CN109320203A - A kind of health dark-red enameled pottery and preparation method thereof - Google Patents
A kind of health dark-red enameled pottery and preparation method thereof Download PDFInfo
- Publication number
- CN109320203A CN109320203A CN201811320636.9A CN201811320636A CN109320203A CN 109320203 A CN109320203 A CN 109320203A CN 201811320636 A CN201811320636 A CN 201811320636A CN 109320203 A CN109320203 A CN 109320203A
- Authority
- CN
- China
- Prior art keywords
- dark
- red enameled
- enameled pottery
- health
- purple
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of health dark-red enameled potteries and preparation method thereof, health dark-red enameled pottery production method is made by adding purple black Hunan jade powder in dark-red enameled pottery raw material, including the following steps: the first step forms mud material for dark-red enameled pottery for mixing in dark-red enameled pottery raw material powder and being uniformly mixed after the black Hunan jade powder of the purple of 5~15% weight percent；Mud material for dark-red enameled pottery is fabricated to raw embryo by second step；Third step, in the black Hunan jade powder of purple that raw embryo inner wall uniformly smears 3~8% weight percent；4th step is cooled into dark-red enameled pottery finished product after firing a period of time with 1100 DEG C~1250 DEG C of high temperature, and health dark-red enameled pottery is made of the production method.The present invention has production method simple, and with the microelement of needed by human body in the brewed water body of the dark-red enameled pottery of production, brewed tea or drinks taste are sweet, can promote human acid-base balance, anion is discharged, the advantages that improving the immunity of the human body.
Description
[technical field]
The present invention relates to the technical field of dark-red enameled pottery, the technology of especially a kind of health dark-red enameled pottery and preparation method thereof is led
Domain.
[background technique]
Purple sand ceramics utensil is a kind of stoneware, is the ceramic between pottery and porcelain, it has compact structure, strong
The characteristics of spending larger, thermal shock resistance, good permeability, and being made tea with purple sand tea set is China by a kind of favorite tradition text of people
Change.Boccaro mine for firing zisha earthenware is the rock of clayey silt containing irony, by hydromica and kaolin, quartz, scrap mica
It is formed with mineral compositions such as ironys, can be divided mainly into purple sand, boccaro, black boccaro etc..The production raw material of traditional dark-red enameled pottery is purple
Sand mud, although the boccaro ware that it makes has the characteristics that above-mentioned zisha earthenware, for the modern for focusing on health care,
It is higher for dark-red enameled pottery performance requirement, the heavy metal in water can be eliminated such as dark-red enameled pottery, improves the mouthfeel of water, promoted negative in water
Ion concentration etc., and traditional dark-red enameled pottery is just unable to satisfy these demands.In addition, purple ink Hunan is beautiful, also known as cordierite is quartzy
Biotitite is beautiful, is a kind of horn stone class metamorphic rock, by the cordierite and biotite of 0.1~0.3mm of partial size or so, quartz, lacks
Measure the matrix minerals composition such as muscovite, opaque mineral matter and micro tourmaline, there is blastoporphyritic texture, containing a large amount of silicon,
The elements such as the mineral elements such as potassium, sodium, iron, magnesium and micro calcium, zinc, manganese, titanium, strontium, it is useful and harmless to human body.
Existing some dark-red enameled potteries in the presence of the mouthfeel that cannot improve brewed tea or drinks, in brewed water body it is contained bear from
The problems such as concentration of son, production method and complex formula.
[summary of the invention]
The object of the invention is to solve the problems of the prior art, a kind of health dark-red enameled pottery and its production side are proposed
Method enables to health dark-red enameled pottery simple, and the taste and sweet mouthfeel by the brewed tea of dark-red enameled pottery or drinks is submissive, supplements human body institute
The microelement needed, dark-red enameled pottery are capable of releasing negative ion.
To achieve the above object, the invention proposes a kind of health dark-red enameled pottery production method, in the dark-red enameled pottery raw material
The purple black Hunan jade powder of addition is made.
Preferably, the health dark-red enameled pottery production method including the following steps: the first step, by 5~15% weights
It mixes in dark-red enameled pottery raw material powder and is uniformly mixed after the black Hunan jade powder of the purple of amount percentage and form mud material for dark-red enameled pottery；Second step, will be purple
Sand pot pug is fabricated to raw embryo；Third step, in the black Hunan jade powder of purple that raw embryo inner wall uniformly smears 3~8% weight percent；4th
Step is cooled into dark-red enameled pottery finished product after firing a period of time with 1100 DEG C~1250 DEG C of high temperature.
Preferably, the diametric requirements of the purple black Hunan jade powder are not less than 700 mesh.
Preferably, the dark-red enameled pottery raw material is the purple clay of 81~92% weight percent.
The invention proposes one kind by health dark-red enameled pottery made from above-mentioned health dark-red enameled pottery production method.
Beneficial effects of the present invention: the present invention has dark-red enameled pottery production method simple, and the dark-red enameled pottery of production has good
Health-care effect, with the microelement of needed by human body in brewed water body, brewed tea or drinks taste are sweet, and mouthfeel is soft
It is suitable, it can promote human acid-base balance, discharge anion, eliminate the free radical in water body, improve the immunity of the human body.
Feature and advantage of the invention will be described in detail by embodiment.
[specific embodiment]
Embodiment 1, a kind of health dark-red enameled pottery production method of the present invention, the purple black Hunan jade powder system of addition in dark-red enameled pottery raw material
At, including the following steps: the first step will mix in dark-red enameled pottery raw material powder simultaneously after the black Hunan jade powder of the purple of 8% weight percent
It is uniformly mixed and forms mud material for dark-red enameled pottery；Mud material for dark-red enameled pottery is fabricated to raw embryo by second step；Third step is uniformly applied in raw embryo inner wall
Smear the black Hunan jade powder of purple of 5% weight percent；4th step goes out after being cooled to room temperature after being fired 24 hours with 1150 DEG C of high temperature
Kiln obtains dark-red enameled pottery finished product；Wherein, the diameter of purple black Hunan jade powder is 750 mesh, and dark-red enameled pottery raw material is 87% weight percent
Purple clay.
More than one state the health dark-red enameled pottery that health dark-red enameled pottery production method is made, including following weight percent
The component of ratio: purple ink Hunan jade powder 13%, purple clay 87%.
According to negative ion concentration in JC/T2110-2012 " room air ion concentration test method " standard testing air:
By the health dark-red enameled pottery of dark-red enameled pottery made of the purple clay of a same size model and the present embodiment be placed on two it is identical
Laboratory Module (two Laboratory Module air-anion concentrations are identical under original state) under environment detects two Laboratory Modules after closed 2h
Interior air-anion concentration, the results are shown in Table 1:
Table 1
Embodiment 2, a kind of health dark-red enameled pottery production method of the present invention, the purple black Hunan jade powder system of addition in dark-red enameled pottery raw material
At, including the following steps: the first step will mix in dark-red enameled pottery raw material powder simultaneously after the black Hunan jade powder of the purple of 8% weight percent
It is uniformly mixed and forms mud material for dark-red enameled pottery；Mud material for dark-red enameled pottery is fabricated to raw embryo by second step；Third step is uniformly applied in raw embryo inner wall
Smear the black Hunan jade powder of purple of 7% weight percent；4th step goes out after being cooled to room temperature after being fired 24 hours with 1180 DEG C of high temperature
Kiln obtains dark-red enameled pottery finished product；Wherein, the diameter of purple black Hunan jade powder is 700 mesh, and dark-red enameled pottery raw material is 85% weight percent
Purple clay.
More than one state the health dark-red enameled pottery that health dark-red enameled pottery production method is made, including following weight percent
The component of ratio: purple ink Hunan jade powder 15%, purple clay 85%.
According to negative ion concentration in JC/T2110-2012 " room air ion concentration test method " standard testing air:
By the health dark-red enameled pottery of dark-red enameled pottery made of the purple clay of a same size model and the present embodiment be placed on two it is identical
Laboratory Module (two Laboratory Module air-anion concentrations are identical under original state) under environment detects two Laboratory Modules after closed 2h
Interior air-anion concentration, the results are shown in Table 2:
Table 2
The pH value identification method for the water that dark-red enameled pottery bubbles out: the health dark-red enameled pottery of a diameter 12cm is taken, fills distillation in pot
Water, standing measure afterwards for 24 hours, and the results are shown in Table 3:
Table 3
| Distilled water PH before addition dark-red enameled pottery | Distilled water PH after addition dark-red enameled pottery |
| 5-7 | 7.3-7.8 |
What above-mentioned experimental data range was obtained by 50 repetition test statistics, it follows that health prepared by the present invention
Dark-red enameled pottery has the acid-base property effect for improving water quality really.
The identification method of heavy metal element in the water that dark-red enameled pottery bubbles out: taking the health dark-red enameled pottery of a diameter 12cm, in pot
Drinking water is filled, is measured after standing 12h, the results are shown in Table 4:
Table 4
As shown in Table 4, it can effectively reduce drinking water using health dark-red enameled pottery filling drinking water of the invention and after standing
In harmful trace heavy metal element.
The total dissolved solid value identification method for the water that dark-red enameled pottery bubbles out: taking a diameter is the health dark-red enameled pottery of 12cm,
Distilled water is inside filled, static to measure afterwards for 24 hours, the results are shown in Table 5:
Table 5
| Element | Content | Element | Content |
| H2SiO3 | 80mg/L | Ca | 23mg/L |
| Mg | 8mg/L | Ti | 5.0μg/L |
| Al | 0.8mg/L | Mn | 0.06mg/L |
| K | 17mg/L | Zn | 0.07mg/L |
| Fe | 0.04mg/L | Na | 10mg/L |
As shown in Table 5, the brewed water body of the health dark-red enameled pottery made of the present invention can have more needed by human body
Microelement, improve the immunity of the human body.
It is available by above-mentioned Tables 1 and 2, had using the health dark-red enameled pottery that the present invention makes capable of releasing negative ion
Effect promotes so removing the free radical in water body using the taste of the brewed tea of the health dark-red enameled pottery or drinks sweetness
Human acid-base balance.
The detection data of the table 3- table 5 is obtained referring to GB5749-2006 " Drinking Water examination criteria " inspection
Above-described embodiment is the description of the invention, is not limitation of the invention, after any pair of simple transformation of the present invention
Scheme all belong to the scope of protection of the present invention.
Claims (5)
1. a kind of health dark-red enameled pottery production method, it is characterised in that: add purple black Hunan jade powder in dark-red enameled pottery raw material and be made.
2. health dark-red enameled pottery production method as described in claim 1, it is characterised in that: including the following steps:
The first step is formed mixing in dark-red enameled pottery raw material powder and being uniformly mixed after the black Hunan jade powder of the purple of 5~15% weight percent
Mud material for dark-red enameled pottery；
Mud material for dark-red enameled pottery is fabricated to raw embryo by second step；
Third step, in the black Hunan jade powder of purple that raw embryo inner wall uniformly smears 3~8% weight percent；
4th step is cooled into dark-red enameled pottery finished product after firing a period of time with 1100 DEG C~1250 DEG C of high temperature.
3. health dark-red enameled pottery production method as described in claim 1, it is characterised in that: the diameter of the purple black Hunan jade powder is wanted
It asks not less than 700 mesh.
4. health dark-red enameled pottery production method as described in claim 1, it is characterised in that: the dark-red enameled pottery raw material be 81~
The purple clay of 92% weight percent.
5. a kind of health dark-red enameled pottery as made from Claims 1-4 described in any item health dark-red enameled pottery production methods.