CN109321013A - A kind of aqueous interfacial agents of revetment - Google Patents
A kind of aqueous interfacial agents of revetment Download PDFInfo
- Publication number
- CN109321013A CN109321013A CN201811212069.5A CN201811212069A CN109321013A CN 109321013 A CN109321013 A CN 109321013A CN 201811212069 A CN201811212069 A CN 201811212069A CN 109321013 A CN109321013 A CN 109321013A
- Authority
- CN
- China
- Prior art keywords
- parts
- revetment
- interfacial agents
- aqueous
- aqueous interfacial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of aqueous interfacial agents of revetment, are composed of the following parts by weight: 36-40 parts of water, 8.5-10 parts of styrene, 5-6 parts of diatomite, 1.5-2 parts of emulsifier, 30-35 parts of butyl acrylate, 3-5 parts of active carbon, 1.5-2 parts of crosslinking agent, different monooctyl ester 16-17 parts, 0.15-0.2 parts of mould inhibitor, 3-3.1 parts of initiator, 0.1-0.15 parts of defoaming agent, 0.2-0.3 parts of thickener, 0.5-1 parts of dispersing agent, 0.5-0.8 parts of multifunctional assistant, 0.1-0.2 parts of disodium hydrogen phosphate.The aqueous interfacial agents of revetment provided by the invention have excellent adhesion strength, cracking resistance, antiseepage, water-tolerant, it is without exception after impregnating 7-10 weeks in water, it is fabulous with cement compatibility, adhesive force is strong, and tensile strength is high, is a kind of environmentally protective aqueous interfacial agents of safe revetment.
Description
Technical field
The invention belongs to technical field of chemical paint, and in particular to a kind of aqueous interfacial agents of revetment.
Background technique
In recent years, with the raising of China's expanding economy and living standards of the people, the propulsion of urbanization process, real estate
It quickly grows, the environmental consciousness and health requirements of people is increasingly enhanced, and the harmful and noxious substance in building decoration materials is to environment
Caused by pollute, influence also to become increasingly conspicuous caused by human health.Harmful substance is mainly derived from building decoration materials release
Formaldehyde out, the pollutants such as ammonia.All building inside and outside wall metopes require to decorate, such as ceramic tile, emulsion paint, lacquer, floor tile etc.
The adhesive force fastness of ornament materials, these ornament materials and base is the biggest problem, therefore develops a kind of peace in the art
The problem of aqueous interfacial agents that loopful is protected are urgent need to resolve.
CN106749875A discloses a kind of self-crosslinking aqueous acrylic emulsion of low ammonia comprising deionized water, acrylic acid
Arrcostab, styrene, acrylamide function monomer, functional acrylic monomer, emulsifier, initiator, pH adjusting agent, oxidant and
Reducing agent.The invention has excellent mechanical performance and adhesive property, but it still has certain ammonia taste, and can not be used as wall
Body binder uses.
Summary of the invention
To solve the above-mentioned problems, the invention proposes a kind of aqueous interfacial agents of revetment.
A kind of aqueous interfacial agents of revetment, are composed of the following parts by weight:
The emulsifier is one or both of odium stearate, lauryl sodium sulfate and calcium dodecyl benzene sulfonate
Mixture.
The initiator is sodium peroxydisulfate.
The multifunctional assistant is AMP-95.
The mould inhibitor is parachlorophenol, 4- chlorine Thymol, 2- methylol ethyl alcohol, 2- methyl -2- methylol ammonia
One or both of base propyl alcohol.
The thickener is polyurethane thickener.
The defoaming agent is poly- silicon substrate ester, dimethicone or polyethers.
The dispersing agent is potassium tripolyphosphate.
Aqueous interfacial agents provided by the invention have excellent water resistance, and alkali resistant, cracking resistance is anti-to saltout, anti-frosting, to substrate
Penetration is strong, and closure is good, good to the adhesive force of bottom and finishing coat, due to containing the sorptive materials such as diatomite and active carbon,
So that the aqueous interfacial agents can also adsorb the pernicious gas (example formaldehyde) in air, it is that a kind of environmentally protective safe revetment is precious
Aqueous interfacial agents.
Specific embodiment
The present invention will be further described combined with specific embodiments below.
Embodiment 1
A kind of aqueous interfacial agents of revetment, are composed of the following parts by weight:
The aqueous revetment interfacial agents of the present embodiment are tested for the property, the results show that the aqueous revetment interfacial agents is anti-
Alkali, cracking resistance, anti-to saltout, anti-frosting is strong to substrate penetration, and closure is good, and water-fast good, the bonding of the aqueous revetment interfacial agents is strong
Degree is 72MPa, and antiseepage is water-fast good, without exception after impregnating in water 5 weeks.
Embodiment 2
A kind of aqueous interfacial agents of revetment, are composed of the following parts by weight:
The aqueous revetment interfacial agents of the present embodiment are tested for the property, the results show that the aqueous revetment interfacial agents is anti-
Alkali, cracking resistance, anti-to saltout, anti-frosting is strong to substrate penetration, and closure is good, water-fast good, adhesion strength 70MPa, and cracking resistance is resistance to
Water is good, without exception after impregnating in water 8 weeks.
Embodiment 3
A kind of aqueous interfacial agents of revetment, are composed of the following parts by weight:
The aqueous revetment interfacial agents of this implementation are tested for the property, the results show that the bonding of the aqueous revetment interfacial agents
Intensity is 75MPa, and antiseepage is water-fast good, without exception after impregnating in water 10 weeks.
Embodiment 4
A kind of aqueous interfacial agents of revetment, are composed of the following parts by weight:
The aqueous revetment interfacial agents of this implementation are tested for the property, the results show that the bonding of the aqueous revetment interfacial agents
Intensity is 79MPa, and antiseepage is water-fast good, without exception after impregnating in water 10 weeks.
Comparative example 1
A kind of aqueous interfacial agents of revetment, are composed of the following parts by weight:
The aqueous revetment interfacial agents of this comparative example are tested for the property, the results show that the aqueous revetment interfacial agents is viscous
Knotting strength is 35MPa, and antiseepage is water-fast good, without exception after impregnating in water 5 weeks.
Comparative example 2
A kind of aqueous interfacial agents of revetment, are composed of the following parts by weight:
The aqueous revetment interfacial agents of this comparative example are tested for the property, the results show that the aqueous revetment interfacial agents is viscous
Knotting strength is 42MPa, weather-proof, water-fast good, without exception after impregnating in water 6 weeks.
Comparative example 3
A kind of aqueous interfacial agents of revetment, are composed of the following parts by weight:
The aqueous revetment interfacial agents of this implementation are tested for the property, the results show that the bonding of the aqueous revetment interfacial agents
Intensity is 25MPa, water-fast good, without exception after impregnating in water 4 weeks.
It can be seen that aqueous revetment interfacial agents dosage of each component of the invention is controlled available within the scope of the present invention
Can excellent aqueous revetment interfacial agents, such as embodiment 1-4, but if some of amounts of components are beyond the scope of this invention,
The aqueous revetment interfacial agents performance that can then make substantially reduces, and such as comparative example 1-3, this illustrates aqueous revetment interface of the invention
Agent mutual cooperation achieves preferable effect.Therefore, aqueous revetment interfacial agents provided by the invention have excellent physical mechanics
Performance, adhesion strength are 70MPa or more, and cracking resistance, antiseepage, water-tolerant is without exception after impregnating 7-10 weeks in water, and due to
Containing diatomite and active carbon, and due to containing by the sorptive materials such as diatomite and active carbon class, so that aqueous revetment circle
Face agent can adsorb the pernicious gas (example formaldehyde) in air, be a kind of aqueous revetment interfacial agents of green safe environmental protection
Aqueous revetment interfacial agents of the invention that the present invention is explained by the above embodiments, but the invention is not limited to upper
Embodiment is stated, that is, does not mean that the present invention must rely on above-described embodiment and could implement, person of ordinary skill in the field answers
This is illustrated, any improvement in the present invention, the addition of equivalence replacement and auxiliary element to each raw material of product of the present invention, specific side
All of which fall within the scope of protection and disclosure of the present invention for selection of formula etc..
Claims (8)
1. a kind of aqueous interfacial agents of revetment, which is characterized in that be composed of the following parts by weight:
2. the aqueous interfacial agents of a kind of revetment according to claim 1, which is characterized in that the emulsifier be odium stearate,
The mixture of one or both of lauryl sodium sulfate and calcium dodecyl benzene sulfonate.
3. the aqueous interfacial agents of a kind of revetment according to claim 1, which is characterized in that the initiator is sodium peroxydisulfate.
4. according to claim 1, which is characterized in that the multifunctional assistant is AMP-95.
5. the aqueous interfacial agents of a kind of revetment according to claim 1, which is characterized in that the mould inhibitor be parachlorophenol,
One or both of 4- chlorine Thymol, 2- methylol ethyl alcohol, 2- methyl -2- methylol propyl alcohol.
6. a kind of aqueous interfacial agents of revetment described in -5 according to claim 1, which is characterized in that the thickener is polyurethane
Thick dose.
7. a kind of aqueous interfacial agents of revetment described in -6 according to claim 1, which is characterized in that the defoaming agent is poly- silicon substrate
Ester, dimethicone or polyethers.
8. the aqueous interfacial agents of a kind of revetment according to claim 1, which is characterized in that the dispersing agent is tripolyphosphate
Potassium.