mixed at 90-105 DEG C with methyl morpholine oxide, mixing time 25-
Then excessive moisture is removed under reduced pressure in 65min, cotton crepe fiber stoste is made;The Down Fiber stoste that will become mildewed and cotton crepe fiber stoste
It pours into hopper and is mixed, then pour into screw extruder from hopper, at 90-125 DEG C after shearing dissolution, spinning is sent in filtering
Filament plate carries out spinning, so that become mildewed Down Fiber and cotton crepe fiber be made, the Down Fiber that then will become mildewed is mixed with cotton crepe fiber
It spins, so that the composite fibre long filament of become mildewed Down Fiber and cotton crepe fiber be made;
Then, bamboo-carbon fibre raw material is poured into immersed with impregnating in the filtrate of ganoderma lucidum and ginseng, soaking time 30-
45min, while bamboo-carbon fibre raw material is stirred, then mixing time 20-30min takes out bamboo-carbon fibre raw material, and
It is put into screw extruder and is squeezed out, spinning is then carried out by melt spinning technology, then pours into spinning containing antibacterial
The solution of softening agent is impregnated again, and then soaking time 25-35min takes out spinning, and carry out sunning 1h, then
Spinning is washed, deburring and bleaching, then carry out winder, so that bamboo charcoal fiber be made;
Then, frivolous layer is made by loom in the composite fibre long filament of become mildewed Down Fiber and cotton crepe fiber, then by penetrating
Luminescent material is ejected into frivolous layer surface by frequency magnetron sputtering technique, and antibacterial then is made by loom in bamboo charcoal fiber
Layer;
Then, frivolous layer is aligned with antibiotic layer, and uniformly smears antimicrobial adhesive between frivolous layer and antibiotic layer, so
Frivolous layer and antibiotic layer are put into press roller afterwards and carry out extrusion forming;
It is dried finally, fabric obtained is placed on drying frame, then the control of sunning time is wound whole in 10-15h
Reason.
Further, the cotton crepe fiber of become mildewed Down Fiber and 70 parts by weight for choosing 30 parts by weight, thus blended
Obtain becoming mildewed the composite fibre long filament of Down Fiber and cotton crepe fiber, and respectively as the warp and weft on loom, thus
Frivolous layer is made by interlacement weave, has the advantages that soft, elasticity is high.
Further, the cotton crepe fiber of become mildewed Down Fiber and 32 parts by weight for choosing 68 parts by weight, thus blended
Obtain becoming mildewed the composite fibre long filament of Down Fiber and cotton crepe fiber, and respectively as the warp and weft on loom, thus
Frivolous layer is made by interlacement weave, has the advantages that good warmth retention effect.
Further, the cotton crepe fiber of become mildewed Down Fiber and 50 parts by weight for choosing 50 parts by weight, thus blended
Obtain becoming mildewed the composite fibre long filament of Down Fiber and cotton crepe fiber, and respectively as the warp and weft on loom, thus
Frivolous layer is made by interlacement weave, has the advantages that soft and warming.
Further, the antibacterial softener is a kind of cationic polymer antibacterial agent, and the antimicrobial adhesive is one kind
Silane quaternary adhesive.
Further, the hole diameter of spinneret is 10-100um.
Further, the luminescent material is the strontium aluminate that a kind of europium and dysprosium are co-doped with.
Beneficial effects of the present invention: a kind of antibacterial light and thin fabric of the invention, the present invention is by adding frivolous layer and resisting
The design of bacterium layer, not only realizes double-deck function, improves warming effect, and has the advantages that elasticity is high, is not easy to be pulled
It is bad, and antibacterial effect is also improved, health-care effect is improved, and aesthetics is also improved by the design of luminescent material.
Specific embodiment
To be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, below with reference to
Specific embodiment, the present invention is further explained.
The present invention provides a kind of technical solution: a kind of antibacterial light and thin fabric, including frivolous layer and antibiotic layer, and frivolous layer is logical
It crosses antimicrobial adhesive and is pasted and fixed on antibiotic layer upper surface, including following preparation process:
Firstly, choosing the Down Fiber that becomes mildewed, the cotton crepe fiber of 32-70 parts by weight and the bamboo charcoal of 100 parts by weight of 30-68 parts by weight
Fiber;
Then, by plush fibrous raw material at 85-100 DEG C with methyl morpholine oxide mixed dissolution, stir 15-35min, obtain
Become mildewed Down Fiber stoste;Cotton crepe fiber raw material is mixed at 90-105 DEG C with methyl morpholine oxide, mixing time 25-
Then excessive moisture is removed under reduced pressure in 65min, cotton crepe fiber stoste is made;The Down Fiber stoste that will become mildewed and cotton crepe fiber stoste
It pours into hopper and is mixed, then pour into screw extruder from hopper, at 90-125 DEG C after shearing dissolution, spinning is sent in filtering
Filament plate carries out spinning, so that become mildewed Down Fiber and cotton crepe fiber be made, the Down Fiber that then will become mildewed is mixed with cotton crepe fiber
It spins, so that the composite fibre long filament of become mildewed Down Fiber and cotton crepe fiber be made;
Then, bamboo-carbon fibre raw material is poured into immersed with impregnating in the filtrate of ganoderma lucidum and ginseng, soaking time 30-
45min, while bamboo-carbon fibre raw material is stirred, then mixing time 20-30min takes out bamboo-carbon fibre raw material, and
It is put into screw extruder and is squeezed out, spinning is then carried out by melt spinning technology, then pours into spinning containing antibacterial
The solution of softening agent is impregnated again, and then soaking time 25-35min takes out spinning, and carry out sunning 1h, then
Spinning is washed, deburring and bleaching, then carry out winder, so that bamboo charcoal fiber be made;
Then, frivolous layer is made by loom in the composite fibre long filament of become mildewed Down Fiber and cotton crepe fiber, then by penetrating
Luminescent material is ejected into frivolous layer surface by frequency magnetron sputtering technique, and antibacterial then is made by loom in bamboo charcoal fiber
Layer;
Then, frivolous layer is aligned with antibiotic layer, and uniformly smears antimicrobial adhesive between frivolous layer and antibiotic layer, so
Frivolous layer and antibiotic layer are put into press roller afterwards and carry out extrusion forming;
It is dried finally, fabric obtained is placed on drying frame, then the control of sunning time is wound whole in 10-15h
Reason.
As an embodiment of the present invention: choosing the cotton crepe fibre of become mildewed Down Fiber and 70 parts by weight of 30 parts by weight
Dimension, thus the composite fibre long filament of blended obtain becoming mildewed Down Fiber and cotton crepe fiber, and respectively as the warp on loom with
And weft has the advantages that soft, elasticity is high so that frivolous layer be made by interlacement weave.
As an embodiment of the present invention: choosing the cotton crepe fibre of become mildewed Down Fiber and 32 parts by weight of 68 parts by weight
Dimension, thus the composite fibre long filament of blended obtain becoming mildewed Down Fiber and cotton crepe fiber, and respectively as the warp on loom with
And weft has the advantages that good warmth retention effect so that frivolous layer be made by interlacement weave.
As an embodiment of the present invention: choosing the cotton crepe fibre of become mildewed Down Fiber and 50 parts by weight of 50 parts by weight
Dimension, thus the composite fibre long filament of blended obtain becoming mildewed Down Fiber and cotton crepe fiber, and respectively as the warp on loom with
And weft has the advantages that soft and warming so that frivolous layer be made by interlacement weave.
As an embodiment of the present invention: antibacterial softener is a kind of cationic polymer antibacterial agent, antimicrobial adhesive
For a kind of silane quaternary adhesive.
As an embodiment of the present invention: the hole diameter of spinneret 10-100um.
As an embodiment of the present invention: luminescent material is the strontium aluminate that a kind of europium and dysprosium are co-doped with.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention, for this field skill
For art personnel, it is clear that invention is not limited to the details of the above exemplary embodiments, and without departing substantially from spirit of the invention or
In the case where essential characteristic, the present invention can be realized in other specific forms.Therefore, in all respects, should all incite somebody to action
Embodiment regards exemplary as, and is non-limiting, the scope of the present invention by appended claims rather than on state
Bright restriction, it is intended that including all changes that fall within the meaning and scope of the equivalent elements of the claims in the present invention
It is interior.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (7)
1. a kind of antibacterial light and thin fabric, including frivolous layer and antibiotic layer, it is characterised in that: the frivolous layer is bonded by antibacterial
Agent is pasted and fixed on antibiotic layer upper surface, including following preparation process:
Firstly, choosing the Down Fiber that becomes mildewed, the cotton crepe fiber of 32-70 parts by weight and the bamboo charcoal of 100 parts by weight of 30-68 parts by weight
Fiber;
Then, by plush fibrous raw material at 85-100 DEG C with methyl morpholine oxide mixed dissolution, stir 15-35min, obtain
Become mildewed Down Fiber stoste;Cotton crepe fiber raw material is mixed at 90-105 DEG C with methyl morpholine oxide, mixing time 25-
Then excessive moisture is removed under reduced pressure in 65min, cotton crepe fiber stoste is made;The Down Fiber stoste that will become mildewed and cotton crepe fiber stoste
It pours into hopper and is mixed, then pour into screw extruder from hopper, at 90-125 DEG C after shearing dissolution, spinning is sent in filtering
Filament plate carries out spinning, so that become mildewed Down Fiber and cotton crepe fiber be made, the Down Fiber that then will become mildewed is mixed with cotton crepe fiber
It spins, so that the composite fibre long filament of become mildewed Down Fiber and cotton crepe fiber be made;
Then, bamboo-carbon fibre raw material is poured into immersed with impregnating in the filtrate of ganoderma lucidum and ginseng, soaking time 30-
45min, while bamboo-carbon fibre raw material is stirred, then mixing time 20-30min takes out bamboo-carbon fibre raw material, and
It is put into screw extruder and is squeezed out, spinning is then carried out by melt spinning technology, then pours into spinning containing antibacterial
The solution of softening agent is impregnated again, and then soaking time 25-35min takes out spinning, and carry out sunning 1h, then
Spinning is washed, deburring and bleaching, then carry out winder, so that bamboo charcoal fiber be made;
Then, frivolous layer is made by loom in the composite fibre long filament of become mildewed Down Fiber and cotton crepe fiber, then by penetrating
Luminescent material is ejected into frivolous layer surface by frequency magnetron sputtering technique, and antibacterial then is made by loom in bamboo charcoal fiber
Layer;
Then, frivolous layer is aligned with antibiotic layer, and uniformly smears antimicrobial adhesive between frivolous layer and antibiotic layer, so
Frivolous layer and antibiotic layer are put into press roller afterwards and carry out extrusion forming;
It is dried finally, fabric obtained is placed on drying frame, then the control of sunning time is wound whole in 10-15h
Reason.
2. a kind of antibacterial light and thin fabric according to claim 1, it is characterised in that: the plush for choosing 30 parts by weight
The cotton crepe fiber of fiber and 70 parts by weight, thus the composite fibre long filament of blended obtain becoming mildewed Down Fiber and cotton crepe fiber, and
Respectively as the warp and weft on loom, so that frivolous layer be made by interlacement weave, there is high excellent of soft, elasticity
Point.
3. a kind of antibacterial light and thin fabric according to claim 1, it is characterised in that: the plush for choosing 68 parts by weight
The cotton crepe fiber of fiber and 32 parts by weight, thus the composite fibre long filament of blended obtain becoming mildewed Down Fiber and cotton crepe fiber, and
Respectively as the warp and weft on loom, so that frivolous layer is made by interlacement weave, it is excellent with good warmth retention effect
Point.
4. a kind of antibacterial light and thin fabric according to claim 1, it is characterised in that: the plush for choosing 50 parts by weight
The cotton crepe fiber of fiber and 50 parts by weight, thus the composite fibre long filament of blended obtain becoming mildewed Down Fiber and cotton crepe fiber, and
Respectively as the warp and weft on loom, so that frivolous layer be made by interlacement weave, have soft and warming
Advantage.
5. a kind of antibacterial light and thin fabric according to claim 1, it is characterised in that: the antibacterial softener be it is a kind of sun from
Sub- polymer antibacterial agent, the antimicrobial adhesive are a kind of silane quaternary adhesive.
6. a kind of antibacterial light and thin fabric according to claim 1, it is characterised in that: the hole diameter of spinneret is 10-
100um。
7. a kind of antibacterial light and thin fabric according to claim 1, it is characterised in that: the luminescent material is a kind of europium and dysprosium
The strontium aluminate being co-doped with.