CN109372026A - 一种绿化带地下工程顶板的组合防水层构造及其施工方法 - Google Patents
一种绿化带地下工程顶板的组合防水层构造及其施工方法 Download PDFInfo
- Publication number
- CN109372026A CN109372026A CN201811331349.8A CN201811331349A CN109372026A CN 109372026 A CN109372026 A CN 109372026A CN 201811331349 A CN201811331349 A CN 201811331349A CN 109372026 A CN109372026 A CN 109372026A
- Authority
- CN
- China
- Prior art keywords
- layer
- waterproof
- construction
- underground engineering
- coiled material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种绿化带地下工程顶板的组合防水层构造,由内向外依次包括:地下工程顶板结构层、防水涂料层、防水卷材层以及保护层;地下工程顶板结构层为振捣密实的浇筑层;防水涂料层为非固化橡胶沥青防水涂料层;防水卷材层为自粘聚酯胎改性沥青化学耐根穿刺防水卷材层;保护层为细石混凝土保护层;本发明还包括上述组合防水层构造的施工方法。本发明利用新型防水材料,设计了两道防水层,结合两种防水材料特有的技术性能和防水应用特点,既修补了建筑内细微的结构裂缝,也解决了传统单一的SBS卷材窜水的问题;不仅构造简单,施工工序简易,重要的是防水效果非常好。
Description
技术领域
本发明属于建筑技术领域,特别涉及一种绿化带地下工程顶板的组合防水层构造及其施工方法。
背景技术
随着建筑的发展,建筑功能不断完善,而且随着对绿化要求的提高,地下结构顶板种植绿化也越来越普遍,如何提高地下室顶板防水的施工质量是研究的关键,防水构造要在技术可行、工艺可靠、保证质量的情况下改善实际问题。
发明内容
技术问题:为了解决现有技术的缺陷,本发明提供了一种绿化带地下工程顶板的组合防水层构造及其施工方法。
技术方案:本发明提供的一种绿化带地下工程顶板的组合防水层构造,其特征在于:由内向外依次包括以下结构:地下工程顶板结构层、防水涂料层、防水卷材层以及保护层;
地下工程顶板结构层为振捣密实的浇筑层;
防水涂料层为非固化橡胶沥青防水涂料层;
防水卷材层为自粘聚酯胎改性沥青化学耐根穿刺防水卷材层;
保护层为细石混凝土保护层。
作为一种优化方案:地下工程顶板结构层平立面交接处的阴阳角为均匀一致、平整光滑的圆角,且圆弧半径不小于50mm。
作为进一步优化方案:防水涂料层厚度为2mm。
作为进一步优化方案:防水卷材层的卷材搭接缝部位溢出热熔沥青宽度为5-8mm,卷材长边搭接宽度为100mm,短边搭接宽度为100mm。
作为进一步优化方案:保护层厚度为50mm。
本发明还包括上述组合防水层构造的施工方法,包括以下步骤:
步骤1:浇筑地下工程顶板,将其振捣密实,且压实收光抹平,地下工程顶板结构层施工结束;
步骤2:将非固化橡胶沥青防水涂料用专用脱桶机脱桶后倒至胶溶机内,待温度达到180°-220°之间后放出,一次成型的均匀涂刮在上述步骤1制成的地下工程顶板结构层上,防水涂料层施工结束;
步骤3:在防水涂料层施工完成后5分钟内进行防水卷材层施工,将卷材粘结在冷却前的非固化橡胶沥青上,防水卷材层施工结束;
步骤4:在上述步骤3施工结束的防水涂料层上铺设细石混凝土,然后整平,细石混凝土铺设保护层施工结束。
作为一种优化方案:步骤1具体施工步骤为:对地下工程顶板结构基层进行平整、清洁和干燥处理,用水泥砂浆进行找平,平立面交接处的阴阳角均做成均匀一致、平整光滑的圆角,且该圆角的圆弧半径不小于50mm,铲除突出基层表面的尖锐硬物,并将尘土杂物清除干净,阴阳角和管根部清理两次,用砂纸和钢丝刷清除干净;阴阳角和变形缝,采用涂刷法施工,分遍涂刷,胎体增强材料夹铺在涂层中间,铺实粘牢,不空鼓、不翘边。
作为进一步优化方案:步骤2具体施工步骤为:非固化橡胶沥青防水涂料用专用脱桶机脱桶后倒至胶溶机内,待温度达到180°-220°之间后放出,均匀涂刮在基层上,涂刮时应均匀一致,防水层一次成型,厚度为2mm,喷涂完50%面积后采用针测法检测涂层厚度,如厚度不达标或局部需要强化,则用橡胶刮板取涂料进行局部重复涂刮。
作为进一步优化方案:步骤3具体施工步骤为:在防水涂料层施工完成后5分钟内进行防水卷材层施工,且卷材跟贴,空置距离不大于6m;铺贴卷材从一边按住,均匀向前铺贴,刮平;相邻卷材搭接缝采用本体预留搭接边自熔融沥青粘结,操作人员手持小压辊,由内向外以垂直于卷材长边方向边压实边移动,搭接缝部位以溢出热熔沥青为度,溢出宽度5-8mm,且均匀顺直,卷材长边搭接宽度为100mm,短边搭接宽度为100mm,搭接缝采用热熔施工,卷材整体铺贴完毕后,对卷材表观质量、搭接质量和局部节点处理进行检查,修补质量缺陷。
作为进一步优化方案:步骤4具体施工步骤为:保护层采用50mm厚细石混凝土铺设,浇筑时振捣密实,整平使保护层平整度误差为5mm。
有益效果:本发明利用新型防水材料,设计了两道防水层,结合两种防水材料特有的技术性能和防水应用特点,既修补了建筑内细微的结构裂缝,也解决了传统单一的SBS卷材窜水的问题;不仅构造简单,施工工序简易,重要的是防水效果非常好。
附图说明
图1为本发明一种绿化带地下工程顶板的组合防水层构造的结构示意图;
附图标记:1-地下工程顶板结构层,2-防水涂料层,3-防水卷材层,4-保护层。
具体实施方式
下面结合附图和具体实施例,进一步阐明本发明,应理解这些实施例仅用于说明本发明而不用于限制本发明的范围,在阅读了本发明之后,本领域技术人员对本发明的各种等价形式的修改均落于本申请所附权利要求所限定的范围。
本发明提供的一种绿化带地下工程顶板的组合防水层构造,由内向外依次包括以下结构:地下工程顶板结构层1、防水涂料层2、防水卷材层3以及保护层4;
地下工程顶板结构层1为振捣密实的浇筑层;防水涂料层2为非固化橡胶沥青防水涂料层;防水卷材层3为自粘聚酯胎改性沥青化学耐根穿刺防水卷材层;保护层4为细石混凝土保护层。
上述组合防水层构造的施工方法,包括以下步骤:
步骤1:对地下工程顶板结构基层处理、细部加强处理,基层表面应平整、清洁、干燥,基层满足平整一致的坡度,不得有集水的局部低凹处,低凹处应用水泥砂浆进行找平处理,平立面交接处的阴阳角均应做成均匀一致、平整光滑的圆角,圆弧半径不小于50mm,突出基层表面的尖锐硬物、砂浆疙瘩等铲除,并将尘土杂物清除干净,阴阳角、管根部等处更应仔细清理,若有不同污渍、铁锈等,应以砂纸、钢丝刷或者溶剂清除干净;阴阳角、变形缝等部位,采用涂刷法施工,分遍涂刷,胎体增强材料应夹铺在涂层中间,铺实粘牢,不空鼓、不翘边。
步骤2:非固化橡胶沥青防水涂料用专用脱桶机脱桶后倒至胶溶机内,待温度达到180°-220°之间后放出,均匀涂刮在基层上,涂刮时应均匀一致,防水层一次成型,厚度为2mm,切勿反复涂刮,喷涂完一定面积后采用针测法检测涂层厚度,如厚度不达标或局部需要强化,则取一些涂料,用橡胶刮板进行局部加强。
步骤3:防水卷材层3施工应在防水涂料层2施工完成后5分钟内进行施工,且卷材应跟贴,空置距离不大于6m;铺贴卷材从一头按住,均匀向前铺贴,刮平;相邻卷材搭接缝应采用本体预留搭接边自熔融沥青粘结,操作人员手持小压辊,由内向外以垂直于卷材长边方向边压实边移动,搭接缝部位宜以溢出热熔沥青为度,溢出宽度5-8mm,且应均匀顺直,卷材长边搭接宽度为100mm,短边搭接宽度为100mm,搭接缝采用热熔施工,卷材整体铺贴完毕后,应对卷材表观质量、搭接质量、局部节点处理等项目进行检查,如发现有质量缺陷,立即修补。
步骤4:保护层4采用50mm厚细石混凝土铺设,浇筑时振捣密实,整平使保护层4平整度符合要求,平整度误差为5mm。
本发明采用两种新型防水材料,结合其特有的技术性能和防水应用特点,非固化橡胶沥青防水涂料是一种非固化、不成膜的新型防水材料,其与改性沥青化学耐根穿刺防水卷材可以结合在一起,既可以修补建筑内部细微的结构裂缝,也能解决传统单一的SBS卷材窜水的问题,结构顶板上基层处理后直接进行防水层施工,不仅构造简单,施工工序简易,最重要是防水效果非常好。
Claims (10)
1.一种绿化带地下工程顶板的组合防水层构造,其特征在于:由内向外依次包括以下结构:地下工程顶板结构层、防水涂料层、防水卷材层以及保护层;
所述地下工程顶板结构层为振捣密实的浇筑层;
所述防水涂料层为非固化橡胶沥青防水涂料层;
所述防水卷材层为自粘聚酯胎改性沥青化学耐根穿刺防水卷材层;
所述保护层为细石混凝土保护层。
2.根据权利要求1所述的组合防水层构造,其特征在于:所述地下工程顶板结构层平立面交接处的阴阳角为均匀一致、平整光滑的圆角,且圆弧半径不小于50mm。
3.根据权利要求1所述的组合防水层构造,其特征在于:所述防水涂料层厚度为2mm。
4.根据权利要求1所述的组合防水层构造,其特征在于:所述防水卷材层的卷材搭接缝部位溢出热熔沥青宽度为5-8mm,卷材长边搭接宽度为100mm,短边搭接宽度为100mm。
5.根据权利要求1所述的组合防水层构造,其特征在于:所述保护层厚度为50mm。
6.上述任一权利要求所述的组合防水层构造的施工方法,其特征在于:包括以下步骤:
步骤1:浇筑地下工程顶板,将其振捣密实,且压实收光抹平,地下工程顶板结构层施工结束;
步骤2:将非固化橡胶沥青防水涂料用专用脱桶机脱桶后倒至胶溶机内,待温度达到180°-220°之间后放出,一次成型的均匀涂刮在上述步骤1制成的地下工程顶板结构层上,防水涂料层施工结束;
步骤3:在防水涂料层施工完成后5分钟内进行防水卷材层施工,将卷材粘结在冷却前的非固化橡胶沥青上,防水卷材层施工结束;
步骤4:在上述步骤3施工结束的防水涂料层上铺设细石混凝土,然后整平,细石混凝土铺设保护层施工结束。
7.根据权利要求6所述的施工方法,其特征在于:所述步骤1具体施工步骤为:对地下工程顶板结构基层进行平整、清洁和干燥处理,用水泥砂浆进行找平,平立面交接处的阴阳角均做成均匀一致、平整光滑的圆角,且该圆角的圆弧半径不小于50mm,铲除突出基层表面的尖锐硬物,并将尘土杂物清除干净,阴阳角和管根部清理两次,用砂纸和钢丝刷清除干净;阴阳角和变形缝,采用涂刷法施工,分遍涂刷,胎体增强材料夹铺在涂层中间,铺实粘牢,不空鼓、不翘边。
8.根据权利要求6所述的施工方法,其特征在于:所述步骤2具体施工步骤为:非固化橡胶沥青防水涂料用专用脱桶机脱桶后倒至胶溶机内,待温度达到180°-220°之间后放出,均匀涂刮在基层上,涂刮时应均匀一致,防水层一次成型,厚度为2mm,喷涂完50%面积后采用针测法检测涂层厚度,如厚度不达标或局部需要强化,则用橡胶刮板取涂料进行局部重复涂刮。
9.根据权利要求6所述的施工方法,其特征在于:所述步骤3具体施工步骤为:在防水涂料层施工完成后5分钟内进行防水卷材层施工,且卷材跟贴,空置距离不大于6m;铺贴卷材从一边按住,均匀向前铺贴,刮平;相邻卷材搭接缝采用本体预留搭接边自熔融沥青粘结,操作人员手持小压辊,由内向外以垂直于卷材长边方向边压实边移动,搭接缝部位以溢出热熔沥青为度,溢出宽度5-8mm,且均匀顺直,卷材长边搭接宽度为100mm,短边搭接宽度为100mm,搭接缝采用热熔施工,卷材整体铺贴完毕后,对卷材表观质量、搭接质量和局部节点处理进行检查,修补质量缺陷。
10.根据权利要求6所述的施工方法,其特征在于:所述步骤4具体施工步骤为:保护层采用50mm厚细石混凝土铺设,浇筑时振捣密实,整平使保护层平整度误差为5mm。