CN109295594A - A kind of preparation process of elastic fabric - Google Patents
A kind of preparation process of elastic fabric Download PDFInfo
- Publication number
- CN109295594A CN109295594A CN201811111709.3A CN201811111709A CN109295594A CN 109295594 A CN109295594 A CN 109295594A CN 201811111709 A CN201811111709 A CN 201811111709A CN 109295594 A CN109295594 A CN 109295594A
- Authority
- CN
- China
- Prior art keywords
- fabric
- wool
- temperature
- elastic
- preparation process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation processes of elastic fabric, and new elastic fabric is made by dyeing, spinning, weaving and finishing process with Sorona fiber blend after graphene is fixed using 80S wool.The product is the new fabric of elastic environmental-protection type, and product is formed by graphene wool/Sorona fiber blend, has the characteristics that wool is soft glutinous smooth, elastic sufficient, is also had good conductive property, stability and wearability.Due to the addition of Sorona fiber, both the primary characteristic of raw material had been remained, the quality of wool is embodied again, the flexibility and skin-friendly of raising fabric, increase drapability and fabric sheen, assign the natural soft feel of fabric, spandex is replaced to have preferable stretching and elastic recovery, cold-proof comfort, dry and comfortable ventilative and washability is good, dangles crease-resistant environment friendly and pollution-free, is the ideal fabric for making high-grade leisure clothes.
Description
Technical field
The invention belongs to place fabric preparation technical field, it is specifically designed a kind of preparation process of elastic fabric.
Background technique
As the fast development with science and technology is continuously improved in people's levels of substance, traditional textile is not obviously able to satisfy people
Primary demand, more and more functional textiles come into being, also more by the favor of consumer.Function textile in addition to
Have the function of that traditional textile possesses warming, beautiful and to be also equipped with some special functions outside covering for example antistatic, conductive, anti-
The functions such as bacterium, uvioresistant.
The finishing functions of wool fabric mainly have flame-proof treatment, fungi-proofing mothproof finish, anti UV finishing and antistatic at present
It arranges, but for conduction, the Revision that generates heat is less, in conjunction with the application of wool, exploitation conduction, fever wool fabric have wide
Development space.Wool antistatic finish at present has satisfactory electrical conductivity essentially by being mixed into or compiling in wool fabric, be woven into
The conductive fiber of energy, or antistatic agent is added and realizes that there are many disadvantages for these means: 1. product wearability are poor: it introduces
Conductive fiber will affect the feel of wool fabric；2. product does not have heating function；3. product stability is poor；It is washable or resistant to bending
Performance is poor, by causing antistatic property to reduce with clear water washing or mechanical stretching, bending；4. lacking preferable elasticity.
Summary of the invention
A kind of preparation process of elastic fabric of the present invention, which comprises the following steps:
1) preliminary treatment process
After wool is handled by oxidizing process, then be placed in the dip dyeing bath of pH2-9.5, toward be added in dip dyeing bath fixed reagent with
Graphene oxide layer dispersion liquid, temperature is warming up to 85 DEG C by the speed with 1-3 DEG C/min in bath, keeps the temperature 30-120min, and
Apply ultrasonic vibration；Then gained graphene oxide wool is impregnated in concentration again is reducing agent in 0.1~8% reducing agent solution
Solution temperature is 70~130 DEG C, restores 10min~180min, is washed 3~5 times with clear water.
Sorona fiber carries out low temperature dyeing with disperse dyes, and holding temperature is controlled at 100~110 DEG C.
When after backwashing, for guarantee strip easily dry, easy grilling, after backwashing bath temperature degree controls in 65 DEG C of 1 slot, 2 slots, 40 DEG C of 3 slot, 4
55 DEG C of slot, using the mixed comb of stamp wool top collocation for being added 40%~50% when mixing comb.
2), spinning process
During recombing, B306 gauge 45mm, 6 times of drawing-offs are taken in each road, and recombing guarantees that fleece is straight, clearly, specifically
Measure: controlling the feed quantity of grease 50mm/ minutes, and 0.3%~1% environmental protection and crude oil agent, preceding spinning various processes are added when silver mixing
In, spun yarn walks 6500 revs/min of compact spinning speed, 650 revs/min of winder, 100~120cN of tension pulley, Temperature and Humidity Control, temperature 30
DEG C, humidity 80%,
3), weaving process
Using the cold slurry agent of macromolecule HG106 warp thread of compounding when beaming, wax is than control 5~10%, and weaving is using import Italy
SMIT rapier loom, 320 ms/min of speed, tension force reduces misdraft in 230N-250N, to guarantee fabric quality, if
It is upper for further adjustments in back rest opening on standby, it is open using isostension, it is 2 grades of back rest level, vertical+2, tension 280N, comprehensive flat
313 degree of time,
Loom knitting technology: upper machine weft density: 194*194 root/10cm, upper gate width 183.5cm, porter 97#, fabric tissue 1/
1 plain weave.
Wherein, further include finishing process:
Open washing connection boil → dry inspection in fixed → braying → bis- boil singe → height wash it is → bis- to boil → absorb water → dry → middle inspection → ripe repairs →
Roll soft → middle inspection → dewing → KD tank steaming → finished product
It is fixed to dry: 160 DEG C, 20m/min, middle overfeeding；It is double to boil: 80 DEG C * 30,1,3,4,6 pressurizations, 200ml HAC, decatizing: pH value control
Tension is not added into machine in 6-7 processed, decatizing nature, and the decatizing of 120s room temperature twice, prevents head tail color difference.
Wherein, in the raw material used, contain 70S wool 60~70%, Sorona fiber 30~40%.
Wherein, the oxidizing process agents useful for same is the hydrogen peroxide of 0.01-40g/L, the peracetic acid of 0.01-40g/L, 0.01-
The peroxy-monosulfate of 30g/L, the potassium permanganate of 0.01-50g/L, the sodium hypochlorite of 0.01-70g/L, 0.01-100g/L sub- chlorine
Sour sodium, available chlorine content be the chlorine water of 0.01-40g/L, any in the dichloroisocyanuric acid of 0.01-40g/L.
Wherein, the fixed reagent is the potassium bichromate of 0.1-30g/L, the aluminum aluminum sulfate of 0.1-30g/L, 0.1-30g/L
The copper sulphate, montmorillonite of aluminum sulfate, 0.1-30g/L of 0.1-30g/L, any in the rare earth of 0.1-30g/L.
Compared with prior art, the invention has the advantages that: the product is the new fabric of elastic environmental-protection type, product by
Graphene wool/Sorona fiber blend forms, and has the characteristics that wool is soft glutinous smooth, elastic sufficient, also has good lead
Electrical property, stability and wearability.Due to the addition of Sorona fiber, the primary characteristic of raw material had not only been remained, but also had been embodied
The quality of wool improves the flexibility and skin-friendly of fabric, increases drapability and fabric sheen, assigns fabric natural soft
Soft feel replaces spandex to have preferable stretching and elastic recovery, and cold-proof comfort, dry and comfortable ventilative and washability is good, pendency
It is crease-resistant environment friendly and pollution-free, it is the ideal fabric for making high-grade leisure clothes.
Specific embodiment
Below by embodiment, the technical solutions of the present invention will be further described.
Embodiment: a kind of preparation process of elastic fabric sequentially includes the following steps:
1) preliminary treatment process
The processing of wool initial oxidation method, the oxidizing process agents useful for same are the mistake second of the hydrogen peroxide of 0.01-40g/L, 0.01-40g/L
Acid, the peroxy-monosulfate of 0.01-30g/L, the potassium permanganate of 0.01-50g/L, the sodium hypochlorite of 0.01-70g/L, 0.01-
The sodium chlorite of 100g/L, available chlorine content are the chlorine water of 0.01-40g/L, appointing in the dichloroisocyanuric acid of 0.01-40g/L
One is a kind of, with this loose wool structure, convenient for the infiltration of graphene, after oxidative treatment, then is placed in the dip dyeing bath of pH2-9.5
In, fixed reagent and graphene oxide layer dispersion liquid are added into dip dyeing bath, using fixed reagent in wool protein and oxidation
By establishing hydrogen bond, Van der Waals force, coordination bonding force etc. between graphene, by the comprehensive function of a variety of binding mechanisms, stone will be aoxidized
Black alkene anchors on wool product, the fixation reagent be the potassium bichromate of 0.1-30g/L, 0.1-30g/L aluminum aluminum sulfate,
The copper sulphate of 0.1-30g/L, the aluminum sulfate of 0.1-30g/L, the montmorillonite of 0.1-30g/L, 0.1-30g/L rare earth in any
One kind, this fixing step promote fastness by complexing, and temperature is warming up to 85 DEG C by the speed with 1-3 DEG C/min in bath,
30-120min is kept the temperature, and is continuously applied ultrasonic vibration during entire dip dyeing, this infects step and strengthens physical action, mentions
The diffusion kinetic energy of graphene fuel is risen, and promotes its penetration；Then gained graphene oxide wool is impregnated in concentration again is
In 0.1~8% reducing agent solution, reducing agent solution temperature is 70~130 DEG C, restores 10min~180min, with clear water washing 3
~5 times, graphene oxide is reduced by graphene with this, to possess electric conductivity.
Sorona fiber carries out low temperature dyeing with disperse dyes, and soaking time is controlled at 110 DEG C, guarantee fiber color yield,
Dyefastness and special elasticity.
When after backwashing, for guarantee strip easily dry, easy grilling, after backwashing bath temperature degree controls at 65 DEG C of 1 slot, 2,3 40 DEG C of slots, 4 slots
55 DEG C, machine wool top reaches refreshing, clean, suitable feel under after backwashing.Using the mixed comb of stamp wool top collocation for being added 40%, color when mixed comb
Pure, finished product face is clearly fine and smooth.
2), spinning process
During recombing, to reduce fibre damage, convenient for combing, close setting, small drawing-off (B306 gauge are taken in each road
45mm, 6 times of drawing-offs), recombing guarantees that fleece is straight, and clearly, concrete measure: controlling the feed quantity of grease 50mm/ minutes, silver mixing
When be added 0.3%~1% environmental protection and crude oil agent, preceding spinnings various processes are all made of small tension receiving coil, the damage to reduce fiber, guarantee
Spinning efficiency spinning process follows light feeding, and small drawing-off, the principle of low speed: spun yarn walks 6500 revs/min of compact spinning speed, winder
650 revs/min, tension pulley 100cN, Temperature and Humidity Control, 30 DEG C of temperature, humidity 80%, resultant yarn strand is uniformly bright and clean, and filoplume is few.
3), weaving process
Ensure that yarn path is smooth when warping, piece yarn tension is uniform, prevents cloth cover to be produced from and hangs.The height of compounding is used when beaming
The cold slurry agent of molecule HG106 warp thread, wax improve the wearability docile filoplume of yarn than control 8%.
Weaving uses import Italy SMIT rapier loom, and 320 ms/min of speed, tension force is reduced in 230N-250N
Misdraft is open upper for further adjustments in the back rest in equipment, is open using isostension to guarantee fabric quality, (back rest water
2 grades flat, vertical+2 313 degree of tension 280N heald level times), face lines is clearly fine and smooth, and grey quality is good.
Loom knitting technology: upper machine weft density: 194*194 root/10cm, upper gate width 183.5cm, porter 97#, fabric group
Knit 1/1 plain weave.
Further, further include finishing process:
Open washing connection boil → dry inspection in fixed → braying → bis- boil singe → height wash it is → bis- to boil → absorb water → dry → middle inspection → ripe repairs →
Roll soft → middle inspection → dewing → KD tank steaming → finished product
It is the Comfortable elastic and softness, the feel of exquisiteness for meeting Human Physiology demand, dyeing and finishing technology that this kind is mainly outstanding
Open washing of singing after walking connection boils strengthening process route (usual processing route is not walked open washing connection and boiled, and double boil only is walked), each road broadwise Xiao Zhang
Power prevents from destroying elastic elongation, the gloss of prominent fabric, soft.It is fixed to dry: 160 DEG C of * 20m/min, middle overfeeding；It is double to boil: 80
DEG C * 30,1,3,4,6 pressurizations, 200ml HAC, decatizing: WPF 7# technique turns around to turn over, (control stress point: wet cloth sizing, enhancing
Wearability, pH value control 6-7, and tension is not added into machine in decatizing nature, and the decatizing of 120s room temperature twice, prevents head tail
Color difference).
It improves crabbing temperature and carries out abundant pre-setting, reduce setting temperature and prevent red change, not only guarantee fabric dimensionally stable
Property, and not discoloration.Final finishing pass through low-temperature shaped arrangement, make fabric have superior elasticity, splendid wrinkle resistance, comfortably
Feel, pure color wearability it is excellent, added value of product is high.
Preferably, in the raw material used, contain 70S wool 60~70%, Sorona fiber 30~40%.
For fiber properties, Sorona stock-dye uses 110 DEG C of low temperature dyeings of hollow sphere, keeps dye molecule fully penetrated
To fibrous inside, it is adsorbed onto fiber inner surface, guarantees that coloured light is accurate, is sufficiently unclogged and readjusted after Sorona stock-dye with stamp wool top mixed
It closes, is uniformly mixed each component fiber, pure color.
Final finishing workshop section is mainly around discoloration and elastic selection process route, for the easily red change of high-temperature shaping, Low-Temperature Size
Elastic effect is not achieved in stability difference, singes after singing again after taking each road broadwise small tension receiving coil, open washing connection to boil to firing technique, boils
At 100 DEG C or so, softening agent usage amount is reduced to 1% for temperature control, and setting temperature control is very regular at 160 ± 5 DEG C
Process route is managed, to guarantee the pure and good wearability of fabric color.
As described below is only the preferred embodiment of the present invention, it should be understood that for the ordinary skill people of the art
For member, under the premise of not departing from the principle of the present invention, other improvements and modification can also be made, it all should be by claims
In identified protection scope.
Claims (8)
1. a kind of preparation process of elastic fabric, which is characterized in that comprising steps of
Preliminary treatment process
After wool is handled by oxidizing process, then be placed in the dip dyeing bath of pH2-9.5, toward be added in dip dyeing bath fixed reagent with
Graphene oxide layer dispersion liquid, temperature is warming up to 85 DEG C by the speed with 1-3 DEG C/min in bath, keeps the temperature 30-120min, and
Apply ultrasonic vibration；Then gained graphene oxide wool is impregnated in concentration again is reducing agent in 0.1~8% reducing agent solution
Solution temperature is 70~130 DEG C, restores 10min~180min, is washed 3~5 times with clear water.
2. Sorona fiber carries out low temperature dyeing with disperse dyes, holding temperature is controlled at 100~110 DEG C.
3. when after backwashing, easily drying for guarantee strip, easy grilling, after backwashing bath temperature degree is controlled in 65 DEG C of 1 slot, 2 slots, 40 DEG C of 3 slot, 4 slots
55 DEG C, using the mixed comb of stamp wool top collocation for being added 40%~50% when mixing comb.
4.2), spinning process
During recombing, B306 gauge 45mm, 6 times of drawing-offs are taken in each road, and recombing guarantees that fleece is straight, clearly, specifically
Measure: controlling the feed quantity of grease 50mm/ minutes, and 0.3%~1% environmental protection and crude oil agent, preceding spinning various processes are added when silver mixing
In, spun yarn walks 6500 revs/min of compact spinning speed, 650 revs/min of winder, 100~120cN of tension pulley, Temperature and Humidity Control, temperature 30
DEG C, humidity 80%,
3), weaving process
Using the cold slurry agent of macromolecule HG106 warp thread of compounding when beaming, wax is than control 5~10%, and weaving is using import Italy
SMIT rapier loom, 320 ms/min of speed, tension force reduces misdraft in 230N-250N, to guarantee fabric quality, if
It is upper for further adjustments in back rest opening on standby, it is open using isostension, it is 2 grades of back rest level, vertical+2, tension 280N, comprehensive flat
313 degree of time,
Loom knitting technology: upper machine weft density: 194*194 root/10cm, upper gate width 183.5cm, porter 97#, fabric tissue 1/
1 plain weave.
5. a kind of preparation process of elastic fabric according to claim 1, which is characterized in that further include finishing process:
Open washing connection boil → dry inspection in fixed → braying → bis- boil singe → height wash it is → bis- to boil → absorb water → dry → middle inspection → ripe repairs →
Roll soft → middle inspection → dewing → KD tank steaming → finished product
It is fixed to dry: 160 DEG C, 20m/min, middle overfeeding；It is double to boil: 80 DEG C * 30,1,3,4,6 pressurizations, 200ml HAC, decatizing: pH value control
Tension is not added into machine in 6-7 processed, decatizing nature, and the decatizing of 120s room temperature twice, prevents head tail color difference.
6. a kind of preparation process of elastic fabric according to claim 1, which is characterized in that in the raw material used, contain
There are 70S wool 60~70%, Sorona fiber 30~40%.
7. a kind of preparation process of elastic fabric according to claim 1, which is characterized in that the oxidizing process agents useful for same is
The hydrogen peroxide of 0.01-40g/L, the peracetic acid of 0.01-40g/L, the peroxy-monosulfate of 0.01-30g/L, 0.01-50g/L Gao Meng
Sour potassium, the sodium hypochlorite of 0.01-70g/L, the sodium chlorite of 0.01-100g/L, available chlorine content be 0.01-40g/L chlorine water,
It is any in the dichloroisocyanuric acid of 0.01-40g/L.
8. a kind of preparation process of elastic fabric according to claim 1, which is characterized in that the fixation reagent is 0.1-
The potassium bichromate of 30g/L, the aluminum aluminum sulfate of 0.1-30g/L, the copper sulphate of 0.1-30g/L, the aluminum sulfate of 0.1-30g/L, 0.1-
It is any in the montmorillonite of 30g/L, the rare earth of 0.1-30g/L.