CN109353090A - A kind of multiple-hearth single side material - Google Patents

A kind of multiple-hearth single side material Download PDF

Info

Publication number
CN109353090A
CN109353090A CN201811409998.5A CN201811409998A CN109353090A CN 109353090 A CN109353090 A CN 109353090A CN 201811409998 A CN201811409998 A CN 201811409998A CN 109353090 A CN109353090 A CN 109353090A
Authority
CN
China
Prior art keywords
layer
fabric
base fabric
single side
water barrier
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811409998.5A
Other languages
Chinese (zh)
Inventor
盛明英
周桂明
钱欢欢
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Gaoyan Textile Technology Co Ltd
Original Assignee
Suzhou Gaoyan Textile Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Gaoyan Textile Technology Co Ltd filed Critical Suzhou Gaoyan Textile Technology Co Ltd
Priority to CN201811409998.5A priority Critical patent/CN109353090A/en
Publication of CN109353090A publication Critical patent/CN109353090A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of multiple-hearth single side material, including Base fabric, lead wet antibiotic layer, film water barrier, enhancement layer and felt bottom；The felt bottom, enhancement layer, film water barrier, lead wet antibiotic layer, Base fabric is cascading from inner layer to surface layer direction；The Base fabric is high-count and high-density woven fabric；It is described to lead wet antibiotic layer as polypropylene fibre woven fabric；The polypropylene fibre woven fabric, as warp thread and weft yarn, is woven by polypropylene fiber yarn using plain weave construction；The Base fabric and polypropylene fibre woven fabric carry out stacking composite joint by yarn stitched；The film water barrier is micropore waterproofing membrane；The enhancement layer is terylene four-side elasticity fabric；The felt bottom is wool felt-cloth.The unidirectional penetrability of the present invention is good, and moisture absorbing and sweat releasing performance is good, and bacteria can be prevented from growing, and antibacterial deodourizing performance is good, and wearability is good, and elasticity is good, and using effect is good.

Description

A kind of multiple-hearth single side material
Technical field
The present invention relates to field of textile, in particular to a kind of multiple-hearth single side material.
Background technique
Currently, textile fabric has become the ordinary articles in people's daily life, fabric on the market is mostly Single layer structure, for example, being made of cotton and polyester fiber material, these fabrics all have certain defect, for example, cotton products Hydrofuge performance is not so good as people's will, and the warming absorbing sweat performance of polyester fiber is poor.The fabric of single structure has been difficult to meet the need of people It asks.Such as sheet fabric, existing sheet fabric is based on single layer pure-cotton fabric or cotton ramie blended spinning fabric, soft although skin-friendly is good It is soft comfortable, but anti-microbial property is poor, moisture absorbing and sweat releasing performance is poor, and moisture easily penetrates sheet, so that mattress is bred bacterium or acarid, even Mouldy, while wrinkle resistance is poor, stiffness is poor, easily slides, can not be smooth be covered on bed surface.
Summary of the invention
It is made up in order to solve the above technical problems, the present invention provides a kind of multiple-hearth single side material using multi-layer compound structure The deficiency of single layer structure sheet solves existing sheet fabric comprehensive performance by the coordinated between different function layer Difference, anti-microbial property is poor, and moisture absorbing and sweat releasing performance is poor, and moisture easily penetrates sheet, so that mattress is bred bacterium or acarid or even mouldy, together When wrinkle resistance it is poor, stiffness is poor, easily slides, the problem being covered on bed surface that can not be smooth.
In order to achieve the above objectives, technical scheme is as follows: a kind of multiple-hearth single side material, including Base fabric, leads Wet antibiotic layer, film water barrier, enhancement layer and felt bottom；The felt bottom, film water barrier, leads wet antibacterial at enhancement layer Layer, Base fabric are cascading from inner layer to surface layer direction；The Base fabric is high-count and high-density woven fabric；It is described to lead wet resist Bacterium layer is polypropylene fibre woven fabric；The polypropylene fibre woven fabric, as warp thread and weft yarn, is woven by polypropylene fiber yarn using plain weave construction It forms；The Base fabric and polypropylene fibre woven fabric carry out stacking composite joint by yarn stitched；The film water barrier is micropore Waterproofing membrane；The enhancement layer is terylene four-side elasticity fabric；The felt bottom is wool felt-cloth.
As a preferred solution of the present invention, the film water barrier is TPU film or PTFE film.
As a preferred solution of the present invention, the Base fabric by tencel or cotton ramie blended spinning yarn through knitting device and At；The Base fabric through it is close be 532/10cm, filling density is 397 root/10cm；The Base fabric uses 1/1 plain weave Institutional framework.
As a preferred solution of the present invention, the polypropylene fiber yarn is 8.3tex/72f.
As a preferred solution of the present invention, water repellent finishing agent coating is coated in the Base fabric.
As a preferred solution of the present invention, the felt bottom with a thickness of 0.8-2.5mm.
As a preferred solution of the present invention, it is described lead wet antibiotic layer, film water barrier, enhancement layer and felt bottom it Between by the hot pressing of micro-porous permeable hot melt adhesive adhere to.
As a preferred solution of the present invention, nanometer silver coating is coated in the film water proof layer surface；It is described to receive Rice silver coating leads wet antibiotic layer side described in being located at.
As a preferred solution of the present invention, spun lacing nonwoven is additionally provided between the film water barrier and enhancement layer Cloth；The spunlace non-woven cloth is made of bamboo pulp fibers；The spunlace non-woven cloth with a thickness of 0.12-0.36mm；The film Water barrier, spunlace non-woven cloth and enhancement layer are glued compound by hot pressing.
As a preferred solution of the present invention, it the Base fabric and leads between wet antibiotic layer through spandex fibre yarn Suture connection.
Through the above technical solutions, the beneficial effect of technical solution of the present invention is: structure of the invention is reasonable, is leading wet antibacterial Unidirectional moisture-inhibiting may be implemented in setting film water barrier between layer and enhancement layer, dry and comfortable between guarantee sheet fabric and mattress, no Bacterium is easily bred, while sheet fabric moisture absorbing and sweat releasing performance is good, polypropylene fibre is almost non-hygroscopic, but wicking capacity is stronger, wet transmitting performance Good, leading wet antibiotic layer can conduct rapidly the steam at the sheet fabric front place of perspiring, and improve disengagement area, and due to polypropylene fibre It is non-hygroscopic, it is able to maintain the pressure difference of film water barrier two sides, realizes unidirectional moisture-inhibiting, and then realize rapid steaming by leading wet antibiotic layer Hair；In addition, leading, wet antibiotic layer antibacterial deodourizing performance is good, and bad smell of perspiration does not remain, wearability is good, and elasticity is good.The present invention is additionally provided with increasing Strong layer can guarantee the tensile strength of fabric, be unlikely to deform, and felt bottom has good heat-insulation warm keeping performance, well-pressed clothes Note is good, and sheet fabric is made to be not easy fold, easily arranges, avoids sliding, using effect is good.
Detailed description of the invention
In order to more clearly explain the embodiment of the invention or the technical proposal in the existing technology, to embodiment or will show below There is attached drawing needed in technical description to be briefly described, it should be apparent that, the accompanying drawings in the following description is only this Some embodiments of invention for those of ordinary skill in the art without creative efforts, can be with It obtains other drawings based on these drawings.
Fig. 1 is the structural diagram of the present invention.
Number and corresponding component title represented by letter in figure:
1. Base fabric 2. leads wet 3. film water barrier of antibiotic layer
4. 5. felt bottom of enhancement layer.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other Embodiment shall fall within the protection scope of the present invention.
Embodiment
In conjunction with Fig. 1, the invention discloses a kind of multiple-hearth single side material, as a kind of novel home textile sheet fabric.The present invention Using laminate composite structure, including Base fabric 1, lead wet antibiotic layer 2, film water barrier 3, enhancement layer 4 and felt bottom 5.Hair Felt bottom 5, enhancement layer 4, film water barrier 3, lead wet antibiotic layer 2, Base fabric 1 is stacked gradually from inner layer to surface layer direction and is set It sets.Base fabric 1 is high-count and high-density woven fabric.Leading wet antibiotic layer 2 is polypropylene fibre woven fabric.Polypropylene fibre woven fabric is by polypropylene fiber yarn as warp Yarn and weft yarn, are woven using plain weave construction.Base fabric 1 and polypropylene fibre woven fabric by it is yarn stitched be laminated it is compound Connection.Preferably, it Base fabric 1 and leads between wet antibiotic layer 2 through the yarn stitched connection of spandex fibre, has that intensity is high, bullet Good, the good advantage of wet guilding of property.Film water barrier 3 is micropore waterproofing membrane.Preferably, film water barrier 3 be TPU film or PTFE film.Enhancement layer 4 is terylene four-side elasticity fabric.Felt bottom 5 is wool felt-cloth.The thickness of felt bottom 5 can be 0.8-2.5mm.Specifically, leading between wet antibiotic layer 2, film water barrier 3, enhancement layer 4 and felt bottom 5 through micro-porous permeable heat Melten gel hot pressing adherency.
In order to guarantee that the comfort of fabric, Base fabric 1 are preferably formed by tencel or cotton ramie blended spinning yarn through knitting device.Together When, Base fabric 1 can control through close in 532/10cm, and filling density can control in 397 root/10cm.Base fabric 1 is adopted With 1/1 plain weave construction, surfacing, sense of touch is comfortable, good permeability.
In the present invention, polypropylene fiber yarn is 8.3tex/72f, can by wicking using ultra-fine polypropylene fiber silk Guarantee wet transmitting performance well.
In order to reduce surface tension, the water repellency of sheet fabric is improved, is applied in Base fabric 1 coated with water repellent finishing agent Layer.
In order to improve the anti-microbial property of sheet fabric, nanometer silver coating is coated on 3 surface of film water barrier；Nano silver applies Layer, which is located at, leads wet 2 side of antibiotic layer.
In order to improve the anti-microbial property of felt bottom 5, be additionally provided between film water barrier 3 and enhancement layer 4 spun lacing without Woven fabric.Spunlace non-woven cloth is made of bamboo pulp fibers.Spunlace non-woven cloth with a thickness of 0.12-0.36mm.Film water barrier 3, water Prick nonwoven cloth and enhancement layer 4 are glued compound by hot pressing.
By above-mentioned specific embodiment, the beneficial effects of the present invention are: structure of the invention is reasonable, wet 2 He of antibiotic layer is being led Film water barrier 3 is arranged between enhancement layer 4 may be implemented unidirectional moisture-inhibiting, dry and comfortable between guarantee sheet fabric and mattress, be not easy Bacterium being bred, while sheet fabric moisture absorbing and sweat releasing performance is good, polypropylene fibre is almost non-hygroscopic, but wicking capacity is stronger, and wet transmitting performance is good, Leading wet antibiotic layer 2 can conduct rapidly the steam at the sheet fabric front place of perspiring, and improve disengagement area, and not due to polypropylene fibre Moisture absorption is able to maintain the pressure difference of 3 two sides of film water barrier, realizes unidirectional moisture-inhibiting, and then realize rapid steaming by leading wet antibiotic layer 2 Hair；In addition, leading, wet 2 antibacterial deodourizing performance of antibiotic layer is good, and bad smell of perspiration does not remain, wearability is good, and elasticity is good.The present invention is additionally provided with increasing Strong layer 4, can guarantee the tensile strength of fabric, be unlikely to deform, and felt bottom 5 has good heat-insulation warm keeping performance, well-pressed Docile property is good, and sheet fabric is made to be not easy fold, easily arranges, avoids sliding, using effect is good.
The foregoing description of the disclosed embodiments enables those skilled in the art to implement or use the present invention. Various modifications to these embodiments will be readily apparent to those skilled in the art, as defined herein General Principle can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore, of the invention It is not intended to be limited to the embodiments shown herein, and is to fit to and the principles and novel features disclosed herein phase one The widest scope of cause.

Claims (10)

1. a kind of multiple-hearth single side material, which is characterized in that including Base fabric, lead wet antibiotic layer, film water barrier, enhancement layer and Felt bottom；The felt bottom, enhancement layer, film water barrier, lead wet antibiotic layer, Base fabric from inner layer to surface layer direction according to It is secondary to be stacked；The Base fabric is high-count and high-density woven fabric；It is described to lead wet antibiotic layer as polypropylene fibre woven fabric；The polypropylene fibre woven fabric by Polypropylene fiber yarn is woven as warp thread and weft yarn using plain weave construction；The Base fabric and polypropylene fibre woven fabric are logical It crosses and yarn stitched carries out stacking composite joint；The film water barrier is micropore waterproofing membrane；The enhancement layer is terylene four sides Elasticity fabric；The felt bottom is wool felt-cloth.
2. multiple-hearth single side material according to claim 1, which is characterized in that the film water barrier be TPU film or PTFE film.
3. multiple-hearth single side material according to claim 1, which is characterized in that the Base fabric is by tencel or cotton ramie blended spinning Yarn is formed through knitting device；The Base fabric through it is close be 532/10cm, filling density is 397 root/10cm；The fabric base Cloth uses 1/1 plain weave construction.
4. multiple-hearth single side material according to claim 3, which is characterized in that the polypropylene fiber yarn is 8.3tex/ 72f。
5. multiple-hearth single side material according to claim 4, which is characterized in that be coated with water repellent finish in the Base fabric Agent coating.
6. multiple-hearth single side material according to claim 4, which is characterized in that the felt bottom with a thickness of 0.8- 2.5mm。
7. multiple-hearth single side material according to claim 6, which is characterized in that described to lead wet antibiotic layer, film water barrier, increase It is adhered between strong layer and felt bottom by the hot pressing of micro-porous permeable hot melt adhesive.
8. multiple-hearth single side material according to claim 7, which is characterized in that be coated with and receive in the film water proof layer surface Rice silver coating；The nanometer silver coating leads wet antibiotic layer side described in being located at.
9. multiple-hearth single side material according to claim 7, which is characterized in that between the film water barrier and enhancement layer It is additionally provided with spunlace non-woven cloth；The spunlace non-woven cloth is made of bamboo pulp fibers；The spunlace non-woven cloth with a thickness of 0.12- 0.36mm；The film water barrier, spunlace non-woven cloth and enhancement layer are glued compound by hot pressing.
10. multiple-hearth single side material according to claim 7, which is characterized in that the Base fabric and lead wet antibiotic layer it Between pass through the yarn stitched connection of spandex fibre.
CN201811409998.5A 2018-11-23 2018-11-23 A kind of multiple-hearth single side material Pending CN109353090A (en)