CN109321986A - A kind of waterproof haze composite material and preparation method and application - Google Patents
A kind of waterproof haze composite material and preparation method and application Download PDFInfo
- Publication number
- CN109321986A CN109321986A CN201810966597.3A CN201810966597A CN109321986A CN 109321986 A CN109321986 A CN 109321986A CN 201810966597 A CN201810966597 A CN 201810966597A CN 109321986 A CN109321986 A CN 109321986A
- Authority
- CN
- China
- Prior art keywords
- waterproof
- layer
- filter layer
- composite material
- haze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to electrostatic spinning technique fields, disclose a kind of waterproof haze composite material and preparation method and application, the composite material includes filter layer and waterproof layer, the waterproof layer includes waterproof coating A and waterproof coating B, the filter layer forms waterproof layer A/ filter layer/waterproof layer B multilayered structure between waterproof layer A and waterproof layer B;Wherein, the filter layer makees solvent with organic solvent or water, obtains macromolecule polymer solution, be made through electrostatic spinning using high molecular polymer as raw material;The waterproof layer and filter layer suppress compound or are applied directly to filter layer and are made.Waterproof coating has both waterproof and two kinds of characteristics of breathing freely, and can reduce indoor humidity, keeps indoor salubrious, and haze effect and service life can be improved.
Description
Technical field
The invention belongs to electrostatic spinning technique fields, more particularly, to a kind of waterproof haze composite material and preparation
Methods and applications.
Background technique
What the aerosol systems of the particulate matters such as dust, sulfate, nitrate in air composition caused dysopia is haze.
When condensation vapor aggravation, air humidity increase, haze will be converted into mist.The difference of haze and mist is to occur relative humidity when haze
Less, the relative humidity and in mist is very big.Haze weather is a kind of atmosphere pollution state, and haze is to suspensions various in atmosphere
The exceeded general statement of grain object content, especially PM2.5 (equivalent aerodynamic diameter is less than or equal to 2.5 microns of particulate matter,
Also become lung particulate matter, Chinese title is fine particle) it is considered as causing haze weather " arch-criminal ".
The whole nation especially Middle Eastern pollution is very serious, and primary pollutant is PM2.5, and partial size is small, opposite specific surface
Product is big, and chemical activity and adsorption capacity are strong, poisonous and harmful substances such as easy CO absorption, oxynitrides, carcinogen and in atmosphere
The middle residence time is long, conveying distance is remote, bronchus and lung is easily inhaled into and is deposited on, to cause respiratory system, angiocarpy
The diseases such as system, severely impact the health of people, or even will increase the risk of sudden death.
Close implementation: 1.CN201220664009- high water repellent filter paper-utility model, the inventive principle is close, function
Energy purposes has difference.The utility model discloses a kind of high water repellent filter paper, is mainly used for solving the problems, such as that air filter paper is moisture-proof,
Including filter layer and waterproof coating, the single side of filter layer or it is two-sided be coated with the waterproof coating, waterproof coating has good
Gas has both achieved the effect that waterproof after excessive influence, the program will not be caused to implement to the filtration resistance of filter layer, right
The performance indexes influence of filter layer is smaller, is very suitable in the filtering environment required to humidity.
2.CN201710965652- a kind of composite nano fiber haze screen window and preparation method thereof-application is open, the invention function phase
Closely, principle has difference.The invention discloses a kind of composite nano fiber haze screen window and preparation method thereof, haze screen window packets
Include screen window base, nanofiber film layer and nonwoven layer;Nanofiber film layer is deposited on nonwoven fabric surface and constitutes composite layer,
The screen window is prepared by screen window base and composite layer by the way that hot pressing is compound.The advantages of invention, is: by non-woven
Depositing nanofibers film layer realizes haze on layer of cloth, then improves the mechanics of entire screen window by screen window base in hot pressing
Intensity.
As air pollution is increasingly severe, occur a variety of haze products in the market, for example, air purifier etc.,
Air purifier only purify the air of a room except haze to reach to indoor air in the case where door and window is completely closed
Effect still closes the doors and windows for a long time so that air can not circulate, causes the consequence of indoor anoxic, door and window can make again
The effect of air purifier is had a greatly reduced quality, and air purifier can not fundamentally carry out except haze, only the air entered the room
It can respite.
Haze is removed in order to carry out purification to the air entered the room, occurs a variety of haze windows at present, it can be in a steady stream
It constantly enters indoor air and carries out purification except haze, so that the air entered the room is purified air, however, existing skill
The filter layer material waterproofing of haze window screening in art is poor, in the biggish area of some humidity, environment, in season, filtering
Layer it is affected by environment, it is easy to fail, damage, influence the service life of filter, using filter effect after the short time it is rapid under
Drop.Meanwhile in rainy season or the biggish place of humidity, such haze window screening can not prevent steam from entering the room, can not reduce room
Interior humidity.Therefore, it is necessary to design a kind of novel significantly more efficient waterproof haze material, in the haze for guaranteeing former filter layer
While effect, water-proof function is provided, is avoided in the biggish area of some humidity, environment, in season, haze filter layer is by ring
Border influences, and then improves haze effect and service life.
Summary of the invention
In order to solve above-mentioned the shortcomings of the prior art and disadvantage, a kind of waterproof haze composite material is provided.This is multiple
Condensation material not only can effectively waterproof haze waterproof, moreover it is possible to reduce indoor humidity, keep indoor salubrious.
Another object of the present invention is to provide the preparation methods of above-mentioned waterproof haze composite material.
A further object of the present invention is to provide the applications of above-mentioned waterproof haze composite material.
The purpose of the present invention is realized by following technical proposals:
A kind of composite material of waterproof haze, the composite material include filter layer and waterproof layer, the waterproof layer packet
Waterproof coating A and waterproof coating B are included, the filter layer is between waterproof layer A and waterproof layer B, formation waterproof layer A/ filter layer/anti-
The multilayered structure of water layer B;Wherein, the filter layer makees solvent using high molecular polymer as raw material with organic solvent or distilled water,
Macromolecule polymer solution is obtained, is made through electrostatic spinning;The waterproof layer and filter layer carry out suppressing compound or direct painting
Filter layer is spread on to be made.
Preferably, the high molecular polymer be polyamide, polyurethane, cellulose acetate, polyacrylonitrile or polyvinyl alcohol,
The waterproof layer is acrylic acid glue.
Preferably, the thickness with a thickness of 500~600nm, the waterproof coating A and waterproof coating B of the filter layer is equal
For 0.1~1mm.
Preferably, the mass concentration of the macromolecule polymer solution is 10~20wt%.
Preferably, the organic solvent is in ethyl alcohol, dimethyl acetamide (DMAC) or n,N-Dimethylformamide (DMF)
More than one.
Preferably, the partial size of high molecular polymerization composition granule is 100~200nm in the filter layer.
10. the preparation method of the composite material of waterproof haze according to claim 1-4, feature exist
In comprising the following specific steps that:
S1. macromolecule polymer solution is put into syringe, syringe needle connects high voltage, and reception device connects low-voltage, macromolecule
Polymer solution flow is controlled by syringe pump;
S2. taylor cone is formed at syringe needle, macromolecule polymer solution overcomes surface tension to form height under electric field force effect
Molecule aggregation fibres, high polymer fiber are collected on the nonwoven layer of movement, are deposited in non-woven cloth layer surface
High molecular polymer layers of nanofibers forms filter layer;
S3. acrylic acid glue is coated to form waterproof layer, then waterproof layer with filter layer suppress it is compound, or directly
Coated on filter layer, waterproof haze composite material is made.
Preferably, the voltage value of high voltage described in step S1 is 10~20KV, the voltage value of the low-voltage is -1~-
3KV。
Preferably, flow described in step S1 is 0.1~1ml/h.
Application of the composite material of the waterproof haze in air purification field.
Compared with prior art, the invention has the following advantages:
1. filter layer is since it uses electrostatic spinning process to manufacture in waterproof haze composite material of the invention, fiber
Characteristic minimum with gap itself, can prevent bulky grain from passing through, it is ensured that the haze effect of filter layer, while providing anti-
Water function.
2. waterproof coating has both waterproof and two kinds of characteristics of breathing freely in waterproof haze composite material of the invention, room can be reduced
Interior humidity keeps indoor salubrious, and haze effect and service life can be improved.
Detailed description of the invention
Fig. 1 is the structural schematic diagram of waterproof haze composite material of the present invention.
Specific embodiment
The contents of the present invention are further illustrated combined with specific embodiments below, but should not be construed as limiting the invention.
Unless otherwise specified, the conventional means that technological means used in embodiment is well known to those skilled in the art.Except non-specifically
Illustrate, reagent that the present invention uses, method and apparatus is the art conventional reagents, method and apparatus.
Embodiment 1
Fig. 1 is the structural schematic diagram of waterproof haze composite material of the present invention.Waterproof haze composite material includes filtering
Layer and waterproof layer.Waterproof layer includes waterproof coating 1 and waterproof coating 3, the filter layer 2 between waterproof layer 1 and waterproof layer 2,
Form the multilayered structure of 1/ filter layer of waterproof layer, 2/ waterproof layer 3.
1. polyvinyl alcohol filter layer uses electrostatic spinning process:
(1) polyvinyl alcohol (PVA) aqueous solution that mass concentration is 15wt% is put into syringe, syringe needle connects high voltage, electricity
Pressure value is 10KV, and reception device connects low-voltage, and the flow of voltage value -3KV, PVA solution are 0.1ml/h, are controlled by syringe pump.
(2) taylor cone is formed at syringe needle, poly-vinyl alcohol solution overcomes surface tension to form polyethylene under electric field force effect
Alcohol fiber, vinal is collected on the nonwoven layer of movement, with electrostatic spinning process weaving fiber non-woven
The layers of nanofibers of cloth layer surface deposited polyethylene alcohol forms filter layer, and the average grain diameter of granule of polyvinyl alcohol is in filter layer
100~200nm, filter layer with a thickness of 500nm.
2. polyacrylic water-proof vapor-permeable type is independently prepared at waterproof layer, with a thickness of 0.1mm, then suppress with filter layer and answer
It closes, obtains acrylic acid/polyvinyl alcohol/acrylic composite of waterproof haze.
Embodiment 2
1. polyethylene nitrile filter layer uses electrostatic spinning process:
(1) the DMAC/DMF solution for the polyethylene nitrile (PAN) that mass concentration is 10wt% is put into syringe, syringe needle connects height
Voltage, voltage value 20KV, reception device connect low-voltage, and voltage value -1KV, PAN liquid inventory 1ml/h is controlled by syringe pump.
(2) taylor cone is formed at syringe needle, polyethylene nitrile solution overcomes surface tension to form polyethylene under electric field force effect
Nitrile fiber, polyethylene nitrile fiber is collected on the nonwoven layer of movement, with electrostatic spinning process weaving fiber non-woven
Cloth layer surface deposited polyethylene nitrile nanofibre layer forms filter layer, and the average grain diameter of polyethylene nitrile particle is 100 in filter layer
~200nm, filter layer with a thickness of 600nm.
2. waterproof material polyacrylic water-proof vapor-permeable type glue, which is directly coated on filter layer two sides, forms waterproof coating, thickness
For 1mm, acrylic acid/polyethylene nitrile/acrylic composite of waterproof haze is obtained.
Embodiment 3
1. polyurethane filter layer uses electrostatic spinning process:
(1) DMF solution for the polyurethane (TPU) that mass concentration is 20wt% is put into syringe, syringe needle connects high voltage, electricity
Pressure value is 15KV, and reception device connects low-voltage, and voltage value is -2KV, and the DMF solution flow of polyurethane is 0.5ml/h, by injecting
Pump control.
(2) taylor cone is formed at syringe needle, it is fine that polyurethane solutions overcome surface tension to form polyurethane under electric field force effect
Dimension, polyurethane fiber is collected on the nonwoven layer of movement, with electrostatic spinning process weaving fiber in nonwoven layer table
Face depositing polyurethane layers of nanofibers forms filter layer, and the average grain diameter of polyurethane particles is 100~200nm, mistake in filter layer
Filtering layer with a thickness of 550nm.
2. waterproof material polyacrylic water-proof vapor-permeable type glue, which is directly coated on filter layer two sides, forms waterproof coating, thickness
For 0.5mm, acrylic/polyurethane/acrylic composite of waterproof haze is obtained.
Embodiment 4
1. polyethylene glycol oxide filter layer uses electrostatic spinning process:
(1) ethyl alcohol (90% ethyl alcohol) solution for the polyethylene glycol oxide (PEO) that mass concentration is 15wt% is put into syringe,
Syringe needle connects high voltage, voltage value 20KV, and reception device connects low-voltage, and voltage value is -3KV, and polyethylene oxide solutions flow is
1ml/h is controlled by syringe pump.
(2) taylor cone is formed at syringe needle, polyethylene oxide solutions overcome surface tension to form polyoxy under electric field force effect
Change vinyl fiber, polyethylene glycol oxide fiber is collected on the nonwoven layer of movement, exists with electrostatic spinning process weaving fiber
Non-woven cloth layer surface deposits polyethylene glycol oxide layers of nanofibers, and the average grain diameter of polyethylene glycol oxide particle is 100 in filter layer
~200nm, the formation filter layer of filter layer, with a thickness of 600nm.
2. waterproof material polyacrylic water-proof vapor-permeable type glue, which is directly coated on filter layer two sides, forms waterproof coating, thickness
For 1mm, acrylic acid/polyethylene glycol oxide/acrylic composite of waterproof haze is obtained.
The above embodiment is a preferred embodiment of the present invention, but embodiments of the present invention are not by above-described embodiment
Limitation, it is other it is any without departing from the spirit and principles of the present invention made by change, modification, substitution, combination and simplify,
It should be equivalent substitute mode, be included within the scope of the present invention.
Claims (10)
1. a kind of composite material of waterproof haze, which is characterized in that the composite material includes filter layer and waterproof layer, described
Waterproof layer includes waterproof coating A and waterproof coating B, and the filter layer forms waterproof layer A/ between waterproof layer A and waterproof layer B
Filter layer/waterproof layer B multilayered structure;Wherein, the filter layer is done using high molecular polymer as raw material with organic solvent or water
Solvent obtains macromolecule polymer solution, is made through electrostatic spinning;The waterproof layer suppress with filter layer compound or straight
It connects and is made coated on filter layer.
2. the composite material of waterproof haze according to claim 1, which is characterized in that the high molecular polymer is poly-
Amide, polyurethane, cellulose acetate, polyacrylonitrile or polyvinyl alcohol, the waterproof layer are acrylic acid glue.
3. the composite material of waterproof haze according to claim 1, which is characterized in that the filter layer with a thickness of
The thickness of 500~600nm, the waterproof coating A and waterproof coating B are 0.1~1mm.
4. the composite material of waterproof haze according to claim 1, which is characterized in that the macromolecule polymer solution
Mass concentration be 10~20wt%.
5. the composite material of waterproof haze according to claim 1, which is characterized in that the organic solvent be ethyl alcohol,
One or more of dimethyl acetamide or n,N-Dimethylformamide.
6. the composite material of waterproof haze according to claim 1, which is characterized in that polyphosphazene polymer in the filter layer
The partial size of polymer beads is 100~200nm.
7. the preparation method of the composite material of waterproof haze according to claim 1-6, which is characterized in that packet
Include following specific steps:
S1. macromolecule polymer solution is put into syringe, syringe needle connects high voltage, and reception device connects low-voltage, high molecular polymerization
Object liquid inventory is controlled by syringe pump;
S2. taylor cone is formed at syringe needle, macromolecule polymer solution overcomes surface tension to form macromolecule under electric field force effect
Polymer fiber, high polymer fiber are collected on the nonwoven layer of movement, deposit high score in non-woven cloth layer surface
Sub- polymeric nanofiber layer forms filter layer;
S3. acrylic acid glue is coated to form waterproof layer, then waterproof layer with filter layer suppress compound, or be directly coated with
In filter layer, waterproof haze composite material is made.
8. the preparation method of the composite material of waterproof haze according to claim 7, which is characterized in that institute in step S1
The voltage value for stating high voltage is 10~20KV, and the voltage value of the low-voltage is -1~-3KV.
9. the preparation method of the composite material of waterproof haze according to claim 7, which is characterized in that institute in step S1
Stating flow is 0.1~1ml/h.
10. application of the composite material of waterproof haze described in any one of claims 1-6 in air purification field.